一种高温烟气过滤多孔陶瓷材料的制备方法
阅读说明：本技术 一种高温烟气过滤多孔陶瓷材料的制备方法 (Preparation method of high-temperature flue gas filtering porous ceramic material ) 是由 丰庆国 蔡新浩 许琦 陈小卫 章亚振 范一鸣 于 2021-10-11 设计创作，主要内容包括：本发明公开了一种高温烟气过滤多孔陶瓷材料的制备方法,属于多孔陶瓷技术领域。所述制备方法包括步骤如下：将氧化镁、氧化铝、氧化硅粉按照堇青石化学计量比称量、球磨、干燥后,得到第一陶瓷粉体；将所述第一陶瓷粉体与助熔剂、造孔剂球磨、干燥后,得到第二陶瓷粉体；将所述第二陶瓷粉体与粘结剂混合,经过干压成型以及高温煅烧,得到高温烟气过滤多孔陶瓷材料。所述制备方法能够有效降低多孔陶瓷烧结温度、降低生产成本、减小过滤阻力的问题。(The invention discloses a preparation method of a high-temperature flue gas filtering porous ceramic material, and belongs to the technical field of porous ceramics. The preparation method comprises the following steps: weighing, ball-milling and drying magnesium oxide, aluminum oxide and silicon oxide powder according to the stoichiometric ratio of cordierite to obtain first ceramic powder; ball-milling and drying the first ceramic powder, a fluxing agent and a pore-forming agent to obtain second ceramic powder; and mixing the second ceramic powder with a binder, and performing dry pressing and high-temperature calcination to obtain the high-temperature flue gas filtering porous ceramic material. The preparation method can effectively reduce the sintering temperature of the porous ceramic, reduce the production cost and reduce the filtration resistance.)
技术领域
本发明属于多孔陶瓷技术领域，具体涉及一种高温烟气过滤多孔陶瓷材料的制备方法。
背景技术
随着中国经济的快速发展，城市化水平的提高和人民生活水平的不断提高，产生的垃圾量日益增加，由此造成的环境污染问题非常严重。许多城市的垃圾增长率超过了GDP增长率，面临着垃圾围困的困境。垃圾焚烧可以实现能源和资源的利用，减少体积容量的效果明显，处理速度快，不需要长期存放，节约了土地资源。但是垃圾焚烧会产生大量的含尘、含有害气体的高温烟气。
目前，净化高温烟气的手段主要有湿法喷淋除尘、电除尘器、金属微孔过滤材料、多孔陶瓷过滤材料等。多孔陶瓷过滤材料作为理想的高温烟气过滤材料，其主要优点主要表现为：具有较高的除尘效率，可达99％以上；具有较高的强度和耐热性；具有良好的耐高温气体腐蚀和化学腐蚀；具有加工容易、施工方便等特点，并且原料来源较为广泛。目前，多孔陶瓷过滤材料存在烧结温度高、原料成本高、过滤阻力偏大等问题。