阅读说明：本技术 一种柔性导电水凝胶及其制备方法和应用 (Flexible conductive hydrogel and preparation method and application thereof ) 是由 齐盼弟 李帅鹏 卢志威 刘兴江 于 2021-09-24 设计创作，主要内容包括：本发明提供一种柔性导电水凝胶的制备方法,包括：将可溶性纤维素水分散液加入至有机-水二元溶剂体系中,搅拌至所述可溶性纤维素水分散液完全混匀分散,得到分散液；将基体加入所述分散液中,加热并搅拌至所述基体完全溶解,得到混合液；所述混合液在油浴中静置,静置完成后转移至模具中,在低温环境中进行低温溶胶-凝胶转变,得到有机水凝胶；将所述有机水凝胶浸泡在无机离子交换平衡液中,达到离子交换平衡,得到柔性导电水凝胶。本发明的有益效果是对于该方法得到柔性导电水凝胶具有高拉伸性,高透明性,同时可耐低温并且在低温环境下具有高离子电导率。(The invention provides a preparation method of flexible conductive hydrogel, which comprises the following steps: adding the soluble cellulose aqueous dispersion into an organic-water binary solvent system, and stirring until the soluble cellulose aqueous dispersion is completely mixed and dispersed to obtain a dispersion; adding a matrix into the dispersion, heating and stirring until the matrix is completely dissolved to obtain a mixed solution; standing the mixed solution in an oil bath, transferring the mixed solution into a mold after standing, and performing low-temperature sol-gel conversion in a low-temperature environment to obtain organic hydrogel; and soaking the organic hydrogel in an inorganic ion exchange balance solution to achieve ion exchange balance, thereby obtaining the flexible conductive hydrogel. The invention has the advantages that the flexible conductive hydrogel obtained by the method has high stretchability and high transparency, can resist low temperature and has high ionic conductivity in a low-temperature environment.)

1. A method of making a flexible, electrically conductive hydrogel, comprising:

adding soluble cellulose into water to form soluble cellulose aqueous dispersion, then adding the soluble cellulose aqueous dispersion into an organic-water binary solvent system, and continuously stirring until the soluble cellulose aqueous dispersion is completely uniformly mixed and dispersed in the organic-water binary solvent system to obtain dispersion;

adding a matrix into the dispersion, heating and stirring until the matrix is completely dissolved to obtain a mixed solution;

standing the mixed solution in an oil bath, transferring the mixed solution into a mold after standing, and performing low-temperature sol-gel conversion in a low-temperature environment to obtain organic hydrogel;

and soaking the organic hydrogel in an inorganic ion exchange balance solution to achieve ion exchange balance, thereby obtaining the flexible conductive hydrogel.

2. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: and adding the soluble cellulose aqueous dispersion into the organic-water binary solvent system, and continuously stirring for 2-6h to obtain the dispersion.

3. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: and adding the matrix into the dispersion, heating to 85-95 ℃, and continuously stirring for 6-8h to obtain the mixed solution.

4. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: and in the process of standing the mixed solution in an oil bath, the oil temperature is 90-110 ℃, the oil bath time is 2-3h, and the foam is removed under the condition of no stirring.

5. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: and (3) after the mixed solution is kept stand, transferring the mixed solution into a mold, and standing the mixed solution for 10 to 24 hours at a low temperature of between 50 ℃ below zero and 10 ℃ below zero to perform conversion to obtain the organic hydrogel.

6. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: and the inorganic ion exchange equilibrium liquid is a solution of inorganic salt dissolved in an organic solvent-water binary solvent system, and the organic gel is soaked in the inorganic ion exchange equilibrium liquid for 10-30h to obtain the flexible conductive hydrogel.

7. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: the substrate is polyvinyl alcohol; the soluble cellulose is one or more of hydroxypropyl cellulose, hydroxymethyl cellulose and nano cellulose.

8. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: the mass ratio of the substrate to the soluble cellulose is 25:1-100: 1.

9. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: in the organic solvent-water binary solvent system, the mass ratio of water to the organic solvent is 0.2-1.5; further, the organic solvent is at least one of ethylene glycol, glycerol, dimethyl sulfoxide, benzyl trimethyl ammonium hydroxide, sweet amino acid and proline.

10. The method for preparing a flexible conductive hydrogel according to claim 1, wherein the method comprises the following steps: the inorganic salt is one or more of sodium chloride, potassium chloride, sodium sulfate and potassium sulfate; further, the concentration of the inorganic salt ion exchange equilibrium liquid is 0.5-2M.

11. A flexible, electrically conductive hydrogel, comprising: the conductive organic hydrogel is prepared by the method of any one of claims 1 to 10.

12. Use of a flexible electrically conductive hydrogel according to claim 11 in the field of strain sensors, temperature sensors, capacitors, ionic conductors or actuators.

Technical Field

The invention belongs to the technical field of high polymer materials, and particularly relates to a flexible conductive hydrogel and a preparation method and application thereof.

Background

As one of the next generation wearable and implantable electronic matrixes, hydrogel can provide very good biocompatibility and flexibility, and the hydrogel is appropriately processed and introduced into a conductive medium or an ion form to prepare a hydrogel material with conductivity, so that the conductive hydrogel is obtained. The conductive hydrogel organically combines a hydrophilic matrix and a conductive medium, is a novel composite hydrogel with good processability, high flexibility and excellent electrochemical performance, has wide application prospects in various fields of electronic skins, flexible strain sensors, supercapacitors, flexible wearable electronic equipment and the like, is an ideal material for future flexible electronic devices, and can connect a human body with the electronic devices.

In general, common hydrogels such as polyacrylic acid (PAA), Polyacrylamide (PAM), polyvinyl alcohol (PVA), etc. have poor mechanical properties due to loose network structure and non-uniform pore structure, which severely limits the practical application of the hydrogel, and meanwhile, the addition of conductive media such as graphene, carbon nanotubes, etc. and various reinforcements makes the hydrogels generally have poor transparency. And because the traditional conductive hydrogel only contains pure water solvent, when the environmental temperature is lower than the freezing point, the traditional conductive hydrogel can be converted into an ice crystal state due to the enhancement of hydrogen bonding between water molecules, so that the conductive hydrogel loses corresponding flexibility, and the application of the conductive hydrogel in a low-temperature severe environment is seriously limited. Therefore, the development of high-performance ion-conductive organic hydrogels with high stretchability and low temperature resistance is still a great challenge.

Disclosure of Invention

The invention aims to provide a flexible conductive hydrogel and a preparation method and application thereof, and effectively solves the problems that the common hydrogel has poor mechanical property and poor transparency, and when the environmental temperature is lower than the freezing point, the conductive hydrogel loses the corresponding flexibility, and the application of the conductive hydrogel in the low-temperature severe environment is seriously limited.

In order to solve the technical problems, the invention adopts the technical scheme that:

in a first aspect, the present application provides a method for preparing a flexible conductive hydrogel, comprising:

adding soluble cellulose into water to obtain soluble cellulose aqueous dispersion, then adding the soluble cellulose aqueous dispersion into an organic-water binary solvent system, and continuously stirring until the soluble cellulose aqueous dispersion is completely uniformly mixed and dispersed in the organic-water binary solvent system to obtain dispersion;

adding a matrix into the dispersion, heating and stirring until the matrix is completely dissolved to obtain a mixed solution;

standing the mixed solution in an oil bath, transferring the mixed solution into a mold after standing, and performing low-temperature sol-gel conversion in a low-temperature environment to obtain organic hydrogel;

and soaking the organic hydrogel in an inorganic ion exchange balance solution to achieve ion exchange balance, thereby obtaining the flexible conductive hydrogel.

Further, adding the soluble cellulose aqueous dispersion into the organic-water binary solvent system, and continuously stirring for 2-6h to obtain the dispersion.

Further, the matrix is added into the dispersion liquid, and the mixture liquid is obtained by heating to 85-95 ℃ and continuously stirring for 6-8 h.

Further, the mixed solution is kept still in an oil bath, the oil temperature is 90-110 ℃, the oil bath time is 2-3h, and the foam is removed under the condition of no stirring.

Further, the mixed solution is transferred to a mold after standing, and is placed in a low-temperature environment of-50 ℃ to-10 ℃ for 10-24 hours to be converted, so that the organic hydrogel is obtained.

Further, the inorganic ion exchange equilibrium liquid is a solution of inorganic salt dissolved in an organic solvent-water binary solvent system, and the organic gel is soaked in the inorganic ion exchange equilibrium liquid for 10-30h to obtain the flexible conductive hydrogel.

Further, the substrate is polyvinyl alcohol; the soluble cellulose is one or more of hydroxypropyl cellulose, hydroxymethyl cellulose and nano cellulose.

Further, the mass ratio of the substrate to the soluble cellulose is 25:1-100: 1.

Further, in the organic solvent-water binary solvent system, the mass ratio of water to the organic solvent is 0.2-1.5; further, the organic solvent is at least one of ethylene glycol, glycerol, dimethyl sulfoxide, benzyl trimethyl ammonium hydroxide, sweet amino acid and proline.

Further, the inorganic salt is one or more of sodium chloride, potassium chloride, sodium sulfate and potassium sulfate; further, the concentration of the inorganic salt ion exchange equilibrium liquid is 0.5-2M.

In a second aspect, the present application provides a flexible, electrically conductive hydrogel, characterized by: the conductive organic hydrogel is prepared by the method of any one of claims 1 to 10.

In a third aspect, the use of a flexible, electrically conductive hydrogel according to claim 11 in the field of strain sensors, temperature sensors, capacitors, ionic conductors or actuators.

By adopting the technical scheme, the organic hydrogel is prepared by taking polyvinyl alcohol as a matrix, soluble cellulose as a reinforcement of an organic hydrogel system, an organic solvent-water binary solvent system as a solvent and conductive ions such as inorganic salt as a conductive medium through a low-temperature sol-gel conversion method; and then putting the organic hydrogel into an inorganic salt ion exchange equilibrium liquid for ion equilibrium to obtain the organic hydrogel with the conductive performance. The organic hydrogel obtained by the method has high stretchability, high transparency, low temperature resistance and high ionic conductivity in a low-temperature environment. The organic hydrogel can be applied to temperature and mechanical sensing in low-temperature severe environment, can be subjected to sensor integrated manufacturing, and can be subjected to sensing monitoring at different temperatures and under different tensile forces.

Drawings

FIG. 1 is a UV-transmittance curve of PVA-1% CNF organic hydrogel obtained in example 1 of the present invention

FIG. 2 is a tensile stress-strain curve of the PVA-1% CNF organic hydrogel obtained in example 1 of the present invention;

FIG. 3 is a UV-transmittance curve of PVA-4% CNF organic hydrogel obtained in example 2 of the present invention

FIG. 4 is a tensile stress-strain curve of PVA-4% CNF organic hydrogel obtained in example 2 of the present invention

Detailed Description

The invention is further illustrated by the following examples and figures:

a method of making a flexible, electrically conductive hydrogel, comprising:

s1: adding soluble cellulose into water to obtain soluble cellulose water dispersion, then adding the soluble cellulose water dispersion into an organic-water binary solvent system, and continuously stirring until the soluble cellulose water dispersion is completely uniformly mixed and dispersed in the organic-water binary solvent system to obtain dispersion; wherein the content of the first and second substances,

the soluble cellulose is one or more of hydroxypropyl cellulose, hydroxymethyl cellulose and nano cellulose; in an organic solvent-water binary solvent system, the mass ratio of water to the organic solvent is 0.2-1.5; further, the organic solvent is at least one of ethylene glycol, glycerol, dimethyl sulfoxide, benzyl trimethyl ammonium hydroxide, sweet amino acid and proline;

adding soluble cellulose into water, dispersing to obtain soluble cellulose water dispersion, adding the soluble cellulose water dispersion into an organic-water binary solvent system, continuously stirring for 2-6h, and uniformly mixing and dispersing all the added soluble cellulose water dispersion to obtain dispersion.

S2: adding the matrix into the dispersion liquid, heating and stirring until the matrix is completely dissolved to obtain a mixed liquid; wherein the content of the first and second substances,

the substrate is polyvinyl alcohol; adding the substrate into the dispersion, heating to 85-95 ℃, continuously stirring for 6-8h, and completely dissolving the substrate in the dispersion to obtain a mixed solution;

the mass ratio of the substrate to the soluble cellulose substrate is 25:1-100: 1.

S3: standing the mixed solution in an oil bath, transferring the mixed solution into a mold after standing, and performing low-temperature sol-gel conversion in a low-temperature environment to obtain organic hydrogel; wherein the content of the first and second substances,

when the mixed solution is subjected to oil bath, the oil temperature is 90-110 ℃, the oil bath time is 2-3h, bubbles in the mixed solution are removed under the condition of no need of stirring, and a standing defoaming mode is usually adopted; and transferring the mixed solution into a mold after oil bath, generally adopting a polytetrafluoroethylene mold, placing the whole mold in a low-temperature environment at the specific temperature of-50 ℃ to-10 ℃ for 10-24h, carrying out low-temperature sol-gel conversion, and obtaining the organic hydrogel after conversion.

S4: soaking the organic hydrogel in an inorganic ion exchange equilibrium solution to achieve ion exchange equilibrium to obtain the flexible conductive hydrogel, wherein,

the inorganic ion exchange equilibrium liquid is a solution of inorganic salt dissolved in an organic solvent-water binary solvent system, and the inorganic salt is one or more of sodium chloride, potassium chloride, sodium sulfate and potassium sulfate; in the organic solvent-water binary solvent, the mass ratio of water to the organic solvent is 0.2-1.5; further, the organic solvent is at least one of ethylene glycol, glycerol, dimethyl sulfoxide, benzyl trimethyl ammonium hydroxide, sweet amino acid and proline; the concentration of the inorganic salt ion exchange equilibrium liquid is generally 0.5-2M;

the method comprises the following steps of soaking organic hydrogel in an inorganic ion exchange equilibrium liquid for 10-30h until the organic hydrogel reaches ion balance in the inorganic ion exchange equilibrium liquid to obtain the flexible conductive hydrogel, wherein the flexible conductive hydrogel has high transparency, high stretchability and low temperature resistance, and can be applied to flexible strain sensors and the field of temperature sensing in a wide temperature range.

The invention also provides a strain sensor, wherein the strain sensor is flexible conductive hydrogel which has high stretchability and high transparency, and the flexible conductive hydrogel and the electrode are manufactured in an integrated manner to obtain the corresponding flexible strain sensor.

The invention also provides a temperature sensor, which is flexible conductive hydrogel with low temperature resistance, and can measure the temperature under the low-temperature severe environment, and the temperature sensor and the electrode are manufactured in an integrated manner to obtain the corresponding temperature sensor.

Several specific examples are listed below:

example 1

S1: adding 1.2g of nano-Cellulose (CNF) water dispersion with the solid content of 1.5% into 6.818g of water and 12g of dimethyl sulfoxide (DMSO), and stirring for 2 hours to ensure that the nano-cellulose is dispersed;

s2: adding 1.8g of polyvinyl alcohol (PVA) into the nano-cellulose aqueous dispersion, continuously stirring and heating to 90 ℃ until all PVA is dissolved;

s3: after the PVA is dissolved, stopping stirring, fixing the PVA-CNF mixture in an oil bath at 100 ℃, removing bubbles, transferring the PVA-CNF mixture without bubbles into a polytetrafluoroethylene mold with the length, width and height of 50, 5 and 2mm, and standing at-20 ℃ for 20 hours for gelation;

s4: and soaking the PVA-CNF organic hydrogel in a 1M NaCl solution for 20 hours to reach ion exchange balance to generate the flexible conductive hydrogel, wherein the NaCl solution is prepared by dissolving 1.4625g of NaCl solid in a binary solvent system of 10g of water and 15g of DMSO.

The conductive organic hydrogel obtained in this example was tested for light transmittance, stretchability, and ionic conductivity at different low temperatures. Firstly, the light transmittance of the conductive organic hydrogel is measured by adopting an ultraviolet visible spectrum mode, the wavelength range is 220-800 nm, and the scanning rate is 100nmmin^-1As can be seen from fig. 1, the light transmittance of the conductive organic hydrogel is as high as 85%, and the conductive organic hydrogel has extremely high transparency. Then, a stress-strain test was performed on the conductive organic hydrogel sample using a universal tester, and as can be seen from fig. 2, the conductive organic hydrogel had a tensile strain as high as 530% and had an extremely high stretchability. Followed byThen, the ion conductivity of the conductive organic hydrogel at different low temperatures (-10 ℃, 30 ℃ and 50 ℃) is tested by using an electrochemical workstation, as shown in table 1, the ion conductivity of the conductive hydrogel gradually decreases with the decrease of the temperature, and the ion conductivity of the ionic conductive organic hydrogel still has 1.34S/m at the low temperature of-50 ℃, which indicates that the material still has very high ion conductivity at the low temperature.

PVA-1％CNF	At normal temperature	-10℃	-30℃	-50℃
					Ion conductivity (S/m)	2.1	1.8	1.5	1.34

TABLE 1

Example 2

S1: adding 4.8g of nano-Cellulose (CNF) water dispersion with the solid content of 1.5% into 6.818g of water and 12g of dimethyl sulfoxide DMSO, and stirring for 2 hours to ensure that the nano-cellulose is dispersed;

s2: adding 1.8g of polyvinyl alcohol (PVA) into the nano-cellulose aqueous dispersion, continuously stirring and heating to 90 ℃ until all PVA is dissolved;

s3: after the PVA is dissolved, stopping stirring, and fixing the PVA-CNF mixture in an oil bath at 90 ℃ to remove bubbles; transferring the bubble-free PVA-CNF mixture into a polytetrafluoroethylene mold with length, width and height of 50 x 5 x 2mm, and standing at-20 ℃ for 18h for gelation;

s4: and soaking the PVA-CNF organic hydrogel in a 1M NaCl solution for 15 hours to reach ion exchange balance to generate the flexible conductive hydrogel, wherein the NaCl solution is prepared by dissolving 1.4625g of NaCl solid in a binary solvent system of 10g of water and 15g of DMSO.

The conductive organic hydrogel obtained in this example was tested for light transmittance, stretchability, and ionic conductivity at different low temperatures. Firstly, the light transmittance of the conductive organic hydrogel is measured by adopting an ultraviolet visible spectrum mode, the wavelength range is 220-800 nm, and the scanning rate is 100nmmin^-1As can be seen from fig. 3, the light transmittance of the conductive organic hydrogel reaches 40%, and still has a certain transparency, but the light transmittance of the conductive organic hydrogel is reduced as the content of the nanocellulose is increased compared to that of PVA-1% CNF. Then, a stress-strain test is carried out on the conductive organic hydrogel sample by using a universal tester, and as can be seen from fig. 4, the tensile strain of the conductive organic hydrogel is up to 570%, and compared with the content of the nanocellulose of PVA-1% CNF, the stretchability of the conductive organic hydrogel is gradually improved along with the increase of the content of the nanocellulose. Subsequently, the ion conductivity of the conductive organic hydrogel at different low temperatures (-10 ℃, 30 ℃ and 50 ℃) was tested by using an electrochemical workstation, as shown in table 2, the ion conductivity of the conductive hydrogel gradually decreased with the decrease of the temperature, and the ion conductivity of the ionic conductive organic hydrogel still remained 1.63S/m at the low temperature of-50 ℃, which indicates that the material still has very high ion conductivity at the low temperature. Meanwhile, compared with the embodiment 1, the ion conductivity of the conductive organic hydrogel is correspondingly improved at the same low temperature along with the increase of the content of the CNF, mainly because the nano-Cellulose (CNF) is a strong biological-based nano material with adjustable surface charge characteristic and is often used for the enhancement of the polymer hydrogel, and meanwhile, the negative surface carboxyl group on the CNF can also promote the migration of counter ionsThus, the ionic conductivity of the hydrogel can be improved well.

PVA-4％CNF	At normal temperature	-10℃	-30℃	-50℃
					Ion conductivity (S/m)	2.3	1.93	1.65	1.63

TABLE 2

Example 3

Compared with example 1, 1.2g of CNF is replaced by 2.4g of CNF, other conditions are not changed, the light transmittance of the finally obtained conductive organic hydrogel can reach 65%, the tensile strain can reach 550%, and the ionic conductivity at-50 ℃ is 1.51S/m, and relevant data are shown in tables 3, 4 and 5.

Comparative example 1

Compared with the example 1, the conductive organic hydrogel obtained by adding no CNF into PVA and keeping other conditions unchanged has the light transmittance of 90 percent, excellent light transmittance, but only 300 percent of tensile strain and poor stretchability, and has the ionic conductivity of only 0.78S/m at the low temperature of-50 ℃, and the related data are shown in tables 3, 4 and 5.

x	0％	1％	2％	4％
					Ion conductivity (S/m)	0.78	1.34	1.51	1.63

TABLE 3 ionic conductivity of PVA-xCNF conductive hydrogels at-50 deg.C

x	0％	1％	2％	4％
					Light transmittance	90％	85％	65％	40％

TABLE 4 transmittance of PVA-xCNF conductive organic hydrogels

x	0％	1％	2％	4％
					Strain of	300％	530％	550％	570％

TABLE 5 tensile Strain of PVA-xCNF conductive organic hydrogels

Example 5

S1: adding 1.2g of nano-Cellulose (CNF) water dispersion with the solid content of 1.5% into 6.818g of water and 10g of dimethyl sulfoxide DMSO, and stirring for 2 hours to ensure that the nano-cellulose is dispersed;

s2: adding 1.8g of polyvinyl alcohol (PVA) into the nano-cellulose aqueous dispersion, continuously stirring and heating to 90 ℃ until all PVA is dissolved;

s3: after the PVA is dissolved, stopping stirring, and fixing the PVA-CNF mixture in an oil bath at 110 ℃ to remove bubbles; transferring the bubble-free PVA-CNF mixture into a polytetrafluoroethylene mold with length, width and height of 50 x 5 x 2mm, and standing at-20 ℃ for 15h for gelation;

s4: and soaking the PVA-CNF organic hydrogel in a 1M NaCl solution for 20 hours to reach ion exchange balance to generate the conductive organic hydrogel, wherein the NaCl solution is prepared by dissolving 1.053g of NaCl solid in a binary solvent system of 8g of water and 10g of DMSO.

For the conductive organic hydrogel obtained in this example, after the ratio of water to organic solvent was changed, the conductive organic hydrogel still had a high ionic conductivity of 1.15S/m at a low temperature of-50 ℃, and the related data are shown in table 6.

Example 6

In comparison with example 5, step 5 is to soak the PVA-CNF organic hydrogel in 1.5M NaCl solution for 20 hours to reach ion exchange equilibrium and generate the conductive organic hydrogel, wherein the NaCl solution is prepared by dissolving 2.19375g NaCl solid in a binary solvent system of 10g water and 15g DMSO. The finally obtained conductive organic hydrogel has high ionic conductivity of 1.45S/m at the low temperature of-50 ℃, as shown in Table 6.

Example 7

In comparison with example 5, step 5 is to soak the PVA-CNF organic hydrogel in 0.05M NaCl solution for 20 hours to reach ion exchange equilibrium and generate the conductive organic hydrogel, wherein the NaCl solution is prepared by dissolving 0.73125g NaCl solid in a binary solvent system of 10g water and 15g DMSO. The finally obtained conductive organic hydrogel has high ionic conductivity of 0.65S/m at the low temperature of-50 ℃, as shown in Table 6.

Concentration of NaCl solution	0.05M	1M	1.5M
				Ion conductivity (S/m)	0.65	1.34	1.45

TABLE 6-ionic conductivity of PVA-1% CNF hydrogels in NaCl solutions of different concentrations at-50 deg.C

Example 8

Compared with the embodiment 1, the dimethyl sulfoxide is changed into the ethylene glycol, other conditions are not changed, and the finally obtained conductive organic hydrogel still has high ionic conductivity of 1.03S/m at the low temperature of 50 ℃ below zero.

Example 9

Compared with example 1, the conductive organic hydrogel is prepared by replacing nano-cellulose with hydroxymethyl cellulose, and other conditions are not changed. The light transmittance of the finally obtained conductive organic hydrogel can reach 83%, the tensile strain can reach 525%, and the ionic conductivity at the temperature of minus 50 ℃ is 1.28S/m.

Comparative example 2

When 1.2g of CNF was changed to 7.2g of CNF, the other conditions were not changed, and the moldability of the finally obtained conductive organic hydrogel was inferior to that of example 1.

The embodiments of the present invention have been described in detail, but the description is only for the preferred embodiments of the present invention and should not be construed as limiting the scope of the present invention. All equivalent changes and modifications made within the scope of the present invention shall fall within the scope of the present invention.