阅读说明：本技术 一种水性聚碳酸酯雨鞋光油、制备方法及其使用方法 (Water-based polycarbonate rain boot gloss oil, preparation method and use method thereof ) 是由 李卫东 李含笑 范建华 于 2019-01-11 设计创作，主要内容包括：本发明提供一种水性聚碳酸酯雨鞋光油,包括以下质量份的原料：聚碳酸酯40-50份、水溶性丙烯酸树脂8-16份、水性成膜助剂2-3份、聚醚0.2-0.4份、二甲基矽油0.2-0.4份、水性流平剂BYK-333 0.1-0.6份、纤维素醚0.2-0.4份、分散剂0.2-0.4份、抗氧化剂0.1-0.3份、光稳定剂0.3-0.6份、乙醇4-12份、水20-40份。水性聚碳酸酯雨鞋光油的制备方法：将各组分充分搅拌,混合均匀,即得水性聚碳酸酯雨鞋光油。其使用方法：将雨鞋浸入水性聚碳酸酯雨鞋光油,取出后干燥,硫化即可。本发明的水性聚碳酸酯雨鞋光油成膜柔软细致,附着力强,抗紫外线,耐水及溶剂并有良好的光泽。(The invention provides water-based polycarbonate rain boot gloss oil which comprises the following raw materials in parts by mass: 40-50 parts of polycarbonate, 8-16 parts of water-soluble acrylic resin, 2-3 parts of water-based film-forming assistant, 0.2-0.4 part of polyether, 0.2-0.4 part of dimethyl silicone oil, 0.6-0.6 part of water-based flatting agent BYK-3330.1, 0.2-0.4 part of cellulose ether, 0.2-0.4 part of dispersant, 0.1-0.3 part of antioxidant, 0.3-0.6 part of light stabilizer, 4-12 parts of ethanol and 20-40 parts of water. The preparation method of the water-based polycarbonate rain shoe polish comprises the following steps: fully stirring the components, and uniformly mixing to obtain the water-based polycarbonate rain boot gloss oil. The using method comprises the following steps: and (3) immersing the rain shoes into the water-based polycarbonate rain shoe polish, taking out, drying and vulcanizing. The water-based polycarbonate rain boot gloss oil disclosed by the invention is soft and fine in film forming, strong in adhesive force, resistant to ultraviolet rays, water and solvents and good in gloss.)

1. The water-based polycarbonate rain boot gloss oil is characterized by comprising the following raw materials in parts by mass: 40-50 parts of polycarbonate, 8-16 parts of water-soluble acrylic resin, 2-3 parts of water-based film-forming assistant, 0.2-0.4 part of polyether, 0.2-0.4 part of dimethyl silicone oil, 0.6-0.6 part of water-based flatting agent BYK-3330.1, 0.2-0.4 part of cellulose ether, 0.2-0.4 part of dispersant, 0.1-0.3 part of antioxidant, 0.3-0.6 part of light stabilizer, 4-12 parts of ethanol and 20-40 parts of water.

2. The aqueous polycarbonate rain boot gloss oil according to claim 1, characterized by comprising the following raw materials in parts by mass: 46-48 parts of polycarbonate, 10-12 parts of water-soluble acrylic resin, 2.5-3 parts of water-based film-forming assistant, 0.2-0.3 part of polyether, 0.2-0.3 part of dimethyl silicone oil, 0.3-0.4 part of water-based flatting agent BYK-3330.3, 0.3-0.4 part of cellulose ether, 0.2-0.3 part of dispersing agent, 0.2 part of antioxidant, 0.5 part of light stabilizer, 6-9 parts of ethanol and 30-34 parts of water.

3. The aqueous polycarbonate rain boot gloss oil of claim 1, further comprising 0.2 to 0.4 parts by mass of nano titanium dioxide.

4. The aqueous polycarbonate rain boot gloss oil of claim 2, wherein the aqueous film forming aid is one or both of propylene glycol butyl ether and propylene glycol methyl ether acetate.

5. The aqueous polycarbonate rain boot polish of claim 1, wherein the cellulose ether is one or more of methylcellulose, hydroxypropyl methylcellulose, sodium carboxymethyl cellulose, hydroxyethyl cellulose.

6. The aqueous polycarbonate rain boot polish of claim 1, wherein the dispersant is a fatty acid sulfonate or a fatty acid sulfonate.

7. The aqueous polycarbonate rain boot gloss oil of claim 1, wherein the antioxidant is one or more of antioxidant 565, antioxidant 1010, antioxidant 4010.

8. The method of preparing the aqueous polycarbonate rain boot gloss oil of any one of claims 1-7, comprising the steps of: fully stirring the components, and uniformly mixing to obtain the water-based polycarbonate rain boot gloss oil.

9. The method of using the aqueous polycarbonate rain boot polish prepared according to claim 8, characterized by comprising the steps of: and (3) immersing the rain shoes into the water-based polycarbonate rain shoe polish, taking out, drying and vulcanizing.

10. The method of using the aqueous polycarbonate rain boot polish of claim 8, wherein the time for immersing the rain boot in the aqueous polycarbonate rain boot polish is 5 to 10 seconds; the drying condition is air drying at 20-50 deg.C; the vulcanization condition is 115-125 ℃, and the time is 40-60 min.

Technical Field

The invention relates to water-based polycarbonate rain boot gloss oil, a preparation method of the water-based polycarbonate rain boot gloss oil and a use method of the water-based polycarbonate rain boot gloss oil, and belongs to the field of rain boot gloss oil.

Background

The existing leather finishing agents are various in types, polyurethane substances are generally used, but the comprehensive performance of the polyurethane gloss oil applied to rain shoes is still required to be improved.

Disclosure of Invention

Aiming at the defects in the prior art, the invention provides the water-based polycarbonate rain boot gloss oil, and the preparation method and the use method thereof, and the water-based polycarbonate rain boot gloss oil has good use performance.

The technical scheme for solving the technical problems is as follows: the water-based polycarbonate rain boot gloss oil comprises the following raw materials in parts by mass: 40-50 parts of polycarbonate, 8-16 parts of water-soluble acrylic resin, 2-3 parts of water-based film-forming assistant, 0.2-0.4 part of polyether, 0.2-0.4 part of dimethyl silicone oil, 0.6-0.6 part of water-based flatting agent BYK-3330.1, 0.2-0.4 part of cellulose ether, 0.2-0.4 part of dispersant, 0.1-0.3 part of antioxidant, 0.3-0.6 part of light stabilizer, 4-12 parts of ethanol and 20-40 parts of water.

The invention is further provided that the water-based polycarbonate rain boot gloss oil comprises the following raw materials in parts by mass: 46-48 parts of polycarbonate, 10-12 parts of water-soluble acrylic resin, 2.5-3 parts of water-based film-forming assistant, 0.2-0.3 part of polyether, 0.2-0.3 part of dimethyl silicone oil, 0.3-0.4 part of water-based flatting agent BYK-3330.3, 0.3-0.4 part of cellulose ether, 0.2-0.3 part of dispersing agent, 0.2 part of antioxidant, 0.5 part of light stabilizer, 6-9 parts of ethanol and 30-34 parts of water.

Wherein, the polyether and the dimethyl silicone oil are used as the water-based defoaming agent, the polyether has stronger foam inhibition capability, the dimethyl silicone oil has strong hydrophobicity and can break foam rapidly, and the cellulose ether is used as the water-based thickening agent.

The invention is further set that the water-based polycarbonate rain boot gloss oil also comprises 0.2-0.4 part by mass of nano titanium dioxide, and the nano titanium dioxide can increase the stability, the optical transparency and the antibacterial property.

The invention is further set that the aqueous film-forming assistant is one or two of propylene glycol butyl ether and propylene glycol methyl ether acetate.

The invention further provides that the cellulose ether is one or more of methylcellulose, hydroxypropyl methylcellulose, sodium carboxymethyl cellulose and hydroxyethyl cellulose.

The invention is further configured that the dispersant is fatty acid sulfonate or fatty acid sulfonate, including sulfosuccinate, fatty acid hydroxyethane sulfonate, unsaturated fatty alcohol ether sulfonate, aryl alkyl sulfonate, and the like.

The invention further provides that the light stabilizer is a hindered amine light stabilizer.

The invention further provides that the antioxidant is one or more of antioxidant 565, antioxidant 1010 and antioxidant 4010.

The invention provides a preparation method of the water-based polycarbonate rain boot gloss oil, which comprises the following steps: fully stirring the components, and uniformly mixing to obtain the water-based polycarbonate rain boot gloss oil.

The invention provides a using method of the prepared water-based polycarbonate rain boot gloss oil, which comprises the following steps: and (3) immersing the rain shoes into the water-based polycarbonate rain shoe polish, taking out, drying and vulcanizing.

The invention is further configured such that the time for immersing the rain shoes in the aqueous polycarbonate rain shoe polish is 5-10 seconds; the drying condition is air drying at 20-50 deg.C; the vulcanization condition is 115-125 ℃, and the time is 40-60 min.

The present invention is further configured such that, in order to increase adhesion, the rain boot is cleaned with water or a surfactant to remove impurities and adhesion before impregnation, so that the water-based polycarbonate rain boot gloss oil is better adhered.

The water-based polycarbonate rain boot gloss oil has the following beneficial effects: the paint has the advantages of soft and fine film forming, strong adhesive force, ultraviolet resistance, high transparency, high film forming speed, water resistance, solvent resistance and good luster, and is suitable for rain shoe polish.

Detailed Description

The technical solutions in the embodiments of the present invention are clearly and completely described below, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.