阅读说明：本技术 一种用于路灯杆制造的防锈剂及其制备方法 (Antirust agent for manufacturing street lamp pole and preparation method thereof ) 是由 李卫松 胡恒全 于 2018-07-23 设计创作，主要内容包括：本发明公开了一种用于路灯杆制造的防锈剂及其制备方法,以重量百分比计,包含以下组分：磷酸30-45％,硫酸锌5-15％,石油醚1.5-2％,羊毛脂防锈剂0.5-1％,多元醇0.3-1％,剩余为水,其制备工艺,按如下步骤进行：(A)混合石油醚与多元醇；(B)进行升温及预热程序,其中温度为50℃-75℃而预热时间为10-30分钟；(C)加入羊毛脂防锈剂、和水混合均匀；(D)执行过滤程序以获得用于路灯杆制造的防锈剂成品；本发明的用于路灯杆制造的防锈剂通过采用磷酸、硫酸锌、石油醚、羊毛脂防锈剂、多元醇和水,没有采用铅等重金属,材料十分的环保,制得的防锈剂环保性能优秀。(The invention discloses an antirust agent for manufacturing a street lamp pole and a preparation method thereof, wherein the antirust agent comprises the following components in percentage by weight: 30-45% of phosphoric acid, 5-15% of zinc sulfate, 1.5-2% of petroleum ether, 0.5-1% of lanolin antirust agent, 0.3-1% of polyalcohol and the balance of water, and the preparation process comprises the following steps: (A) mixing petroleum ether with a polyol; (B) heating and preheating for 10-30 min at 50-75 deg.c; (C) adding lanolin rust inhibitor and water, and mixing; (D) executing a filtering program to obtain a finished antirust agent for manufacturing a light pole; the antirust agent for manufacturing the street lamp pole is prepared from phosphoric acid, zinc sulfate, petroleum ether, lanolin antirust agent, polyhydric alcohol and water, and does not adopt heavy metals such as lead and the like, so that the material is very environment-friendly, and the prepared antirust agent has excellent environment-friendly performance.)

1. The rust inhibitor for manufacturing the street lamp pole is characterized by comprising the following components in percentage by weight: 30-45% of phosphoric acid, 5-15% of zinc sulfate, 1.5-2% of petroleum ether, 0.5-1% of lanolin antirust agent, 0.3-1% of polyhydric alcohol and the balance of water.

2. The rust inhibitor for manufacturing street lamp poles as claimed in claim 1, wherein: the lanolin rust inhibitor is a lanolin magnesium soap rust inhibitor.

3. The rust inhibitor for manufacturing street lamp poles as claimed in claim 1, wherein: the mass percent of the petroleum ether is 1.8%.

4. The rust inhibitor for manufacturing street lamp poles as claimed in claim 1, wherein: the mass percentage of the lanolin antirust agent is 0.8%.

5. A preparation process of an antirust agent for manufacturing a street lamp pole is characterized by comprising the following steps:

(A) mixing petroleum ether with a polyol;

(B) heating and preheating for 10-30 min at 50-75 deg.c;

(C) adding lanolin rust inhibitor and water, and mixing;

(D) and executing a filtering program to obtain a finished antirust agent for manufacturing the light pole.

Technical Field

The invention relates to the field of antirust agent production, in particular to an antirust agent for manufacturing a street lamp pole and a preparation method thereof.

Background

The metal workpiece is easy to rust in the production, processing and transportation processes, so that a layer of film is formed on the surface of the metal by using antirust oil to prevent the metal from rusting, and the antirust agent is formed by selecting high-quality anticorrosive raw materials and various additives and can protect the surface from being damaged by moisture, chemicals, air and other corrosive products. Belongs to an environment-friendly product. Can be widely used for rust prevention among working procedures of components and materials of steel products, stainless steel products and alloy steel products in the industry.

The traditional antirust agents contain lead and other heavy metals, are not very environment-friendly, the requirements of the current society on environment protection are more and more strict, and an environment-friendly antirust agent is in the trend.

Disclosure of Invention

The purpose of the invention is as follows: the invention aims to solve the problems and provides an antirust agent for manufacturing a street lamp pole and a preparation method thereof.

The technical scheme is as follows: the rust inhibitor for manufacturing the street lamp pole is characterized by comprising the following components in percentage by weight: 30-45% of phosphoric acid, 5-15% of zinc sulfate, 1.5-2% of petroleum ether, 0.5-1% of lanolin antirust agent, 0.3-1% of polyhydric alcohol and the balance of water.

Preferably, the lanolin rust inhibitor is a lanolin magnesium soap rust inhibitor.

Preferably, the mass percent of the petroleum ether is 1.8%.

Preferably, the lanolin rust inhibitor is 0.8% by mass.

A preparation process of an antirust agent for manufacturing a street lamp pole comprises the following steps:

(A) mixing petroleum ether with a polyol;

(B) heating and preheating for 10-30 min at 50-75 deg.c;

(C) adding lanolin rust inhibitor and water, and mixing;

(D) and executing a filtering program to obtain a finished antirust agent for manufacturing the light pole.

Has the advantages that: the antirust agent for manufacturing the street lamp pole is prepared from phosphoric acid, zinc sulfate, petroleum ether, lanolin antirust agent, polyhydric alcohol and water, and does not adopt heavy metals such as lead and the like, so that the material is very environment-friendly, and the prepared antirust agent has excellent environment-friendly performance.

Detailed Description

The present invention will be further described with reference to the following specific examples.