阅读说明：本技术 一种木地板封边剂及其使用方法 (Wood floor edge sealing agent and using method thereof ) 是由 杨素文 郑胜根 周强 于 2019-10-17 设计创作，主要内容包括：一种木地板封边剂及其使用方法,将木蜡油45～55质量份、软蜡35～45质量份、硬蜡5～15质量份置于封蜡机料斗中,在120～160℃的温度下加热熔化并搅拌至充分混合,并在110～130℃温度下对木地板进行封边；所述木蜡油包括下列质量份数的各组份：聚合亚麻籽油50～55份,巴西棕榈蜡5份,有机硅改性手感蜡浆10份,达玛树脂17～23份,柑橘油D-柠烯10份,无水酒精2份,虫胶1份；所述软蜡的熔点为42～47℃；所述硬蜡的熔点为不低于50℃。(A wood floor edge sealing agent and a using method thereof are disclosed, wherein 45-55 parts by mass of wood wax oil, 35-45 parts by mass of soft wax and 5-15 parts by mass of hard wax are placed in a wax sealing machine hopper, heated and melted at the temperature of 120-160 ℃, stirred to be fully mixed, and edge sealing is carried out on a wood floor at the temperature of 110-130 ℃; the wood wax oil comprises the following components in parts by weight: 50-55 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organic silicon modified hand feeling wax slurry, 17-23 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 42-47 ℃; the melting point of the hard wax is not lower than 50 ℃.)

1. The edge sealing agent for the wood floor is characterized by comprising the following components in parts by mass: 45-55 parts of wood wax oil; 35-45 parts of soft wax; 5-15 parts of hard wax; the wood wax oil comprises the following components in parts by weight: 50-55 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organic silicon modified hand feeling wax slurry, 17-23 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 42-47 ℃; the melting point of the hard wax is not lower than 50 ℃; is prepared by mixing, heating, melting and uniformly stirring wood wax oil, soft wax and hard wax.

2. The edge banding agent for wood floor according to claim 1, wherein said edge banding agent is prepared by heating 50 parts by mass of wood wax oil, 40 parts by mass of soft wax and 10 parts by mass of hard wax at 130 ℃ until they are melted and uniformly mixed.

3. The edge banding agent for wood floors as claimed in claim 1, wherein the wood wax oil comprises the following components in parts by mass: 53 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organosilicon modified handfeel wax slurry, 18.7 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 45 ℃; the melting point of the hard wax is 51 ℃.

4. The using method of the wood floor edge sealing agent is characterized by comprising the steps of placing 45-55 parts by mass of wood wax oil, 35-45 parts by mass of soft wax and 5-15 parts by mass of hard wax in a wax sealing machine hopper, heating and melting at the temperature of 120-160 ℃, stirring until the materials are fully mixed, and sealing edges of a wood floor at the temperature of 110-130 ℃; the wood wax oil comprises the following components in parts by weight: 50-55 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organic silicon modified hand feeling wax slurry, 17-23 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 42-47 ℃; the melting point of the hard wax is not lower than 50 ℃.

Technical Field

The invention relates to the technical field of wood floors, in particular to a wood floor edge sealing agent; the invention also relates to a use method of the wood floor edge sealing agent.

Background

The existing wood floor in the market generally adopts a paraffin edge sealing process, the purpose of the paraffin edge sealing is to form a layer of paraffin film on an exposed tongue-and-groove of a wood floor substrate, the waterproof and noise reduction effects are achieved, and the wax sealing temperature is generally 80-100 ℃.

CN106832965A discloses a wood floor negative ion formaldehyde-removing edge-sealing wax and a preparation method thereof, wherein the wood floor negative ion formaldehyde-removing edge-sealing wax comprises the following components in parts by weight: 50-85 parts of paraffin, 10-45 parts of high polymer material, 0.5-15 parts of anion powder, 0-10 parts of formaldehyde scavenger and 1-10 parts of surfactant.

Because the used paraffin has different melting points and the temperature has great influence on the wax sealing effect, once the temperature exceeds 40 ℃ in the transportation and use processes of the wood floor, the paraffin on the rabbet is easy to soften and absorbed by the base material fiber, so that the waterproof and noise reduction capabilities are lost, and the paraffin often permeates into the fiber with rough base material due to overhigh temperature and cannot play a waterproof role; or a large amount of wood floor grooves and tongues are accumulated due to low temperature, so that the assembly is difficult. The durability of the waterproof effect of the wood floor after wax sealing is not strong, and after the wood floor is contacted with water for many times (such as mopping floor frequently using a dripping mop), the water-proof effect can be greatly reduced, so that the floor is still easy to bulge.

Disclosure of Invention

In order to overcome the defects of the prior art, the invention aims to provide the wood floor edge sealing agent which has low cost, easy operation, good waterproof effect and strong durability and can reduce abnormal sound generated by the friction of the tongue and groove of the floor and the use method of the wood floor edge sealing agent.

In order to solve the technical problem, on one hand, the invention provides a wood floor edge sealing agent which comprises the following components in parts by mass: 45-55 parts of wood wax oil; 35-45 parts of soft wax; 5-15 parts of hard wax; the wood wax oil comprises the following components in parts by weight: 50-55 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organic silicon modified hand feeling wax slurry, 17-23 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 42-47 ℃; the melting point of the hard wax is not lower than 50 ℃; is prepared by mixing, heating, melting and uniformly stirring wood wax oil, soft wax and hard wax.

As a further improved technical scheme, the wood floor edge sealing agent provided by the invention is prepared by heating to be molten at the temperature of 130 ℃ according to the proportion of 50 parts by mass of wood wax oil, 40 parts by mass of soft wax and 10 parts by mass of hard wax, and uniformly stirring and mixing.

As a further improved technical scheme, the wood floor edge sealing agent provided by the invention comprises the following components in parts by weight: 53 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organosilicon modified handfeel wax slurry, 18.7 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 45 ℃; the melting point of the hard wax is 51 ℃.

In order to solve the technical problems, on the other hand, the invention provides a using method of a wood floor edge sealing agent, which comprises the steps of putting 45-55 parts by mass of wood wax oil, 35-45 parts by mass of soft wax and 5-15 parts by mass of hard wax into a wax sealing machine hopper, heating and melting at the temperature of 120-160 ℃, stirring until the materials are fully mixed, and sealing edges of a wood floor at the temperature of 110-130 ℃; the wood wax oil comprises the following components in parts by weight: 50-55 parts of polymerized linseed oil, 5 parts of carnauba wax, 10 parts of organic silicon modified hand feeling wax slurry, 17-23 parts of dammar resin, 10 parts of citrus oil D-limonene, 2 parts of absolute alcohol and 1 part of shellac; the melting point of the soft wax is 42-47 ℃; the melting point of the hard wax is not lower than 50 ℃.

The aforementioned improvements can be implemented individually or in combination without conflict.

According to the technical scheme provided by the invention, oil in the wood wax oil can permeate into the wood, so that deep moistening and maintenance are given to the wood; the wax can be tightly combined with wood fibers, so that the surface hardness is enhanced, and the wood fiber is waterproof, antifouling, wear-resistant and scratch-resistant; the soft wax has good softness, adhesiveness and water resistance; the hard wax has good anti-crushing performance, excellent insulating performance and strong water resistance. The combination of the three components has durability to the waterproof effect of the wood floor, the waterproof effect is far superior to that of common paraffin, the noise reduction function is realized, and abnormal sound caused by friction of the floor rabbet in the using process is reduced.

Detailed Description

The invention is further described in detail below with reference to examples:

the wood wax oil, the soft wax, the anion powder and the hard wax are all sold in the market.