阅读说明：本技术 一种墙壁粘贴瓷砖的施工方法 (Construction method for pasting ceramic tiles on wall ) 是由 韩建国 于 2019-09-25 设计创作，主要内容包括：本发明属于装修施工技术领域,尤其涉及一种墙壁粘贴瓷砖的施工方法,首先用水平仪监测墙面是否平整和垂直,在墙面的两侧根据水平仪的线,做出两道垂直平整的水泥筋；然后中间低的部分用水泥填满,再用刮尺把墙面整体刮平；再用木抹子将墙面整体抹一遍,以保证墙面的麻面状态；按照上述步骤把墙面整体处理平整垂直之后,然后开始进行瓷砖的粘贴,首先在瓷砖的背面刷一层胶,然后晾0－12小时,然后将粘接剂不惨加任何材料,用水和粘接剂进行搅拌到适合的粘度,然后涂在瓷砖的背面,厚度为2－10mm,然后将瓷砖直接粘接在墙面上。(The invention belongs to the technical field of decoration construction, and particularly relates to a construction method for pasting tiles on a wall, which comprises the steps of monitoring whether the wall is flat and vertical by using a level gauge, and manufacturing two cement ribs which are vertically flat on two sides of the wall according to lines of the level gauge; then filling the lower part of the middle part with cement, and then scraping the whole wall surface by using a scraping ruler; then, the wall surface is integrally plastered once by using a wooden trowel so as to ensure the pitted surface state of the wall surface; after the wall surface is integrally processed to be flat and vertical according to the steps, the ceramic tiles are pasted, firstly, a layer of glue is brushed on the back surfaces of the ceramic tiles, then, the ceramic tiles are dried for 0-12 hours, then, any material is unmistakably added into the adhesive, water and the adhesive are stirred to be proper in viscosity, then, the adhesive is coated on the back surfaces of the ceramic tiles, the thickness of the adhesive is 2-10 mm, and then, the ceramic tiles are directly pasted on the wall surface.)

1. A construction method for pasting ceramic tiles on a wall is characterized in that: the method comprises the following steps:

firstly, monitoring whether a wall surface is flat and vertical by using a level meter, and obtaining an accurate number according to the difference between the highest and the lowest;

secondly, selecting the highest value, and making two vertical and flat cement ribs on two sides of the wall surface according to the line of the gradienter;

thirdly, filling the lower middle part with cement, and scraping the whole wall surface by using a scraping ruler;

fourthly, smearing the wall surface integrally by using a wooden trowel to ensure the rough surface state of the wall surface;

fifthly, if the whole wall surface is too wide, two vertical cement ribs are formed on two sides of the wall surface, a horizontal cement rib is formed in the middle of the wall surface, then the interior of the wall surface is smoothed by cement according to the cement ribs, then the wall surface is smoothed by a scraping ruler, and finally a rough surface is smoothed by a wood trowel;

sixthly, after the wall surface is integrally processed to be flat and vertical according to the steps, the ceramic tiles are pasted, firstly, a layer of glue is brushed on the back surfaces of the ceramic tiles, then, the ceramic tiles are dried for 0-12 hours, then, any material is not added into the adhesive, water and the adhesive are stirred to reach proper viscosity, then, the adhesive is coated on the back surfaces of the ceramic tiles, the thickness of the adhesive is 2-10 mm, and then, the ceramic tiles are directly pasted on the wall surface;

and seventhly, when the ceramic tiles are pasted, the ceramic tiles are pasted from bottom to top, the bottommost layer is free of the height of one tile, the ceramic tiles at the bottommost layer are laid in a first mode, the ceramic tiles are firstly laid, then the ceramic tiles at the bottommost layer are filled on the basis of the ceramic tiles, the mode is called wall ground pressing, the mode is attractive, corners cannot have gaps due to indoor irregularity, the ceramic tiles at the bottommost layer are firstly filled, then the ceramic tiles are laid, and the mode is called ground top wall.

Technical Field

The invention belongs to the technical field of decoration construction, and particularly relates to a construction method for pasting ceramic tiles on a wall.

Background

Decoration is also called decoration or decoration, and refers to a whole set of construction scheme and design scheme which is implemented in a certain area and range, including hydropower construction, wall, floor, ceiling, landscape and the like, and is formed according to a certain design concept and aesthetic rules. In the in-process of fitment, because the position of wall is more striking, the area is bigger again, so the construction of wall is the process of a consumption of time power more, also is the process that the quality requirement is higher, the pasting of present wall ceramic tile, because wall surface unevenness, need scribble thicker cement at the back of ceramic tile to make the ceramic tile surfacing pleasing to the eye, this kind of construction mode complex operation, the construction cycle is long, and construction quality also can not guarantee moreover, falls brick, hollowing easily.

Disclosure of Invention

The invention provides a construction method for pasting tiles on a wall, which aims to solve the problems of complex operation and poor construction quality in the background technology.

The technical problem solved by the invention is realized by adopting the following technical scheme:

a construction method for pasting ceramic tiles on a wall comprises the following steps:

firstly, monitoring whether a wall surface is flat and vertical by using a level meter, and obtaining an accurate number according to the difference between the highest and the lowest;

secondly, selecting the highest value, and making two vertical and flat cement ribs on two sides of the wall surface according to the line of the gradienter;

thirdly, filling the lower middle part with cement, and scraping the whole wall surface by using a scraping ruler;

fourthly, smearing the wall surface integrally by using a wooden trowel to ensure the rough surface state of the wall surface;

fifthly, if the whole wall surface is too wide, two vertical cement ribs are formed on two sides of the wall surface, a horizontal cement rib is formed in the middle of the wall surface, then the interior of the wall surface is smoothed by cement according to the cement ribs, then the wall surface is smoothed by a scraping ruler, and finally a rough surface is smoothed by a wood trowel;

sixthly, after the wall surface is integrally processed to be flat and vertical according to the steps, the ceramic tiles are pasted, firstly, a layer of glue is brushed on the back surfaces of the ceramic tiles, then, the ceramic tiles are dried for 0-12 hours, then, any material is not added into the adhesive, water and the adhesive are stirred to reach proper viscosity, then, the adhesive is coated on the back surfaces of the ceramic tiles, the thickness of the adhesive is 2-10 mm, and then, the ceramic tiles are directly pasted on the wall surface;

and seventhly, when the ceramic tiles are pasted, the ceramic tiles are pasted from bottom to top, the bottommost layer is free of the height of one tile, the ceramic tiles at the bottommost layer are laid in a first mode, the ceramic tiles are firstly laid, then the ceramic tiles at the bottommost layer are filled on the basis of the ceramic tiles, the mode is called wall ground pressing, the mode is attractive, corners cannot have gaps due to indoor irregularity, the ceramic tiles at the bottommost layer are firstly filled, then the ceramic tiles are laid, and the mode is called ground top wall.

The invention has the beneficial effects that:

through this technical scheme, the operation is more convenient, great improvement the efficiency of construction, saved manpower and materials, the ceramic tile can not drop forever moreover, can not hollowly, has guaranteed construction quality, and it is very ideal to implement the effect.

Detailed Description

A construction method for pasting ceramic tiles on a wall comprises the following steps:

firstly, monitoring whether a wall surface is flat and vertical by using a level meter, and obtaining an accurate number according to the difference between the highest and the lowest;

secondly, selecting the highest value, and making two vertical and flat cement ribs on two sides of the wall surface according to the line of the gradienter;

thirdly, filling the lower middle part with cement, and scraping the whole wall surface by using a scraping ruler;

fourthly, smearing the wall surface integrally by using a wooden trowel to ensure the rough surface state of the wall surface;

fifthly, if the whole wall surface is too wide, two vertical cement ribs are formed on two sides of the wall surface, a horizontal cement rib is formed in the middle of the wall surface, then the interior of the wall surface is smoothed by cement according to the cement ribs, then the wall surface is smoothed by a scraping ruler, and finally a rough surface is smoothed by a wood trowel;

sixthly, after the wall surface is integrally processed to be flat and vertical according to the steps, the ceramic tiles are pasted, firstly, a layer of glue is brushed on the back surfaces of the ceramic tiles, then, the ceramic tiles are dried for 0-12 hours, then, any material is not added into the adhesive, water and the adhesive are stirred to reach proper viscosity, then, the adhesive is coated on the back surfaces of the ceramic tiles, the thickness of the adhesive is 2-10 mm, and then, the ceramic tiles are directly pasted on the wall surface;

and seventhly, when the ceramic tiles are pasted, the ceramic tiles are pasted from bottom to top, the bottommost layer is free of the height of one tile, the ceramic tiles at the bottommost layer are laid in a first mode, the ceramic tiles are firstly laid, then the ceramic tiles at the bottommost layer are filled on the basis of the ceramic tiles, the mode is called wall ground pressing, the mode is attractive, corners cannot have gaps due to indoor irregularity, the ceramic tiles at the bottommost layer are firstly filled, then the ceramic tiles are laid, and the mode is called ground top wall.

The cement in the present case may be ordinary cement, generally 325 type, the cement in the embodiment is shield time cement produced by findong cement, the glue in the present case may be selected according to actual needs and cost budget, the glue in the present embodiment is a building upper strong adhesive, the adhesive in the present embodiment is an ordinary adhesive, and the adhesive in the present embodiment is a beauty nest brand strong adhesive.