阅读说明：本技术 一种新型降低收卷暴筋的大分切系统及工艺 (Novel large slitting system and process for reducing rolling violent ribs ) 是由 赵洪亮 翁星星 沈亚定 贡晶晶 于 2020-11-19 设计创作，主要内容包括：本发明公开一种新型降低收卷暴筋的大分切系统及工艺。包括放卷、展平系统、分切系统、收卷压力控制系统和收卷卷芯；展平系统包括过辊一和展平辊；隔膜在展平辊上两个切点之间圆弧的弧高为5-15mm、包角为20-45°；分切系统包括切刀辊、计速辊和过辊二；收卷压力控制系统为收卷压辊,收卷压辊包括内芯和包裹在其外的橡胶层；收卷压辊直径为100-120mm,橡胶层表面设置有外展的双螺旋结构；收卷压辊与收卷卷芯滚动连接。工艺：应用大分切系统；设置收卷卷芯的收卷速度为80-120m/min、收卷张力为5-8N/m；设置放卷张力为收卷张力的1-2倍；设置收卷压力为收卷张力的1.5-4倍。通过本发明的新型降低收卷暴筋的大分切系统及工艺收卷暴筋明显降低,实现大分切收卷较高的一次良品率。(The invention discloses a novel large slitting system and a novel large slitting process for reducing rolling rib violence. The device comprises an unreeling system, a flattening system, a slitting system, a reeling pressure control system and a reeling core; the flattening system comprises a first passing roller and a flattening roller; the arc height of the circular arc of the diaphragm between two tangent points on the flattening roller is 5-15mm, and the wrap angle is 20-45 degrees; the slitting system comprises a cutter roller, a speed counting roller and a second passing roller; the rolling pressure control system is a rolling compression roller, and the rolling compression roller comprises an inner core and a rubber layer wrapped outside the inner core; the diameter of the winding compression roller is 100-120mm, and the surface of the rubber layer is provided with an outward-extending double-spiral structure; the rolling compression roller is connected with the rolling winding core in a rolling way. The process comprises the following steps: applying a large slitting system; setting the winding speed of a winding core to be 80-120m/min and the winding tension to be 5-8N/m; setting the unreeling tension to be 1-2 times of the reeling tension; the winding pressure is set to be 1.5-4 times of the winding tension. The novel large slitting system and the novel process for reducing the rolling rib bursting provided by the invention have the advantages that the rolling rib bursting is obviously reduced, and the high one-time yield of large slitting rolling is realized.)

1. A novel large slitting system for reducing winding rib violence is characterized by comprising an unwinding (1), a flattening system, a slitting system, a winding pressure control system and a winding core (10);

the unreeling device (1) is used for releasing the diaphragm (2) and enabling the diaphragm to enter a subsequent system;

the flattening system comprises a plurality of first passing rollers (3) and flattening rollers (4); the arc height of the circular arc of the diaphragm (2) between two tangent points on the flattening roller (4) is 5-15 mm; the wrap angle of the diaphragm (2) between two tangent points on the flattening roller (4) is 20-45 degrees; the flattening roller (4) is made of rubber, and the Shore hardness of the rubber is 60-65 degrees;

the slitting system comprises a cutter roller (5), a speed counting roller (6) and a plurality of second passing rollers (7);

the rolling pressure control system is a rolling press roller (8); the winding press roller (8) comprises an inner core (9) and a rubber layer (11) wrapped outside the inner core (9); the diameter of the winding compression roller (8) is 100-120mm, and the surface of the rubber layer (11) is provided with an outward-extending double-spiral structure (12); the winding compression roller (8) is in rolling connection with the winding core (10).

2. A novel large slitting system for reducing rolling violent ribs according to claim 1, characterized in that the arc height of the circular arc of the diaphragm (2) between the two tangent points on the flattening roll (4) is 8-10 mm; the wrap angle of the diaphragm (2) between two tangent points on the flattening roll (4) is 30-35 degrees.

3. The novel large slitting system for reducing rolling rib violence as claimed in claim 1, wherein the diameter of the rolling compression roller (8) is 110-115 mm.

4. The novel large slitting system capable of reducing rolling ribs according to claim 1, wherein the rubber layer (11) is made of rubber materials with Shore hardness of 60-65 degrees.

5. A novel large slitting system for reducing rolling rib scrap according to claim 1 wherein the pitch of the spirals of the double spiral structure (12) is between 80 and 120 mm.

6. The novel large slitting system for reducing rolling rib violence of claim 1, wherein the width of the spiral groove of the double-spiral structure (12) is 3-5 mm.

7. A novel large slitting system for reducing rolling rib scrap according to claim 1 wherein the double helix structure (12) has a helix groove depth of 3-5 mm.

8. A novel large slitting process for reducing rolling rib violence is characterized in that the large slitting system of any one of claims 1-7 is applied to the process, and the novel large slitting process specifically comprises the following steps:

(1) as the large slitting system operates, the unreeling (1) starts to release the diaphragm (2);

(2) the diaphragm (2) sequentially enters the subsequent flattening system, the slitting system and the winding pressure control system and is finally wound on the winding core (10);

(3) setting the winding speed of the winding core (10) when the diaphragm (2) is wound to be 80-120m/min, and setting the winding core (10) to the winding tension F of the diaphragm (2)_OIs 5-8N/m;

(4) set the unwinding tension F when the unwinding (1) releases the diaphragm (2)₁Is the winding tension F_O1-2 times of the total weight of the composition;

(5) setting the winding pressure F of the winding compression roller (8) to the winding core (10)₂Is the winding tension F_O1.5-4 times of the total weight of the composition.

Technical Field

The invention relates to the technical field of diaphragms, in particular to a novel large slitting system and a novel large slitting process for reducing rolling rib violence.

Background

The large splitting machine is a device for splitting and winding the base film produced by the main line, and the final winding effect of the diaphragm can be directly influenced by the process design of large splitting. Improper process design can cause winding rib bumping during winding of the diaphragm, severe dead wrinkles (which cannot be completely flattened after a certain tension is applied) can occur at rib bumping positions, the defect of the diaphragm can not only cause the problem of missing coating during subsequent ceramic coating, but also cause rib bumping or dead wrinkles during slitting of a final finished product, and equipment faults and poor product winding can occur during winding of a battery by a battery manufacturer. The structural differences of large splitting machines are not very large, and the splitting capacity of the large splitting machines directly influences the final yield of the diaphragm. The problem of the muscle is violently existed in present big cutting machine cutting, rolling, not only seriously influences the final yields of diaphragm production, more probably leads to the customer service problem behind the product delivery customer simultaneously.

Therefore, the rolling flatness of the large slitting is improved, the rolling rib breaking of the large slitting is reduced, the yield of the final products of the large slitting is improved, and a new technological method is needed to be matched with the slitting equipment to ensure higher yield of the final products.

Disclosure of Invention

The invention aims to provide a novel large slitting system and a novel large slitting process for reducing rolling violent ribs, and the large slitting system and the large slitting process are improved, and the design matching and the adjustment of the large slitting process are adopted to realize the high primary yield of large slitting rolling; by the novel large slitting system and the novel large slitting process for reducing the rolling rib bursting, the rolled diaphragm is slit, the rolling rib bursting is obviously reduced, and the problems of poor excessive rolling rib bursting and poor dead wrinkle of the diaphragm are solved.

The invention is realized by the following technical scheme:

a novel large slitting system for reducing rolling violent ribs is characterized by comprising an unwinding system, a flattening system, a slitting system, a rolling pressure control system and a rolling winding core which are sequentially arranged; the winding core is used for winding the diaphragm and finally winding the diaphragm on the winding core;

the unwinding is used for releasing the diaphragm and enabling the diaphragm to enter a subsequent system;

the flattening system comprises a plurality of first passing rollers and flattening rollers; the arc height of the circular arc of the diaphragm between the two tangent points on the flattening roller is 5-15 mm; the wrap angle of the diaphragm between two tangent points on the flattening roller is 20-45 degrees; the flattening roller is made of rubber, and the Shore hardness of the rubber is 60-65 degrees;

the slitting system comprises a cutter roller, a speed counting roller and a plurality of second passing rollers;

the rolling pressure control system is a rolling compression roller; the winding press roller comprises an inner core and a rubber layer wrapped outside the inner core; the diameter of the winding compression roller is 100-120mm, and the surface of the rubber layer is provided with an outward-extending double-spiral structure; the winding compression roller is connected with the winding core in a rolling manner. Specifically, the unreeling is used for releasing the diaphragm and enabling the diaphragm to enter a subsequent system, namely the unreeling releases the diaphragm to be cut at a certain speed and enables the diaphragm to enter the subsequent system, so that the diaphragm is enabled to be flatly fed into the roller, and meanwhile, the tension change smoothness of the diaphragm after unreeling is ensured; the diaphragm enters a flattening system, and the flattening system adopts a flattening roller with a certain arc shape to control the flatness of the diaphragm surface; the cutting knife roller in the slitting system splits the diaphragm, and then the diaphragm is wound on the winding core through the winding pressure control system (namely the winding compression roller), wherein the winding compression roller presses the diaphragm on the winding core under certain pressure, so that the smooth discharge of air between the small mother winding layers after slitting is ensured, the winding is smooth, and the violent ribs are reduced. Preferably, the rubber layer is provided with an outward-extending double-spiral structure, so that the diaphragm can be further flattened during rolling, and the rib breaking is reduced. Preferably, the inner core is an aluminum inner core. When the membrane is rolled, the double helix expands towards two sides (namely, the double helix expands outwards), and the membrane is flattened.

Further, the arc height of the circular arc of the diaphragm between two tangent points on the flattening roller is 8-10 mm; the wrap angle of the diaphragm between two tangent points on the flattening roller is 30-35 degrees. Specifically, the diaphragm can pass through the flattening roller and then enter a subsequent slitting system after being released through unreeling, the diaphragm can form two tangent points with the flattening roller after passing through the flattening roller, the two tangent points are located on the flattening roller, the arc height of an arc surface formed between the two tangent points on the flattening roller is 8-10 mm (namely, referred to as middle height in the industry), and the arc surface is not the rest of arc surfaces on the flattening roller but is the surface in contact with the diaphragm. The wrap angle of the flattening roll is an included angle formed by the circle center of the flattening roll and a connecting line of two tangent points.

Further, the diameter of the winding compression roller is 110-115 mm.

Further, the rubber layer is made of a rubber material with the Shore hardness of 60-65 degrees.

Further, the spiral pitch of the double-spiral structure is 80-120 mm.

Further, the width of the spiral groove of the double-spiral structure is 3-5 mm.

Further, the depth of the spiral groove of the double-spiral structure is 3-5 mm.

The utility model provides a novel reduce big technology of cutting of rolling violence muscle, foretell big system of cutting is applied to this technology, specifically includes following step:

(1) as the large slitting system operates, unwinding starts to release the diaphragm;

(2) the diaphragm sequentially enters the subsequent flattening system, the slitting system and the winding pressure control system and is finally wound on the winding core;

(3) setting the winding speed of the winding core when the diaphragm is wound to be 80-120m/min, and setting the winding tension F of the winding core to the diaphragm_OIs 5-8N/m; by setting certain parameters, the slitting is ensuredThe rear diaphragm can be tightened and leveled before being wound, and enters a winding core for leveling winding;

(4) set up unreel when unreeling release diaphragm unreel tension F₁Is the winding tension F_O1-2 times of the total weight of the composition; will unreel tension F₁And the winding tension F_OIs denoted as K₁I.e. K₁＝F₁/F_O×100％＝100％-200％；

(5) Setting the winding pressure F of the winding roll core of the winding compression roller pair₂Is the winding tension F_O1.5-4 times of the total weight of the composition. The winding pressure F₂And the winding tension F_OIs denoted as K₂I.e. K₂＝F₂/F_O×100％＝150％-400％。

By using the novel large slitting process for reducing the rolled rib breaking, the average reject ratio of the rib breaking after the large slitting and rolling can be controlled to be below 10%. The setting of cutting winding core speed is mainly used for the terminal surface regularity of supplementary assurance rolling, and is not having obvious influence to the rolling rib blasting harmfully of membrane book in the settlement scope. When the rolling rib is broken, K is added₁The value is adjusted to be small (to make the initial unwinding tension F of the diaphragm₁And final membrane wrap tension F_OThe change between the two steps is reduced, so that the initial → final tension change is smooth, and the rolling rib breaking caused by the fact that the membrane cannot be flattened due to too fast tension change caused by too large tension change is avoided; k₂The value is adjusted to be larger (the rolling pressure F of the rolling compression roller is enabled₂Increasing, when the diaphragm has a certain thickness difference or excessive air exists between the diaphragm layers, the diaphragm is flattened at the rolling position while the excessive air is extruded out, and the final flatness of the rolling is ensured); f₀The diaphragm at the winding core is adjusted to be small (the diaphragm at the winding core becomes loose to a certain extent, and the winding press roller can flatten the diaphragm in a loose state, otherwise, the diaphragm is too tight, the press roller cannot flatten longitudinal stripes or streaks, and a rib is easy to be exposed); the priority adjustment order is K₁→K₂→F₀Firstly, the smoothness of tension change of the diaphragm in the whole process from unreeling to reeling is ensured on the whole, sudden change is avoided, and then the diaphragm is enlargedThe pressure flattens the lines or the slack parts of the diaphragm, and if the tension is too tight, the rolling tension F needs to be reduced finally₀The diaphragm is loosened to a certain degree, so that the diaphragm is flattened by the rolling compression roller during final rolling, and the rolling smoothness is ensured.

Specifically, the novel large slitting process for reducing rolling violent ribs comprises the following steps:

(1) starting the large slitting system to operate during production and processing, and then starting unwinding to release the diaphragm;

(2) after being released from unreeling, the diaphragm firstly enters a first roller in the flattening system, passes through the flattening roller and then enters the slitting system from the other first rollers; the diaphragm is cut by a cutter roller in the cutting system and then sequentially passes through a speed counting roller and a second roller, the cut diaphragm separately enters different winding compression rollers, is further pressed and flattened by the winding compression rollers, and finally the cut diaphragm is wound on a winding core;

(3) setting the winding speed of the winding core when the diaphragm is wound to be 80-120m/min, and setting the winding tension F of the winding core to the diaphragm_OIs 5-8N/m;

(4) set up unreel when unreeling release diaphragm unreel tension F₁Is the winding tension F_O1-2 times of the total weight of the composition;

(5) setting the winding pressure F of the winding roll core of the winding compression roller pair₂Is the winding tension F_O1.5-4 times of the total weight of the composition.

The invention has the beneficial effects that:

(1) the novel large slitting system and process for reducing rolling violent ribs are characterized in that the unwinding tension F of large slitting is set₁And a winding tension F₀And setting the winding pressure F of the winding pressure roller₂And a winding tension F₀The proportion of (3) ensures the change trend of the diaphragm from unreeling to final reeling tension, and meanwhile, the specification and style of the reeling compression roller (rubber roller) are set, and the specification and the use mode of the flattening roller are adjusted to ensure that the diaphragm is fully flattened in the whole process from unreeling to reeling, so that the diaphragm reeling tension device can ensure that the diaphragm reeling tension is greatly improvedThe flatness of the rolled diaphragm reduces the generation of bad winding rib bursting of the diaphragm, and improves the final yield of large-scale slitting production.

(2) By the novel large slitting system and the novel large slitting process for reducing the rolling violent ribs, provided by the invention, the rolled diaphragm is slit, the rolling violent ribs are obviously reduced, the problems of poor high violent rib rolling of the diaphragm and poor dead wrinkle of the diaphragm are solved, and the high primary yield of large slitting rolling is realized.

Drawings

In order to more clearly illustrate the technical solutions of the embodiments of the present invention, the drawings needed to be used in the description of the embodiments will be briefly introduced below, and it is obvious that the drawings in the following description are only some embodiments of the present invention, and it is obvious for those skilled in the art to obtain other drawings based on these drawings without creative efforts.

FIG. 1 is a schematic view of a novel large slitting system for reducing rolling rib violence according to the present invention;

fig. 2 is a schematic structural diagram of a rolling compression roller in the novel large slitting system for reducing rolling rib exposure.

In the figure: 1 unreeling, 2 diaphragms, 3 roll passing rollers I, 4 flattening rollers, 5 cutter rollers, 6 speed counting rollers, 7 roll passing rollers II, 8 rolling compression rollers, 9 inner cores, 10 rolling winding cores, 11 rubber layers and 12 double-spiral structures.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the drawings in the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. The following description of at least one exemplary embodiment is merely illustrative in nature and is in no way intended to limit the invention, its application, or uses. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

Example 1

As shown in fig. 1-2, a novel large slitting system for reducing winding rib bursting comprises an unwinding 1, a flattening system, a slitting system, a winding pressure control system and a winding core 10, wherein the unwinding 1, the flattening system, the slitting system, the winding pressure control system and the winding core are used for releasing a diaphragm 2 and enabling the diaphragm to enter a subsequent system; the flattening system comprises a plurality of first passing rollers 3 and flattening rollers 4; the arc height of the circular arc of the diaphragm 2 between the two tangent points on the flattening roller 4 is 5mm (namely, the middle height is 5 mm); the wrap angle of the diaphragm 2 between the two tangent points on the nip roll 4 is 20 °; the flattening roller 4 is made of rubber, and the Shore hardness of the rubber is 60 degrees; the slitting system comprises a cutter roller 5, a speed counting roller 6 and a plurality of second passing rollers 7; the rolling pressure control system is a rolling compression roller 8; the winding press roller 8 comprises an inner core 9 and a rubber layer 11 wrapped outside the inner core 9; the diameter of the winding compression roller 8 is 100 mm, the surface of the rubber layer 11 is provided with an outward-extending double-spiral structure 12, the spiral distance is 90 mm, the width of a spiral groove is 3 mm, and the depth of the groove is 4 mm; the rolling compression roller 8 is in rolling connection with the rolling winding core 10.

The utility model provides a novel reduce big technology of cutting of rolling violence muscle, foretell big system of cutting is applied to this technology, specifically includes following step:

(1) during production, the large slitting system is started to operate, and the unwinding 1 starts to release the diaphragm 2;

(2) after being released from the unreeling 1, the diaphragm 2 firstly enters a first roller 3 in the flattening system, passes through a flattening roller 4 and then enters the slitting system from the other first rollers 3; the diaphragm 2 is cut by a cutter roller 5 in the cutting system and then sequentially passes through a speed counting roller 6 and a second passing roller 7, the cut diaphragm 2 is separately fed into different winding compression rollers 8, the diaphragm is further pressed and flattened by the winding compression rollers (namely rubber rollers 11), and finally the cut diaphragm 2 is wound on a winding core 10;

(3) setting the winding speed of the winding core 10 when winding the diaphragm 2 is 100m/min, and setting the winding tension F of the winding core 10 to the diaphragm 2_OIs 5N/m;

(4) set the unwinding tension F₁And a winding tension F_OThe proportion of (A) is 100%;

(5) setting the winding pressure F₂And a winding tension F_OThe proportion of (B) is 150%.

The final defective rate of winding and rib breaking is 16.7 percent

Example 2

As shown in fig. 1-2, a novel large slitting system for reducing winding rib bursting comprises an unwinding 1, a flattening system, a slitting system, a winding pressure control system and a winding core 10, wherein the unwinding 1, the flattening system, the slitting system, the winding pressure control system and the winding core are used for releasing a diaphragm 2 and enabling the diaphragm to enter a subsequent system; the flattening system comprises a plurality of first passing rollers 3 and flattening rollers 4; the arc height of the circular arc of the diaphragm 2 between the two tangent points on the flattening roller 4 is 10mm (namely 10mm higher); the wrap angle of the diaphragm 2 between the two tangent points on the nip roll 4 is 30 °; the flattening roller 4 is made of rubber, and the Shore hardness of the rubber is 65 degrees; the slitting system comprises a cutter roller 5, a speed counting roller 6 and a plurality of second passing rollers 7; the rolling pressure control system is a rolling compression roller 8; the winding press roller 8 comprises an inner core 9 and a rubber layer 11 wrapped outside the inner core 9; the diameter of the winding compression roller 8 is 110 mm, the surface of the rubber layer 11 is provided with an outward-extending double-spiral structure 12, the spiral distance is 90 mm, the width of a spiral groove is 3 mm, and the depth of the groove is 4 mm; the rolling compression roller 8 is in rolling connection with the rolling winding core 10.

The utility model provides a novel reduce big technology of cutting of rolling violence muscle, foretell big system of cutting is applied to this technology, specifically includes following step:

(1) during production, the large slitting system is started to operate, and the unwinding 1 starts to release the diaphragm 2;

(2) after being released from the unreeling 1, the diaphragm 2 firstly enters a first roller 3 in the flattening system, passes through a flattening roller 4 and then enters the slitting system from the other first rollers 3; the diaphragm 2 is cut by a cutter roller 5 in the cutting system and then sequentially passes through a speed counting roller 6 and a second passing roller 7, the cut diaphragm 2 is separately fed into different winding compression rollers 8, the diaphragm is further pressed and flattened by the winding compression rollers (namely rubber rollers 11), and finally the cut diaphragm 2 is wound on a winding core 10;

(3) setting the winding speed of the winding core 10 when winding the diaphragm 2 is 100m/min, and setting the winding tension F of the winding core 10 to the diaphragm 2_OIs 5N/m;

(4) set the unwinding tension F₁And a winding tension F_OThe proportion of (A) is 100%;

(5) setting the winding pressure F₂And a winding tension F_OThe proportion of (A) is 400%.

The final defective rate of winding and rib breaking is 0 percent

Example 3

Unwinding tension F₁And a winding tension F_OThe proportion of (A) is 200%; winding pressure F₂And a winding tension F_OThe other conditions were the same as in example 2; the final defective rate of winding and rib breaking is 0%.

Example 4

Unwinding tension F₁And a winding tension F_OThe proportion of (A) is 200%; winding pressure F₂And a winding tension F_OThe other conditions were the same as in example 2; the final defective rate of winding and rib breaking is 0%.

Example 5

Winding tension F_OIs 8N/m, and the unwinding tension F₁And a winding tension F_OThe proportion of (A) is 100%; winding pressure F₂And a winding tension F_OThe other conditions were the same as in example 2 except that the ratio of (A) to (B) was 150%.

The final defective rate of winding and rib breaking is 0 percent

Example 6

Unwinding tension F₁And a winding tension F_OThe proportion of (A) is 100%; winding pressure F₂And a winding tension F_OThe other conditions were the same as in example 5; the final defective rate of winding and rib breaking is 0%.

Example 7

Unwinding tension F₁And a winding tension F_OThe proportion of (A) is 200%; winding pressure F₂And a winding tension F_OThe other conditions were the same as in example 5; the final defective rate of winding and rib breaking is 0%.

Example 8

Unwinding tension F₁And a winding tension F_OThe proportion of (A) is 200%; winding pressure F₂And a winding tension F_OThe other conditions were the same as in example 5; the final defective rate of winding and rib breaking is 16.7%.

Example 9

As shown in fig. 1-2, a novel large slitting system for reducing winding rib bursting comprises an unwinding 1, a flattening system, a slitting system, a winding pressure control system and a winding core 10, wherein the unwinding 1, the flattening system, the slitting system, the winding pressure control system and the winding core are used for releasing a diaphragm 2 and enabling the diaphragm to enter a subsequent system; the flattening system comprises a plurality of first passing rollers 3 and flattening rollers 4; the arc height of the circular arc between the two tangent points of the diaphragm 2 on the flattening roller 4 is 15 mm; the wrap angle of the diaphragm 2 between the two tangent points on the nip roll 4 is 35 °; the flattening roller 4 is made of rubber, and the Shore hardness of the rubber is 60 degrees; the slitting system comprises a cutter roller 5, a speed counting roller 6 and a plurality of second passing rollers 7; the rolling pressure control system is a rolling compression roller 8; the winding press roller 8 comprises an inner core 9 and a rubber layer 11 wrapped outside the inner core 9; the diameter of the winding compression roller 8 is 120mm, the surface of the rubber roller 11 is provided with an outward-extending double-spiral structure 12, the spiral distance is 90 mm, the width of a spiral groove is 3 mm, and the depth of the groove is 4 mm; the rolling compression roller 8 is in rolling connection with the rolling winding core 10.

The utility model provides a novel reduce big technology of cutting of rolling violence muscle, foretell big system of cutting is applied to this technology, specifically includes following step:

(1) during production, the large slitting system is started to operate, and the unwinding 1 starts to release the diaphragm 2;

(2) after being released from the unreeling 1, the diaphragm 2 firstly enters a first roller 3 in the flattening system, passes through a flattening roller 4 and then enters the slitting system from the other first rollers 3; the diaphragm 2 is cut by a cutter roller 5 in the cutting system and then sequentially passes through a speed counting roller 6 and a second passing roller 7, the cut diaphragm 2 is separately fed into different winding compression rollers 8, the diaphragm is further pressed and flattened by the winding compression rollers (namely rubber rollers 11), and finally the cut diaphragm 2 is wound on a winding core 10;

(3) setting the winding speed of the winding core 10 when winding the diaphragm 2 is 100m/min, and setting the winding tension F of the winding core 10 to the diaphragm 2_OIs 6.5N/m;

(4) set the unwinding tension F₁And a winding tension F_OThe proportion of (C) is 150%;

(5) setting the winding pressure F₂And a winding tension F_OThe proportion of (B) is 275%.

The final defective rate of winding and rib breaking is 16.7 percent

The parameters in examples 1-9 above were recorded as shown in table 1:

in the above embodiments 1 to 9, 9 large rolls are cut in total, and each roll is cut and then cut and rolled into 6 finished product rolls in total, wherein the total number of bad rolled up broken ribs is 3 rolls, and 9 × 6 cut total number of rolls is 54 rolls, so that the average reject ratio of rolled broken ribs is calculated to be 3/54 × 100%, which is 5.6%, by using the novel large cutting system and process for reducing rolled broken ribs of the present invention, the average reject ratio of broken ribs after large cutting and rolling is 5.6%, and is controlled to be below 10%; make the rolling violently muscle obviously reduce, solved the bad too high and the diaphragm of diaphragm rolling violently muscle bad problem of wrinkle, realize cutting the higher one time yields of rolling greatly.

The above-mentioned preferred embodiments of the present invention are provided for illustration only and not for the purpose of limiting the invention. Obvious variations or modifications of the present invention are within the scope of the present invention.