阅读说明：本技术 一种用阳离子改性棉及纳米纤维实现花灰纺纱效果的制备方法 (Preparation method for realizing effect of gray spinning by using cation modified cotton and nano fibers ) 是由 魏旭巍 李景川 权震震 余燕平 覃小红 于 2020-06-19 设计创作，主要内容包括：本发明涉及一种用阳离子改性棉及纳米纤维实现花灰纺纱效果的制备方法,包括：在棉条梳棉过程中,采用共混法和静电纺丝工序对棉进行阳离子改性,经纺纱和上染工序即可生产出一种具有花灰效果的纱线或面料。本发明极大缩短了花灰纱生产时间,降低了成本,提高了生产效率。(The invention relates to a preparation method for realizing a gray spinning effect by using cation modified cotton and nano fibers, which comprises the following steps: in the cotton sliver cotton carding process, a blending method and an electrostatic spinning process are adopted to carry out cationic modification on cotton, and a yarn or fabric with a cotton ash effect can be produced through a spinning process and a dyeing process. The invention greatly shortens the production time of the gray yarn, reduces the cost and improves the production efficiency.)

1. A preparation method of a gray effect yarn or fabric comprises the following steps:

(1) in the cotton carding process of cotton bundles obtained by opening and picking, simultaneously carrying out electrostatic spinning on the spinning solution to mix the nanofibers with the cotton net to obtain mixed cotton slivers, and then carrying out combing, drawing, roving and spun yarn on the mixed cotton slivers in sequence or preparing the mixed cotton slivers into fabrics;

wherein the spinning solution components comprise: cationic modifiers, polyacrylonitrile, and solvents; the nano-fiber is cation modified nano-fiber;

(2) and (3) carrying out modification treatment on the spun yarn or the fabric, and dyeing to obtain the yarn or the fabric with the effect of graying.

2. The preparation method according to claim 1, wherein the cation modifier in the step (1) is 2, 3-epoxypropyltrimethylammonium chloride; the weight average molecular weight of polyacrylonitrile is 80000-90000; the solvent is N, N-dimethylformamide.

3. The preparation method according to claim 1, wherein the concentration of polyacrylonitrile in the spinning solution in the step (1) is 8-12 wt%, and the mass percentage of the cationic modifier is 2-5%.

4. The preparation method according to claim 1, wherein the electrostatic spinning in the step (1) is specifically: the voltage applied to the electrostatic spinning is 15-20 kV, the distance between the electrostatic spinning nozzle and the cotton net is 20-30 cm, the ambient temperature of the electrostatic spinning is 20-30 ℃, the humidity is 50-60%, and the filament output of the single nozzle of the electrostatic spinning is 60-100 g/h; the speed of the cotton carding is 10-40 m/min.

5. The preparation method according to claim 1, wherein the mass of the cation modified nanofiber in the step (1) accounts for 3-6% of the mass of the composite cotton sliver.

6. The preparation method according to claim 1, wherein the modification treatment in the step (2) is specifically: preparing modified treatment liquid by using 2, 3-epoxypropyl trimethyl ammonium chloride as a cationic modifier, wherein the bath ratio is 1: 30, then soaking for 30-45min at the temperature of 45-70 ℃, baking, washing and drying.

7. The preparation method of claim 1, wherein the dye used in the dyeing in the step (1) is an anionic dye, and the dyeing is carried out by a dip dyeing process and a one-bath two-step method.

8. The method of claim 7, wherein the anionic dye is an acid reactive dye yellow RC-3R, defined at a concentration of 50 g/L.

9. A marbled effect yarn or fabric made by the method of claim 1.

10. Use of the graying effect yarn or fabric of claim 9.

Technical Field

The invention belongs to the field of gray yarns or fabrics, and particularly relates to a preparation method for realizing a gray yarn effect by using cation modified cotton and nano fibers.

Background

The yarn commonly used in the field of textile at present is divided into two types of natural color yarn and dyed yarn, wherein the natural color yarn is spun by fiber through the processes of opening and picking, cotton carding, combing, drawing, roving and spinning, the dyed yarn is made by the natural color yarn through the process of dyeing and finishing to form yarns with different colors, and the mixed color yarn is blended by fibers with different colors and different properties, and has the performance and the color which are not possessed by the natural color yarn after dyeing. The gray yarn is one of mixed color yarns, is a single-color mixed color yarn in a broad sense, is blended by black-dyed fibers and natural-color fibers in a narrow sense, and is one of the most common mixed color yarns at present.

Nanofibers in the narrow sense refer to fibrous materials having diameters in the range of 1-100nm, and fibers having diameters in the sub-micron scale are also collectively referred to as nanofibers. The diameter of the nano fiber is in the range of submicron or even nano scale, so that the nano fiber has various characteristics such as small size effect, cladding and interface effect and the like, has large specific surface area, high porosity and high surface energy of a membrane structure, and is widely applied to the fields of filtration, biological tissue engineering, antibacterial slow release, sensing detection, catalysis, energy and the like. As a way to prepare nanofibers continuously, rapidly and in batch, the electrospinning technology has received attention and extensive attention from academia and industry, but the low strength problem due to the extremely low fineness severely limits the application field of industrial mass production. The traditional spinning and weaving technology solves the problem of dressing hundreds of millions of people at home and abroad, plays an indispensable role in the field of industry, and is a supporting industry which is developed by the nation. However, in recent years, with the improvement of living standard of people and the vigorous development of the country, the diversification of textile functions gradually becomes a focus of social focusing, and the improvement of the functionality of the textile to improve the additional value and the application field of the traditional textile becomes one of the important directions of scientific research and technical development.

Cotton fibers generally have a certain amount of charges on the surface of the fibers when contacting with a dye solution, under neutral or alkaline conditions, the fibers are ionized due to carboxyl groups, sulfonic acid groups and the like or carboxyl groups generated by fiber oxidation, and the fibers adsorb negatively charged particles in the dye solution, the surface is generally negatively charged, and most of the fibers used for dyeing cellulose fibers (such as reactive dyes, direct dyes, vat dyes and the like) are also negatively charged in a dye bath. The dye uptake is hindered by allowing electrostatic repulsion between the dye and the fiber so that the dye uptake is reduced. The traditional method for solving the problem is to add a large amount of neutral electrolyte in the dye bath to improve the dye uptake, but relatively causes great pressure on the environment. The cellulose fiber is subjected to cationic modification, namely covalent bonding is formed by chemical reaction with hydroxyl on the fiber to enable the fiber to be positively charged, or the fiber is positively charged in a physical adsorption mode, so that dye molecules with negative charges are promoted to be dyed on the fiber, the dyeing rate of the dye on the fabric is improved, and the generation of dyeing wastewater is reduced.

CN 110144658A discloses a production method of composite yarn with a gray effect, but after experiments are carried out by accurately controlling experiment parameters, the phenomenon that electrostatic spinning film is attached to the surface of cotton fiber, the cotton fiber is not uniformly combined with dye is found, and the obtained gray yarn effect is not obvious, so that the method utilizes an electrostatic spinning process to carry out cationic modification on cotton, then enhances the cationic modification effect, and finally dyes the yarn to obtain the gray yarn or fabric, thereby not only reducing pollution and saving raw materials, but also improving the gray yarn effect.

Disclosure of Invention

The invention aims to solve the technical problem of providing a preparation method for realizing a gray spinning effect by using cation modified cotton and nano-fibers, and overcomes the defects that electrostatic spinning film is formed and attached to the surface of cotton fibers, the combination of the cotton fibers and dyes is not uniform and the gray yarn effect is not obvious in the prior art.

The invention relates to a preparation method of a gray effect yarn or fabric, which comprises the following steps:

(1) in the cotton carding process of cotton bundles obtained by opening and picking, simultaneously carrying out electrostatic spinning on the spinning solution to mix the nanofibers with the cotton net to obtain mixed cotton slivers, and then carrying out combing, drawing, roving and spun yarn on the mixed cotton slivers in sequence or preparing the mixed cotton slivers into fabrics;

wherein the spinning solution components comprise: cationic modifiers, polyacrylonitrile, and solvents; the nano-fiber is cation modified nano-fiber;

(2) and (3) carrying out modification treatment on the spun yarn or the fabric, and dyeing to obtain the yarn or the fabric with the effect of graying.

The preferred mode of the above preparation method is as follows:

the cotton bundles obtained by opening and cleaning cotton in the step (1) are as follows: opening and cleaning the cotton fiber, and removing impurities.

The cation modifier in the step (1) is 2, 3-epoxypropyltrimethylammonium chloride; the weight average molecular weight of polyacrylonitrile is 80000-90000; the solvent is N, N-dimethylformamide.

In the step (1), the concentration of polyacrylonitrile in the spinning solution is 8-12 wt%, and the mass percentage of the cationic modifier is 2-5%.

The spinning solution specifically comprises: firstly, dissolving polyacrylonitrile in a solvent to obtain a polyacrylonitrile solution, and then adding a cation modifier into the polyacrylonitrile solution to obtain a mixed spinning solution.

Further, a cation modifier 2, 3-epoxypropyl trimethyl ammonium chloride is added into the polyacrylonitrile solution, and the concentration is 50 g/L; adding a cationic modifier, stirring and dissolving to obtain a mixed spinning solution.

The stirring and dissolving temperature is 40-60 ℃, the stirring speed is 1000-2000 r/h, and the stirring time is 8-12 h.

The electrostatic spinning in the step (1) is specifically as follows: the voltage applied to the electrostatic spinning is 15-20 kV, the distance between the electrostatic spinning nozzle and the cotton net is 20-30 cm, the ambient temperature of the electrostatic spinning is 20-30 ℃, the humidity is 50-60%, and the filament output of the single nozzle of the electrostatic spinning is 60-100 g/h; the speed of the cotton carding is 10-40 m/min.

In the step (1), the mass of the cation modified nano fiber accounts for 3-6% of the mass of the composite cotton sliver.

And (2) drawing passes through 2-3 passes in the step (1).

And (2) setting the modification temperature and time for the spun yarn or the fabric to enhance the cationic modification effect.

The modification treatment in the step (2) is specifically as follows: preparing modified treatment liquid by using 2, 3-epoxypropyl trimethyl ammonium chloride as a cationic modifier, wherein the bath ratio is 1: 30, then soaking for 30-45min at the temperature of 45-70 ℃, baking, washing and drying.

The dye adopted in the dyeing in the step (1) is an anionic dye, the dyeing adopts a dip dyeing process, and the dyeing is carried out by a one-bath two-step method.

The anionic dye is acid reactive dye yellow RC-3R, and the concentration is 50 g/L.

The gray effect yarn or fabric prepared by the method is provided.

The invention relates to application of the yarn or the fabric with the effect of graying.

The method takes cotton fiber as a raw material, firstly, opening and cleaning the cotton fiber, removing impurities, and mixing a cation modified solution, polyacrylonitrile and a solvent to obtain a mixed spinning solution; then, in the cotton carding process, performing electrostatic spinning on the mixed spinning solution to obtain mixed cotton slivers; the obtained composite cotton sliver is subjected to combing, drawing, roving and spinning in sequence or is made into a fabric; and finally, setting the modification temperature and time for the spun yarn or the fabric, enhancing the cationic modification effect, and dyeing with anionic dye to obtain the yarn or the fabric with the graying effect.

In the cotton sliver cotton carding process, the blending method and the electrostatic spinning process are adopted to carry out cationic modification on cotton, and then the yarn or fabric with the effect of cotton ash can be produced through the spinning and dyeing processes, so that the production time of the cotton ash yarn is shortened, the cost is reduced, and the production efficiency is improved. The yarn or fabric produced by the invention has a gray color effect and good hand feeling, and can reach the national standard in the aspects of color fastness and the like.

Advantageous effects

Compared with the direct dyeing of common cotton, the method reduces the generation of dyeing wastewater by carrying out cationic modification on the cotton. The cationic modified nanofiber is produced by utilizing electrostatic spinning, the process is simple and convenient, and the operability is strong. Meanwhile, the produced gray yarn or fabric has short production cycle, is energy-saving and environment-friendly, and has important significance for the industry. Experiments show that the quality of the cotton absorbing dye is improved along with the cationic modification treatment of the cotton fiber, the subsequent modification treatment is very important, the upper limit of the improvement of the dye uptake of the modified cotton fiber is established, and the higher the dye uptake of the cotton is, the higher the utilization efficiency of the raw material is, and the less the dyeing wastewater is generated.

Drawings

FIG. 1 is a flow chart of a process for producing a yarn or fabric with a graying effect according to an embodiment of the present invention;

FIG. 2 is a scanning electron micrograph of a composite yarn prepared according to example 1 of the present invention;

fig. 3 is a photograph of a composite yarn prepared in example 1 of the present invention.

Detailed Description

The invention will be further illustrated with reference to the following specific examples. It should be understood that these examples are for illustrative purposes only and are not intended to limit the scope of the present invention. Further, it should be understood that various changes or modifications of the present invention may be made by those skilled in the art after reading the teaching of the present invention, and such equivalents may fall within the scope of the present invention as defined in the appended claims. The cotton fiber adopted in the experiment is commercially available short fiber with the model number of L233A, polyacrylonitrile (with the molecular weight of 85000) and N, N-dimethylformamide and 2, 3-epoxypropyltrimethylammonium chloride in the electrostatic spinning solution are provided by the chemical reagent company Limited of the national medicine group, and the yellow RC-3R specification of the acid reactive dye is 2% (OWF) and is provided by the chemical industry company Limited of Shanghai Yizhen.