阅读说明：本技术 透光膜和包括其的电致变色装置 (Light-transmitting film and electrochromic device including the same ) 是由 金容赞 金起焕 于 2018-04-23 设计创作，主要内容包括：本申请涉及透光膜和包括其的装置。所述膜具有透光特性,能够根据施加的电压实现可逆的颜色转换,并且在膜改变其颜色的驱动电压范围内具有优异的耐久性。(The present application relates to light transmissive films and devices including the same. The film has light transmission characteristics, is capable of realizing reversible color conversion according to applied voltage, and has excellent durability in a driving voltage range in which the film changes its color.)

1. A light-transmitting film comprising an oxynitride containing two or more metals selected from Ti, Nb, Mo, Ta, and W and having a light transmittance of 60% or more.

2. The light transmitting film of claim 1 wherein the oxynitride comprises Mo and Ti.

3. The light-transmitting film according to claim 2, wherein the oxynitride is represented by the following formula 1:

[ formula 1]

Mo_aTi_bO_xN_y

(wherein a represents an element content ratio of Mo, b represents an element content ratio of Ti, x represents an element content ratio of O, and y represents an element content ratio of N, wherein a >0, b >0, x >0, y >0, 0.5< a/b <4.0, and 0.005< y/x < 0.02).

4. The light transmissive film of claim 1, wherein the film has a thickness of 150nm or less.

5. The light transmissive film of claim 1, wherein the film has a refractive index in the range of 1.5 to 3.0 in visible light.

6. The light transmitting film of claim 1 wherein the film has a level of coloration of 2V or greater.

7. An electrochromic device comprising an electrode layer; the light transmissive film of any one of claims 1-6; and an electrolyte layer.

8. The electrochromic device according to claim 7, comprising a first electrode layer, an electrolyte layer, the light-transmitting film, and a second electrode layer in this order.

9. The electrochromic device of claim 8, further comprising a second electrochromic layer between the first electrode layer and the electrolyte layer.

10. The electrochromic device of claim 9, wherein the second electrochromic layer comprises an oxidizing electrochromic material.

Technical Field

Cross Reference to Related Applications

This application claims the benefit of priority based on korean patent application No. 10-2017-0052047 filed 24.4.2017 and korean patent application No. 10-2018-0045418 filed 19.4.2018, the disclosures of which are incorporated herein by reference in their entireties.

Background

Electrochromic refers to a phenomenon in which optical characteristics of an electrochromic material are changed by reversible electrochemical oxidation or reduction reactions, wherein a device using the phenomenon is referred to as an electrochromic device. Typically, the change in the optical properties of the device may be achieved by a change in the colour of a layer or film comprising the electrochromic material. For example, when using WO which is almost colorless and transparent₃As an electrochromic material and when electrolyte ions and electrons are moved by voltage application, a reduction reaction occurs and the color of a layer or film containing the electrochromic material is colored into a blue-based color. In contrast, when an oxidation reaction occurs in the layer or film, the layer or film is discolored to an original transparent state. In order to sufficiently realize such electrochromism in the device, the other layer or film structure to be laminated together and the electrochromic layer or film in a decolored state must also have sufficient transparency (light transmission property).

Disclosure of Invention

Technical problem

It is an object of the present application to provide a light transmissive film that can be used in electrochromic devices.

It is another object of the present application to provide a light transmissive film capable of achieving reversible electrochromism depending on applied voltage.

Another object of the present application is to provide a light-transmitting film for an electrochromic device having excellent durability.

It is another object of the present application to provide an electrochromic device including a light-transmissive film capable of achieving reversible electrochromic according to applied voltage.

The above and other objects of the present application can be fully solved by the present application described in detail below.

Technical scheme

In one example of the present application, the present application relates to a light transmissive film. In the present application, the "light transmission property" may mean a case that is transparent enough to clearly see a change in optical properties, such as a color change, occurring in the electrochromic device, and, for example, may mean a case in which the corresponding layer has a light transmittance of at least 60% or more even in a state where no external factor, such as a potential, is applied (i.e., a decolored state as described below). More specifically, the lower limit of the light transmittance of the light-transmitting film of the present application may be 60% or more, 70% or more, or 75% or more, and the upper limit of the light transmittance may be 95% or less, 90% or less, or 85% or less. Unless otherwise specified, "light" in the present application may mean visible light in a wavelength range of 380nm to 780nm, more specifically, visible light having a wavelength of 550 nm. The transmittance may be measured using a known Haze Meter (HM).

The light transmissive film may include oxynitride. In one example, the light-transmitting film may be an oxynitride having a layer or film form, or may be a laminate of an oxynitride having a layer or film form and other layer or film structures. In the present application, oxynitride is used separately from oxide or nitride.

In one example, the oxynitride may include two or more metals selected from Ti, Nb, Mo, Ta, and W.

In another example, the oxynitride of the light-transmitting film may contain both Mo and Ti. In this regard, a nitride, oxide, or oxynitride containing only Mo has poor adhesion to an adjacent thin film, and a nitride, oxide, or oxynitride containing only Ti has poor durability, such as decomposition upon application of an electric potential. In particular, since a nitride or oxynitride containing any one of the above-listed metals (for example, Ti alone or Mo alone) has low light transmission characteristics, such as a visible light transmittance of 40% or less, 35% or less, or 30% or less, even in a state where no electric potential or the like is applied, it is not suitable for use as a member of an electrochromic film requiring transparency at the time of decoloring. Further, when a film having a low transmittance at the time of decoloring as described above is used, for example, when the difference between the transmittance at the time of coloring and the transmittance at the time of decoloring is 30% or more, it is difficult to exhibit a clear change in the optical characteristics of coloring and decoloring required in an electrochromic device.

In one example, the oxynitride may be represented by formula 1 below.

[ formula 1]

Mo_aTi_bO_xN_y

In formula 1, a represents the element content ratio of Mo, b represents the element content ratio of Ti, x represents the element content ratio of O, and y represents the element content ratio of N, wherein a >0, b >0, x >0, y >0, 0.5< a/b <4.0, and 0.005< y/x < 0.02. In the present application, the term "element content ratio" may be atomic%, and may be measured by XPS (X-ray photoelectron spectroscopy). When the element content ratio (a/b) is satisfied, a film having excellent adhesion to other layer configuration and durability can be provided. When the element content ratio (y/x) is satisfied, the light transmittance of the film may be 60% or more. In particular, when the element content ratio (y/x) is not satisfied, the film has very low transparency (light transmission property), for example, visible light transmittance of 40% or less, or 35% or less, and thus the related film cannot be used as a member of an electrochromic device.

In one example, the light transmission film may be a variable transmittance film whose light transmission characteristics change when a predetermined voltage is applied. The variable transmittance characteristic is attributed to the reduced electrochromic characteristic of the oxynitride as described above. Specifically, the oxynitride contained in the film has a light transmission characteristic close to colorless (achroma) in an original state without undergoing an electrochemical reaction, but when a predetermined voltage is applied, it may change its color, that is, be colored while undergoing a reduction reaction with the electrolyte at a certain level or higher. That is, the oxynitride is a reductive electrochromic material. When the light transmitting film is colored, its light transmittance is reduced to less than 60%. In summary, the film is an electrochromic variable transmittance film capable of having a light transmittance of 60% or more when discolored (or decolored) and having a light transmittance of less than 60% when colored.

In one example, the light transmissive film may be colored under a voltage application condition of-2V or less, for example, -2.5V or less, or-3V or less. That is, the level of coloration of the light-transmitting film may be 2V, 2.5V, or 3V. In the present application, the "coloring level" may mean a "minimum amplitude (absolute value)" of a voltage capable of causing coloring of the relevant film, for example, a case where the transmittance of the film is reduced when the light-transmitting film has a color by causing an electrochemical reaction by a voltage of a predetermined amplitude applied to the light-transmitting film or a laminate (half cell) including the film and a conductive layer. Since the coloring level, i.e. the minimum amplitude (absolute value) of the voltage causing coloring, acts as a kind of barrier to coloring, when a potential of a value less than said amplitude (absolute value) is applied, practically no coloring occurs (even if coloring occurs minutely, it is not recognized or not recognized enough by the user). The level of coloration of the light transmissive film may vary in the range of 2V or more depending on the particular configuration. When colored, the light-transmitting film may have a (dark) gray or black-based color. The light-transmitting film of the present application can be said to have excellent durability against high voltage in consideration of the coloring level of a known electrochromic material (for example, an oxide containing any of Ti, Nb, Mo, Ta, and W) being about 1V.

As for the coloring level, the upper limit of the magnitude (absolute value) of the voltage applied for coloring the film is not particularly limited, but may be, for example, 6V or less. If it exceeds 6V, the light-transmitting film or other adjacent structure may deteriorate.

In one example, the light transmissive film may have a thickness of 150nm or less. For example, the light transmissive film may have a thickness of 140nm or less, 130nm or less, or 120nm or less. If it exceeds the upper limit of the thickness, the insertion or desorption of electrolyte ions may be reduced, and the color conversion speed may be reduced. The lower limit of the thickness of the light-transmitting film is not particularly limited, but may be, for example, 10nm or more, 20nm or more, or 30nm or more. If the thickness is less than 10nm, the film stability is poor.

In one example, the light refractive index of the light transmissive film may be in a range of 1.5 to 3.0 or in a range of 1.8 to 2.8. If the visible light refractive index thereof is within the above range, the light-transmitting film can achieve appropriate transparency and visibility of the change in optical characteristics.

The method of forming the light-transmitting film is not particularly limited. For example, a known deposition method such as sputtering deposition may be used in forming the light-transmitting film, provided that the above configuration is satisfied.

In another example of the present application, the present application relates to an electrochromic device. The device may include an electrode layer, a light-transmissive film, and an electrolyte (layer). The form in which the device includes the electrode layer, the light-transmitting film, and the electrolyte (layer) is not particularly limited. For example, the device may sequentially include an electrode layer, a light-transmitting film, and an electrolyte (layer).

The light-transmitting film used in the electrochromic device may have the same configuration as described above. Since the visible light transmittance of the light transmitting film having the above configuration may be 60% or more, it is suitable as a film for an electrochromic device. Further, as described above, since the film can be colored when a predetermined voltage is applied, it can also be used as a so-called electrochromic layer. Specifically, the light transmissive film itself may have a transmittance of 60% or more when decolored (i.e., in its uncolored state), and the light transmissive film may have a transmittance of less than 60% while the transmittance when colored is reduced, for example, a transmittance of 45% or less, 30% or less, or 20% or less. In one example, the difference in light transmittance of the light transmissive film upon coloring and decoloring may be 20% or more, or 30% or more.

Without particular limitation, other structures used together in the electrochromic device other than the light-transmitting film may also have a visible light transmittance in the range of 60% or more, more specifically 60% to 95%. In one example, the electrochromic device may have a light transmittance difference of 10% or more, 20% or more, or 30% or more when colored and decolored.

The electrode layer may comprise a conductive compound, a metal mesh, or an OMO (oxide/metal/oxide).

In one example, the transparent conductive compound used In the electrode layer may be exemplified by ITO (indium tin oxide), In₂O₃(indium oxide), IGO (indium gallium oxide), FTO (fluorine-doped tin oxide), AZO (aluminum-doped zinc oxide), GZO (gallium-doped zinc oxide), ATO (antimony-doped tin oxide), IZO (indium-doped zinc oxide), NTO (niobium-doped titanium oxide), ZnO (zinc oxide), CTO (cesium tungsten oxide), or the like. However, the material of the transparent conductive compound is not limited to the above-listed materials.

In one example, the metal mesh for the electrode layer includes Ag, Cu, Al, Mg, Au, Pt, W, Mo, Ti, Ni, or an alloy thereof, which may have a mesh form. However, materials that can be used for the metal mesh are not limited to the above-listed metal materials.

In one example, the electrode layer may comprise an OMO (oxide/metal/oxide). Since the OMO has a lower sheet resistance than the transparent conductive oxide typified by ITO, improvement in electrical characteristics of an electrochromic device, such as shortening of color conversion speed, can be achieved.

The OMO may include an upper layer, a lower layer, and a metal layer disposed between the two layers. In the present application, the upper layer may mean a layer relatively distant from the light-transmitting film among layers constituting the OMO.

In one example, the upper and lower layers of the OMO electrode may comprise an oxide of Sb, Ba, Ga, Ge, Hf, In, La, Se, Si, Ta, Se, Ti, V, Y, Zn, Zr, or alloys thereof. The types of the respective metal oxides contained in the upper and lower layers may be the same or different.

In one example, the thickness of the upper layer may be in the range of 10nm to 120nm or in the range of 20nm to 100 nm. Further, the refractive index of visible light of the upper layer may be in the range of 1.0 to 3.0 or in the range of 1.2 to 2.8. Having the refractive index and the thickness within the above ranges, an appropriate level of optical characteristics can be imparted to the electrode layer and the device.

In one example, the thickness of the lower layer may be in the range of 10nm to 100nm or in the range of 20nm to 80 nm. Further, the refractive index of visible light of the lower layer may be in the range of 1.3 to 2.7 or in the range of 1.5 to 2.5. Having the refractive index and the thickness within the above ranges, an appropriate level of optical characteristics can be imparted to the electrode layer and the device.

In one example, the metal layer included in the OMO electrode may include a low resistance metal material. Without particular limitation, for example, one or more of Ag, Cu, Zn, Au, Pd, and alloys thereof may be contained in the metal layer.

In one example, the thickness of the metal layer may be in a range of 3nm to 30nm or in a range of 5nm to 20 nm. Further, the metal layer may have a refractive index of visible light of 1 or less or 0.5 or less. Having the refractive index and the thickness within the above ranges, an appropriate level of optical characteristics can be imparted to the electrode layer and the device.

Without particular limitation, the thickness of the electrode layer having the above configuration may be 50nm to 400nm or less. The light transmittance can be suitably realized within the above thickness range.

In one example, the device may comprise a further electrode layer. In this case, the electrode layers may be referred to as a first electrode layer and a second electrode layer according to relative positions to other structures. For example, the device may sequentially include a first electrode layer, an electrolyte layer, a light-transmitting film, and a second electrode layer. The structure of each electrode layer is the same as described above.

The electrolyte layer may be of a configuration that provides electrolyte ions that participate in the electrochromic reaction. The electrolyte ion may be a monovalent cation, such as H⁺、Li⁺、Na⁺、K⁺、Rb⁺Or Cs⁺Which can be inserted into the light transmissive film to participate in the electrochromic reaction.

The type of electrolyte is not particularly limited. For example, a liquid electrolyte, a gel polymer electrolyte, or an inorganic solid electrolyte may be used without limitation.

The composition of the specific compound used in the electrolyte layer is not particularly limited as long as it can contain a compound capable of supplying a monovalent cation such as H to the configuration of the electrochromic-capable film⁺、Li⁺、Na⁺、K⁺、Rb⁺Or Cs⁺The compound of (1). For example, the electrolyte may comprise a lithium salt compound, such as LiClO₄、LiBF₄、LiAsF₆Or LiPF₆(ii) a Or sodium salt compounds, e.g. NaClO₄。

In another example, the electrolyte layer may include a carbonate compound as a solvent. Since the carbonate-based compound has a high dielectric constant, the ionic conductivity can be improved. As a non-limiting example, a solvent such as PC (propylene carbonate), EC (ethylene carbonate), DMC (dimethyl carbonate), DEC (diethyl carbonate), or EMC (ethyl methyl carbonate) may be used as the carbonate-based compound.

In one example, when the electrolyte layer comprises a gel polymer electrolyte, the electrolyte layer may comprise a polymer, such as polyvinylidene fluoride (PVdF), Polyacrylonitrile (PAN), polymethyl methacrylate (PMMA), polyvinyl chloride (PVC), polyethylene oxide (PEO), polypropylene oxide (PPO), poly (vinylidene fluoride-hexafluoropropylene) (PVdF-HFP), polyvinyl acetate (PVAc), Polyethylene Oxide (POE), and Polyamideimide (PAI).

The thickness of the electrolyte layer may be in the range of 10 μm to 200 μm without particular limitation.

In one example, the electrochromic device of the present application may further include a second electrochromic layer. When the second electrochromic layer is included in the device, the device may further include a second electrochromic layer between the first electrode layer and the electrolyte. In this case, the light transmissive film capable of electrochromic may be referred to as a first electrochromic layer.

The second electrochromic layer may have electrochromic characteristics different from those of the first electrochromic layer. That is, the second electrochromic layer may comprise an oxidizing electrochromic material that may color when oxidized. When the electrochromic materials used in the first electrochromic layer and the second electrochromic layer have different coloring (electrochromic) characteristics, the second electrochromic layer may match the charge balance with the first electrochromic layer.

In one example, includeThe oxidizing electrochromic material in the second electrochromic layer may be one or more selected from the group consisting of: oxides of Cr, Mn, Fe, Co, Ni, Rh or Ir, e.g. LiNiO_x、IrO₂、NiO、V₂O₅、Li_xCoO₂、Rh₂O₃Or CrO₃(ii) a Hydroxides of Cr, Mn, Fe, Co, Ni, Rh or Ir; and prussian blue.

The thickness of the second electrochromic layer may be in the range of 50nm to 450nm, without particular limitation.

In one example, the electrochromic device may also include a substrate. The substrate may be located on a side surface of the device, for example, on a side surface of the first electrode layer and/or the second electrode layer.

The substrate may also have a visible light transmittance in the range of 60% to 95%. If the transmittance within the above range is satisfied, the type of the substrate used is not particularly limited. For example, glass or polymer resins may be used. More specifically, a polyester film such as PC (polycarbonate), PEN (poly (ethylene naphthalate)) or PET (poly (ethylene terephthalate)); acrylic films such as PMMA (poly (methyl methacrylate)); or a polyolefin film such as PE (polyethylene) or PP (polypropylene), etc., but not limited thereto.

In another example, the electrochromic device may also include a power source. The method of electrically connecting the power source to the device is not particularly limited, and may be appropriately performed by one of ordinary skill in the related art.

Advantageous effects

According to an example of the present application, a film that is capable of reversible electrochromism according to applied voltage and has excellent durability against high voltage and has light transmission characteristics can be provided.

Drawings

Fig. 1 is a diagram showing a state in which the laminate of example 1 of the present application was driven without decreasing durability when a voltage of ± 5V was applied.

Detailed Description

hereinafter, the present application will be described in detail by examples. However, the scope of protection of the present application is not limited by the following examples.

Experimental example 1: comparison of the elemental content of the oxynitride layer and its transmission