阅读说明：本技术 一种纳米级超滤生物集成膜的制备方法 (Preparation method of nano-scale ultrafiltration biological integrated membrane ) 是由 李天栋 李天舒 于 2019-10-23 设计创作，主要内容包括：本发明涉及一种纳米级超滤生物集成膜的制备方法,由超细化处理后的主料及辅料经切割、共混、填充、改性、挤压成型、真空干燥、连续焙烧、硬处理后制成多孔吸附支撑体,多孔吸附支撑体再经清洗、烘干、全自动喷涂刮膜、高温热解、活化后制成孔径为0.1～0.01μm,成孔率＞50％的纳米级超滤膜；纳米级超滤膜再经培养驯化后的微生物挂膜制成纳米级超滤生物集成膜。本发明将膜技术与污水生物处理工艺有机结合,集超精过滤、超强吸附及生物膜操作于一体,运用现代超细化处理技术,针对不同污水源培养驯化特异工程菌,所制备的纳米级超滤生物集成膜制造成本低、吸附处理效果好,为高效处理各类有机废水提供了基础。(The invention relates to a preparation method of a nano-scale ultrafiltration biological integrated membrane, which is characterized in that a main material and an auxiliary material after superfine treatment are cut, blended, filled, modified, extruded, formed, dried in vacuum, continuously roasted and hard treated to prepare a porous adsorption support body, and the porous adsorption support body is cleaned, dried, sprayed and scraped with a membrane in full-automatic mode, pyrolyzed at high temperature and activated to prepare the nano-scale ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the pore forming rate of more than 50 percent; the nano-scale ultrafiltration membrane is cultured and domesticated to form a microbial biofilm to form the nano-scale ultrafiltration biological integrated membrane. The invention organically combines the membrane technology and the sewage biological treatment process, integrates the operations of ultra-fine filtration, ultra-strong adsorption and biological membrane, applies the modern ultra-fine treatment technology, and cultures and domesticates specific engineering bacteria aiming at different sewage sources, and the prepared nano-scale ultrafiltration biological integrated membrane has low manufacturing cost and good adsorption treatment effect, and provides a foundation for efficiently treating various organic wastewater.)

1. A preparation method of a nanometer ultrafiltration biological integrated membrane is characterized in that a main material and an auxiliary material after superfine treatment are cut, blended, filled, modified, extruded, formed, vacuum-dried, continuously roasted and hard-treated to prepare a porous adsorption support body, and the porous adsorption support body is cleaned, dried, fully-automatically sprayed and scraped with a membrane, pyrolyzed at high temperature and activated to prepare the nanometer ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the pore forming rate of more than 50 percent; the nano-scale ultrafiltration membrane is cultured and domesticated to form a microbial biofilm to form a nano-scale ultrafiltration biological integrated membrane;

the main material is activated carbon fiber and/or activated carbon with liquid phase mesopore porosity of more than 50 percent, and the pore diameter of the liquid phase mesopore is

2. The method for preparing a nano-scale ultrafiltration bio-integrated membrane according to claim 1, wherein the activated carbon fiber is polyacrylonitrile-based activated carbon fiber, viscose-based activated carbon fiber or synthetic-based activated carbon fiber; the active carbon is coconut shell active carbon or coal-based active carbon.

3. The method of claim 1, wherein the ultra-high molecular weight polyethylene is ultra-high molecular weight polyethylene particles having a particle size of 10-100 μm.

4. The method of claim 1, wherein the nanoscale metal oxide is a metal oxide with a particle size of 1-100 nm, and the metal oxide comprises TiO₂、Al₂O₃、ZnO₂And when the metal oxides are multiple, the metal oxides are mixed according to any proportion.

5. The method for preparing a nano-scale ultrafiltration bio-integrated membrane according to claim 1, wherein the raw material of the porous adsorption support further comprises a filler, the filler is polyamide fiber, alumina fiber, carbon fiber or glass fiber, the filler is chopped according to an aspect ratio L/D of 4-16, and the filler is added in an amount of 5-20 parts by weight.

6. The method for preparing a nano-scale ultrafiltration bio-integrated membrane according to claim 1, wherein the packing density of the main material is 53-76%, the length-diameter ratio L/D of the activated carbon fiber is 4-16, and the particle size of the activated carbon is determined according to the particle diameter/fiber diameter of 0.1-17.

7. The method according to claim 1, wherein one or more of a coupling agent, a cementing agent, a pore-forming agent, a release agent, and a bactericidal bacteriostatic agent is added in an amount of 1 to 10 parts by weight during the preparation of the porous adsorption support.

8. The method for preparing a nano-scale ultrafiltration bio-integrated membrane according to any one of claims 1 to 7, comprising the following steps:

1) cutting and blending the main material, the auxiliary material and the filler according to a ratio, filling the mixture into a mold for pressure forming after ensuring uniform mixing, sending the mixture into a roasting furnace for continuous roasting under the protection of nitrogen after vacuum drying, wherein the temperature of the roasting furnace is 150-260 ℃, the temperature rising speed is 30-50 ℃, the temperature is kept for 2-2.5 hours after roasting, and the porous adsorption support body is prepared after hot core pulling and water cooling mold stripping;

2) coating a polyacrylonitrile coated layer on a porous adsorption support, performing high-temperature pyrolysis under the protection of nitrogen to generate an ultrathin carbon film, and activating to prepare a nano ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the porosity of more than 50%;

3) determining a specific strain for biofilm formation according to the wastewater to be treated; taking 3-4 water samples and active sludge samples on site, and determining strains, nutrient sources, refractory organic matters, heavy metals and harmful substance types; selecting nutrient medium, screening strains, and replicating specific environment including temperature, pH value, oxygen content, nutrient source, air holes and illumination intensity according to field environment conditions; culturing and domesticating the determined specific strain in a specific environment to adapt to the water quality condition of the wastewater to be treated;

4) the nano-scale ultrafiltration membrane is cultured and domesticated to form a specific strain biofilm, and then the nano-scale ultrafiltration biological integrated membrane is prepared.

Technical Field

The invention relates to the technical field of sewage treatment, in particular to a preparation method of a nano-scale ultrafiltration biological integrated membrane.

Background

With the rapid development of national economy and the increasing severity of water environment pollution, a second water resource platform is urgently needed to be constructed to relieve the shortage of urban water and agricultural irrigation water, so that a wastewater treatment technology suitable for the development of the times is urgently needed.

In recent years, various new and improved high-efficiency wastewater treatment processes, equipment and new materials have been developed, and among them, the application of membrane separation technology, especially Membrane Bioreactor (MBR) combined treatment process, in wastewater treatment has attracted attention. Compared with the traditional biological wastewater treatment process, the process has the advantages of good effluent quality, nearly zero suspended matters and turbidity, direct reuse, small occupied area of equipment, high activated sludge concentration, low residual sludge amount, convenience for automatic control and the like. However, the combined treatment process of the membrane bioreactor has high energy consumption and high component cost in the current practical application, which hinders the development of the combined treatment process, and the MBR is believed to be more widely applied and popularized in the wastewater treatment along with the reduction of the manufacturing cost of the membrane due to the development of the membrane technology and the continuous research and development of novel membrane components and membrane bioreactors.

Chinese patent publication No. CN1336248A discloses a "method for manufacturing activated microfiltration sintered membrane", which is characterized by using activated carbon fibers as a main material, ceramic, powder of high molecular material or fiber product as an aggregate, and a targeted filler as an auxiliary material, performing high-power cutting type blending, filling, reinforcing modification, pressure forming, melt sintering, cooling at 150-230 ℃, quenching and post-processing to manufacture a sintering method with high-strength activated microfiltration integration. The active microfiltration sintered membrane has the functions of adsorption and microfiltration, and adopts general active carbon fiber (the specific surface area is 1000-²Per g, mean pore diameter

The micropore volume is 0.4-0.7ml/g), thus being particularly suitable for gas phase purification of organic steam or poisonous and harmful smoke, and the like, and only realizing the interception and removal of particles and bacteria with the particle diameter of 0.02-10 mu m for liquid phase.

Disclosure of Invention

The invention provides a preparation method of a nano-scale ultrafiltration biological integrated membrane, which organically combines a membrane technology and a sewage biological treatment process, integrates operations of ultra-fine filtration, ultra-strong adsorption and a biological membrane, applies a modern ultra-fine treatment technology, and cultures and acclimates specific engineering bacteria aiming at different sewage sources.

In order to achieve the purpose, the invention adopts the following technical scheme:

a preparation method of a nanometer ultrafiltration biological integrated membrane comprises the steps of cutting, blending, filling, modifying, extruding and forming, vacuum drying, continuous roasting and hard processing main materials and auxiliary materials after superfine processing to prepare a porous adsorption support body, and then cleaning, drying, full-automatic spraying and membrane scraping, high-temperature pyrolysis and activation are carried out on the porous adsorption support body to prepare the nanometer ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the pore forming rate of more than 50%; the nano-scale ultrafiltration membrane is cultured and domesticated to form a microbial biofilm to form a nano-scale ultrafiltration biological integrated membrane;

the main material is activated carbon fiber and/or activated carbon with liquid phase mesopore porosity of more than 50 percent, and the pore diameter of the liquid phase mesopore is

The auxiliary materials are micron-sized ultrahigh molecular weight polyethylene and nano-sized metal oxides; the weight parts of the main material are 60-80 parts, the micron-sized ultrahigh molecular weight polyethylene is 40-50 parts, and the nano-sized metal oxide is 6-10 parts.

The activated carbon fiber is polyacrylonitrile-based activated carbon fiber, viscose-based activated carbon fiber or synthetic-based activated carbon fiber; the active carbon is coconut shell active carbon or coal-based active carbon.

The micron-sized ultra-high molecular weight polyethylene is ultra-high molecular weight polyethylene particles with the particle size of 10-100 mu m.

The nano-scale metal oxide is metal oxide with the particle size of 1-100 nm, and the metal oxide comprises TiO₂、Al₂O₃、ZnO₂And when the metal oxides are multiple, the metal oxides are mixed according to any proportion.

The raw materials of the porous adsorption support body also comprise a filler, the filler is polyamide fiber, alumina fiber, carbon fiber or glass fiber, the filler is chopped according to the length-diameter ratio L/D of 4-16, and the adding amount of the filler is 5-20 parts by weight.

The stacking density of the main material is 53-76%, the length-diameter ratio L/D of the activated carbon fiber is 4-16, and the particle size of the activated carbon is determined according to the particle diameter/fiber diameter which is 0.1-17.

And adding one or more of a coupling agent, a cementing agent, a pore-forming agent, a release agent and a sterilization and bacteriostat in the preparation process of the porous adsorption support body, wherein the adding amount is 1-10 parts by weight.

A preparation method of a nano-scale ultrafiltration bio-integrated membrane specifically comprises the following steps:

1) cutting and blending the main material, the auxiliary material and the filler according to a ratio, filling the mixture into a mold for pressure forming after ensuring uniform mixing, sending the mixture into a roasting furnace for continuous roasting under the protection of nitrogen after vacuum drying, wherein the temperature of the roasting furnace is 150-260 ℃, the temperature rising speed is 30-50 ℃, the temperature is kept for 2-2.5 hours after roasting, and the porous adsorption support body is prepared after hot core pulling and water cooling mold stripping;

2) coating a polyacrylonitrile coated layer on a porous adsorption support, performing high-temperature pyrolysis under the protection of nitrogen to generate an ultrathin carbon film, and activating to prepare a nano ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the porosity of more than 50%;

3) determining a specific strain for biofilm formation according to the wastewater to be treated; taking 3-4 water samples and active sludge samples on site, and determining strains, nutrient sources, refractory organic matters, heavy metals and harmful substance types; selecting nutrient medium, screening strains, and replicating specific environment including temperature, pH value, oxygen content, nutrient source, air holes and illumination intensity according to field environment conditions; culturing and domesticating the determined specific strain in a specific environment to adapt to the water quality condition of the wastewater to be treated;

4) the nano-scale ultrafiltration membrane is cultured and domesticated to form a specific strain biofilm, and then the nano-scale ultrafiltration biological integrated membrane is prepared.

Compared with the prior art, the invention has the beneficial effects that:

1) the main raw materials of the membrane material reach the micron level or the submicron level, and simultaneously, the nano metal oxide is added, so that the function of the product is greatly improved, and the prepared nano ultrafiltration bio-integrated membrane presents the characteristics which are not possessed by the conventional membrane material in the aspects of light, electricity, magnetism, heat, various quantum small-size effects and the like;

2) the high-efficiency adsorption material-liquid-phase mesoporous activated carbon fiber or activated carbon is selected as a main material, so that organic matters in sewage can be strongly adsorbed, dissolved oxygen is enriched on the carbon surface, an excellent environment is provided for the growth and the propagation of microorganisms, the situation that high-concentration organic matters, oxygen molecules and microorganisms exist on the carbon surface at the same time is formed, and favorable conditions are created for biochemical treatment;

3) specific engineering bacteria are cultured and domesticated aiming at different sewage sources, the integration of a membrane and biological strains is realized, various specific engineering bacteria can effectively treat organic matters and harmful matters in sewage, the inorganic and harmless treatment of sewage is realized, organic matters, heavy metals and the like which are difficult to degrade are removed, the purposes of good quality of effluent, nearly zero suspended matters and turbidity and direct recycling are achieved, and the recycling of wastewater is realized;

4) the nano-scale ultrafiltration biological integrated membrane has the synergistic enhancement effect of the high-efficiency adsorption function of liquid-phase active carbon fibers or active carbon and the purification of the biological membrane in the use process; through being equipped with the self-cleaning membrane system, make the biology of ageing in time drop, the charcoal surface of integrated membrane is constantly renewed, can form the operation mode of absorption while, degradation, fresh absorption (promptly regeneration) simultaneously, makes active material adsorption capacity enlarge, effective increase of service life, has reduced use cost correspondingly.

Detailed Description

The invention relates to a preparation method of a nanometer ultrafiltration biological integrated membrane, which is characterized in that a main material and an auxiliary material after superfine treatment are cut, blended, filled, modified, extruded, formed, dried in vacuum, continuously roasted and hard treated to prepare a porous adsorption support body, and the porous adsorption support body is cleaned, dried, sprayed and scraped with a membrane in full-automatic mode, pyrolyzed at high temperature and activated to prepare the nanometer ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the pore forming rate of more than 50 percent; the nano-scale ultrafiltration membrane is cultured and domesticated to form a microbial biofilm to form a nano-scale ultrafiltration biological integrated membrane;

the main material is activated carbon fiber and/or activated carbon with liquid phase mesopore porosity of more than 50 percent, and the pore diameter of the liquid phase mesopore is

The auxiliary materials are micron-sized ultrahigh molecular weight polyethylene and nano-sized metal oxides; the weight parts of the main material are 60-80 parts, the micron-sized ultrahigh molecular weight polyethylene is 40-50 parts, and the nano-sized metal oxide is 6-10 parts.

The activated carbon fiber is polyacrylonitrile-based activated carbon fiber, viscose-based activated carbon fiber or synthetic-based activated carbon fiber; the active carbon is coconut shell active carbon or coal-based active carbon.

The micron-sized ultra-high molecular weight polyethylene is ultra-high molecular weight polyethylene particles with the particle size of 10-100 mu m.

The nano-scale metal oxide is metal oxide with the particle size of 1-100 nm, and the metal oxide comprises TiO₂、Al₂O₃、ZnO₂And when the metal oxides are multiple, the metal oxides are mixed according to any proportion.

The raw materials of the porous adsorption support body also comprise a filler, the filler is polyamide fiber, alumina fiber, carbon fiber or glass fiber, the filler is chopped according to the length-diameter ratio L/D of 4-16, and the adding amount of the filler is 5-20 parts by weight.

The stacking density of the main material is 53-76%, the length-diameter ratio L/D of the activated carbon fiber is 4-16, and the particle size of the activated carbon is determined according to the particle diameter/fiber diameter which is 0.1-17.

And adding one or more of a coupling agent, a cementing agent, a pore-forming agent, a release agent and a sterilization and bacteriostat in the preparation process of the porous adsorption support body, wherein the adding amount is 1-10 parts by weight.

A preparation method of a nano-scale ultrafiltration bio-integrated membrane specifically comprises the following steps:

1) cutting and blending the main material, the auxiliary material and the filler according to a ratio, filling the mixture into a mold for pressure forming after ensuring uniform mixing, sending the mixture into a roasting furnace for continuous roasting under the protection of nitrogen after vacuum drying, wherein the temperature of the roasting furnace is 150-260 ℃, the temperature rising speed is 30-50 ℃, the temperature is kept for 2-2.5 hours after roasting, and the porous adsorption support body is prepared after hot core pulling and water cooling mold stripping;

2) coating a polyacrylonitrile coated layer on a porous adsorption support, performing high-temperature pyrolysis under the protection of nitrogen to generate an ultrathin carbon film, and activating to prepare a nano ultrafiltration membrane with the aperture of 0.1-0.01 mu m and the porosity of more than 50%;

3) determining a specific strain for biofilm formation according to the wastewater to be treated; taking 3-4 water samples and active sludge samples on site, and determining strains, nutrient sources, refractory organic matters, heavy metals and harmful substance types; selecting nutrient medium, screening strains, and replicating specific environment including temperature, pH value, oxygen content, nutrient source, air holes and illumination intensity according to field environment conditions; culturing and domesticating the determined specific strain in a specific environment to adapt to the water quality condition of the wastewater to be treated;

4) the nano-scale ultrafiltration membrane is cultured and domesticated to form a specific strain biofilm, and then the nano-scale ultrafiltration biological integrated membrane is prepared.

According to different working conditions of treatment objects, liquid phases and media, different chemical and physical properties and great difference of functional requirements on the membrane, such as strength, water-gas flux, pollutant carrying capacity or whether special filtration is needed or not, specific adsorption requirements and the like, the following substances can be added according to requirements when the nano-scale ultrafiltration bio-integrated membrane is prepared:

reinforcing filler: polyamide fibers, alumina fibers, carbon fibers, glass fibers, and the like.

Coupling agent: silane coupling agents are commonly used.

Cementing agent: paraffin, water glass, paper pulp, polyvinyl alcohol aqueous solution, starch and the like.

Pore-forming agent: charcoal, wood powder, coke powder, paraffin, plastic powder, inorganic salt,

Releasing agent: graphite powder, mica powder, talcum powder and the like.

And (3) sterilization and bacteriostat: triiodine resin, high-purity copper-zinc alloy powder and the like.

The nano-scale ultrafiltration biological integrated membrane of the inventionThe ultrafiltration, adsorption and biomembrane operation units are integrated into a whole, the fired aperture is 0.01-0.1 mu m, the pore forming rate is more than 50 percent, and the liquid phase mesopore

Activated carbon fiber suitable for liquid phase entrapment

Macromolecular solute and colloidal protein particles of 5nm to 10nm adsorb soluble organic matters of 3nm to 50 nm; the nanometer level ultrafiltering integrated biological membrane has the advantages that the nanometer level ultrafiltering integrated biological membrane has the characteristics of light, electricity, magnetism, heat and the like which are not possessed by a series of conventional materials, can lead harmful substances to be inorganic and harmless in sewage purification, removes organic substances which are difficult to degrade and fully recycles purified water.

For example: ti0₂In application, the particle size is an important factor influencing the performance of the membrane, and nano Ti0 is added into the nano ultrafiltration biological integrated membrane₂Average particle size of 6nm and surface area of up to 500m²/cm³The Ti atoms in the surface structure lack oxygen atom coordination, so that the surface has high activity, and has stronger ultraviolet light absorption capacity under the irradiation of purple external light, thereby having more excellent photocatalytic degradation capacity.

In the treatment of wastewater, the nano Ti0₂The strong photocatalytic and oxidation effects of the compound can fully, quickly and completely oxidize organic matters in the sewage such as hydrocarbons, hydroxy acids, surface neutral agents, dyes, organic phosphorus pesticides and the like to generate CO₂And H₂O, and the like.

Compared with the Chinese patent 'active microfiltration sintered membrane manufacturing method' with the publication number of CN1336248A, the nano-scale ultrafiltration bio-integrated membrane has the following advantages:

1) the microfiltration is upgraded to the ultrafiltration, namely the treatment granularity is greatly improved.

2) More than two operation units are integrated, so that the treatment process is more complete.

3) The nanometer ultrafiltration biological integrated membrane has the pre-selectivity of function, shape and structure according to different treatment objects.

4) The main materials, the aggregates and the auxiliary materials of the nano-scale ultrafiltration biological integrated membrane are mostly treated by adopting an ultra-fine technology (the particles, fibers and other functional raw materials are micron materials with the particle size of more than 1 mu m, submicron materials with the particle size of less than 1 mu m and more than 0.1 mu m, and nano materials with the particle size of 0.001-0.1 mu m (1-10 nm)).

For a single micron or submicron material, the physical and chemical characteristics of the material are not much different from those of a bulk material, but two different micron or submicron materials are compounded to prepare a new composite material, the properties of the new composite material are greatly changed, characteristics completely different from those of raw materials are generated, such as melting point reduction, chemical activity improvement, catalytic effect enhancement and the like, and novel functional materials with completely different performances can be prepared.

Particularly, after the nano metal oxide (with the particle size of 1-100 nm) is added, the crystal period boundary condition is destroyed, and the acoustic, optical, electrical, electromagnetic and thermodynamic properties all show new size effects. Because the dispersed phase has small particle size, large surface area, high activity and serious surface atom vacancy, the nano-scale ultrafiltration bio-integrated membrane is very easy to combine with other atoms to generate a new heterofacial effect and simultaneously generate a quantum size effect, a macroscopic quantum tunneling effect and the like, the nano-scale ultrafiltration bio-integrated membrane has the characteristics which are not possessed by a series of conventional materials, and the characteristics that organic matters and heavy metals which are difficult to degrade can be treated in sewage purification are removed, so that the purification effect is improved.

5) By using mesopores in liquid phase

The activated carbon fiber (felt, cloth, silk paper, etc.) or liquid-phase mesoporous activated carbon (powder or particles) is used as a main material, and various functions in the liquid phase are fully exerted in the application.

6) Fully exerts the high-efficiency adsorption function of the activated carbon fiber or the activated carbon and the synergistic effect of the biological membrane. Mesopores in the liquid phase during the treatment of waste water

Activated carbon fiber ofThe vitamin adsorbs organic matters in water, meanwhile, the dissolved oxygen in the water is enriched on the surface of the carbon, a good environment is provided for the growth and the propagation of microorganisms, and the situation that high-concentration organic matters, oxygen molecules and microorganisms exist simultaneously is formed on the surface of the carbon, so that the synergistic effect of adsorption and biochemical treatment is achieved. Compared with the conventional single biochemical treatment, the biological treatment method is more favorable, the contact time of organic matters and microorganisms is prolonged by the adsorption of the activated carbon fibers or the activated carbon, a favorable living environment is provided for the domestication of the microorganisms, the domesticated specific flora can improve the purification efficiency of the treated sewage, and the removal capacity of the organic matters and heavy metals which are difficult to degrade in the treated sewage is enhanced. If an efficient automatic cleaning system is equipped to timely remove the aged biological membrane during operation, the carbon surface of the integrated membrane is continuously updated, the situations of adsorption, degradation and fresh absorption (namely regeneration) can be formed, so that the adsorption capacity of the nano-scale ultrafiltration biological integrated membrane is enlarged, and the service cycle of the carbon is prolonged. In the continuous operation, the treatment process and the regeneration process are carried out simultaneously to form the synergistic effect of adsorption and degradation, so that the sewage treatment and the activated carbon fiber or activated carbon regeneration process are carried out simultaneously, and the win-win result with high efficiency and low cost is realized.

The following examples are carried out on the premise of the technical scheme of the invention, and detailed embodiments and specific operation processes are given, but the scope of the invention is not limited to the following examples. The methods used in the following examples are conventional methods unless otherwise specified.

[ example 1 ]

In this example, the main material is liquid phase mesopore (pore diameter is

) The polypropylene gum base active carbon fiber and the coconut shell active carbon; wherein the adding amount of the polypropylene gum base active carbon fiber is 50 parts by weight; the addition amount of the coconut shell activated carbon is 30 parts by weight. The length-diameter ratio L/D of the chopped polypropylene gum base activated carbon fiber is 4, and the specific surface area is 960m²The methylene blue adsorption value is 200 mg/g. The particle size of the coconut shell activated carbon is 400 meshes.

The auxiliary materials adopt 60 parts by weight of ultra-high molecular weight polyethylene (the granularity is 10 mu m) and 8 parts by weight of metal oxideTiO₂(particle size 6 nm).

The filler is 10 parts by weight of chopped carbon fibers, and the length-diameter ratio L/D is 4.

The raw materials are fully cut, blended and dried, the mixture is ensured to be uniform, then the mixture is filled into a mold for pressure forming, the mixture is continuously roasted after vacuum drying, the roasting temperature is 260 ℃, the heating rate is 30 ℃, the temperature is kept for 2 hours after roasting, and the nano ultrafiltration membrane with the porosity of more than 70 percent and the pore diameter of 0.1 to 0.01 mu m is prepared through hot core extraction and water cooling mold stripping.

[ example 2 ]

In this example, the main material is liquid phase mesopore (pore diameter is

) The aspect ratio L/D of the chopped viscose-based activated carbon fiber (2) is 4, and the specific surface area is 1200m²The methylene blue adsorption value is 200 mg/g.

The auxiliary materials adopt 60 parts by weight of ultra-high molecular weight polyethylene (with the grain diameter of 10 mu m) and 8 parts by weight of metal oxide Tio₂(particle size 6 nm).

6 parts by weight of polyamide fiber is adopted as the filler, and the length-diameter ratio of the chopped polyamide fiber is 4.

In addition, 5 parts by weight of high-purity copper-zinc alloy powder with the granularity of 400 meshes is added.

The raw materials are fully cut, blended, dried and pressurized, then are loaded into a mold with a stainless steel mesh support liner, and are sent into a roasting furnace to be continuously roasted under the protection of nitrogen, the roasting temperature is 200 ℃, the heating rate is 20 ℃, the temperature is kept for 2 hours after the roasting, the raw materials are taken out of the furnace, and after hot core pulling and water cooling, the nano ultrafiltration membrane with the porosity of more than 50 percent and the pore diameter of 0.1-0.01 um is prepared.

The specification of the nano-scale ultrafiltration biological integrated membrane for determining the biological hanging membrane and the strains is as follows:

with the development of chemical industry, a large number of artificially synthesized compounds enter various fields of daily life and agricultural production, such as detergents, insecticides, herbicides, plastic agents and the like, the organic compounds enter ecological environments through various ways, water pollution is serious day by day, most of the organic compounds have complex aromatic hydrocarbon or heterohydrocarbon structures, are relatively stable and are difficult to degrade by microorganisms. In the past, the effect of single-strain microbial degradation is not obvious, and the single-strain microbial degradation must be realized by means of interaction of two or more microbes in the same environment. A single microorganism often generates toxic end products for the biodegradation of organic matters, and the toxic microorganism has an inhibiting effect on the growth, so that a plurality of microorganisms form a stable microbial community to eliminate the influence of toxic metabolites on degrading bacteria in the biodegradation process of the organic matters. For example, the microbial community for methane oxidation consists of four microorganisms, the main members of which are bacteria of the genus Pseudomonas, which oxidize methane, and the metabolic product of which is methanol, which inhibits the growth of the microorganisms, but the microbial community has the genus Microbacterium, which utilizes methanol as a growth substrate, so that the metabolic relationship is balanced in the microbial community for methane oxidation. Microorganisms have great potential for degrading or converting organic contaminants, and almost all natural substances, especially organic compounds, can find their microbial populations responsible for their biodegradation.

The nano-scale ultrafiltration biological integrated membrane is a hotbed which only provides carbon sources and oxygen sources required for survival and propagation of various microorganisms, and specifically what strains are adopted is one or more, and is determined according to the actual conditions of a sewage site and the standard met by the requirements.

At present, various wastewater treatment plants in the environmental protection scientific research institutions of China have microorganism samples for treating phenol and phenolic compounds, halogen-containing organic matters, nitrogen-containing organic matters, synthetic surfactants, petroleum hydrocarbons, various refractory organic matters and the like and reference data, and users can share the microorganism samples.

In view of the complex structure and diversity of the species of the present pollutants, it is suggested to select a plurality of microbial communities in which the respective bacteria exert the best physiological functions and utilize the synergistic effects thereof to degrade the pollutants with high efficiency.

The water area to be treated with the pollution needs to provide detailed water quality indexes and effluent reaching standards so as to determine a BOD5/COD value; the ratio is more than 0.4, which indicates that the biodegradation rate is higher; the ratio is 0.4-0.3, which indicates that the biodegradation rate is general; the ratio is 0.3-0.2, which indicates that the biodegradation rate is slow and the microorganism needs to be domesticated; the ratio is less than 0.2, which indicates that the biodegradation rate is very slow and the microorganisms need to be domesticated for a long time.

The procedure of the nano ultrafiltration integrated membrane hanging microorganism is as follows:

1. taking 3-4 water samples and activated sludge samples in the sewage site, and carrying out detailed assay, analysis and summary of the distribution of the pollution source microorganisms and a list of substances needing to be degraded.

2. The strain is removed to domestic scientific research institutions and sewage treatment plants which are already established, the information is consulted to compare the relevant strains, the degradation results and the efficiency with the condition of wastewater to be treated, and the feasible flora is screened or the strains are introduced and inoculated.

3. The biological degradation simulation laboratory replicates environmental factors, is similar in hydraulics, and contains nutrient medium, additive components and the like. Introducing strains or flora, inoculating liquid, etc., preparing, culturing in water area from shallow to deep for 3-5 days, adding degradation product, domesticating microorganism for one week, and testing.

4. In a wastewater treatment laboratory, the conditions of hydraulics indexes such as water environment, flow rate and the like, temperature, pH value, osmotic pressure, illumination and the like of wastewater to be treated are copied, cultured and domesticated strains or flora are propagated in a good growth environment and rapidly contacted with a nanoscale ultrafiltration integrated membrane forming component assembled on a biological rotating disk, various organic matters and dissolved oxygen in sewage are enriched in carbon stone, microorganisms fall on the carbon stone, a membrane is timely hung to create good biochemical conditions, harmful substances in the sewage are innovated and innoxious, organic matters and heavy metals which are difficult to degrade are removed, and the ultrafiltration membrane and the biological membrane are organically combined to form high-quality clear and transparent effluent, suspended matters and turbidity are close to zero, so that the aim of direct recycling is fulfilled.

[ example 3 ]

One rural pond is polluted by the drainage of laundry water, the flushing drainage of livestock pens and high-concentration pesticides, herbicides and the like for a long time, the BOD5/COD is 0.23, and other details are not shown.

After investigation and on-site sampling and screening, activated sludge is adopted to acclimate pseudomonas, bacillus and synthetic detergent in the sewage.

1. Introducing excellent strains and corresponding culture data, taking sludge sample liquid at the lower part of a synthetic detergent drain outlet, culturing in a laboratory for one day, preparing 10 finished products of the nano ultrafiltration integrated biological membrane according to [ example 2 ], immersing in culture solution, reaching 20mg/L in concentration of 1mg/L detergent, pesticide, herbicide and the like within seven days, culturing and propagating for three days, and detecting to obtain a suspended biological membrane with the thickness of 0.5mm, thus being capable of being sent to a wastewater laboratory plant.

2. In a wastewater laboratory, water samples at 3-4 points in a water area to be treated, hydraulic indexes, temperature, illumination, nutrient media, oxygen sources and the like are copied, 10 biological membrane pieces are hung on a biological rotating disk device and are immersed in a water depth of 0.5M for 1.2kg/h of oxygenation capacity, the biological rotating disk device is suitable for observing the oxidation rate and metabolites of strains for 24h, and the biological membrane can leave a factory after being detected to be more than 1 mm.

The above description is only for the preferred embodiment of the present invention, but the scope of the present invention is not limited thereto, and any person skilled in the art should be considered to be within the technical scope of the present invention, and the technical solutions and the inventive concepts thereof according to the present invention should be equivalent or changed within the scope of the present invention.