阅读说明：本技术 一种低水解呋喃树脂及其制备方法 (Low-hydrolysis furan resin and preparation method thereof ) 是由 侯学臻 孙志勇 潘月宝 孙笃新 刘萌 于 2020-05-09 设计创作，主要内容包括：本发明公开了一种低水解呋喃树脂及其制备方法,属于呋喃树脂生产技术领域,所述呋喃树脂包括以下重量份数的原料：甲醛8-12份、糠醇70-80份、尿素7-13份、聚四氢呋喃二醇3-5份、三乙醇胺0.5份、二乙二醇0.3份、异氰酸酯0.5份、偶联剂0.6份、氢氧化钠溶液0.04份、有机酸催化剂0.05份。本发明先是采用聚四氢呋喃二醇代替部分糠醇,抵消掉部分反应生成的水,然后采用二乙二醇、异氰酸酯来吸收剩余的水分,阻断硅烷偶联剂的水解过程,解决反应过程中生成水量很大和偶联剂水解的问题,减小了呋喃树脂中的含水量,使呋喃树脂的强度更长久,满足铸造生产的要求。(The invention discloses a furan resin with low hydrolysis and a preparation method thereof, belonging to the technical field of furan resin production, wherein the furan resin comprises the following raw materials in parts by weight: 8-12 parts of formaldehyde, 70-80 parts of furfuryl alcohol, 7-13 parts of urea, 3-5 parts of polytetrahydrofuran glycol, 0.5 part of triethanolamine, 0.3 part of diethylene glycol, 0.5 part of isocyanate, 0.6 part of coupling agent, 0.04 part of sodium hydroxide solution and 0.05 part of organic acid catalyst. The method adopts polytetrahydrofuran glycol to replace partial furfuryl alcohol to offset partial water generated in the reaction, then adopts diethylene glycol and isocyanate to absorb the residual water to block the hydrolysis process of the silane coupling agent, solves the problems of large water amount generated in the reaction process and hydrolysis of the coupling agent, reduces the water content in the furan resin, enables the strength of the furan resin to be longer, and meets the requirement of casting production.)

1. The low-hydrolysis furan resin is characterized by comprising the following raw materials in parts by weight: 8-12 parts of formaldehyde, 70-80 parts of furfuryl alcohol, 7-13 parts of urea, 3-5 parts of polytetrahydrofuran glycol, 0.5 part of triethanolamine, 0.3 part of diethylene glycol, 0.5 part of isocyanate, 0.6 part of coupling agent, 0.04 part of sodium hydroxide solution and 0.05 part of organic acid catalyst.

2. The resin of claim 1, wherein the formaldehyde is a 36% formaldehyde solution.

3. The furan resin with low hydrolysis content as claimed in claim 1, wherein the coupling agent is N- (beta-aminoethyl) -gamma-aminopropylmethyldimethoxysilane.

4. The resin of claim 1, wherein the sodium hydroxide solution is 30% concentrated.

5. The resin of claim 1, wherein the organic acid catalyst is maleic anhydride.

6. The method for preparing a furan resin with low hydrolysis content of any one of claims 1-5, comprising the steps of:

(1) adding formaldehyde and urea into a reaction kettle, stirring and mixing, adjusting the pH value to 8.5 by using a sodium hydroxide solution, reacting at 85 ℃, and keeping the temperature constant for 3 hours to obtain polymer hydroxymethyl urea;

(2) cooling to 70 ℃, adjusting the pH value to 2.5-3 by using an organic acid catalyst, adding furfuryl alcohol and polytetrahydrofuran diol, stirring and mixing uniformly, heating to 100-;

(3) regulating the pH value to 7-7.5 by using triethanolamine, cooling to 95 ℃, adding diethylene glycol, isocyanate and a coupling agent, stirring and mixing uniformly, reacting for 1 hour, cooling to 55-60 ℃, and discharging to obtain the low hydrolysis furan resin.

Technical Field

The invention relates to the technical field of furan resin production, in particular to a low hydrolysis furan resin and a preparation method thereof.

Background

The furan resin has the advantages of high strength, quick solidification, low gas evolution, good collapsibility and the like, and is widely applied to casting, especially the precision casting industry. In the production process of furan resin, the raw materials comprise formaldehyde, furfuryl alcohol, urea and auxiliary additives, and the production process has obvious influence on the utilization rate and the polymerization state of the raw materials and also has obvious influence on the service performance of the product, including the adhesive strength and collapsibility of molding sand and the protection of casting environment.

The traditional furan resin production method comprises the steps of firstly carrying out addition reaction on formaldehyde and urea under an alkaline condition, then carrying out polycondensation reaction on the formaldehyde and the urea under an acidic condition, and finally carrying out neutralization reaction on the formaldehyde and the urea under an alkaline condition. In the process, the amount of water generated by the reaction is large, so that the water content in the furan resin is greatly increased, the moisture is large, the use of a high-requirement casting is not facilitated, and in addition, the moisture is high and can generate hydrolysis reaction with a coupling agent in the resin to damage the amino group of the coupling agent, so that the strength of the furan resin is reduced.

Disclosure of Invention

Aiming at the technical problems, the invention provides the low hydrolysis furan resin and the preparation method thereof, which improve the hydrolysis resistance of the furan resin by selecting polytetrahydrofuran glycol, diethylene glycol and isocyanate, increase the strength of the furan resin and reduce the production cost at the same time.

In order to achieve the purpose, the invention adopts the following technical scheme:

a furan resin with low hydrolysis comprises the following raw materials in parts by weight: 8-12 parts of formaldehyde, 70-80 parts of furfuryl alcohol, 7-13 parts of urea, 3-5 parts of polytetrahydrofuran glycol, 0.5 part of triethanolamine, 0.3 part of diethylene glycol, 0.5 part of isocyanate, 0.6 part of coupling agent, 0.04 part of sodium hydroxide solution and 0.05 part of organic acid catalyst.

Preferably, the formaldehyde is a 36% formaldehyde solution.

Preferably, the coupling agent is N- (beta-aminoethyl) -gamma-aminopropylmethyldimethoxysilane.

Preferably, the concentration of the sodium hydroxide solution is 30%.

Preferably, the organic acid catalyst is maleic anhydride.

The invention also provides a preparation method of the furan resin with low hydrolysis, which comprises the following steps:

(1) adding formaldehyde and urea into a reaction kettle, stirring and mixing, adjusting the pH value to 8.5 by using a sodium hydroxide solution, reacting at 85 ℃, and keeping the temperature constant for 3 hours to obtain polymer hydroxymethyl urea;

(2) cooling to 70 ℃, adjusting the pH value to 2.5-3 by using an organic acid catalyst, adding furfuryl alcohol and polytetrahydrofuran diol, stirring and mixing uniformly, heating to 100-;

(3) regulating the pH value to 7-7.5 by using triethanolamine, cooling to 95 ℃, adding diethylene glycol, isocyanate and a coupling agent, stirring and mixing uniformly, reacting for 1 hour, cooling to 55-60 ℃, and discharging to obtain the low hydrolysis furan resin.

The beneficial technical effects of the invention are as follows: the invention adopts polytetrahydrofuran diol to replace partial furfuryl alcohol to offset partial water generated in reaction, solves the problem of large water amount generated in the reaction process, reduces the water content in furan resin and meets the requirement of using castings; the invention also adopts diethylene glycol and isocyanate to absorb the residual moisture, blocks the hydrolysis process of the silane coupling agent, solves the problem that the amino group of the coupling agent is damaged by the hydrolysis of the coupling agent, avoids the strength reduction of the furan resin and enables the strength of the furan resin to be longer; the invention reduces the furfuryl alcohol consumption and the cost.

Detailed Description

The present invention will be further described with reference to the following specific examples.