阅读说明：本技术 一种纤维复合材料的制备方法 (Preparation method of fiber composite material ) 是由 汤学红 戴云 王博 李玲 杨雷 于 2018-07-12 设计创作，主要内容包括：本发明公开了一种纤维复合材料的制备方法,它是将配方量的组分共混后,经挤压造粒即得；其中,所述的配方量的组分为如下质量份数的组分：碳纤维30～60份、二氧化钛粉末20～40份、树脂15～30份、发泡剂5～10份、稳定剂5～10份。与现有技术相比,本发明产品性能优异,环境友好且制备方法简单,适于大规模推广。(The invention discloses a preparation method of a fiber composite material, which is obtained by blending components with a formula amount and then extruding and granulating the mixture; the formula comprises the following components in parts by mass: 30-60 parts of carbon fiber, 20-40 parts of titanium dioxide powder, 15-30 parts of resin, 5-10 parts of foaming agent and 5-10 parts of stabilizer. Compared with the prior art, the invention has the advantages of excellent product performance, environmental protection and simple preparation method, and is suitable for large-scale popularization.)

一种纤维复合材料的制备方法

技术领域

本发明属于材料领域，具体涉及一种纤维复合材料的制备方法。

背景技术

复合材料是人们运用先进的材料制备技术将不同性质的材料组分优化组合而成的新材料。复合材料的基体材料分为金属和非金属两大类。金属基体常用的有铝、镁、铜、钛及其合金。非金属基体主要有合成树脂、橡胶、陶瓷、石墨、碳等。增强材料主要有玻璃纤维、碳纤维、硼纤维、芳纶纤维、碳化硅纤维、石棉纤维、晶须、金属。目前，具有优异性能的复合材料是社会所亟需的。

发明内容

本发明要解决的技术问题是提供一种纤维复合材料的制备方法，以解决现有技术存在的效果不佳等问题。

为解决上述技术问题，本发明采用的技术方案如下：

一种纤维复合材料，它包括如下质量份数的组分：

其中，优选如下质量份数的组分：

其中，所述的树脂为乙醛树脂。

其中，所述的发泡剂为玻璃发泡剂。

其中，所述的稳定剂为三盐基硫酸铅。

上述纤维复合材料的制备方法包括如下步骤：

将配方量的组分共混后，经挤压造粒即得。

有益效果：

与现有技术相比，本发明产品性能优异，环境友好且制备方法简单，适于大规模推广。

具体实施方式

根据下述实施例，可以更好地理解本发明。然而，本领域的技术人员容易理解，实施例所描述的内容仅用于说明本发明，而不应当也不会限制权利要求书中所详细描述的本发明。

实施例1

材料及其份数：碳纤维54份、二氧化钛粉末26份、树脂22份、发泡剂6份、稳定剂8份。

制备方法：将配方量的组分共混后，经挤压造粒即得。