阅读说明：本技术 一种防水粘贴布染整工艺 (Dyeing and finishing process for waterproof adhesive cloth ) 是由 宋学强 沈楚良 杨新根 范惠松 朱芬南 傅伟 于 2019-10-21 设计创作，主要内容包括：本发明公开了一种防水粘贴布染整工艺,包括以下步骤,染色→脱水开幅→预定→拉毛→抛光→成定,其中,染色：一浴法加匀染剂、染料后升温到80℃保温5分钟,再升温到110℃保温10分钟,然后升温到132℃保温30分钟；脱水开幅：对染色后的半成品进行脱水开幅处理,便于定型。该防水粘贴布染整工艺定型效果好,成品面料硬挺,线圈竖起,立体感强。(The invention discloses a dyeing and finishing process of waterproof adhesive cloth, which comprises the following steps of dyeing → dewatering scutching → reserving → napping → polishing → finalizing, wherein the dyeing comprises the following steps: adding a leveling agent and a dye by a one-bath method, heating to 80 ℃, keeping the temperature for 5 minutes, heating to 110 ℃, keeping the temperature for 10 minutes, and heating to 132 ℃, keeping the temperature for 30 minutes; dewatering and scutching: and carrying out dehydration scutching treatment on the dyed semi-finished product, so as to facilitate shaping. The dyeing and finishing process for the waterproof adhesive cloth has the advantages of good shaping effect, stiff finished fabric, upright coil and strong stereoscopic impression.)

1. A dyeing and finishing process for waterproof adhesive cloth is characterized in that: comprises the steps of dyeing → dewatering scutching → reserving → napping → polishing → fixing, wherein,

dyeing: adding a leveling agent and a dye by a one-bath method, heating to 75-82 ℃, keeping the temperature for 5 minutes, heating to 100-112 ℃, keeping the temperature for 6-12 minutes, and heating to 130-135 ℃, keeping the temperature for 25-30 minutes;

dewatering and scutching: carrying out dehydration scutching treatment on the dyed semi-finished product, so as to facilitate shaping;

predetermining: presetting the standard of x 65 yards at 180 ℃, 7 percent of fluffing agent and 0.5 percent of silicone oil softening agent;

napping: raising the grey cloth, and pulling up the coil without breaking;

polishing: the surface fluff of the grey cloth is treated by the wool-eating agent to achieve the effect of smoothness;

and (3) finalizing: and (3) shaping the finished product of the fluffed cloth blank at 210 ℃ by 50 yards, adding 9% of stiffening agent, and using a padder with the air pressure of 3.5 kg to ensure that the fabric is stiff and the coils are erected.

2. The waterproof adhesive fabric dyeing and finishing process according to claim 1, characterized in that: adding a leveling agent and a dye by a one-bath method, heating to 80 ℃, keeping the temperature for 5 minutes, heating to 110 ℃, keeping the temperature for 10 minutes, and then heating to 132 ℃, and keeping the temperature for 30 minutes.

The technical field is as follows:

the invention relates to the field of textile printing and dyeing, in particular to a dyeing and finishing process for waterproof adhesive cloth.

Background art:

The invention content is as follows:

the invention aims to solve the technical problem of providing a dyeing and finishing process of waterproof adhesive cloth with good shaping effect, stiff finished fabric and upright coils.

The technical solution of the present invention is to provide a dyeing and finishing process for waterproof adhesive cloth, comprising the steps of dyeing → dewatering scutching → reserving → napping → polishing → finalizing, wherein,

dyeing: adding a leveling agent and a dye by a one-bath method, heating to 80 ℃, keeping the temperature for 5 minutes, heating to 110 ℃, keeping the temperature for 10 minutes, and heating to 132 ℃, keeping the temperature for 30 minutes;

dewatering and scutching: carrying out dehydration scutching treatment on the dyed semi-finished product, so as to facilitate shaping;

predetermining: presetting the standard of x 65 yards at 180 ℃, 7 percent of fluffing agent and 0.5 percent of silicone oil softening agent;

napping: raising the grey cloth, and pulling up the coil without breaking;

polishing: the surface fluff of the grey cloth is treated by the wool-eating agent to achieve the effect of smoothness;

and (3) finalizing: and (3) shaping the finished product of the fluffed cloth blank at 210 ℃ by 50 yards, adding 9% of stiffening agent, and using a padder with the air pressure of 3.5 kg to ensure that the fabric is stiff and the coils are erected.

Preferably, the leveling agent and the dye are added by one-bath method, then the temperature is raised to 80 ℃ and the temperature is kept for 5 minutes, then the temperature is raised to 110 ℃ and the temperature is kept for 10 minutes, and then the temperature is raised to 132 ℃ and the temperature is kept for 30 minutes.

The invention has the beneficial effects that: the shaping effect is good, the finished fabric is stiff, and the coils are erected.

The specific implementation mode is as follows:

the invention will be further illustrated with reference to specific embodiments:

a dyeing and finishing process for water-proof adhesive cloth includes the following steps of dyeing → dewatering open → reserving → napping → polishing → fixing, wherein,

dyeing: adding a leveling agent, namely peregal X-102 and a dye by a one-bath method, heating to 80 ℃, preserving heat for 5 minutes, heating to 110 ℃, preserving heat for 10 minutes, and then heating to 132 ℃, preserving heat for 30 minutes;

dewatering and scutching: carrying out dehydration scutching treatment on the dyed semi-finished product, so as to facilitate shaping;

predetermining: setting the temperature of 180 ℃ multiplied by 65 yards, setting the type 7% of raising agent FS202 and 0.5% of silicone oil softener;

napping: raising the grey cloth, and pulling up the coil without breaking;

polishing: treating the fluff on the surface of the grey cloth by using a wool-eating agent which is neutral polishing enzyme to achieve the effect of smoothness;

and (3) finalizing: and (3) shaping the finished product of the cloth blank after fluffing at 210 ℃ for 50 yards, adding 9% of stiffening agent, and using a padder at an air pressure of 3.5 kg to ensure that the fabric is stiff, and erecting coils, wherein the stiffening agent is an acrylic multi-element copolymer.

The invention has the beneficial effects that: the shaping effect is good, the finished fabric is stiff, and the coils are erected.