阅读说明：本技术 一种双金属化合物/碳复合材料的制备方法 (Preparation method of bimetallic compound/carbon composite material ) 是由 梁业如 胡书宇 张伟财 刘应亮 于 2021-06-17 设计创作，主要内容包括：本发明属于材料科学技术领域,特别涉及一种双金属化合物/碳复合材料的制备方法。该方法是将两种金属盐类的溶液与功能性高分子聚合物混合发生配位反应,随后通过管式炉高温热处理即可制得双金属化合物/碳复合材料。本发明所涉及的双金属化合物/碳复合材料制备方法工艺简单,普适性极强,可以满足大规模生产的需要。并且不需要额外添加硫/磷/硒源进行化合反应,使其高度符合节能环保的迫切需求。所制得的材料由于独特的多金属协同效应,因此在诸多领域具有广阔的应用前景。(The invention belongs to the technical field of material science, and particularly relates to a preparation method of a bimetallic compound/carbon composite material. The method comprises the steps of mixing solutions of two metal salts with a functional high molecular polymer to perform a coordination reaction, and then performing high-temperature heat treatment in a tubular furnace to obtain the bimetallic compound/carbon composite material. The preparation method of the bimetallic compound/carbon composite material has simple process and strong universality, and can meet the requirement of large-scale production. And no extra sulfur/phosphorus/selenium source is needed to be added for chemical combination reaction, so that the method highly meets the urgent requirements of energy conservation and environmental protection. The prepared material has wide application prospect in various fields due to the unique multi-metal synergistic effect.)
技术领域
本发明属于材料科学技术领域，特别涉及一种双金属化合物/碳复合材料的制备方法。
背景技术
双金属化合物/碳复合材料具有独特的结构优势，可充分发挥金属化合物(例如，硫化钴、硫化锡、磷化镍、磷化铜、硒化锡、硒化铁)以及碳材料之间的协同作用优势，提升材料的导电性、稳定性、使用寿命等性能，在储能、催化、传感、吸附等领域具有广泛的应用前景。
目前，双金属化合物/碳复合材料的制备方法普遍复杂多步，需要进行碳材料的引入、双金属氧化物的合成、金属氧化物向金属化合物的转化等多个步骤，导致制备效率严重低下。同时，相较于传统的金属化合物/碳复合材料，双金属化合物/碳复合材料的制备还需分段引入两种不同的金属离子，这进一步加剧了双金属化合物/碳复合材料的制备难度。典型方法如喷雾热解法和气固相加热法虽然可以制备出各种形貌结构的晶体颗粒和碳基体，但是普遍需要复杂的制备步骤以及添加大量会污染环境的硫/磷/硒源，并且制备效率低下，导致其难以应用于实际生产中。其他典型方法如水热法可以在一定程度上降低制备过程的复杂度，但仍不可避免碳材料的引入以及分段引入两种不同的金属离子等步骤。并且因为水热条件的限制导致其难以扩大生产规模，只能停留在实验室合成的阶段。最后，上述方法一般都只适用于一种双金属化合物/碳复合材料的合成，不能扩展成通用的制备方法。因此，传统的双金属化合物/碳复合材料的制备方法仍存在很多不足，开发一种新型的简便且通用的双金属化合物/碳复合材料制备方法仍是一个重要的研究领域。