阅读说明：本技术 石膏面板、方法和系统 (Gypsum panels, methods and systems ) 是由 查尔斯·R·哈里森 斯图尔特·布兰登·吉利 于 2019-02-08 设计创作，主要内容包括：提供了石膏面板和制备石膏面板的方法。制备石膏面板的方法包括将石膏灰泥和卤化物盐螯合剂与水混合以形成石膏浆料,以及使该石膏浆料凝固以形成石膏芯的至少一部分,其中所述卤化物盐螯合剂以有效螯合所述石膏灰泥中存在的卤化物盐的至少一部分的量存在。石膏面板包括石膏芯,该石膏芯包含凝固石膏和卤化物盐螯合剂,其中所述卤化物螯合剂螯合所述石膏芯中存在的卤化物盐的至少一部分。(Gypsum panels and methods of making gypsum panels are provided. A method of making a gypsum panel includes mixing gypsum stucco and a halide salt sequestrant with water to form a gypsum slurry, and allowing the gypsum slurry to set to form at least a portion of a gypsum core, wherein the halide salt sequestrant is present in an amount effective to sequester at least a portion of the halide salt present in the gypsum stucco. The gypsum panel includes a gypsum core comprising set gypsum and a halide salt sequestrant, wherein the halide sequestrant sequesters at least a portion of the halide salt present in the gypsum core.)

1. A method of making a gypsum panel, comprising:

mixing gypsum stucco and a halide salt chelating agent with water to form a gypsum slurry; and

allowing the gypsum slurry to set to form at least a portion of the gypsum core,

wherein the halide salt chelating agent is present in an amount effective to chelate at least a portion of the halide salt present in the gypsum stucco.

2. The method of claim 1, wherein the halide salt sequestrant comprises aluminum oxide or perlite.

3. The method of claim 1, wherein the halide salt chelating agent comprises activated alumina present in an amount of about 0.01% to about 10% by weight based on the weight of the gypsum stucco.

4. The method of claim 3, wherein the activated alumina is present in an amount of about 0.01% to about 3% by weight based on the weight of the gypsum stucco.

5. The method of claim 3, wherein the activated alumina has an average particle size of less than 5 mm.

6. The method of claim 3, wherein the activated alumina has an average particle size of less than 1 mm.

7. The method of claim 1, wherein the halide sequestrant comprises perlite present in an amount of about 0.01% to about 10% by weight based on the weight of the gypsum stucco.

8. The method of claim 7, wherein the perlite is perlite ore.

9. The method of claim 8, wherein the perlite ore has an average particle size of less than 30 mesh.

10. The method of claim 7, wherein the perlite is expanded perlite.

11. The method of claim 10, wherein the expanded perlite has an average particle size of less than 16 mesh.

12. The method of claim 1, further comprising heating the halide chelating agent prior to mixing the halide chelating agent with the gypsum stucco.

13. The method of claim 12, wherein the heating is effective to expand or activate at least a portion of the halide sequestering agent.

14. The method of claim 1, further comprising associating a facing material with the gypsum slurry or the gypsum core.

15. The method of claim 1, further comprising depositing the gypsum slurry onto a facing material.

16. The method of claim 15, wherein the facing material comprises a paper facing material.

17. The method of claim 16 wherein the gypsum panel exhibits a wet bond strength of the paper facing to the core of at least about 121 bs/f.

18. The method of claim 1, wherein the gypsum stucco comprises gypsum obtained from a natural source or from a flue gas desulfurization process.

19. A gypsum panel prepared by the method of any one of claims 1 to 18.

20. A gypsum panel, comprising:

a gypsum core comprising set gypsum and a halide salt chelating agent;

wherein the halide chelating agent chelates at least a portion of the halide salt present in the gypsum core.

21. The gypsum panel of claim 20, wherein the halide salt sequestrant comprises alumina or perlite.

22. The gypsum panel of claim 20, wherein the halide salt sequestrant comprises activated alumina present in an amount of from about 0.01 wt% to about 10 wt% by weight of the set gypsum.

23. The gypsum panel of claim 22, wherein said activated alumina is present in an amount of from about 0.01% to about 3% by weight based on the weight of the set gypsum.

24. The gypsum panel of claim 22, wherein said activated alumina has an average particle size of less than 5 mm.

25. The gypsum panel of claim 22, wherein said activated alumina has an average particle size of less than 1 mm.

26. The gypsum panel of claim 20, wherein the halide sequestrant comprises perlite present in an amount of from about 0.01% to about 10% by weight based on the weight of the gypsum stucco.

27. The gypsum panel of claim 26, wherein said perlite is perlite ore.

28. The gypsum panel of claim 27, wherein said perlite ore has an average particle size of less than 30 mesh.

29. The gypsum panel of claim 26, wherein said perlite is expanded perlite.

30. The gypsum panel of claim 29, wherein said expanded perlite has an average particle size of less than 16 mesh.

31. The gypsum panel of claim 20, further comprising a facing material associated with said gypsum core.

32. The gypsum panel of claim 31, wherein said facing material comprises a paper facing material.

33. The gypsum panel of claim 32, wherein said gypsum panel exhibits a wet bond strength of paper facing to core of at least about 121 bs/f.

34. A building sheathing system, comprising at least two gypsum panels according to any one of claims 20 to 33.

Background

The present disclosure relates generally to gypsum panels and methods of making gypsum panels, and in particular to gypsum panels in which the effects of salts within the gypsum material have been mitigated.

Panels with a set gypsum core have long been used as structural elements in the manufacture of buildings. Such panels (also commonly referred to as "siding," "drywall," or "gypsum board") are commonly used to form partitions or walls for rooms, elevator shafts, stairwells, ceilings, and the like, and represent a lower cost and faster alternative to conventional gypsum walls.

In its most common form, gypsum wallboard is made by sandwiching a solid gypsum core made from an aqueous slurry of calcined gypsum (typically a slurry of calcium sulfate hemihydrate) between two sheets of facing material (typically thick paper or a fibrous mat, such as fiberglass). Gypsum wallboard is continuously manufactured at high speeds by continuously depositing an aqueous slurry of calcined gypsum and other ingredients onto one of two facing sheets, and then contacting the second facing sheet with the free surface of the gypsum slurry to form a sandwich-like structure.

The calcined gypsum slurry deposited between the two facing sheets sets (i.e., the calcined gypsum reacts with water from the aqueous slurry) to form a rigid plate-like structure. The panel so formed is then cut into panels of a desired length (e.g., eight to sixteen feet). If the board so formed contains an excess of water (water is not only necessary to hydrate the calcined gypsum but is also necessary to ensure adequate fluidity of the gypsum slurry during board preparation), the board may then be passed through a drying kiln where the excess water is removed and the gypsum wallboard is brought to a final hydrated but dry state. After the core has set and dried completely, the sandwich structure becomes a rigid fire resistant building material.

However, it is desirable to produce gypsum panels having improved strength and/or improved bonding between the gypsum core and the panel facing material.

Disclosure of Invention

In one aspect, a method of making a gypsum panel is provided that includes mixing gypsum stucco and a halide salt sequestrant with water to form a gypsum slurry, and allowing the gypsum slurry to set to form at least a portion of a gypsum core, wherein the halide salt sequestrant is present in an amount effective to sequester at least a portion of the halide salt present in the gypsum stucco.

In another aspect, a gypsum panel is provided that includes a gypsum core comprising set gypsum and a halide salt chelating agent, wherein the halide chelating agent chelates at least a portion of the halide salt present in the gypsum core.

In another aspect, a sheathing system is provided, comprising at least two of the gypsum panels described herein.

Drawings

Referring now to the drawings, which are intended to be exemplary and not limiting, and wherein like elements are numbered alike. The detailed description is set forth in connection with the appended drawings showing examples of the disclosure, wherein like reference numerals are used to refer to similar or identical items. Certain embodiments of the present disclosure may include elements, components, and/or configurations other than those shown in the figures, and in certain embodiments, some of the elements, components, and/or configurations shown in the figures may not be present.

Fig. 1 is a cross-sectional view of a gypsum panel having one paper material facing.

Fig. 2 is a cross-sectional view of a gypsum panel having two paper material facings.

FIG. 3 is a schematic view of a method of producing gypsum wallboard.

Fig. 4 is a perspective view of a building sheathing system.

Fig. 5 is a graph showing the results of the wet adhesion test of example 1.

Fig. 6 is a graph showing the results of the wet adhesion test of example 2.

Fig. 7 is a graph showing the results of the nail pull test of example 2.

Fig. 8 is a graph showing the results of the ion chromatography test of example 3.

Fig. 9 is a graph showing the results of the ion chromatography test of example 3.

Fig. 10 is a graph showing the results of the ion chromatography test of example 4.

Fig. 11 is a graph showing the results of the ion chromatography test of example 5.

Fig. 12 is a graph showing the results of the wet adhesion test of example 6.

Fig. 13 is a graph showing the results of the wet adhesion test of example 6.

Detailed Description

Provided herein are gypsum panels and panel systems and methods of making the same. The panels exhibit improved strength and/or improved bonding between the gypsum core and the panel facing material. In particular, the panels may exhibit a relatively high bond strength between the gypsum core and the paper facing material.

The gypsum used to form gypsum panels is obtained from a variety of natural sources as well as Flue Gas Desulfurization (FGD), also known as by-product or synthetic gypsum, which is obtained from electric power companies. Thus, the chemical composition of gypsum can vary greatly between sources. It has been found that these differences in chemical composition can result in differences in the properties of the resulting panel, including strength and adhesion between the core and facing materials. In particular, it has been found that the presence of salt in the gypsum can negatively impact the performance of the panel in these areas. The present disclosure relates to methods of mitigating the effects of salt on these performance characteristics. In particular, the present disclosure relates to methods of making gypsum panels by mixing a halide salt chelating agent with gypsum stucco in an amount effective to chelate at least a portion of any salt present in the gypsum stucco, as well as panels and panel systems produced by these methods.

The method of making the gypsum panel and the resulting panel will be described in detail. It should be understood that although features of the present disclosure may be described with reference to particular embodiments, the present disclosure is intended to cover any number of variations, alterations, substitutions or equivalent arrangements not explicitly described herein, and should not be limited to such explicitly disclosed embodiments.

Method for preparing gypsum panel

In one aspect, a method of making a gypsum panel to mitigate the effects of salts present in gypsum plaster is provided. In certain embodiments, the methods comprise mixing gypsum stucco and a halide salt sequestrant with water to form a gypsum slurry, and allowing the gypsum slurry to set to form at least a portion of the gypsum core, wherein the halide salt sequestrant is present in an amount effective to sequester at least a portion of the halide salt present in the gypsum stucco. These methods can be used to produce gypsum panels having any feature or combination of features described herein.

As used herein, the phrase "halide salt chelating agent" refers to a material effective to capture or bind halide ions (e.g., chloride, fluoride, bromide) of a halide salt to inactivate it. For example, the halide salt may include sodium chloride (NaCl), calcium chloride (CaCl)₂) Potassium chloride (KCl), potassium iodide (KI), lithium chloride (LiCl), copper (II) chloride (CuCl)₂) Silver chloride (AgCl). For example, the halide salt chelating agent may chelate halide ions by any suitable mechanism. In certain embodiments, the halide salt chelating agent has a porous surface that provides increased surface area to capture halide salts.

As used herein, the phrase "in an amount effective to sequester at least a portion of the halide salt present in the gypsum stucco" refers to an agent that deactivates at least some portion (if any) of the halide ions present in the gypsum stucco. For example, the halide salt chelating agent can be provided in an amount effective to chelate at least 25 wt.% of the halide salt present in the gypsum stucco. For example, the halide salt chelating agent can be provided in an amount effective to chelate at least 50 wt.%, at least 75 wt.%, at least 90 wt.%, or at least 95 wt.% of the halide salt present in the gypsum stucco.

In certain embodiments, the halide chelating agent is alumina (i.e., aluminum oxide), perlite (an amorphous volcanic glass containing compounds such as silica and/or aluminum oxide), or combinations thereof. Other suitable materials that effectively chelate halide ions may also be used. For example, the alumina may be activated alumina prepared by reacting aluminum hydroxide with aluminum hydroxideAre dehydroxylated in a manner that produces a highly porous material having a relatively high surface area to weight ratio. For example, the alumina may have a thickness of about 200m²A surface area of/g or greater, such as about 300m²A surface area of/g or greater.

In certain embodiments, the halide salt chelating agent comprises activated alumina present in an amount of about 0.01% to about 10% by weight based on the weight of gypsum stucco. In some embodiments, the activated alumina is present in an amount from about 0.01% to about 3% by weight based on the weight of the gypsum stucco. The alumina can have a relatively small particle size, thereby increasing the available surface area of the reagent for a given mass of material. For example, the alumina may have an average particle size of less than about 5mm, such as an average particle size of less than about 4mm, less than about 2mm, or less than about 1 mm.

In certain embodiments, the halide sequestrant comprises perlite present in an amount of from about 0.01% to about 10% by weight based on the weight of the gypsum stucco. In some embodiments, the perlite is perlite ore. In other embodiments, the perlite is expanded perlite. For example, perlite ore can have an average particle size of less than 30 mesh (i.e., a particle size smaller than it). For example, perlite ore can have a particle size range that exhibits the following screening analysis (screening size; cumulative total weight percent of maximum and minimum ranges retained): (16 mesh; - -/3; -/0); (20 mesh; 7/15; 0/5); (30 mesh; 35/42; 12/25); (50 mesh; 95/98; 75/80); (100 mesh; 100/100; 95/95). For example, the expanded perlite can have an average particle size of less than about 16 mesh (i.e., smaller than it). For example, expanded perlite can have a particle size range that exhibits the following screening analysis (screen size; cumulative total weight percent retained): (8 mesh; 0); (16 mesh; 1-11); (20 mesh; 41-69); (30 mesh; 68-88); (50 mesh; 93-96); (100 mesh; 96-100).

In certain embodiments, the methods of making these gypsum panels further comprise heating the halide-chelating agent (e.g., perlite, alumina, unexpanded aluminum oxide) prior to mixing the halide-chelating agent with the gypsum stucco. For example, the heating is effective to expand or activate at least a portion of the halide chelating agent. That is, the method may include the step of forming expanded perlite or activated alumina. Such heating may be performed on-line or off-line as the gypsum panel is formed, such as in a kiln, kettle, oven, or other suitable heating device.

As in any gypsum wallboard, the largest single ingredient in the gypsum slurry, other than water where possible, is the source of calcined gypsum, usually calcium sulfate hemihydrate, commonly referred to as "stucco" or "plaster of paris". Typically, a large amount of calcined gypsum is used to prepare the gypsum slurry. The calcined gypsum typically comprises from about 30% to about 60% by weight of the gypsum slurry, such as from about 40% to 50% by weight of the gypsum slurry. However, the present disclosure is not limited to any particular source of calcined gypsum, and calcined gypsum made from both natural minerals extracted from quarries and synthetic gypsum (referred to as desulfurized gypsum) produced from desulfurization of power plant flue gas effluent (i.e., FGD gypsum) may be used. Calcined gypsum made from a combination of natural and synthetic gypsum can also be used. After hydration and drying, set gypsum typically comprises over 85% by weight of the set gypsum core.

Whether natural rock or synthetic, the gypsum can be dried, ground, calcined and stored as stucco, which is calcium sulfate hemihydrate. The drying step of stucco manufacture typically involves passing the raw gypsum rock through a rotary kiln to remove free moisture, and then grinding the rock to the desired fineness using, for example, a roller mill. The dried, ground gypsum (commonly referred to as "landplaster") is then heated, usually in a "calciner," to remove the water of hydration, resulting in calcined gypsum that exhibits the valuable property of chemically reacting with water and setting to form a rigid structure. Stucco can take two forms, calcium sulfate alpha hemihydrate and calcium sulfate beta hemihydrate. As will be understood by those skilled in the art, these two types of stucco are produced by different calcination procedures. The present disclosure may generally use stucco in either the beta or alpha form; however, as is the case in conventional gypsum wallboard production, the lower cost β form is typically used.

In certain embodiments, calcined gypsum is mixed with a halide salt chelating agent and any other additives, typically in a "paddle" mixer, in the presence of water to form a gypsum slurry. In some embodiments, the halide salt chelating agent is dry mixed with the gypsum stucco; however, other processes may be used. Thus, the aqueous gypsum slurry comprises at least gypsum, water, and a halide salt sequestrant; however, other additives will generally be used. For example, any suitable additive known in the industry may be used. For example, suitable additives may include starches (such as common starch and pregelatinized starch), agents that reduce the density of the gypsum core (such as foaming agents, surfactants, microspheres), dispersants, set retarders, set accelerators, biocides (mold and mildew control agents), fillers, water-resistant additives (such as waxes or wax emulsions or silicones), flame retardants, reinforcing fibers (such as chopped glass fibers or other inorganic fibers), strength enhancers (such as sodium trimetaphosphate or polymeric binders), and combinations thereof.

An amount of water is also included in the gypsum slurry to ensure proper fluidity of the slurry. Water is added to the process to hydrate the calcined gypsum to provide the desired fluidity. As is the case in conventional wallboard production, most of this water must eventually be drained by heating the set gypsum wallboard. Therefore, the less the amount of water used, the lower the drying cost. In certain embodiments, the weight ratio of water to calcined gypsum can vary over a wide range of weight ratios (i.e., the weight of water divided by the weight of calcined gypsum). In some embodiments, the weight ratio of water to calcined gypsum (water: calcined gypsum) is established at about 0.5: 1 to about 1.5: 1, such as about 0.7: 1 to about 1.3: 1.

The gypsum slurry can be formed into a long continuous sheet between two facing materials. In an alternative embodiment, the gypsum slurry may be placed in a mold.

One method for making a wallboard according to the present disclosure is schematically illustrated in fig. 3. In this embodiment, the calcined gypsum is fed, along with other dry components, to the top of a mixer of the type commonly referred to as a paddle mixer (not shown). In particular, the halide salt sequestrant and any other optionally included dry additive components that form the gypsum slurry may be pre-mixed and then fed as a dry mixture to the paddle mixer. The water and other liquid components used to form the gypsum slurry (e.g., soap or foam prepared separately using high shear mixing and used to control the density of the slurry) are also metered through other ports into the lobe mixer where they are mixed with the dry components to form an aqueous gypsum slurry 41 which is discharged from the discharge conduit 40 of the lobe mixer. The residence time in the blade mixer is usually very short.

The slurry is deposited through one or more outlets of the discharge conduit 40 onto a continuous, horizontally moving lower facing sheet 24 that includes a facing material (e.g., paper, fibrous web) that may be slightly wider than the desired width of the wallboard. The lower facing sheet 24 and the deposited gypsum slurry 41 move in the direction of arrow B. An upper facing sheet 22 (also comprising a material such as paper) is fed from a roll (not shown) in the direction of arrow C and applied to the upper surface of the gypsum slurry 41. The "sandwich" of slurry and adjacent facing sheets is then passed through a die or other forming device (rolls, guides, or plates (50 and 52)) to form gypsum board of the desired width and thickness. The amount of slurry deposited can be controlled in a manner known in the art such that it forms a panel of the desired width and thickness with the facer sheets 22 and 24 and the facer panels 50 and 52. The facing sheets 22 and 24 are typically a type of paper, such as multi-ply paper commonly used for facing sheets of wallboard products, or a fibrous web, such as fiberglass, although other facing materials may be used.

The lower facing sheet 24 is fed from a roll (not shown). In some embodiments, prior to receiving the gypsum slurry 41, the lower facing sheet 24 may be scored by one or more scoring devices, allowing the edges of the lower facing sheet 24 to fold upward and around the deposited gypsum slurry. These edges may then be glued or adhered to the overlapping portions of the upper facing sheet 22 with gypsum slurry according to methods known in the art. Prior to applying the (upper) facing sheet 22 to the upper surface of the gypsum slurry, glue may be applied to the facing sheet along the portion of the facing sheet that will overlap and contact the edge of the folded mat (glue application not shown).

In certain embodiments, the gypsum core comprises multiple layers that are sequentially applied to the glass fiber mat and allowed to set sequentially or simultaneously. In other embodiments, the gypsum core comprises a single layer. Although not shown, the present disclosure also contemplates that, in certain embodiments, a small amount of gypsum slurry may be discharged through suitable outlets to provide a relatively thin layer of gypsum slurry on the inner surfaces of the facing sheets 22 and 24. The thin gypsum slurry layer is somewhat denser than the aqueous slurry of gypsum used to form the major portion of the set gypsum core (the main core slurry that is discharged through outlet 40 to form the gypsum slurry layer). This higher density region of the core (also referred to as the "slate coating") is intended to help form a strong bond between the lower density portion of the core and the facing sheet, such as by penetrating into the interstices of the fibrous facing material.

In some embodiments, the density of the slurry used to form the slate coating is about 18% to 20% higher than the density of the slurry used to form the major portion of the set gypsum core. In certain embodiments, depositing the gypsum slurry comprises depositing a first gypsum slurry having a wet density of about 88pcf to about 98pcf onto the surface of the glass fiber mat, the first gypsum slurry. In certain embodiments, the first gypsum slurry has a wet density of from about 93pcf to about 96 pcf. In some embodiments, the gypsum core comprises at least three gypsum layers, wherein the outermost gypsum layer of the gypsum core (i.e., the layer that forms the interface with the facing mat) is the slate coating. In certain embodiments, both outermost layers have a relatively high density or are otherwise chemically altered to enhance permeability. Thus, the third gypsum slurry can have a wet density of from about 88pcf to about 98pcf, or from about 93pcf to about 96 pcf. In certain embodiments, the first gypsum slurry (or each outermost gypsum slurry layer) is deposited in an amount from about 5% to about 20% by weight of the gypsum core. Additionally, it is also contemplated that, in some embodiments, some of this higher density gypsum slurry may also be used to form a flow of gypsum slurry at each edge of the facing sheet to form a hard edge of the wallboard.

In the embodiment shown, the nascent sheet 16 then travels in the direction of arrow D over a roller or conveyor 54 for several minutes. During this time, the slurry is set by the hydrated stucco and forms a set gypsum core. During this setting, the core becomes rigid as the gypsum mineral (calcium sulfate dihydrate) forms.

The wallboard is then cut to length, flipped over and dried, such as in a continuous oven or by allowing the material to set (i.e., self-harden) at room temperature. The individual panels may then be taped face-to-face in pairs and stacked for shipping. For molded articles, the gypsum slurry can alternatively be introduced directly into the mold and the slurry set to form the article.

As noted above, in certain embodiments, the slurry comprises more water than is required to reconstitute gypsum from stucco alone. This additional water is used in the board forming stage to reduce the viscosity of the stucco slurry sufficiently so that it is evenly distributed over and between the facing sheets at the desired thickness (e.g., by using forming rolls). The gypsum board remains wet after hydration due to the excess water used (although the board can now be cut to the desired size). Thus, the formed board can be finally dried.

In certain embodiments, the drying operation includes applying heat to evaporate excess water by circulating hot air around the wet gypsum board (e.g., in a drying oven). Thus, it may be desirable to have sufficient porosity in the facing sheet to allow these excess water to readily evaporate without adverse effects, such as delamination, tearing, cracking, etc. of the facing sheet. The ability of the facing sheet to allow water vapor to escape may also promote uniform dryness. This can improve the overall quality of the board, since insufficiently dried gypsum boards have storage problems, while excessive drying leads to calcination and causes a reduction in mechanical strength. Typical drying conditions may include maintaining ambient or ambient hot air temperatures at 200 ° F to 600 ° F (about 95 ℃ to 315 ℃) for drying times of 10 minutes to 2 hours. For example, at a line speed of about 70 to about 600 linear feet per minute, a drying time of about 30 minutes to about 60 minutes may be used. However, these parameters are exemplary and are influenced by the particular configuration of the board production line.

Conventional gypsum wallboard (nominal thickness 1/2 inches or 5/8 inches) is typically made at a weight of about 1200 pounds to 2000 pounds per 1,000 square feet (MSF) board (about 5,900kg to about 9,800kg per thousand square meters). This corresponds to about 38lb/ft ³To about 43lb/ft³(about 0.61g/cc to 0.69 g/cc). Gypsum wallboard made according to the present disclosure may have such relatively high weight and density, or may have a reduced density relative to standard wallboard. For example, reducing the weight of each gypsum panel by 30 pounds per MSF can save a significant amount of money. For example, by adjusting the proportion of foam in the gypsum slurry, the set gypsum core of the present disclosure can have a much lower density than commercially available gypsum products. In certain embodiments, a gypsum wallboard having a nominal thickness of 1/2 inches of the present disclosure has a weight of about 1000 to 1300 pounds per MSF board. This corresponds to about 24lb/ft³To about 31lb/ft³(about 0.38g/cc to 0.50 g/cc).

In certain embodiments, the gypsum core comprises about 80% by weight or more of set gypsum (i.e., fully hydrated calcium sulfate). For example, the gypsum core can comprise about 85% by weight set gypsum. In some embodiments, the gypsum core comprises about 95% by weight set gypsum.

The facing sheet, also interchangeably referred to herein as a "facing material" or "facing mat," may comprise any fibrous material known to be suitable for facing gypsum board. Specific materials include paper, such as heavy, single or multi-ply paper (e.g., medium or heavy kraft paper, manila paper, etc.) and paperboard. For example, the multi-ply paper used for the facing sheet of the gypsum board product may have a basis weight of 40 to 65 pounds per MSF, a total thickness of 250 to 350 microns, and a gurley porosity of 15 to 145 seconds. In some embodiments, a different type of paper is used for each gypsum board surface. For example, manila paper may be used on one side, while newsprint (newsler) may be used on the opposite side.

Paper and cardboard facing materials may be made from recycled fibers (e.g., used corrugated, kraft or waste newsprint), but they may also be made partially or wholly from natural fibers. Other natural or synthetic fiber materials may also be used, including those derived from metal or glass (e.g., glass fiber mats, chopped or continuous strand mats, or glass rovings, whether woven or non-woven). Other useful materials for the facing sheet include synthetic organic polymers (e.g., nylon, polyester, polypropylene, polyethylene, rayon, and cellulose) that form filaments, ceramics, cotton, cloth, hair, felt, and the like. The fibrous mat may be bonded or coated with a resin binder. Multiple layers of fibrous materials, such as composite sheets of glass mat and kraft paper, may also be used.

In certain embodiments, one or both mat facings may be coated on the outer and/or inner surfaces of the mat facings to provide additional performance characteristics of the panels and/or facings.

It has been found that the incorporation of a halide salt chelating agent into a gypsum slurry is effective in removing salts, such as chloride salts, from the resulting set gypsum composition to reduce the effect of these salts on the performance of the resulting gypsum panel. In particular, it has been found that these agents can be added to gypsum compositions having high chloride salt content and the bond strength of the facing to the core returns to the desired performance level in the absence of chloride salt. For example, these compositions may be particularly useful for panels having a paper facing, as the halide salt chelating agent may reduce the effect of the salt on the bond strength of the paper to the core. For example, the gypsum panels of the present disclosure can exhibit a wet bond strength of the paper facing to the core of at least about 12 pounds per force.

In contrast to alternative methods of washing salt content from gypsum material and disposing of high salt content water, the present disclosure allows for the chelation of salt within the halide salt chelating agent, trapping salt within the wallboard. As such, it is believed that the present disclosure reduces the environmental impact of the gypsum cleaning process.

Gypsum panels and systems

Gypsum panels and systems of such panels are also provided herein. The gypsum panel can be manufactured to have any of the properties described herein or can be manufactured by any method. In certain embodiments, the gypsum panel comprises a gypsum core comprising set gypsum and a halide salt sequestrant, wherein the halide sequestrant sequesters at least a portion of the halide salt present in the gypsum core. For example, such panels may exhibit enhanced strength and veneer bonding characteristics.

In certain embodiments, as shown in fig. 1, the gypsum panel 100 includes a gypsum core 101 having a first surface and a second, opposite surface, and a first facing pad 104 associated with the first surface of the gypsum core 101 such that the gypsum of the gypsum core penetrates and/or adheres to at least a portion of the first facing pad 104. For ease of illustration, the various layers are shown as separate layers in the figures; however, it should be understood that the overlap of these materials may occur at their interface.

In certain embodiments, as shown in fig. 2, the gypsum core 101 includes two or more gypsum layers 102, 108. For example, the gypsum core may include various gypsum layers having different compositions. In some embodiments, the first gypsum layer 102 in contact with the veneer pad 104 is a slate coating, as discussed above. In some embodiments, the first gypsum layer 102 is present in an amount from about 5% to about 20% by weight of the gypsum core 101. In certain embodiments, as shown in fig. 2, the gypsum panel 100 includes two facing material mats 104, 112 associated with the gypsum core 101.

As discussed above, the panel may have a thickness of about 1/4 inches to about 1 inch. For example, the panel may have a thickness of about 1/2 inches to about 5/8 inches.

Also provided herein are building sheathing systems comprising at least two gypsum panels described herein, including any feature or combination of features of the panels described herein. For example, the gypsum panels can each include a gypsum core comprising a halide salt chelating agent. In certain embodiments, as shown in fig. 4, a building sheathing system includes at least two gypsum panels 300 and a seaming component 320 configured to provide a seam at an interface between the at least two gypsum panels 300. In certain embodiments, the seaming component comprises tape or a bonding material.