阅读说明：本技术 一种钻铰刀的焊接方法 (Welding method of drilling reamer ) 是由 董向阳 于 2018-06-26 设计创作，主要内容包括：本发明涉及一种钻铰刀的焊接方法。包括以下步骤：第一步,将刀柄立起来,在焊接面上涂上焊膏,放上焊片,焊片为含银35%的三明治型焊片,焊片厚度为0.5-0.6mm；第二步,将刀头和刀柄对正,施加20公斤的压力,用焊机焊接,焊接的温度为600-650摄氏度,焊接时间控制在30-40秒；刀头和刀柄的焊接面呈V字型；第三步,将焊接好的钻铰刀放入保温箱内进行保温处理,保温时间为8-10小时。本发明的工艺方法简单,通过采用本方法对钻铰刀焊接,焊接牢固,能够消除内应力且不易变形。(The invention relates to a welding method of a drilling reamer. The method comprises the following steps: step one, erecting a tool handle, coating soldering paste on a welding surface, and placing a soldering lug which is a sandwich type soldering lug containing 35% of silver, wherein the thickness of the soldering lug is 0.5-0.6 mm; secondly, aligning the tool bit and the tool handle, applying 20 kilograms of pressure, and welding by using a welding machine, wherein the welding temperature is 600-650 ℃, and the welding time is controlled within 30-40 seconds; the welding surface of the tool bit and the tool handle is V-shaped; and thirdly, placing the welded drilling reamer into a heat preservation box for heat preservation for 8-10 hours. The process method is simple, and the drilling reamer is welded firmly by adopting the method, so that the internal stress can be eliminated, and the drilling reamer is not easy to deform.)

一种钻铰刀的焊接方法

技术领域

本发明涉及一种钻铰刀的焊接方法。

背景技术

为了降低刀具成本，在保证刀具能够正常使用的前提下，经常采用不同两种材料进行焊接制造钻头、铰刀等。但是两种不同材料的刀具在焊接时，焊接容易不牢固，存在内应力、变形和刀具精度差等问题。

发明内容

针对上述缺陷，本发明的目的在于提供一种工艺方法简单，焊接牢固，能够消除内应力且不易变形的一种钻铰刀的焊接方法。

为此本发明所采用的技术方案是：

包括以下步骤：

第一步，将刀柄立起来，在焊接面上涂上焊膏，放上焊片，焊片为含银35%的三明治型焊片，焊片厚度为0.5-0.6mm；

第二步，将刀头和刀柄对正，施加20公斤的压力，用焊机焊接，焊接的温度为600-650摄氏度，焊接时间控制在30-40秒；刀头和刀柄的焊接面呈V字型；

第三步，将焊接好的钻铰刀放入保温箱内进行保温处理，保温时间为8-10小时。

作为上述技术方案的进一步改进，在第三步中，焊接好的钻铰刀竖直放置。

本发明的优点是：

本发明的工艺方法简单，通过采用本方法对钻铰刀焊接，焊接牢固，能够消除内应力且不易变形。

具体实施方式

一种钻铰刀的焊接方法，包括以下步骤：

第一步，将刀柄立起来，在焊接面上涂上焊膏，放上焊片，焊片为含银35%的三明治型焊片，焊片厚度为0.5-0.6mm；

第二步，将刀头和刀柄对正，施加20公斤的压力，用焊机焊接，焊接的温度为600-650摄氏度，焊接时间控制在30-40秒；刀头和刀柄的焊接面呈V字型；

第三步，将焊接好的钻铰刀放入保温箱内进行保温处理，保温时间为8-10小时。

作为上述技术方案的进一步改进，在第三步中，焊接好的钻铰刀竖直放置。