阅读说明：本技术 一种聚合物材料表面用硬化防划伤涂料及其制备方法 (A kind of surface of polymer material hardening anti-scratch coating and preparation method thereof ) 是由 闵永刚 程鹏鹏 刘屹东 于 2019-09-16 设计创作，主要内容包括：本发明属于TPO、PVC、TPO与PVC的共聚物、TPO与PVC的共混物这四类聚合物材料制备的技术领域,具体涉及TPO、PVC、TPO与PVC的共聚物、TPO与PVC的共混物这四类聚合物表面用硬化防划伤涂料及其制备方法。本发明以玻璃粉和陶瓷微球来提供表面的硬化和防刮伤的要求,本方法简单易实施,可将此方法广泛应用到聚合物的表面硬化和防刮伤等领域。(The invention belongs to the technical fields of the blend these fourth types polymer material of the copolymer of TPO, PVC, TPO and PVC, TPO and PVC preparation, and in particular to the blend these fourth types polymer surfaces of the copolymer of TPO, PVC, TPO and PVC, TPO and PVC hardening anti-scratch coating and preparation method thereof.The present invention is simply easily implemented with glass powder and ceramic microsphere come the hardening for providing surface and anti-scratch requirement, this method, the method can be widely applied to polymer Surface hardened layer and anti-scratch equal fields.)

一种聚合物材料表面用硬化防划伤涂料及其制备方法

技术领域

本发明属于TPO、PVC、TPO与PVC的共聚物、TPO与PVC的共混物这四类聚合物材料材料制备的技术领域，具体涉及一种TPO、PVC、TPO与PVC的共聚物、TPO与PVC的共混物这四类聚合物材料表面用硬化防划伤涂料及其制备方法。

背景技术

热塑性弹性体(TPE)是一种具有橡胶的高弹性，高强度，高回弹性，又具有可注塑加工的特征的材料。TPE具有环保无毒安全，应用范围广，有优良的着色性，触感柔软，耐候性，抗疲劳性和耐温性，加工性能优越，无须硫化，可以循环使用降低成本，既可以二次注塑成型，与PP、PE、PC、PS、ABS等基体材料包覆粘合，也可以单独成型。因此，经常被用作在汽车门窗上的水切条材料，起到密封、去除玻璃表面上的水滴、水雾、灰尘及美观等作用。烯烃类TPE系是以PP为硬链段和EPDM为软链段的共混物，简称TPO。由于它比其它TPE的比重轻(仅为0.88)，耐热性高达100℃，耐天候性和耐臭氧性也好，因而成为TPE中又一发展很快的品种。但TPO表面在使用的过程中容易被刮伤。

发明内容

本发明的目的在于提供一种具有耐刮擦功能的TPO、PVC、TPO与PVC的共聚物、TPO与PVC的共混物这四类聚合物材料，以增加抗磨组分的涂料涂覆在材料的表面。

1：本发明中的取环氧树脂环氧值为0.1-0.25，玻璃粉粒径为1.5-2.5um，陶瓷微球粒径为0.5-2.5um。

2：本发明中的固化剂包括脂肪族二胺和多胺、芳香族多胺、其它含氮化合物及改性脂肪胺还包括有机酸、酸酐、和三氟化硼及其络合物。

具体实施方式

下面结合具体实施例，进一步阐述本发明。应理解，这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解，在阅读了本发明讲授的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等价形式同样落于本申请所附权利要求书所限定的范围

实施例1：

本取环氧树脂15份，玻璃粉15份，陶瓷微球15份，稀释剂9份，各类助剂15份，聚烯烃树脂35份，填料25份，混合构成A组分；

步骤2，B组分固化剂10份，偶联剂1份，促进剂1份；

步骤3，将AB组分等量混合均匀涂布在TPO的表面，固化两小时后可以达到TPO表面硬化防刮伤的作用其测试结果如表1所示。

表1TPO材料的性能指标