阅读说明：本技术 一种复合硬质解冻菜板的制造方法及复合硬质解冻菜板 (A kind of manufacturing method and composite ganoine defrosting chopping board of composite ganoine defrosting chopping board ) 是由 应伟明 于 2019-08-18 设计创作，主要内容包括：一种复合硬质解冻菜板的制造方法,包括以下步骤：选材,对单层不锈钢板及单层铝板进行裁切到预设的尺寸规格,然后进行热轧成型,成为一块复合板；硬质氧化处理,在复合板的不锈钢板的外表面涂设感光油墨并烘烤；将复合板置于酸性药液中,联接电极进行硬质氧化层的合成；成型,对复合板各表面进行精磨,成品检测及包装。复合硬质解冻菜板,包括不锈钢层和铝层,所述铝层远离不锈钢层一侧的表面设有硬质氧化层。本发明提供一种复合硬质解冻菜板的制造工艺及一种复合硬质解冻菜板,利用该解冻菜板能迅速将被冻住物品降温解冻,本解冻菜板无需通电,就能迅速对食物进行解冻,降低了烹调前的等待时间,提高了食品卫生程度。(A kind of manufacturing method of composite ganoine defrosting chopping board, comprising the following steps: selection carries out being cut to preset dimensions, then carries out hot-roll forming to single layer stainless steel plate and single layer aluminium sheet, becomes one piece of composite plate；Hardening oxidation processing, is coated with photosensitive-ink in the outer surface of the stainless steel plate of composite plate and toasts；Composite plate is placed in acid medical fluid, connection electrode carries out the synthesis of hardening oxidation layer；Molding, refines each surface of composite plate, finished product detection and packaging.Composite ganoine defrosting chopping board, including stainless steel layer and aluminium layer, the aluminium layer are equipped with hardening oxidation layer far from the surface of stainless steel layer side.The present invention provide a kind of composite ganoine defrosting chopping board manufacturing process and a kind of composite ganoine defrosting chopping board, using the defrosting chopping board will can be frozen in rapidly article cooling thaw, this defrosting chopping board is without being powered, it can thaw to food rapidly, the waiting time before cooking is reduced, food hygiene degree is improved.)

1. a kind of manufacturing method of composite ganoine defrosting chopping board, which comprises the following steps:

S1, selection are carried out being cut to preset dimensions, be then rolled into single layer stainless steel plate and single layer aluminium sheet Type becomes one piece of composite plate；

S2, hardening oxidation processing, are coated with photosensitive-ink in the outer surface of the stainless steel plate of composite plate and toast；Composite plate is placed in In acid medical fluid, connection electrode carries out the synthesis of hardening oxidation layer；

S3, molding refine each surface of composite plate, finished product detection and packaging.

2. according to claim 1, which is characterized in that the step S1 needs to carry out dustless processing step before hot-roll forming Suddenly, dustless polishing specifically is carried out to the surface of single layer stainless steel plate and single layer aluminium sheet.

3. a kind of manufacturing method of composite ganoine defrosting chopping board according to claim 2, which is characterized in that the step S1 Further include the baking procedure after dustless processing step, single layer stainless steel plate and single layer aluminium sheet are placed in 450 ° -500 ° of height Temperature carries out vacuum bakeout.

4. a kind of manufacturing method of composite ganoine defrosting chopping board according to claim 1 to 3, which is characterized in that described Step S2 specifically includes the following steps:

S21, polishing carry out surface polishing to composite plate；

S22, cleaning remove the impurity on surface；

S23, spraying, the photosensitive-ink on the stainless steel surface even application of composite plate；

S24, baking toast the composite plate for being coated with photosensitive-ink；

S25, light irradiation, the light for carrying out ultraviolet light to composite plate irradiate, cured printing ink；

S26, bound edge carry out seamless bonding using side of the erosion-resisting adhesive tape to composite plate；

S27, fixed composite plate are placed in acid medical fluid and couple the synthesis that electrode carries out hardening oxidation layer；

S28, cleaning clean up the acid medical fluid in composite plate；

S29, move back paint, using the photosensitive-ink of medical fluid stainless steel surface carry out cleaning move back paint after, clean medical fluid with clear water；

The composite plate cleaned up is carried out vacuum heating treatment, removed produced by hardening oxidation rear surface by S210, Seal treatment Viscous layer.

5. a kind of manufacturing method of composite ganoine defrosting chopping board according to claim 4, which is characterized in that the step It is additionally provided with a checking step between S26 and S27, checks whether the surface of aluminum plate of composite plate has trachoma or scratch, if any then carrying out Skin patching.

6. a kind of manufacturing method of composite ganoine defrosting chopping board according to claim 1 to 3, which is characterized in that described Step S3 is specifically included:

Composite plate is placed in mold and carries out processing and forming, is removed from the molds composite plate by S31, molding；

S32, fine grinding, refine composite surface and side；

Whether S33, detection, detection each index of composite plate meet preset standard, and as do not met, return step S32 is refined；

S34, composite plate is packed.

7. a kind of composite ganoine defrosting chopping board, which is characterized in that including stainless steel layer (1) and aluminium layer (2), the aluminium layer (2) is remote Surface from stainless steel layer (1) side is equipped with hardening oxidation layer (3).

8. a kind of manufacturing process of composite ganoine defrosting chopping board according to claim 7, which is characterized in that the stainless steel Layer (1) is with a thickness of 0.1-2.0MM；

Alternatively, the aluminium layer (2) is with a thickness of 0.1-10MM and is less than 10MM；

Alternatively, the hardening oxidation layer (3) with a thickness of 0.0001-3.0MM.

9. according to claim 7, which is characterized in that the stainless steel layer (1), aluminium layer (2) and hardening oxidation layer (3) three The overall thickness of person is 1-10MM.

10. a kind of composite ganoine defrosting chopping board according to claim 7, which is characterized in that the entirety of the defrosting chopping board Shape is rectangle or square or circle or ellipse.

Technical field

The invention belongs to the technical fields for articles for daily use of living, and in particular to a kind of manufacturer of composite ganoine defrosting chopping board Method and composite ganoine defrosting chopping board.

Background technique

Currently, the molding making of chopping board on the market is intended to wooden, bamboo, plastics and single layer stainless steel, contribute to It cuts the dish so that product function is excessively single, be not achieved multi-functional easy cleaning the effect of not high using hygienic index.It is bamboo it is wooden and After a number of uses, the cutting intolerant to cutter and various kitchen appliances scratches the chopping board of plastic production, and surface is easy to be stayed by kitchen knife Lower scratch and the irregular strip slot inside chopping board is cut by kitchen knife, not only influences the beauty on surface, and is also easy to produce accumulation Bacterium, it is not easy to clean, be easy mouldy, to generate harmful bacteria, be used for a long time to being unfavorable for human health.Because cutting scratches Friction be easy to make surface irregularity, food is cut and is scratched well to the later period and brings bigger difficulty.To be difficult to reach The satisfactory use for claiming hand.

In addition, in daily dietetic life, as the foods such as meat, fishes and shrimps due to that can not eat in time, people are in order to prolong Food can be put into cryogenic freezing in refrigerator and stored by the long holding time.Although this mode extends the holding time, but take again When cooking out, need that the food freezed thaws first, traditional defreezing method mainly there are 3 kinds:

One is most common are placed in air to carry out natural thaw, is walked in food using air flowing and temperature band Cold air restores normal temperature state so that food is released from freezing state；This mode thawing rate is very slow, needs larger time etc. To just can be carried out food cutting or culinary art processing；And it places at room temperature, bacterium easy to breed；

Second is put into frozen food in normal-temperature water or hot water, carries out soaked defrosting using water temperature, food it is entire or Part is dipped in water, and this mode is thawed using water temperature, is absorbed cold air or is carried out cold and hot neutralization, same easy to breed Bacterium causes food nutrition to be lost in water, and hot water defrosting be easy to cause that foodstuff surface is cooked by scalding but the inside does not thaw；

The third is using household electrical appliances i.e. micro-wave oven come thawed foodstuff, and micro-wave oven heat makes microwave oven internal air heats, To food carry out heat transfer, although and this mode thawing rate accelerates much than two kinds of front thawing mode, high temperature adds Thermal capacitance destroys the mouthfeel of food itself it is easier that food becomes outer ripe interior life.And micro-wave oven use needs to consume electric energy, energy Consumption is big.

Therefore, existing for traditional thawing mode greatly needs Improvement requirement, to reduce the waiting time of defrosting, improves solution The speed of jelly.

Summary of the invention

The purpose of the present invention is to solve above-mentioned problem, provide a kind of composite ganoine defrosting chopping board manufacturing process and A kind of composite ganoine defrosting chopping board.It is thawed using the defrosting chopping board article cooling that will can be frozen in rapidly, this defrosting chopping board is not necessarily to It is powered, can thaw to food rapidly, reduce the waiting time before cooking, improve food hygiene degree.

In order to achieve the above object of the invention, the present invention uses following technical scheme.

A kind of manufacturing method of composite ganoine defrosting chopping board, comprising the following steps:

S1, selection carry out being cut to preset dimensions, then carry out hot rolling to single layer stainless steel plate and single layer aluminium sheet Molding, becomes one piece of composite plate；

S2, hardening oxidation processing, are coated with photosensitive-ink in the outer surface that composite plate is located at stainless steel plate and toast；It will be compound Plate is placed in acid medical fluid, and connection electrode carries out the synthesis of hardening oxidation layer；

S3, molding refine each surface of composite plate, finished product detection and packaging.

Further, the step S1 needs to carry out dustless processing step before hot-roll forming, specifically stainless to single layer The surface of steel plate and single layer aluminium sheet carries out dustless polishing.

Further, the step S1 further includes the baking procedure after dustless processing step, by single layer stainless steel plate And single layer aluminium sheet is placed in 450 ° -500 ° of high temperature progress vacuum bakeout.

Further, the step S1 further includes the baking procedure after dustless processing step, by single layer stainless steel plate And single layer aluminium sheet is placed in 450 ° -500 ° of high temperature progress vacuum bakeout.

Further, the step S1 specifically includes the following steps:

S21, polishing carry out surface polishing to composite plate；

S22, cleaning remove the impurity on surface；

S23, spraying, the photosensitive-ink on the stainless steel surface even application of composite plate；

S24, baking toast the composite plate for being coated with photosensitive-ink；

S25, light irradiation, the light for carrying out ultraviolet light to composite plate irradiate, cured printing ink；

S26, bound edge carry out seamless bonding to the side of composite plate using erosion-resisting adhesive tape or anticorrosive paint；

S27, fixed composite plate, are placed in acid medical fluid, and connection electrode carries out the synthesis of hardening oxidation layer；

S28, cleaning clean up the acid medical fluid in composite plate；

S29, move back paint, using the photosensitive-ink of medical fluid stainless steel surface carry out cleaning move back paint after, clean medical fluid with clear water；

The composite plate cleaned up is carried out vacuum heating treatment (50 degrees Celsius), removes hard oxygen by S210, Seal treatment Surface viscosity layer caused by changing.

Further, it is additionally provided with a checking step between the step S26 and S27, checks that the surface of aluminum plate of composite plate is It is no to have trachoma or scratch, if any then carrying out skin patching.

Further, the step S3 is specifically included:

Composite plate is placed in mold and carries out processing and forming, is removed from the molds composite plate by S31, molding；One-sheet composite board Greater than mold blank size, go out desired specification shape using mould punching；

S32, fine grinding, refine composite surface and side；

Whether S33, detection, detection each index of composite plate meet preset standard, and surface wants bright and clean indefectible, thickness and smooth Degree will meet, and as do not met, return step S32 is refined；

S34, composite plate is packed.

The present invention also provides a kind of composite ganoine defrosting chopping boards, including stainless steel layer and aluminium layer, and the aluminium layer is far from stainless The surface of steel layer side is equipped with hardening oxidation layer.

Further, the stainless steel layer is with a thickness of 0.1-2.0MM；

Alternatively, the aluminum layer thickness is 0.1-10MM and is less than 10MM；

Alternatively, the hardening oxidation layer with a thickness of 0.0001-3.0MM.

Further, the overall thickness of the stainless steel layer, aluminium layer and hardening oxidation layer three is 1-10MM.

Further, the global shape of the defrosting chopping board is rectangle or square or circle or ellipse.

Compared with prior art, the present invention beneficial effect is:

1. the cooling capacity of frozen food is carried out Assimilation and conductivity rapidly using the rapid thermal conduction characteristic of aluminium sheet, expand with Air contact area accelerates heat exchange, to faster thaw；

2. having reached the function that chopping board is cut the dish, meet edible demand；Make surface abrasion smaller using stainless steel, utilizes Aluminium layer face can play green defrosting characteristic.On aluminium layer surface by handling, certain thickness hardening oxidation layer is formed, that is, is reached Hardness requirement, and prevent aluminium and air from generating oxidation, prolong the service life, so that stainless steel chopping board and defrosting function are realized Perfect combination；

3. passing through the combination of stainless steel and aluminum material, and surface treatment, so as to effectively prolong the service life, make dish Plate has excellent defrosting effect, reaches sanitary standard and excellent defrosting function；

4. being resistant to the cutting of cutter and kitchen appliance and scratching, it is not easy to damaging for chopping board in itself, be provided simultaneously with The function of defrosting achievees the effect that a plate is multi-purpose；It compares traditional chopping board and effectively extends service life, reduce food thawing etc. To the time, more spaces are vacateed to kitchen, the cost of kitchen buying multiple types of tools has been saved, has also improved the use of consumer Satisfaction.

Detailed description of the invention

Fig. 1 is a kind of side schematic view of composite ganoine defrosting chopping board；

Fig. 2 is the positive structure schematic of Fig. 1；

Fig. 3 is the structural schematic diagram of the composite ganoine defrosting chopping board of another structure；

Fig. 4 is the partial enlarged view of Fig. 3；

Fig. 5 is the front schematic view of Fig. 3.

Fig. 6 is the schematic diagram of two pieces of defrosting chopping board splicing states.

In figure: stainless steel layer 1, raised line 11, lug boss 12, lug boss bottom surface 13, aluminium layer 2, groove 21, recessed portion 22 are recessed Concave portion bottom surface 23, hardening oxidation layer 3, through-hole 4, top 41, catch basin 5, bolt 6, connector 7, elastic washer 8, first thaws Chopping board 9, the second defrosting chopping board 10.

Specific embodiment

Below by specific embodiment the technical scheme of the present invention will be further described explanation so that the technical program is more Add clear, clear.