阅读说明：本技术 一种适用于铝合金的包装涂料 (Packaging coating suitable for aluminum alloy ) 是由 程峰 于 2019-10-21 设计创作，主要内容包括：本发明是一种适用于铝合金的包装涂料,包含添加剂和载体,配方中的原料按重量百分比组成分别是：0.5～6%石墨粉,10～35%锡粉,1～10%六甲基苯,0～3%硅烷偶联剂,0～2.5%稳定剂,5～20%悬浮剂,10～20%硫磺粉,30～60%粘结剂,通过本方法制备的产品,导热性提高,金属型铸件的晶粒得到细化,性能得到提高,冷却速度提高,细化铝合金表面的晶粒,显著增加表层细晶区的厚度,提高铝合金铸件表面的性能。(The invention relates to a packaging coating suitable for aluminum alloy, which comprises an additive and a carrier, wherein the raw materials in the formula comprise the following components in percentage by weight: the product prepared by the method has the advantages that the heat conductivity is improved, the crystal grains of the metal casting are refined, the performance is improved, the cooling speed is improved, the crystal grains on the surface of the aluminum alloy are refined, the thickness of a surface layer fine grain region is remarkably increased, and the performance of the surface of the aluminum alloy casting is improved.)

一种适用于铝合金的包装涂料

技术领域

本发明公开了一种适用于铝合金的包装涂料。

背景技术

由于压铸件和金属型铸件的组织比较致密，因此其力学性能较高，在铸型上涂刷激冷型涂料可以有效细化铸件组织，提高铸件的质量和力学性能，由于金属型铸件和压铸件表面通常需要进行修整加工，现有的技术中，金属表面加工成本较高。

发明内容

针对上述现有技术存在的问题，本发明提供一种适用于铝合金的包装涂料，导热性提高，金属型铸件的晶粒得到细化，性能得到提高，冷却速度提高，细化铝合金表面的晶粒，显著增加表层细晶区的厚度，提高铝合金铸件表面的性能。

为了实现上述目的，本发明通过以下技术方案实现：一种适用于铝合金的包装涂料，配方中的原料按重量百分比组成分别是：0.5～6%石墨粉，10～35%锡粉，1～10%六甲基苯， 0～3%硅烷偶联剂，0～2.5%稳定剂，5～20%悬浮剂，10～20%硫磺粉，30～60%粘结剂。

有益效果：通过本方法制备的产品，导热性提高，金属型铸件的晶粒得到细化，性能得到提高，冷却速度提高，细化铝合金表面的晶粒，显著增加表层细晶区的厚度，提高铝合金铸件表面的性能。

具体实施方式

实施例1

一种适用于铝合金的包装涂料，配方中的原料按重量百分比组成分别是：0.5%石墨粉，10%锡粉，1%六甲基苯，1%硅烷偶联剂，1%稳定剂，5%悬浮剂，10%硫磺粉，30%粘结剂，此时导热性提高不明显，合金铸件的晶粒不能得到足够的细化。

实施例2

一种适用于铝合金的包装涂料，配方中的原料按重量百分比组成分别是：6%石墨粉，35%锡粉，10%六甲基苯，3%硅烷偶联剂，2.5%稳定剂，20%悬浮剂，20%硫磺粉，60%粘结剂，此时冷却速度较慢，铝合金铸件的铸件表面性能不足。

实施例3

一种适用于铝合金的包装涂料，配方中的原料按重量百分比组成分别是：4%石墨粉，23%锡粉，5%六甲基苯， 1.5%硅烷偶联剂，1.25%稳定剂，13%悬浮剂，15%硫磺粉，45%粘结剂，此时导热性提高，金属型铸件的晶粒得到细化，性能得到提高，冷却速度提高，细化锌合金表面的晶粒，显著增加表层细晶区的厚度，提高锌合金铸件表面的性能。