Resin composition for soldering, solder composition, resin core solder, flux, and solder paste

文档序号：214038 发布日期：2021-11-05 浏览：49次中文

阅读说明：本技术 软钎焊用树脂组合物、软钎料组合物及树脂芯软钎料、助焊剂及焊膏 (Resin composition for soldering, solder composition, resin core solder, flux, and solder paste ) 是由川崎浩由白鸟正人仓泽阳子鬼冢基泰北泽和哉高木晶子于 2020-03-27 设计创作，主要内容包括：本发明提供一种与松香系树脂的相溶性优异、温度循环可靠性优异而适合作为软钎焊用助焊剂的软钎焊用树脂组合物、使用该软钎焊用树脂组合物的软钎料组合物及树脂芯软钎料。软钎焊用树脂组合物含有丙烯酸系树脂,以及松香系树脂、聚乙烯系树脂或聚丙烯系树脂,所述丙烯酸系树脂通过使用飞行时间型质谱仪的质谱分析法得到的数均分子量为500以上且小于2000；另外,软钎焊用树脂组合物含有丙烯酸系树脂,以及松香系树脂、聚乙烯系树脂或聚丙烯系树脂,所述丙烯酸系树脂通过使用飞行时间型质谱仪的质谱分析法得到的重均分子量为500以上且小于2000。(The invention provides a resin composition for soldering, which has excellent compatibility with rosin resin and excellent temperature cycle reliability and is suitable for being used as a soldering flux, a solder composition using the resin composition for soldering and a resin core solder. The resin composition for soldering contains an acrylic resin having a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, and a rosin resin, a polyethylene resin, or a polypropylene resin; the resin composition for soldering contains an acrylic resin having a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, and a rosin resin, a polyethylene resin, or a polypropylene resin.)

1. A resin composition for soldering, which contains an acrylic resin and a rosin resin, and which contains 14 to 60 wt% of the acrylic resin,

the acrylic resin contains an acrylate or a methacrylate, or contains an acrylate and a methacrylate, and has a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer.

2. A resin composition for soldering, which contains an acrylic resin and a rosin resin, and which contains 14 to 60 wt% of the acrylic resin,

the acrylic resin contains an acrylate or a methacrylate, or contains an acrylate and a methacrylate, and has a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer.

3. The resin composition for soldering according to claim 1 or 2, wherein the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is 0.2 to 2.0.

4. The solder resin composition according to any one of claims 1 to 3, wherein the solder resin composition contains 30 wt% or more and 80 wt% or less of the rosin-based resin.

5. The solder resin composition according to any one of claims 1 to 3, wherein the solder resin composition further contains another resin.

6. The resin composition for soldering according to claim 5, wherein the content of the other resin is 35 wt% or less.

7. The solder resin composition according to any one of claims 1 to 6, further comprising at least one of an organic acid, an amine, an organic halogen compound, an amine hydrohalide salt, an organic phosphorus compound, silicone, and a solvent.

8. The resin composition for soldering according to claim 7, wherein the content of the organic acid is 0 to 20 wt%, the content of the amine is 0 to 10 wt%, the content of the organic halogen compound is 0 to 15 wt%, the content of the amine hydrohalide salt is 0 to 5 wt%, the content of the organic phosphorus compound is 0 to 10 wt%, the content of the silicone is 0 to 5 wt%, and the content of the solvent is 0 to 13 wt%.

9. A solder composition characterized by containing the solder resin composition according to any one of claims 1 to 8.

10. A linear solder filled with the resin composition for soldering according to any one of claims 1 to 8.

11. A solder composition characterized in that the solder is coated with the resin composition for soldering as set forth in any one of claims 1 to 8.

12. A flux comprising an acrylic resin, a rosin resin, an activator and a solvent, wherein the acrylic resin is contained in an amount of 7.0 to 50.0 wt%, the rosin resin is contained in an amount of more than 0 to 30.0 wt%,

the ratio of the weight of one or more acrylic resins to the total weight of one or more rosin-based resins is 0.7 or more,

13. A flux comprising an acrylic resin, a rosin resin, an activator and a solvent, wherein the acrylic resin is contained in an amount of 7.0 to 50.0 wt%, the rosin resin is contained in an amount of more than 0 to 30.0 wt%,

the ratio of the weight of one or more acrylic resins to the total weight of one or more rosin-based resins is 0.7 or more,

The acrylic resin contains an acrylate or a methacrylate, or contains an acrylate and a methacrylate, and has a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer.

14. A flux comprising an acrylic resin, an activator and a solvent, wherein the acrylic resin is contained in an amount of 7.0 to 50.0 wt%, the rosin resin is contained in an amount of 0 to 30.0 wt%,

the acrylic resin is composed of an acrylate or a methacrylate, or an acrylate and a methacrylate, and has a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer.

15. A flux comprising an acrylic resin, an activator and a solvent, wherein the acrylic resin is contained in an amount of 7.0 to 50.0 wt%, the rosin resin is contained in an amount of 0 to 30.0 wt%,

the acrylic resin is composed of an acrylate or a methacrylate, or an acrylate and a methacrylate, and has a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer.

16. The flux according to claim 14 or 15, wherein when the rosin-based resin is contained, a ratio of the weight of one or more kinds of the acrylic resins to the weight of one or more kinds of the rosin-based resins is 0.7 or more.

17. The flux of any one of claims 12 to 16, further comprising 0 wt% or more and 10.0 wt% or less of another resin.

18. The flux of any one of claims 12 to 17, wherein the active agent comprises one or more of an organic acid, an amine, an organohalogen compound, and an amine hydrohalide salt.

19. A flux comprising an acrylic resin, a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, and a solvent, wherein the acrylic resin is contained in an amount of 7.0 wt% to 50.0 wt%,

20. A flux comprising an acrylic resin, a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, and a solvent, wherein the acrylic resin is contained in an amount of 7.0 wt% to 50.0 wt%,

21. The flux according to claim 19 or 20, wherein the ratio of the weight of one kind of the acrylic resin or the total weight of two or more kinds of the acrylic resins to the weight of one kind of the polyethylene resin or the polypropylene resin, or the total weight of two or more kinds of the polyethylene resin or the polypropylene resin, or the total weight of the polyethylene resin and the polypropylene resin is 1.0 or more and 120.0 or less.

22. The flux according to any one of claims 19 to 21, wherein the flux contains 0.1 wt% or more and 10.0 wt% or less of the polyethylene-based resin or the polypropylene-based resin, or 0.1 wt% or more and 10.0 wt% or less of the polyethylene-based resin and the polypropylene-based resin.

23. The flux according to any one of claims 19 to 22, further comprising a rosin-based resin.

24. The flux according to claim 23, wherein the flux contains more than 0 wt% and 30.0 wt% or less of the rosin-based resin.

25. The soldering flux according to any one of claims 19 to 24, wherein the soldering flux further comprises an active agent, and the active agent comprises one or more of an organic acid, an amine, an organic halogen compound and an amine hydrohalide salt.

26. The flux according to claim 18 or 25, wherein the organic acid contains 0 wt% or more and 25.0 wt% or less of any one of dimer acid as a dimer in a reactant of monocarboxylic acid, hydrogenated dimer acid obtained by hydrogenation of dimer acid, trimer acid as a trimer in a reactant of monocarboxylic acid, and hydrogenated trimer acid obtained by hydrogenation of trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid, and 0 wt% or more and 15.0 wt% or less of other organic acids than dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid,

the total content of any one of dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, and one or more of other organic acids is 30.0 wt% or less.

27. The flux of claim 18, 25 or 26, wherein the flux comprises 0 wt% or more and 10.0 wt% or less of amine, 0 wt% or more and 5.0 wt% or less of organic halogen compound, 0 wt% or more and 2.0 wt% or less of amine hydrohalide salt.

28. The flux according to any one of claims 12 to 27, further comprising 0 wt% or more and 10.0 wt% or less of a thixotropic agent, 0 wt% or more and 10.0 wt% or less of a hindered phenol-based metal deactivator, and 0 wt% or more and 5.0 wt% or less of a nitrogen compound-based metal deactivator.

29. A solder paste comprising the flux of any one of claims 12 to 28 and a metal powder.

30. A solder paste according to claim 29 wherein the metal powder has the following alloy composition: as: 25 to 300 mass ppm, and Sb: more than 0 ppm by mass and 3000 ppm by mass or less, Bi: more than 0 mass ppm and 10000 mass ppm or less and Pb: more than 0 ppm by mass and 5100 ppm by mass or less, the balance being Sn, and satisfying the following formulas (1) and (2),

275≤2As+Sb+Bi+Pb···(1)

0.01≤(2As+Sb)/(Bi+Pb)≤10.00···(2)

in the above formulas (1) and (2), As, Sb, Bi and Pb respectively represent the contents (mass ppm) in the alloy composition.

31. A solder paste according to claim 30, wherein the alloy composition further satisfies the following formula (1a),

275≤2As+Sb+Bi+Pb≤25200···(1a)

in the above formula (1a), As, Sb, Bi and Pb respectively represent the contents (mass ppm) in the alloy composition.

32. A solder paste according to claim 30, wherein the alloy composition further satisfies the following formula (1b),

275≤2As+Sb+Bi+Pb≤5300···(1b)

in the above formula (1b), As, Bi and Pb respectively represent the contents (mass ppm) in the alloy composition.

33. A solder paste according to any one of claims 30 to 32 wherein the alloy composition further satisfies the following formula (2a),

0.31≤(2As+Sb)/(Bi+Pb)≤10.00···(2a)

in the above formula (2a), As, Sb, Bi and Pb respectively represent the contents (mass ppm) in the alloy composition.

34. A solder paste according to any one of claims 30 to 33 wherein the alloy composition further comprises Ag: 0-4 mass% and Cu: 0 to 0.9 mass% of at least one.

Technical Field

The present invention relates to a resin composition for soldering, a resin core solder using the same, and a solder composition. The present invention also relates to a flux for soldering and a solder paste using the flux.

Background

In general, a flux used for soldering has a function of chemically removing a metal oxide present on a solder and a metal surface of a bonding object to be soldered, and allowing a metal element to move at a boundary between the two. Therefore, by soldering using the flux, an intermetallic compound can be formed between the solder and the metal surface of the object to be bonded, and a strong bond can be obtained.

In a conventional flux, a technique has been proposed in which an acrylic resin containing a polymer imparts flexibility to a residue to ensure reliability of temperature cycle (for example, see patent document 1).

Documents of the prior art

Patent document

Patent document 1: japanese patent laid-open publication No. 2010-515576

Disclosure of Invention

Problems to be solved by the invention

However, the acrylic resin, which is a polymer, is poor in compatibility with the rosin resin. Therefore, when a high-molecular acrylic resin is applied to a flux containing a rosin-based resin, the acrylic resin and the rosin-based resin are separated from each other in the flux, and the residue may become a layer. If the residue is formed into a layer, cracks are likely to be generated during temperature cycling, and the temperature cycling reliability is also lowered.

The present invention has been made to solve the above problems, and an object thereof is to provide a resin composition for soldering which has excellent compatibility with a rosin resin and excellent temperature cycle reliability and is suitable as a flux for soldering, a solder composition using the resin composition for soldering, and a resin core solder.

In addition, the acrylic resin, which is a polymer, has poor compatibility with an active agent. Therefore, if a high molecular acrylic resin is used for the flux, the acrylic resin and the active agent are separated from each other in the flux, and thus the wettability of the solder may be affected. Further, as described above, the acrylic resin of a polymer has poor compatibility with the rosin resin. Therefore, if the residue is layered, cracks are likely to occur during temperature cycling, and even if an acrylic resin is contained, the temperature cycling reliability is lowered.

The present invention has been made to solve the above problems, and an object of the present invention is to provide a flux which has excellent compatibility with an activator and a rosin-based resin, excellent temperature cycle reliability, and excellent wettability to solder, and a solder paste using the flux.

Means for solving the problems

The present inventors have found that an acrylic resin having a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, and an acrylic resin having a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, have excellent compatibility with a rosin resin and excellent temperature cycle properties.

Thus, the present invention is a resin composition for soldering, which contains an acrylic resin and a rosin resin, and contains 14 to 60 wt% of the acrylic resin, wherein the acrylic resin contains an acrylic ester or a methacrylic ester, or both an acrylic ester and a methacrylic ester, and has a number average molecular weight of 500 to less than 2000 as obtained by mass spectrometry using a time-of-flight mass spectrometer.

The present invention also provides a resin composition for soldering, which contains an acrylic resin and a rosin resin, and contains 14 to 60 wt% of the acrylic resin, wherein the acrylic resin contains an acrylic ester or a methacrylic ester, or both an acrylic ester and a methacrylic ester, and has a weight average molecular weight of 500 to less than 2000 as measured by mass spectrometry using a time-of-flight mass spectrometer.

Preferably, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is 0.2 to 2.0.

Further, the rosin-based resin is preferably contained in an amount of 30 to 80 wt%.

Preferably, the resin composition further contains another resin, and the content of the other resin is preferably 35 wt% or less.

Preferably, the paint further contains at least one of an organic acid, an amine, an organic halogen compound, an amine hydrohalide, an organic phosphorus compound, a silicone and a solvent, preferably, the organic acid is contained in an amount of 0 to 20 wt%, the amine is contained in an amount of 0 to 10 wt%, the organic halogen compound is contained in an amount of 0 to 15 wt%, the amine hydrohalide is contained in an amount of 0 to 5 wt%, the organic phosphorus compound is contained in an amount of 0 to 10 wt%, the silicone is contained in an amount of 0 to 5 wt%, and the solvent is contained in an amount of 0 to 13 wt%.

The present invention also relates to a solder composition containing the above-mentioned resin composition for soldering, a resin core solder obtained by filling a linear solder with the above-mentioned resin composition for soldering, and a solder composition obtained by coating a solder with the above-mentioned resin composition for soldering.

The present inventors have also found that an acrylic resin having a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, and an acrylic resin having a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, have excellent compatibility with an active agent, and that an acrylic resin having a molecular weight within the above range has excellent temperature cyclability.

The present invention is a flux comprising an acrylic resin, a rosin resin, an activator, and a solvent, wherein the acrylic resin is 7.0 wt% or more and 50.0 wt% or less, the rosin resin is more than 0 wt% and 30.0 wt% or less, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is 0.7 or more, the acrylic resin contains an acrylic ester or a methacrylic ester, or contains an acrylic ester and a methacrylic ester, and the number average molecular weight obtained by mass spectrometry using a time-of-flight mass spectrometer is 500 or more and less than 2000.

The present invention also provides a flux comprising an acrylic resin, an activator, and a solvent, wherein the acrylic resin comprises at least 7.0 wt% and not more than 50.0 wt% of an acrylic resin and at least 0 wt% and not more than 30.0 wt% of a rosin resin, wherein the acrylic resin comprises an acrylate or a methacrylate, or comprises an acrylate and a methacrylate, and has a number average molecular weight of 500 or more and less than 2000 as obtained by mass spectrometry using a time-of-flight mass spectrometer.

The present invention is also a flux comprising an acrylic resin, a rosin resin, an activator, and a solvent, wherein the acrylic resin is 7.0 wt% or more and 50.0 wt% or less, the rosin resin is more than 0 wt% and 30.0 wt% or less, the ratio of the weight of one or more acrylic resins to the total weight of one or more rosin resins is 0.7 or more, the acrylic resin contains an acrylic ester or a methacrylic ester, or contains an acrylic ester and a methacrylic ester, and the weight average molecular weight obtained by mass spectrometry using a time-of-flight mass spectrometer is 500 or more and less than 2000.

The present invention also provides a flux comprising an acrylic resin, an activator, and a solvent, wherein the acrylic resin comprises at least 7.0 wt% and not more than 50.0 wt% of an acrylic resin and at least 0 wt% and not more than 30.0 wt% of a rosin resin, wherein the acrylic resin comprises an acrylate or a methacrylate, or comprises an acrylate and a methacrylate, and has a weight average molecular weight of 500 or more and less than 2000 as measured by mass spectrometry using a time-of-flight mass spectrometer.

Acrylic resins having a number average molecular weight of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer and acrylic resins having a weight average molecular weight of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer are also excellent in compatibility with rosin resins. Therefore, when the flux of the present invention contains a rosin-based resin, the ratio of the weight of one or more kinds of acrylic resins to the weight of one or more kinds of rosin-based resins (acrylic resin/rosin-based resin) is preferably 0.7 or more. The weight ratio of the acrylic resin to the rosin resin is preferably 0.8 or more, more preferably 1.0 or more, and most preferably 2.0 or more and 6.0 or less.

The content of the acrylic resin is preferably 7.0 wt% or more and 35.0 wt% or less, and most preferably 10.0 wt% or more and 30.0 wt% or less. The content of the rosin-based resin is most preferably 2.0 wt% or more and 15.0 wt% or less.

The flux of the present invention preferably further contains 0 to 10.0 wt% of another resin.

The flux of the present invention contains one or more of an organic acid, an amine, an organic halogen compound and an amine hydrohalide salt as an active agent.

The flux of the present invention preferably contains, as the organic acid, 0 wt% or more and 25.0 wt% or less of any one of dimer acid as a dimer in a reactant of monocarboxylic acid, hydrogenated dimer acid obtained by hydrogenating the dimer acid, trimer acid as a trimer in a reactant of monocarboxylic acid, and hydrogenated trimer acid obtained by hydrogenating the trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid, and 0 wt% or more and 15.0 wt% or less of other organic acids than dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid. In addition, the total content of any one of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid, and one or two or more other organic acids is preferably 30.0 wt% or less.

The flux of the present invention preferably contains 0 wt% to 10.0 wt% of an amine, 0 wt% to 5.0 wt% of an organic halogen compound, 0 wt% to 2.0 wt% of an amine hydrohalide salt, and 0 wt% to 10.0 wt% of a thixotropic agent. The content of the organic halogen compound is preferably 0 wt% or more and 2.5 wt% or less, and the content of the amine hydrohalide salt is preferably 0 wt% or more and 1.2 wt% or less. The flux of the present invention preferably further contains 0 wt% to 10.0 wt% of a hindered phenol-based metal deactivator and 0 wt% to 5.0 wt% of a nitrogen compound-based metal deactivator. And the balance being solvent.

The present invention is also a solder paste containing the flux and the metal powder.

The metal powder had the following alloy composition: as: 25 to 300 mass ppm, and Sb: more than 0 ppm by mass and 3000 ppm by mass or less, Bi: more than 0 mass ppm and 10000 mass ppm or less and Pb: more than 0 ppm by mass and 5100 ppm by mass or less, the balance being Sn, and satisfying the following formulas (1) and (2).

275≤2As+Sb+Bi+Pb···(1)

0.01≤(2As+Sb)/(Bi+Pb)≤10.00···(2)

In the above formulas (1) and (2), As, Sb, Bi and Pb respectively represent the contents (mass ppm) in the above alloy composition.

Further, the alloy composition satisfies the following formula (1 a).

275≤2As+Sb+Bi+Pb≤25200···(1a)

In the formula (1a), As, Sb, Bi and Pb each represent the content (mass ppm) in the alloy composition.

Further, the alloy composition satisfies the following formula (1 b).

275≤2As+Sb+Bi+Pb≤5300···(1b)

In the formula (1b), As, Bi and Pb each represent the content (mass ppm) in the alloy composition.

Further, the alloy composition satisfies the following formula (2 a).

0.31≤(2As+Sb)/(Bi+Pb)≤10.00···(2a)

In the formula (2a), As, Sb, Bi and Pb each represent the content (mass ppm) in the alloy composition.

Further, the alloy composition contains Ag: 0-4 mass% and Cu: 0 to 0.9 mass% of at least one.

Further, the present invention has found that an acrylic resin having a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, and an acrylic resin having a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, have excellent compatibility with an active agent, and that acrylic resins, polyethylene resins, and polypropylene resins having molecular weights within the above ranges have excellent temperature cyclability.

The present invention is thus a flux comprising an acrylic resin, a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin (also referred to as polyethylene-polypropylene resin), and a solvent, wherein the acrylic resin contains an acrylic ester or a methacrylic ester, or an acrylic ester and a methacrylic ester, and has a number average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer, and contains 7.0 wt% or more and 50.0 wt% or less of the acrylic resin.

The present invention also provides a flux containing an acrylic resin, a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, and a solvent, wherein the acrylic resin contains an acrylic ester or a methacrylic ester, or an acrylic ester and a methacrylic ester, and contains 7.0 wt% or more and 50.0 wt% or less of the acrylic resin, and has a weight average molecular weight of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer.

In the flux of the present invention, the ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene resin or polypropylene resin, or the ratio of the total weight of two or more kinds of polyethylene resin or polypropylene resin (acrylic resin/polyethylene-polypropylene resin) is preferably 1.0 to 120.0. The weight ratio of the acrylic resin to the polyethylene-polypropylene resin is more preferably 2.0 or more and 100.0 or less, and still more preferably 4.0 or more and 30.0 or less.

Further, it is preferable to contain 0.1 to 10.0 wt% of a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin. The content of the acrylic resin is preferably 7.0 wt% or more and 35.0 wt% or less, and most preferably 10.0 wt% or more and 30.0 wt% or less.

Acrylic resins having a number average molecular weight of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer and acrylic resins having a weight average molecular weight of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer are also excellent in compatibility with rosin resins. Therefore, the flux of the present invention may contain a rosin resin, and preferably contains more than 0 wt% and 30.0 wt% or less of the rosin resin. The content of the rosin-based resin is most preferably 2.0 wt% or more and 15.0 wt% or less.

The soldering flux of the present invention further contains an active agent, and the active agent contains one or more of an organic acid, an amine, an organic halogen compound, and an amine hydrohalide salt.

The flux of the present invention preferably contains, as the organic acid, any one of dimer acid as a dimer in a reactant of monocarboxylic acid, hydrogenated dimer acid as a hydrogenated dimer acid to the dimer acid, trimer acid as a trimer in a reactant of monocarboxylic acid, and hydrogenated trimer acid as a hydrogenated trimer acid to the trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid in an amount of 0 wt% or more and 25.0 wt% or less, and 0 wt% or more and 15.0 wt% or less of organic acids other than dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid. The total content of any one of dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, and one or 2 or more other organic acids is preferably 30.0 wt% or less.

The present invention is a solder paste containing the flux and the metal powder.

Effects of the invention

In the present invention, a resin composition for soldering containing an acrylic resin and a rosin resin, wherein the rosin resin and the acrylic resin are layered while being inhibited from becoming non-uniform, the acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), the acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), or the acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS).

Further, the resin composition for soldering containing the acrylic resin and the rosin resin having the molecular weights within the above ranges is excellent in temperature cycle reliability, and cracking of the resin composition for soldering which is cured after heating is suppressed.

Thus, the solder resin composition of the present invention can be used in a solder composition such as a resin core solder or a flux coating solder, and can suppress formation of a residue layer. In addition, the residue is made flexible, and the residue can be prevented from cracking.

Further, the present invention is a flux containing an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), or an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and is excellent in temperature cycle reliability and capable of suppressing cracking of flux residue that is cured after heating.

Further, the acrylic resin having a molecular weight within the above range is excellent in compatibility with the activator, and solder wettability is improved. Further, the acrylic resin having a molecular weight within the above range is excellent in compatibility with the rosin resin, and when the rosin resin is contained in the flux, the rosin resin and the acrylic resin are prevented from becoming uneven and becoming layered.

Further, in the present invention, a flux containing an acrylic resin and a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin is excellent in temperature cycle reliability, suppresses cracking of flux residue cured after heating, wherein the acrylic resin has a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by a mass analysis method using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time of flight mass spectrometer (TOF-MS), or a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time of flight mass spectrometer (TOF-MS).

Thus, the flux of the present invention is used for a solder paste, and can impart flexibility to the residue and suppress the residue from cracking. Further, when the rosin-based resin is contained, the formation of a layer of the residue can be suppressed. In addition, in the solder paste containing the metal powder having the alloy composition, in addition to the temperature cycle reliability of the flux residue, a sufficient effect can be obtained with respect to the thickening suppression effect of the solder paste.

Detailed Description

< one example of the resin composition for soldering in the present embodiment >

The resin composition for soldering of the present embodiment contains an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000, which is obtained by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a rosin resin.

The resin composition for soldering according to the present embodiment contains an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000, which is obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a rosin resin.

Here, the ratio (Mn/Mw) of the number average molecular weight (Mn) to the weight average molecular weight (Mw) determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) is about 1.00 or more and 1.30 or less, and the number average molecular weight (Mn) determined by the above method substantially matches the weight average molecular weight (Mw).

Therefore, it can be said that the resin composition for soldering of the present embodiment contains an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000, which are obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a rosin resin.

An acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) is called a so-called acrylic oligomer. The acrylic resin is a monomer containing acrylic acid, acrylic acid ester as a reactant of acrylic acid and alcohol, methacrylic acid, and methacrylic acid ester as a reactant of methacrylic acid and alcohol, and examples thereof include: polymers of acrylic acid, polymers of acrylic esters, polymers of acrylic acid and acrylic esters, and the like. In addition, there may be mentioned: polymers of methacrylic acid, polymers of methacrylic acid esters, polymers of methacrylic acid and methacrylic acid esters, and the like. Further, there may be mentioned: polymers of acrylic acid and methacrylic acid, polymers of acrylic acid and methacrylic acid ester, polymers of methacrylic acid and acrylic acid ester, polymers of acrylic acid ester and methacrylic acid ester, polymers of acrylic acid and methacrylic acid and acrylic acid ester, polymers of acrylic acid and methacrylic acid ester, polymers of acrylic acid and methacrylic acid ester, polymers of acrylic acid and acrylic acid ester and methacrylic acid ester, polymers of methacrylic acid and acrylic acid ester and methacrylic acid ester, and the like. Examples of the acrylic ester include butyl acrylate, and examples of the acrylic resin containing butyl acrylate as a monomer include: butyl acrylate polymers, polymers of acrylic esters other than butyl acrylate and butyl acrylate, polymers of acrylic acid and acrylic esters other than butyl acrylate and butyl acrylate, and the like. Examples of the methacrylate ester include butyl methacrylate, and examples of the acrylic resin containing butyl methacrylate as a monomer include: butyl methacrylate polymers, polymers of butyl methacrylate and other methacrylates, butyl methacrylate polymers, methacrylic acid and other methacrylates, butyl methacrylate polymers, and the like. Further, there may be mentioned a polymer of acrylic acid and butyl methacrylate, a polymer of acrylic acid and a methacrylate other than butyl methacrylate and butyl methacrylate, a polymer of methacrylic acid and butyl acrylate, a polymer of methacrylic acid and an acrylate other than butyl acrylate and butyl acrylate, a polymer of butyl acrylate and butyl methacrylate, a polymer of an acrylate other than butyl acrylate and butyl methacrylate, a polymer of butyl acrylate and a methacrylate other than butyl methacrylate and the like. The polymerization reaction may be random copolymerization or block copolymerization. The alcohol is an alcohol having 1 to 24 carbon atoms with a linear carbon chain or an alcohol having 3 to 24 carbon atoms with a branched carbon chain, and examples of the alcohol include: methanol having 1 carbon atom, ethanol having 2 carbon atoms, 1-propanol having 3 carbon atoms, 2-propanol having 3 carbon atoms, ethylene glycol monomethyl ether having 3 carbon atoms, 1-butanol having 4 carbon atoms, 2-butanol having 4 carbon atoms, isobutanol having 4 carbon atoms, 1-hexanol having 6 carbon atoms, diethylene glycol monoethyl ether having 6 carbon atoms, benzyl alcohol having 7 carbon atoms, 1-octanol having 8 carbon atoms, 2-ethylhexanol having 8 carbon atoms, phenyl glycol having 8 carbon atoms, 1-decanol having 9 carbon atoms, lauryl alcohol having 12 carbon atoms, cetyl alcohol having 16 carbon atoms, stearyl alcohol having 18 carbon atoms, oleyl alcohol having 18 carbon atoms, behenyl alcohol having 22 carbon atoms, and the like. Examples of such acrylic resins include: butyl acrylate oligomer, alkyl acrylate oligomer, butyl methacrylate oligomer, isotridecyl methacrylate oligomer, butyl acrylate-butyl acrylate co-oligomer, butyl acrylate-polyethylene co-oligomer, and the like, and one or two or more of them may be used.

Examples of the rosin-based resin include: raw material rosins such as gum rosin, wood rosin and tall oil rosin, and derivatives derived from the raw material rosin. Examples of the derivatives include: purified rosin, hydrogenated rosin, disproportionated rosin, polymerized rosin, acid-modified rosin, phenol-modified rosin, and a modified product of an α, β -unsaturated carboxylic acid (acrylated rosin, maleated rosin, fumarated rosin, etc.), as well as a purified product, a hydrogenated product, and a disproportionated product of the polymerized rosin, and a purified product, a hydrogenated product, and a disproportionated product of the modified product of the α, β -unsaturated carboxylic acid, etc.

The resin composition for soldering of the present embodiment contains 15 wt% or more and 60 wt% or less of an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000, which are obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and 30 wt% or more and 80 wt% or less of a rosin resin. In the resin composition for soldering of the present embodiment, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is preferably 0.2 to 2.0. The ratio of the weight of the acrylic resin to the rosin resin is more preferably 0.3 to 1.5, and still more preferably 0.4 to 1.0.

The resin composition for soldering of the present embodiment may contain other resins in addition to the rosin-based resin. The other resin may further contain at least one resin selected from the group consisting of terpene resins, modified terpene resins, terpene phenol resins, modified terpene phenol resins, styrene resins, modified styrene resins, xylene resins, modified xylene resins, polyethylene, polypropylene, polyvinyl acetate, polyvinyl alcohol, polyethylene polypropylene copolymers and polyethylene polyvinyl acetate copolymers. As the modified terpene resin, an aromatic modified terpene resin, a hydrogenated aromatic modified terpene resin, or the like can be used. As the modified terpene-phenol resin, a hydrogenated terpene-phenol resin or the like can be used. As the modified styrene resin, a styrene acrylic resin, a styrene maleic acid resin, or the like can be used. As the modified xylene resin, phenol-modified xylene resin, alkylphenol-modified xylene resin, phenol-modified resol-type xylene resin, polyol-modified xylene resin, polyoxyethylene-addition xylene resin, and the like can be used. The content of the other resin is preferably 35 wt% or less.

The resin composition for soldering of the present embodiment may further contain at least one of an organic acid, an amine, an organic halogen compound, an amine hydrohalide salt, an organic phosphorus compound, silicone, and a solvent.

Examples of the organic acid include: glutaric acid, adipic acid, azelaic acid, eicosanedioic acid, citric acid, glycolic acid, succinic acid, salicylic acid, diglycolic acid, dipicolinic acid, dibutylanilino diglycolic acid, suberic acid, sebacic acid, thioglycolic acid, phthalic acid, isophthalic acid, terephthalic acid, dodecanedioic acid, p-hydroxyphenylacetic acid, picolinic acid, phenylsuccinic acid, fumaric acid, maleic acid, malonic acid, lauric acid, benzoic acid, tartaric acid, tris (2-carboxyethyl) isocyanurate, glycine, 1, 3-cyclohexanedicarboxylic acid, 2-bis (hydroxymethyl) propionic acid, 2-bis (hydroxymethyl) butyric acid, 4-tert-butylbenzoic acid, 2, 3-dihydroxybenzoic acid, 2, 4-diethylglutaric acid, 2-quinolinecarboxylic acid, 3-hydroxybenzoic acid, Malic acid, p-anisic acid, palmitic acid, stearic acid, 12-hydroxystearic acid, oleic acid, linoleic acid, linolenic acid, etc.

Examples of the organic acid include dimer acid which is a reactant of oleic acid and linoleic acid, trimer acid which is a reactant of oleic acid and linoleic acid, hydrogenated dimer acid obtained by hydrogenating dimer acid which is a reactant of oleic acid and linoleic acid, and hydrogenated trimer acid obtained by hydrogenating trimer acid which is a reactant of oleic acid and linoleic acid.

Further, as the organic acid, a dimer acid other than a reactant of oleic acid and linoleic acid, a trimer acid other than a reactant of oleic acid and linoleic acid, a hydrogenated dimer acid obtained by hydrogenating a dimer acid other than a reactant of oleic acid and linoleic acid, or a hydrogenated trimer acid obtained by hydrogenating a trimer acid other than a reactant of oleic acid and linoleic acid, there may be mentioned: dimer acid as a reactant of acrylic acid, trimer acid as a reactant of acrylic acid, dimer acid as a reactant of methacrylic acid, trimer acid as a reactant of methacrylic acid, dimer acid as a reactant of acrylic acid and methacrylic acid, trimer acid as a reactant of acrylic acid and methacrylic acid, dimer acid as a reactant of oleic acid, trimer acid as a reactant of oleic acid, dimer acid as a reactant of linoleic acid, trimer acid as a reactant of linoleic acid, dimer acid as a reactant of linolenic acid, trimer acid as a reactant of linolenic acid, dimer acid as a reactant of acrylic acid and oleic acid, trimer acid as a reactant of acrylic acid and oleic acid, dimer acid as a reactant of acrylic acid and linoleic acid, trimer acid as a reactant of acrylic acid and linoleic acid, dimer acid as a reactant of acrylic acid and linolenic acid, trimer acid as a reactant of acrylic acid and linolenic acid, dimer acid, trimer acid as a reactant of methacrylic acid and linoleic acid, trimer acid, and/or a reactant of methacrylic acid, and/or a polymer, Trimer acid as a reactant of acrylic acid and linolenic acid, dimer acid as a reactant of methacrylic acid and oleic acid, trimer acid as a reactant of methacrylic acid and oleic acid, dimer acid as a reactant of methacrylic acid and linoleic acid, trimer acid as a reactant of methacrylic acid and linoleic acid, dimer acid as a reactant of methacrylic acid and linolenic acid, trimer acid as a reactant of methacrylic acid and linolenic acid, a dimer acid that is a reaction product of oleic acid and linolenic acid, a dimer acid that is a reaction product of linoleic acid and linolenic acid, a trimer acid that is a reaction product of linoleic acid and linolenic acid, a hydrogenated dimer acid obtained by hydrogenating a dimer acid other than the reaction product of oleic acid and linoleic acid, a hydrogenated trimer acid obtained by hydrogenating a trimer acid other than the reaction product of oleic acid and linoleic acid, and the like.

As the organic acid, one or two or more of them may be used. The content of the organic acid is preferably 0 wt% or more and 20 wt% or less. The content of the organic acid is more preferably 1 to 20 wt%, and still more preferably 4 to 15 wt%. The content of the organic acid is more preferably 5 wt% or more and 10 wt% or less.

Examples of the amine include: monoethanolamine, diphenylguanidine, ethylamine, triethylamine, ethylenediamine, triethylenetetramine, 2-methylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 1, 2-dimethylimidazole, 2-ethyl-4-methylimidazole, 2-phenylimidazole, 2-phenyl-4-methylimidazole, 1-benzyl-2-phenylimidazole, 1-cyanoethyl-2-methylimidazole, 1-cyanoethyl-2-undecylimidazole, 1-cyanoethyl-2-ethyl-4-methylimidazole, 1-cyanoethyl-2-phenylimidazole, 1-cyanoethyl-2-undecylimidazolium trimellitate, a salt thereof with a carboxylic acid or a derivative thereof, 1-cyanoethyl-2-phenylimidazolium trimellitate, 2, 4-diamino-6- [2 ' -methylimidazolyl- (1 ') ] -ethyl-s-triazine, 2, 4-diamino-6- [2 ' -undecylimidazolyl- (1 ') ] -ethyl-s-triazine, 2, 4-diamino-6- [2 ' -ethyl-4 ' -methylimidazolyl- (1 ') ] -ethyl-s-triazine, 2, 4-diamino-6- [2 ' -methylimidazolyl- (1 ') ] -ethyl-s-triazine isocyanuric acid adduct, 2-phenylimidazole isocyanuric acid adduct, and mixtures thereof, 2-phenyl-4, 5-dihydroxymethylimidazole, 2-phenyl-4-methyl-5-hydroxymethylimidazole, 2, 3-dihydro-1H-pyrrolo [1,2-a ] benzimidazole, 1-dodecyl-2-methyl-3-benzylimidazolium chloride, 2-methylimidazoline, 2-phenylimidazoline, 2, 4-diamino-6-vinyl-s-triazine isocyanuric acid adduct, 2, 4-diamino-6-methacryloyloxyethyl-s-triazine, epoxy-imidazole adduct, 2-methylbenzimidazole, 2-dimethylbenzimidazole, 2-methyl-3-methyl-imidazolium chloride, 2-dodecyl-2-methyl-3-benzylimidazolium chloride, 2-methylimidazolium chloride, 2-methyl-6-vinyl-s-triazine, 2-methyl-imidazole, 2-methyl-ethyl-one, 2-methyl-imidazole, 2-methyl-imidazole, 2-methyl-one or a mixture thereof, 2-octylbenzimidazole, 2-pentylbenzimidazole, 2- (1-ethylpentyl) benzimidazole, 2-nonylbenzimidazole, 2- (4-thiazolyl) benzimidazole, 2- (2 ' -hydroxy-5 ' -methylphenyl) benzotriazole, 2- (2 ' -hydroxy-3 ' -tert-butyl-5 ' -methylphenyl) -5-chlorobenzotriazole, 2- (2 ' -hydroxy-3 ', 5 ' -di-tert-pentylphenyl) benzotriazole, 2- (2 ' -hydroxy-5 ' -tert-octylphenyl) benzotriazole, 2 ' -methylenebis [6- (2H-benzotriazol-2-yl) -4-tert-octylphenol ]), 6- (2-benzotriazolyl) -4-tert-octyl-6 '-tert-butyl-4' -methyl-2, 2 '-methylenebiphenol, 1,2, 3-benzotriazole, 1- [ N, N-bis (2-ethylhexyl) aminomethyl ] benzotriazole, carboxybenzotriazole, 1- [ N, N-bis [ 2-ethylhexyl ] aminomethyl ] methylbenzotriazole, 2' - [ [ (methyl-1H-benzotriazol-1-yl) methyl ] imino ] diethanol, 1- (1 ', 2' -dicarboxyethyl) benzotriazole, 1- (2, 3-dicarboxypropyl) benzotriazole, 1- [ (2-ethylhexylamino) methyl ] benzotriazole, 2-dimethylcarbonylbisphenol, bis (phenylimidazole), 2-phenyl) amino) phenyl) s), 2-4-tert-octyl-methyl) benzotriazole, 2-4-methyl) benzotriazole, 2-phenyl, 2-benzotriazole, 2-phenyl, 2-4-methyl-4-benzotriazole, 2-phenyl, and 2-phenyl, 2-methyl-phenyl, 2-bis (methyl) benzotriazole, 2, 6-bis [ (1H-benzotriazol-1-yl) methyl ] -4-methylphenol, 5-methylbenzotriazole, 5-phenyltetrazole and the like.

As the amine, one or two or more of them may be used. The content of the amine is preferably 0 wt% or more and 10 wt% or less. The content of the amine is more preferably 1 wt% or more and 10 wt% or less, and still more preferably 4 wt% or more and 10 wt% or less. The content of the amine is more preferably 5 wt% or more and 10 wt% or less.

Examples of the organic halogen compound include: trans-2, 3-dibromo-1, 4-butenediol, triallyl isocyanurate 6 bromide, 1-bromo-2-butanol, 1-bromo-2-propanol, 3-bromo-1, 2-propanediol, 1, 4-dibromo-2-butanol, 1, 3-dibromo-2-propanol, 2, 3-dibromo-1-butanol, 2, 3-dibromo-1, 4-butanediol, 2, 3-dibromo-2-butene-1, 4-diol, trans-2, 3-dibromo-2-butene-1, 4-diol, cis-2, 3-dibromo-2-butene-1, 4-diol, tetrabromophthalic acid, bromosuccinic acid, and the like. In addition, there may be mentioned: chloroalkane, chlorinated fatty acid ester, hydantoin, and the like as the organic chlorine compound. There can be also mentioned: fluorine-based surfactants, perfluoroalkyl-containing surfactants, polytetrafluoroethylene, and the like are used as the organic fluorine compound.

As the organic halogen compound, one or two or more of them can be used. The content of the organic halogen compound is preferably 0 wt% or more and 15 wt% or less. The content of the organic halogen compound is more preferably 1 wt% or more and 10 wt% or less, and still more preferably 4 wt% or more and 10 wt% or less. The content of the organic halogen compound is more preferably 5 wt% or more and 10 wt% or less.

The amine hydrohalide is a compound obtained by reacting an amine with a hydrogen halide, and includes: aniline hydrogen chloride, aniline hydrogen bromide, and the like. As the amine of the amine hydrohalide salt, the above-mentioned amines can be used, and there are exemplified: ethylamine, ethylenediamine, triethylamine, methylimidazole, 2-ethyl-4-methylimidazole, and the like, and examples of the hydrogen halide include: hydrides of chlorine, bromine, iodine, fluorine (hydrogen chloride, hydrogen bromide, hydrogen iodide, hydrogen fluoride). Further, a boron fluoride may be contained instead of or together with the amine hydrohalide, and examples of the boron fluoride include fluoroboric acid.

As the amine hydrohalide salt, one or two or more of them may be used. The content of the amine hydrohalide salt is preferably 0 wt% or more and 5 wt% or less.

As the organic phosphorus compound, there may be mentioned: methyl acid phosphate, ethyl acid phosphate, isopropyl acid phosphate, monobutyl acid phosphate, butyl acid phosphate, dibutyl acid phosphate, butoxyethyl acid phosphate, 2-ethylhexyl acid phosphate, bis (2-ethylhexyl) acid phosphate, monoisodecyl acid phosphate, isodecyl acid phosphate, lauryl acid phosphate, isotridecyl acid phosphate, stearyl acid phosphate, oleyl acid phosphate, tallow phosphate, cocoyl phosphate, isostearyl acid phosphate, alkyl acid phosphate, ditetradecyl acid phosphate, ethylene glycol acid phosphate, 2-hydroxyethyl methacrylate acid phosphate, dibutyl acid phosphate, mono-2-ethylhexyl 2-ethylphosphonate, alkyl (alkyl) phosphonate, and the like.

As the organic phosphorus compound, one or two or more of them can be used. The content of the organic phosphorus compound is preferably 0 wt% or more and 10 wt% or less.

Examples of the silicone oil include: dimethyl silicone oil, cyclic silicone oil, methylphenyl silicone oil, methylhydrogen silicone oil, higher fatty acid-modified silicone oil, alkyl-aralkyl-modified silicone oil, amino-modified silicone oil, epoxy-modified silicone oil, polyether-modified silicone oil, alkyl-polyether-modified silicone oil, methanol-modified silicone oil, and the like.

As the silicone oil, one or two or more of them can be used. The content of the silicone oil is preferably 0 wt% or more and 5 wt% or less.

Examples of the solvent include: water, ester solvents, alcohol solvents, glycol ether solvents, terpineol, and the like. Examples of the ester-based solvent include: fatty acid alkyl esters, butyl stearate, 2-ethylhexyl stearate, isotridecyl stearate, methyl oleate, isobutyl oleate, methyl coconut fatty acid, methyl laurate, isopropyl myristate, isopropyl palmitate, 2-ethylhexyl palmitate, octyl dodecyl myristate. Examples of the alcohol solvent include: ethanol, industrial ethanol (a mixed solvent of ethanol and/or isopropanol), isopropanol, 1, 2-butanediol, isobornyl cyclohexanol, 2, 4-diethyl-1, 5-pentanediol, 2-dimethyl-1, 3-propanediol, 2, 5-dimethyl-2, 5-hexanediol, 2, 5-dimethyl-3-hexyne-2, 5-diol, 2, 3-dimethyl-2, 3-butanediol, 1,1, 1-tris (hydroxymethyl) ethane, 2-ethyl-2-hydroxymethyl-1, 3-propanediol, 2' -oxybis (methylene) bis (2-ethyl-1, 3-propanediol), 2, 2-bis (hydroxymethyl) -1, 3-propanediol, 1,2, 6-trihydroxyhexane, bis [2,2, 2-tris (hydroxymethyl) ethyl ] ether, 1-ethynyl-1-cyclohexanol, 1, 4-cyclohexanediol, 1, 4-cyclohexanedimethanol, erythritol, threitol, guaiacol glyceryl ether, 3, 6-dimethyl-4-octyne-3, 6-diol, 2,4,7, 9-tetramethyl-5-decyne-4, 7-diol, and the like. Examples of the glycol ether solvent include: diethylene glycol hexyl ether, diethylene glycol mono-2-ethylhexyl ether, ethylene glycol monophenyl ether, 2-methylpentane-2, 4-diol, diethylene glycol dibutyl ether, triethylene glycol monobutyl ether, and the like.

As the solvent, one or two or more of them may be used. The content of the solvent is preferably 0 wt% or more and 13 wt% or less. Further, it is more preferable that no solvent is contained.

< example of Forming solder composition of the present embodiment >

The solder composition of the present embodiment contains the above-described solder resin composition. Examples of such a solder composition include a solder composition called a resin core solder in which the above-described resin composition for soldering is filled in a linear solder, and a solder composition called a flux coating in which a solder is coated with the above-described resin composition for soldering.

< example of the Structure of resin core solder of the present embodiment >

The resin core solder of the present embodiment is a linear solder filled with the above-described resin composition for soldering. The solder resin composition used for the resin core solder is required to be in a solid state at normal temperature so as not to flow out in the step of processing the solder into a linear shape, or to have a predetermined high viscosity so as not to flow out. When used for the resin core solder, the viscosity required of the solder resin composition is, for example, 3500Pa · s or more.

The solder is preferably free of Pb and is composed of a Sn-based single substance, Sn-Ag, Sn-Cu, Sn-Ag-Cu, Sn-Bi, Sn-In, or the like, or an alloy obtained by adding Sb, Bi, In, Cu, Zn, As, Ag, Cd, Fe, Ni, Co, Au, Ge, P, or the like to these alloys.

< example of the structure of flux coating solder of the present embodiment >

The flux coating solder of the present embodiment is a solder coated with the above-described resin composition for soldering. The solder has a spherical shape called a ball, or a columnar shape called a column or a pellet, for example. The solder resin composition in a state of being coated with a solder is a solid adhered to the surface of the solder at normal temperature.

< examples of the effects of the solder resin composition of the present embodiment and the solder composition using the same >

An acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and an acrylic resin having an excellent compatibility with a rosin resin. Thus, the resin composition for soldering containing the acrylic resin and the rosin resin having the molecular weights within the above ranges can prevent the rosin resin and the acrylic resin from becoming non-uniform and becoming layered.

Thus, the solder resin composition of the present embodiment can be used in a solder composition such as a resin core solder or a flux coating solder, and can suppress formation of a residue layer. In addition, the residue is made flexible, and the residue can be prevented from cracking.

< example of flux in first embodiment >

The flux of the first embodiment contains an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), an active agent, and a solvent.

The flux of the first embodiment contains an acrylic resin having a weight-average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), an active agent, and a solvent.

As described above, the number average molecular weight (Mn) and the weight average molecular weight (Mw) obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) have a ratio (Mn/Mw) of the number average molecular weight (Mn) to the weight average molecular weight (Mw) of about 1.00 or more and 1.30 or less, and the number average molecular weight (Mn) obtained by the above method substantially matches the weight average molecular weight (Mw).

Therefore, it can also be said that the flux of the first embodiment contains an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 as measured by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), an active agent, and a solvent.

The flux of the first embodiment may contain a rosin resin. Specific examples of the rosin-based resin are the same as those described in the above-mentioned resin composition for soldering, and one or two or more compounds described in the specific examples of the resin composition for soldering can be used.

The flux of the first embodiment contains 7.0 wt% or more and 50.0 wt% or less of an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and 0 wt% or more and 30.0 wt% or less of a rosin resin. When the flux of the first embodiment contains a rosin-based resin, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin-based resins (acrylic resin/rosin-based resin) is preferably 0.7 or more. The weight ratio of the acrylic resin to the rosin resin is preferably 0.8 or more, more preferably 1.0 or more, and most preferably 2.0 or more and 6.0 or less. The content of the acrylic resin is preferably 7.0 wt% or more and 35.0 wt% or less, and most preferably 10.0 wt% or more and 30.0 wt% or less. The content of the rosin-based resin is most preferably 2.0 wt% or more and 15.0 wt% or less.

The flux of the first embodiment may contain other resins in addition to the rosin-based resin. Specific examples of the other resins are the same as those described above for the soldering resin composition, and the content of the other resins is preferably 0 wt% or more and 10.0 wt% or less.

The flux of the first embodiment contains one or more of an organic acid, an amine, an organic halogen compound, and an amine hydrohalide salt as an active agent.

The flux of the first embodiment may further include a thixotropic agent, a hindered phenol-based metal deactivator, and a nitrogen compound-based metal deactivator.

Examples of the organic acid include: dimer acid which is a dimer in a reactant of monocarboxylic acid, hydrogenated dimer acid obtained by hydrogenating dimer acid, trimer acid which is a trimer in a reactant of monocarboxylic acid, and hydrogenated trimer acid obtained by hydrogenating trimer acid. As the dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid, there can be mentioned: a dimer acid as a reactant of oleic acid and linoleic acid, a trimer acid as a reactant of oleic acid and linoleic acid, a hydrogenated dimer acid obtained by hydrogenating a dimer acid as a reactant of oleic acid and linoleic acid, or a hydrogenated trimer acid obtained by hydrogenating a trimer acid as a reactant of oleic acid and linoleic acid.

Further, as the dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid, there may be mentioned: specific examples thereof are the same as the dimer acid described in the above-mentioned resin composition for soldering, and the like.

As the dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, one or two or more of them may be used alone. In the flux of the first embodiment, when one or two or more components selected from other organic acids, amines, organic halogen compounds, and amine hydrohalides are contained within the range specified in the present invention, the content of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid is preferably 0 wt% or more and 25.0 wt% or less. In addition, when any of other organic acids, amines, organic halogen compounds, and amine hydrohalides is not contained, the content of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid is preferably more than 0 wt% and 25.0 wt% or less. The content of one or two or more of the dimer acid, the hydrogenated dimer acid, the trimer acid, and the hydrogenated trimer acid is more preferably 1.0 wt% or more and 25.0 wt% or less, still more preferably 3.0 wt% or more and 25.0 wt% or less, and most preferably 5.0 wt% or more and 25.0 wt% or less.

Specific examples of the organic acids other than the dimer acid, the hydrogenated dimer acid, the trimer acid and the hydrogenated trimer acid are the same as those described for the above-mentioned resin composition for soldering.

As the other organic acid, one or two or more of them may be used. In the flux of the first embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, amine, organic halogen compound, and amine hydrohalide salt are contained within the range specified in the present invention, the content of the other organic acid is preferably 0 wt% or more and 15.0 wt% or less. When any one of the dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, amine, organic halogen compound and amine hydrohalide salt is not contained, the content of the other organic acid is preferably more than 0 wt% and 15.0 wt% or less. The content of the other organic acid is more preferably 1.0 wt% or more and 15.0 wt% or less, still more preferably 3.0 wt% or more and 15.0 wt% or less, and most preferably 5.0 wt% or more and 15.0 wt% or less. Further, the total content of any one of dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, or two or more of dimer acid, hydrogenated dimer acid, trimer acid and hydrogenated trimer acid, and one or two or more other organic acids is preferably 30.0 wt% or less.

As a specific example of the amine, one kind or two or more kinds of them can be used as the amine, as in the case of the amine described in the above-mentioned resin composition for soldering. In the flux of the first embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, organic halogen compound, and amine hydrohalide salt are contained within the range specified in the present invention, the amine content is preferably 0 wt% or more and 10.0 wt% or less. When any one of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acids, organic halogen compounds, and amine hydrohalide salts is not contained, the content of amine is preferably more than 0 wt% and 10.0 wt% or less. The content of the amine is more preferably 1.0 wt% or more and 10.0 wt% or less, and when the activity of the amine is not required, it is more preferably 1.0 wt% or more and 3.0 wt% or less. When the activity of the amine is required, the content of the amine is more preferably 3.0 wt% or more and 10.0 wt% or less, and most preferably 5.0 wt% or more and 10.0 wt% or less.

As a specific example of the organohalogen compound, one or two or more kinds of them can be used as the organohalogen compound, similarly to the organohalogen compound described in the above-mentioned resin composition for soldering. In the flux of the first embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, amine, and amine hydrohalide salt are contained within the range specified in the present invention, the content of the organic halogen compound is preferably 0 wt% or more and 5.0 wt% or less, and more preferably 0 wt% or more and 2.5 wt% or less. In addition, when any one of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acids, amines, and amine hydrohalides is not contained, the content of the organic halogen compound is preferably more than 0 wt% and 5.0 wt% or less, more preferably more than 0 wt% and 2.5 wt% or less.

As a specific example of the amine hydrohalide salt, one or two or more kinds of the amine hydrohalide salts can be used as the amine hydrohalide salt, similarly to the amine hydrohalide salt described in the above-mentioned soldering resin composition. In the flux of the first embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, amine, and organic halogen compound are contained within the range specified in the present invention, the content of the amine hydrohalide salt is preferably 0 wt% or more and 2.0 wt% or less, and more preferably 0 wt% or more and 1.2 wt% or less. In addition, when any of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acids, amine, and organic halogen compound is not contained, the content of the amine hydrohalide is preferably more than 0 wt% and 2.0 wt% or less, and more preferably more than 0 wt% and 1.2 wt% or less.

As a specific example of the thixotropic agent, one or two or more of them can be used as the thixotropic agent, similarly to the thixotropic agent described in the above-mentioned soldering resin composition. In the flux of the first embodiment, the content of the thixotropic agent is preferably 0 wt% or more and 10.0 wt% or less. The content of the thixotropic agent is preferably more than 0 wt% and 10.0 wt% or less, more preferably 1.0 wt% or more and 10.0 wt% or less, further preferably 3.0 wt% or more and 10.0 wt% or less, and most preferably 5.0 wt% or more and 10.0 wt% or less.

Examples of the metal deactivator include: hindered phenol-based metal deactivators, nitrogen compound-based metal deactivators, and the like. Examples of the hindered phenol-based metal deactivator include: bis (3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid), N' -hexamethylenebis (3- (3, 5-di-tert-butyl-4-hydroxyphenyl) propionamide), and the like. Examples of the nitrogen compound-based metal deactivator include N- (2H-1,2, 4-triazol-5-yl) salicylamide and the like.

As the metal deactivator, one or two or more of them may be used. The content of the metal deactivator is preferably 0 wt% or more and 10.0 wt% or less with respect to the hindered phenol-based metal deactivator, and preferably 0 wt% or more and 5.0 wt% or less with respect to the nitrogen compound-based metal deactivator. The content of the hindered phenol-based metal deactivator is preferably more than 0 wt% and 10.0 wt% or less, more preferably 1.0 wt% or more and 10.0 wt% or less, further preferably 2.0 wt% or more and 10.0 wt% or less, and most preferably 5.0 wt% or more and 10.0 wt% or less. The content of the nitrogen compound-based metal deactivator is preferably more than 0 wt% and 5.0 wt% or less, more preferably 0.1 wt% or more and 5.0 wt% or less, still more preferably 0.5 wt% or more and 5.0 wt% or less, and most preferably 1.0 wt% or more and 5.0 wt% or less.

Specific examples of the solvent include the same solvents as those described above for the soldering resin composition, and one or two or more of them can be used as the solvent. In the flux of the first embodiment, when only the acrylic resin and the activator are contained as essential components, the content of the solvent is the balance of the content of the essential components.

In the flux of the first embodiment, when any one or a combination of the thixotropic agent and the metal deactivator is contained in the predetermined content in addition to the essential components, the balance is the essential components and the content of the optionally added components.

< example of flux in second embodiment >

The flux of the second embodiment contains an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, and a solvent.

The flux of the second embodiment contains an acrylic resin having a weight-average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, and a solvent.

Therefore, the flux of the second embodiment can be said to contain an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, and a solvent.

Specific examples of the acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time of flight mass spectrometer (TOF-MS) include, as in the flux of the first embodiment: butyl acrylate oligomer, alkyl acrylate oligomer, butyl methacrylate oligomer, isotridecyl methacrylate oligomer, butyl acrylate-butyl acrylate co-oligomer, butyl acrylate-polyethylene co-oligomer, and the like, and one or two or more of them may be used.

Examples of the Polyethylene (PE) resin include: polyethylene resins, acid-modified polyethylene resins, oxidized polyethylene resins, and the like. Examples of the polypropylene (PP) resin include: polypropylene resins, acid-modified polypropylene resins, oxidized polypropylene resins, and the like. One or more of polyethylene resin and polypropylene resin may be used. The polyethylene resin and the polypropylene resin may be a copolymer of the polyethylene resin and the polypropylene resin.

The flux of the second embodiment contains 7.0 wt% to 50.0 wt% of an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), and 0 wt% to 10.0 wt% of a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin. In the flux of the second embodiment, the ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene resin or polypropylene resin, or the weight of two or more kinds of polyethylene resin or polypropylene resin, or the total weight of polyethylene resin and polypropylene resin (acrylic resin/polyethylene-polypropylene resin) is preferably 1.0 to 120.0. The weight ratio of the acrylic resin to the polyethylene-polypropylene resin is more preferably 2.0 or more and 100.0 or less, and still more preferably 4.0 or more and 30.0 or less. The content of the acrylic resin is preferably 7.0 wt% or more and 35.0 wt% or less, and most preferably 10.0 wt% or more and 30.0 wt% or less.

The flux of the second embodiment may contain a rosin resin. As a specific example of the rosin-based resin, one or two or more kinds of them can be used as in the flux of the first embodiment.

The flux of the second embodiment contains 0 wt% to 30.0 wt% of a rosin-based resin. The content of the rosin-based resin is most preferably 2.0 wt% or more and 15.0 wt% or less.

The flux of the second embodiment further includes an active agent, and the active agent includes one or more of an organic acid, an amine, an organic halogen compound, and an amine hydrohalide salt.

The flux of the second embodiment may further include a thixotropic agent, a hindered phenol-based metal deactivator, and a nitrogen compound-based metal deactivator.

Specific examples of the organic acid, the amine, the organic halogen compound, the amine hydrohalide salt, the thixotropic agent, the hindered phenol-based metal deactivator, the nitrogen compound-based metal deactivator, and the solvent are the same as those of the flux of the first embodiment.

In the flux of the second embodiment, when one or two or more of other organic acids, amines, organic halogen compounds, and amine hydrohalides are contained within the range specified in the present invention, the content of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid is preferably 0 wt% or more and 25.0 wt% or less. In addition, when any of other organic acids, amines, organic halogen compounds, and amine hydrohalides is not contained, the content of dimer acid, hydrogenated dimer acid, trimer acid, and hydrogenated trimer acid is preferably more than 0 wt% and 25.0 wt% or less. The content of one or two or more of the dimer acid, the hydrogenated dimer acid, the trimer acid, and the hydrogenated trimer acid is more preferably 1.0 wt% or more and 25.0 wt% or less, still more preferably 3.0 wt% or more and 25.0 wt% or less, and most preferably 5.0 wt% or more and 25.0 wt% or less.

In the flux of the second embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, amine, organic halogen compound, and amine hydrohalide salt are contained within the range defined by the present invention, the content of the other organic acid is preferably 0 wt% or more and 15.0 wt% or less. When any one of the dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, amine, organic halogen compound and amine hydrohalide salt is not contained, the content of the other organic acid is preferably more than 0 wt% and 15.0 wt% or less. The content of the other organic acid is more preferably 1.0 wt% or more and 15.0 wt% or less, still more preferably 3.0 wt% or more and 15.0 wt% or less, and most preferably 5.0 wt% or more and 15.0 wt% or less. In addition, the total content of any one of the dimer acid, the hydrogenated dimer acid, the trimer acid, and the hydrogenated trimer acid, two or more of the dimer acid, the hydrogenated dimer acid, the trimer acid, and the hydrogenated trimer acid, and one or more other organic acids is preferably 30.0wt or less.

In the flux of the second embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, organic halogen compound, and amine hydrohalide salt are contained within the range specified in the present invention, the amine content is preferably 0 wt% or more and 10.0 wt% or less. When any one of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, organic halogen compound, and amine hydrohalide salt is not contained, the content of amine is preferably more than 0 wt% and 10.0 wt% or less. The content of the amine is more preferably 1.0 wt% or more and 10.0 wt% or less, and when the activity of the amine is not required, it is more preferably 1.0 wt% or more and 3.0 wt% or less. When the activity of the amine is required, the content of the amine is more preferably 3.0 wt% or more and 10.0 wt% or less, and most preferably 5.0 wt% or more and 10.0 wt% or less.

In the flux of the second embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, amine, and amine hydrohalide salt are contained within the range specified in the present invention, the content of the organic halogen compound is preferably 0 wt% or more and 5.0 wt% or less, and more preferably 0 wt% or more and 2.5 wt% or less. In addition, when any one of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acids, amines, and amine hydrohalides is not contained, the content of the organic halogen compound is preferably more than 0 wt% and 5.0 wt% or less, more preferably more than 0 wt% and 2.5 wt% or less.

In the flux of the second embodiment, when one or two or more of dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, amine, and organic halogen compound are contained within the range specified in the present invention, the content of the amine hydrohalide salt is preferably 0 wt% or more and 2.0 wt% or less, and more preferably 0 wt% or more and 1.2 wt% or less. When any of the dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, other organic acid, amine, and organic halogen compound is not contained, the content of the amine hydrohalide is preferably more than 0 wt% and 2.0 wt% or less, and more preferably more than 0 wt% and 1.2 wt% or less.

In the flux of the second embodiment, the content of the thixotropic agent is preferably 0 wt% or more and 10.0 wt% or less. The content of the thixotropic agent is preferably more than 0 wt% and 10.0 wt% or less, more preferably 1.0 wt% or more and 10.0 wt% or less, further preferably 3.0 wt% or more and 10.0 wt% or less, and most preferably 5.0 wt% or more and 10.0 wt% or less.

In the flux of the second embodiment, the content of the metal deactivator is preferably 0 wt% or more and 10.0 wt% or less with respect to the hindered phenol-based metal deactivator, and preferably 0 wt% or more and 5.0 wt% or less with respect to the nitrogen compound-based metal deactivator. The content of the hindered phenol-based metal deactivator is preferably more than 0 wt% and 10.0 wt% or less, more preferably 1.0 wt% or more and 10.0 wt% or less, further preferably 2.0 wt% or more and 10.0 wt% or less, and most preferably 5.0 wt% or more and 10.0 wt% or less. The content of the nitrogen compound-based metal deactivator is preferably more than 0 wt% and 5.0 wt% or less, more preferably 0.1 wt% or more and 5.0 wt% or less, still more preferably 0.5 wt% or more and 5.0 wt% or less, and most preferably 1.0 wt% or more and 5.0 wt% or less.

In the flux of the second embodiment, when only the acrylic resin and the activator are contained as essential components, the content of the solvent is the balance of the content of the essential components.

When any one or a combination of the thixotropic agent and the metal deactivator is contained in the above-described predetermined content in addition to the essential components, the content is the balance between the essential components and the content of these optional components.

< example of solder paste of the present embodiment >

The solder paste of the present embodiment contains the flux of the first embodiment or the second embodiment and the metal powder. The metal powder is composed of a powder of a solder of Sn alone, or a powder of a solder alloy In which Sb, Bi, In, Cu, Zn, As, Ag, Cd, Fe, Ni, Co, Au, Ge, P, Pb, etc. are added to the alloy, or a Sn-Ag system, a Sn-Cu system, a Sn-Ag-Cu system, a Sn-Bi system, a Sn-In system, etc.

The solder alloy preferably has the following alloy composition: as: 25 mass ppm or more and 300 mass ppm or less, and Sb: more than 0 ppm by mass and 3000 ppm by mass or less, Bi: more than 0 mass ppm and 10000 mass ppm or less and Pb: at least one of more than 0 ppm by mass and 5100 ppm by mass or less, and the balance being Sn. The solder alloy may further contain Ag: 0% by mass or more and 4% by mass or less and Cu: at least one of 0 mass% or more and 0.9 mass% or less.

As is an element capable of suppressing a change in viscosity of the solder paste with time. As is low in reactivity with flux and is a noble element with respect to Sn, and therefore, it is presumed that the thickening suppression effect can be exhibited. The lower limit of the As content is, for example, 25 mass ppm or more, preferably 50 mass ppm or more, and more preferably 100 mass ppm or more. On the other hand, if As is too much, the wettability of the solder alloy deteriorates. The upper limit of the As content is, for example, 300 mass ppm or less, preferably 250 mass ppm or less, and more preferably 200 mass ppm or less.

Sb is an element having low reactivity with the flux and exhibiting an effect of suppressing thickening. When the solder alloy contains Sb, the lower limit of the Sb content is, for example, more than 0 mass ppm, preferably 25 mass ppm or more, more preferably 50 mass ppm or more, further preferably 100 mass ppm or more, and particularly preferably 300 mass ppm or more. On the other hand, if the Sb content is too large, the wettability deteriorates, so that it is necessary to set an appropriate content. The upper limit of the Sb content is, for example, 3000 mass ppm or less, preferably 1150 mass ppm or less, and more preferably 500 mass ppm or less.

Like Sb, Bi and Pb are elements that have low reactivity with flux and exhibit an effect of suppressing thickening. In addition, Bi and Pb are elements that can suppress the deterioration of wettability by As because they lower the liquidus temperature of the solder alloy and lower the viscosity of the molten solder.

If at least one element of Sb, Bi, and Pb is present, wettability deterioration due to As can be suppressed. When the solder alloy contains Bi, the lower limit of the Bi content is, for example, more than 0 mass ppm, preferably 25 mass ppm or more, more preferably 50 mass ppm or more, still more preferably 75 mass ppm or more, particularly preferably 100 mass ppm or more, and most preferably 250 mass ppm or more. When the solder alloy contains Pb, the lower limit of the Pb content is more than 0 mass ppm, preferably 25 mass ppm or more, more preferably 50 mass ppm or more, further preferably 75 mass ppm or more, particularly preferably 100 mass ppm or more, and most preferably 250 mass ppm or more.

On the other hand, when the content of Bi and Pb elements is too large, the solidus temperature is significantly lowered, and therefore the temperature difference Δ T between the liquidus temperature and the solidus temperature becomes too wide. If Δ T is too wide, a high melting point crystal phase with a small Bi or Pb content precipitates during solidification of the molten solder, and thus Bi or Pb in the liquid phase is concentrated. When the temperature of the molten solder is further lowered, a low melting point crystal phase having a high Bi or Pb concentration is segregated. Therefore, the solder alloy has deteriorated mechanical strength and the like, and the reliability is deteriorated. In particular, since the crystal phase having a high Bi concentration is hard and brittle, the reliability is significantly reduced when the crystal phase is segregated in the solder alloy.

From such a viewpoint, when the solder alloy contains Bi, the upper limit of the Bi content is, for example, 10000 ppm by mass or less, preferably 1000 ppm by mass or less, more preferably 600 ppm by mass or less, and still more preferably 500 ppm by mass or less. When the solder alloy contains Pb, the upper limit of the Pb content is, for example, 5100 mass ppm or less, preferably 5000 mass ppm or less, more preferably 1000 mass ppm or less, further preferably 850 mass ppm or less, and particularly preferably 500 mass ppm or less.

The solder alloy preferably satisfies the following formula (1).

275≤2As+Sb+Bi+Pb···(1)

In the above formula (1), As, Sb, Bi and Pb respectively represent the contents (mass ppm) in the alloy composition.

As, Sb, Bi and Pb are all elements showing an effect of suppressing thickening. Preferably, the total amount of these components is 275 ppm by mass or more. In the formula (1), the content of As is 2 times As high As the thickening-inhibiting effect of As compared with Sb, Bi and Pb.

The lower limit of formula (1) is preferably 350 or more, more preferably 1200 or more. On the other hand, the upper limit of (1) is not particularly limited from the viewpoint of the thickening suppressing effect, but from the viewpoint of making Δ T within an appropriate range, it is preferably 25200 or less, more preferably 10200 or less, further preferably 5300 or less, and particularly preferably 3800 or less.

The upper limit and the lower limit are appropriately selected from the above preferred embodiments and are represented by the following formulae (1a) and (1 b).

275≤2As+Sb+Bi+Pb≤25200···(1a)

275≤2As+Sb+Bi+Pb≤5300···(1b)

In the above formulas (1a) and (1b), As, Sb, Bi and Pb respectively represent the contents (mass ppm) in the alloy composition.

The solder alloy preferably satisfies the following formula (2).

0.01≤(2As+Sb)/(Bi+Pb)≤10.00···(2)

In the above formula (2), As, Sb, Bi and Pb each represent the content (mass ppm) in the alloy composition.

When the content of As and Sb is large, the wettability of the solder alloy deteriorates. On the other hand, Bi and Pb suppress deterioration of wettability due to As-containing, but when the content is too large, Δ T increases. Particularly, in an alloy composition containing Bi and Pb at the same time, Δ T is likely to increase. In view of these circumstances, if the wettability is excessively improved by increasing the contents of Bi and Pb, Δ T is enlarged. On the other hand, if the thickening inhibition effect is improved by increasing the content of As or Sb, the wettability is deteriorated. Therefore, when the groups are divided into As and Sb groups and Bi and Pb groups and the total amount of the two groups is within an appropriate prescribed range, the thickening suppressing effect, the narrowing of Δ T, and the wettability are simultaneously satisfied.

When the formula (2) is less than 0.01, the total content of Bi and Pb is relatively larger than the total content of As and Pb, and thus Δ T becomes wider. The lower limit of formula (2) is preferably 0.02 or more, more preferably 0.41 or more, further preferably 0.90 or more, particularly preferably 1.00 or more, and most preferably 1.40 or more. On the other hand, when the formula (2) exceeds 10.00, the total content of As and Sb becomes relatively larger than the total content of Bi and Pb, and thus the wettability deteriorates. (2) The upper limit is preferably 5.33 or less, more preferably 4.50 or less, further preferably 2.67 or less, and particularly preferably 2.30 or less.

The denominator of the formula (2) is "Bi + Pb", and if these are not contained, the formula (2) does not hold. Therefore, the solder alloy preferably contains at least one of Bi and Pb. As described above, the alloy composition containing no Bi and Pb is poor in wettability.

The upper limit and the lower limit are appropriately selected from the above preferred embodiments and are expressed by the following formula (2 a).

0.31≤(2As+Sb)/(Bi+Pb)≤10.00···(2a)

In the above formula (2a), As, Sb, Bi and Pb each represent the content (mass ppm) in the alloy composition.

Ag is capable of forming Ag at crystal interface₃Sn is an arbitrary element that improves the reliability of the solder alloy. Ag is an element whose ionization coefficient is relatively expensive to Sn, and promotes the thickening-inhibiting effect thereof by coexisting with As, Pb, and Bi. The Ag content is preferably 0 mass% or more and 4 mass% or less, more preferably 0.5 mass% or more and 3.5 mass% or less, and further preferably 1.0 mass% or more and 3.0 mass% or less.

Cu is an arbitrary element that can improve the bonding strength of the soldered joint. Cu is an element whose ionization coefficient is relatively expensive to Sn, and promotes the thickening-inhibiting effect thereof by coexisting with As, Pb, and Bi. The Cu content is preferably 0 mass% or more and 0.9 mass% or less, more preferably 0.1 mass% or more and 0.8 mass% or less, and further preferably 0.2 mass% or more and 0.7 mass% or less.

The balance of the solder alloy is preferably Sn. The solder alloy may contain inevitable impurities in addition to the above elements. Even when unavoidable impurities are contained, the above effects are not affected. When the In content is too large, the Δ T becomes wide, and therefore, the above-mentioned effects are not impaired if the In content is 1000 mass ppm or less.

< examples of effects of flux and solder paste of the present embodiment >

The flux of the first embodiment, which contains an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), and an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by a mass analysis method using a time-of-flight mass spectrometer (TOF-MS), is excellent in temperature cycle reliability, and suppresses cracking of flux residue that is cured after heating.

The flux of the second embodiment, which contains an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a polyethylene resin or a polypropylene resin, or a polyethylene resin and a polypropylene resin, is also excellent in temperature cycle reliability and suppresses cracking of a flux residue that is cured after heating.

Further, the acrylic resin having a molecular weight within the above range is excellent in compatibility with the activator, and the wettability of the solder is improved by suppressing the activator and the acrylic resin from becoming uneven and affecting the wettability of the solder.

Further, the acrylic resin having a molecular weight within the above range is excellent in compatibility with the rosin resin. Accordingly, the flux of the first embodiment containing the acrylic resin and the rosin-based resin having molecular weights within the above ranges can suppress the rosin-based resin and the acrylic resin from becoming non-uniform and becoming layered.

Thus, the flux of each embodiment is used for a solder paste, and solder wettability is improved. In addition, the formation of a residue layer can be suppressed. Further, the residue is made flexible, and breakage of the residue can be suppressed.

Further, an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 1000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 1000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 1000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) are reduced in softening point due to their small molecular weights. On the other hand, acrylic resins having a number average molecular weight (Mn) of 1000 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), acrylic resins having a weight average molecular weight (Mw) of 1000 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), acrylic resins having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 1000 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and particularly acrylic resins having a molecular weight high, have an effect of increasing the viscosity of a flux and function as a thickener. However, if the ink is thickened due to the change with time, the printability is deteriorated, and the workability is deteriorated. Therefore, as a method for suppressing the thickening, it is preferable to include a hindered phenol-based metal deactivator and a nitrogen compound-based metal deactivator as the metal deactivator within the ranges specified in the present invention.

In addition, it is preferable to use a solder alloy containing As, Sb, Bi and Pb within the above-mentioned range defined in the present invention As a solder paste. Further, the solder alloy containing As, Sb, Bi and Pb within the above-mentioned range defined in the present invention preferably satisfies the above-mentioned formula (1), and more preferably satisfies the formulas (1a) and (1 b). The solder alloy containing As, Sb, Bi and Pb within the above-mentioned range defined in the present invention preferably satisfies the above-mentioned formula (2), and more preferably satisfies the formula (2 a).

Examples

< measurement of molecular weight of acrylic resin >

The molecular weight of the acrylic resin used in the examples was measured by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS).

A time-of-flight mass spectrometer (TOF-MS) is a device that measures a mass number from the time of arrival at a detector, using the fact that the time of flight of ions accelerated by an electric field in a vacuum differs according to a mass-to-charge ratio. The ionization of the components was performed by electrospray ionization (ESI). The ionized components are accelerated by the electric field to reach the detector. The mass number is determined from the flight time of the ion at this time, that is, the time difference between arrival at the detector, and the structural analysis of the target component is performed.

The molecular weight of the acrylic resin used in the examples was measured using a resin manufactured by Nippon electronics Co., Ltd: JMS-T100 LPACuTOF (registered trademark) LC-PLUS, and the number average molecular weight (Mn) and the weight average molecular weight (Mw) were determined, the number average molecular weight (Mn) was determined by the following formula (3), and the mass average molecular weight (Mw) was determined by the following formula (4).

[ mathematical formula 1]

In the formulae (3) and (4), M_iMolecular weight at m/z value corresponding to peak of desired component detected by time of flight mass spectrometer (TOF-MS). In addition, N_iCorresponding to the molecular weight at peak intensity.

The names and molecular weights of the acrylic resins used in examples and comparative examples are shown in table 1 below.

[ Table 1]

Kind of material	Detailed names	Mn	Mw	Mw/Mn
					Acrylic acid oligomer A	Butyl acrylate oligomer	853.86	900.42	1.05
Acrylic acid oligomer B	Butyl acrylate oligomer	982.40	1097.53	1.12
					Acrylic acid oligomer C	Butyl acrylate oligomer	1096.51	1236.01	1.13
Acrylic acid oligomer D	Alkyl acrylate oligomers	1315.06	1507.79	1.15
					Acrylic acid oligomer E	Butyl methacrylate oligomer	757.93	844.62	1.11
Acrylic acid oligomer F	Isotridecyl methacrylate oligomer	1028.82	1138.20	1.11
					Acrylic acid oligomer G	Acrylic acid-butyl acrylate copolymer oligomer	518.79	625.29	1.21
Acrylic acid oligomer H	Acrylic acid-butyl acrylate copolymer oligomer	846.23	925.36	1.09
					Acrylic acid oligomer I	Butyl acrylate-polyethylene co-oligomer	841.10	914.19	1.09
Acrylic acid oligomer J	Butyl acrylate-polyethylene co-oligomer	921.86	1047.26	1.14
					Acrylic acid polymer	Butyl acrylate polymers	＞4000	＞4000	-

The acrylic acid oligomers A to C are all butyl acrylate oligomers. The acrylic oligomer a was a butyl acrylate oligomer having a number average molecular weight (Mn) of 853.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a weight average molecular weight (Mw) of 900.42 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.05, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method were substantially the same.

The acrylic oligomer B was a butyl acrylate oligomer having a number average molecular weight (Mn) of 982.40, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 1097.53, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mn/Mw) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.12, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method were substantially the same.

The acrylic oligomer C was a butyl acrylate oligomer having a number average molecular weight (Mn) of 1096.51, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 1236.01, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mn/Mw) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.13, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method were substantially the same.

Thus, the number average molecular weight (Mn) and the weight average molecular weight (Mw) of the butyl acrylate oligomer used in the examples were determined by the above-mentioned methods and were within the ranges specified in the present invention.

The acrylic oligomer D was an alkyl acrylate oligomer having a number average molecular weight (Mn) of 1315.06, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 1507.79, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.15, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method were substantially the same.

Thus, the number average molecular weight (Mn) and the weight average molecular weight (Mw) of the alkyl acrylate oligomers used in the examples were determined by the above-mentioned methods and were within the ranges specified in the present invention.

The acrylic oligomer E was a butyl methacrylate oligomer having a number average molecular weight (Mn) of 757.93, which was determined by mass analysis using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 844.62, which was determined by mass analysis using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) to the weight average molecular weight (Mw) determined by the above method was 1.11, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method substantially coincided.

Thus, the number average molecular weight (Mn) and the weight average molecular weight (Mw) of the butyl methacrylate oligomer used in the examples, which were determined by the above-mentioned methods, were within the ranges specified in the present invention.

The acrylic oligomer F was an isotridecyl methacrylate oligomer having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) to the weight average molecular weight (Mw) determined by the above method was 1.11, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method substantially coincided.

Thus, the number average molecular weight (Mn) and the weight average molecular weight (Mw) of the isotridecanol methacrylate oligomer used in the examples were determined by the above-mentioned method to be within the ranges specified in the present invention.

Acrylic oligomer G, H is an acrylic acid-butyl acrylate co-oligomer. The acrylic oligomer G was an acrylic acid-butyl acrylate copolymer oligomer having a number average molecular weight (Mn) of 518.79, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 625.29, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.21, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method substantially coincided.

The acrylic acid oligomer H was an acrylic acid-butyl acrylate copolymer oligomer having a number average molecular weight (Mn) of 846.23, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 925.36, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.09, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method substantially coincided.

Thus, the number average molecular weight (Mn) and the weight average molecular weight (Mw) of the butyl acrylate-co-oligomer used in the examples were determined by the above-mentioned methods and were within the ranges specified in the present invention.

Acrylic oligomer I, J is a butyl acrylate-polyethylene co-oligomer. The acrylic oligomer I was a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 841.10, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 914.14, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.09, and it was found that the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method substantially coincided.

The acrylic oligomer J was a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 921.86, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a weight average molecular weight (Mw) of 1047.26, which was determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS). The ratio (Mw/Mn) of the number average molecular weight (Mn) and the weight average molecular weight (Mw) determined by the above method was 1.14, and it was found that the number average molecular weight (Mn) determined by the above method substantially coincided with the weight average molecular weight (Mw).

Thus, the number average molecular weight (Mn) and the weight average molecular weight (Mw) of the butyl acrylate-polyethylene co-oligomer used in the examples were determined by the above-mentioned methods to be within the ranges specified in the present invention.

In addition, the butyl acrylate polymer used in the comparative example was an acrylic polymer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) exceeding 4000.

< evaluation of compatibility in resin composition to be soldered and reliability of temperature cycle >

The solder resin compositions of examples and comparative examples were prepared in the compositions shown in tables 2 to 7 below, and the compatibility and the temperature cycle reliability were examined. The composition ratios in tables 2 to 7 are wt% (by weight) based on 100% of the total amount of the resin composition for soldering.

< evaluation of compatibility >

(1) Verification method

The evaluation of compatibility was carried out by heating and stirring the resin compositions for soldering of examples and comparative examples, and storing them at room temperature for 48 hours. The stored resin composition for soldering was left at 25 ℃ and visually checked.

(2) Criterion for judgment

Good: the materials are not separately soluble.

X: each material is separated into two or more components.

< evaluation of reliability of temperature cycle >

(1) Verification method

The flux of examples and comparative examples was applied to a Cu plate to form a residue on the Cu plate for evaluation of temperature cycle reliability. The residue formed on the Cu plate was subjected to repeated tests for 500 times in which the treatment was carried out at-30 ℃ and +110 ℃ for 30 minutes, respectively, and the presence or absence of cracking in the residue was visually evaluated.

(2) Criterion for judgment

O: no cracks were found in the residue

X: cracks were found to occur in the residue

< comprehensive evaluation >

O: the evaluation of compatibility and the evaluation of temperature cycle reliability are good

X: any or all of the evaluation of compatibility and the evaluation of temperature cycle reliability are

[ Table 2]

[ Table 3]

[ Table 4]

[ Table 5]

[ Table 6]

[ Table 7]

Examples 1X to 10X are examples in which the acrylic resin was changed. In example 1X, the acrylic resin contained 30.0 wt% of the acrylic oligomer A shown in Table 1 within the range specified by the present invention. The acrylic oligomer a was a butyl acrylate oligomer having a number average molecular weight (Mn) of 853.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 1X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 1X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 1X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 1X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 2X, the acrylic resin contained 30.0 wt% of the acrylic oligomer B shown in Table 1 within the range specified by the present invention. The acrylic oligomer B was a butyl acrylate oligomer having a number average molecular weight (Mn) of 982.40 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1097.53 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 2X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 2X, the organic acid contained 1.0 wt% of adipic acid and 2.0 wt% of 12-hydroxystearic acid within the range specified in the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 2X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined in the present invention.

In example 2X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 3X, the acrylic resin contained 30.0 wt% of the acrylic oligomer C shown in Table 1 within the range specified by the present invention. The acrylic oligomer C was a butyl acrylate oligomer having a number average molecular weight (Mn) of 1096.51 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1236.01 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 3X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 3X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 3X, the organic halogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined in the present invention.

In example 3X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 4X, the acrylic resin contained 30.0 wt% of the acrylic oligomer D shown in Table 1 within the range specified by the present invention. The acrylic oligomer D is an alkyl acrylate oligomer having a number average molecular weight (Mn) of 1315.06 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1507.79 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 4X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 4X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 4X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 4X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 5X, the acrylic resin contained 30.0 wt% of the acrylic oligomer E shown in Table 1 within the range specified by the present invention. The acrylic oligomer E was a butyl methacrylate oligomer having a number average molecular weight (Mn) of 757.93 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 844.62 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 5X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 5X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 5X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 5X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 6X, the acrylic resin contained 30.0 wt% of the acrylic oligomer F shown in Table 1 within the range specified by the present invention. The acrylic oligomer F was an isotridecyl methacrylate oligomer having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 6X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 6X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 6X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 6X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 7X, the acrylic resin contained 30.0 wt% of the acrylic oligomer G shown in Table 1 within the range specified by the present invention. The acrylic oligomer G was an acrylic acid-butyl acrylate co-oligomer having a number average molecular weight (Mn) of 518.79 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 7X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 7X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 7X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 7X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 8X, the acrylic resin contained 30.0 wt% of the acrylic oligomer H shown in Table 1 within the range specified by the present invention. The acrylic oligomer H was an acrylic acid-butyl acrylate co-oligomer having a number average molecular weight (Mn) of 846.23 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 925.36 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 8X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 8X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 8X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 8X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 9X, the acrylic resin contained 30.0 wt% of the acrylic oligomer I shown in Table 1 within the range specified by the present invention. The acrylic oligomer I is a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 841.10 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 9X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 9X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 9X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 9X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 10X, the acrylic resin contained 30.0 wt% of the acrylic oligomer J shown in Table 1 within the range specified by the present invention. The acrylic oligomer J was a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 921.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1047.26 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 10X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 10X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 10X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 10X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

Example 11X is an example containing a plurality of acrylic resins. In example 11, 3.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as an acrylic resin within the ranges specified in the present invention.

In example 11X, 3.0 wt% of a butyl acrylate oligomer (acrylic oligomer B) having a number average molecular weight (Mn) of 982.40 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1097.53 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 11X, 3.0 wt% of a butyl acrylate oligomer (acrylic oligomer C) having a number average molecular weight (Mn) of 1096.51 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1236.01 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 11X, the acrylic resin contained 3.0 wt% of an alkyl acrylate oligomer (acrylic oligomer D) having a number average molecular weight (Mn) of 1315.06 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1507.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11X, 3.0 wt% of a butyl methacrylate oligomer (acrylic oligomer E) having a number average molecular weight (Mn) of 757.93 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 844.62 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 11X, as the acrylic resin, 3.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 11X, 3.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 11X, 3.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic acid oligomer H) having a number average molecular weight (Mn) of 846.23 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 925.36 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 11X, 3.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as an acrylic resin within the ranges defined in the present invention.

In example 11X, 3.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer J) having a number average molecular weight (Mn) of 921.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1047.26 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

The total amount of each acrylic resin is within the range specified in the present invention.

In example 11X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 11X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 11X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 11X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 12X, as the acrylic resin, 60.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 12X, 30.0 wt% of an acrylic-modified hydrogenated rosin and 5.0 wt% of a rosin ester were contained as rosin-based resins. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 12X, the organic acid contained 3.0% by weight of 12-hydroxystearic acid within the range defined by the present invention. In example 12X, the organic halogen compound contained triallyl isocyanurate 6 bromide in an amount of 2.0 wt% within the range defined in the present invention.

In example 12X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 13X, as the acrylic resin, 50.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 13X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 10.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 13X, the organic acid contained 3.0% by weight of 12-hydroxystearic acid within the range defined by the present invention. In example 13X, the organic halogen compound contained triallyl isocyanurate 6 bromide in an amount of 2.0 wt% within the range defined in the present invention.

In example 13X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 14X, the acrylic resin contained 45.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, within the ranges specified in the present invention.

In example 14X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 15.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 14X, the organic acid contained 3.0% by weight of 12-hydroxystearic acid within the range defined by the present invention. In example 14X, the organic halogen compound contained triallyl isocyanurate 6 bromide in an amount of 2.0 wt% within the range defined in the present invention.

In example 14X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 15X, as the acrylic resin, 20.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 15X, 30.0 wt% of an acrylic-modified hydrogenated rosin and 45.0 wt% of a hydrogenated rosin were contained as rosin-based resins. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 15X, the organic acid contained 3.0% by weight of 12-hydroxystearic acid within the range defined by the present invention. In example 15X, the organic halogen compound contained triallyl isocyanurate 6 bromide in an amount of 2.0 wt% within the range defined in the present invention.

In example 15X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 16X, as the acrylic resin, 30.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 16X, the rosin-based resin contained 10.0 wt% of an acrylic-modified hydrogenated rosin, 10.0 wt% of a maleic-modified hydrogenated rosin, 10.0 wt% of a phenol-modified rosin, 10.0 wt% of a disproportionated rosin, 10.0 wt% of a hydrogenated rosin, 10.0 wt% of a polymerized rosin, and 5.0 wt% of a rosin ester. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 16X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 16X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 16X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 17X, as the acrylic resin, 30.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 17X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 35.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 17X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 18X, as the acrylic resin, 30.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 18X, 30.0 wt% of an acrylic-modified hydrogenated rosin and 35.0 wt% of a hydrogenated rosin were contained as rosin-based resins. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 18X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 18X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 18X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 19X, as the acrylic resin, 30.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 19X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 20.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention. In example 19, the other resin contained 10.0 wt% of the polyethylene resin within the range specified by the present invention.

In example 19X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 19X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 19X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 20X, as the acrylic resin, 30.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 20X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 20.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention. In example 20, the acid-modified polyethylene resin was contained in an amount of 10.0 wt% in the range defined in the present invention as the other resin.

In example 20X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 20X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 20X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 21X, as the acrylic resin, 30.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 21X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 20.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention. In example 21, the other resin contained 10.0 wt% of the polyolefin having terminal OH groups within the range defined by the present invention.

In example 21X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 21X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 21X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 22X, as the acrylic resin, 20.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 22X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 5.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention. In example 22, as the other resins, 10.0 wt% of the polyethylene resin was contained within the range defined by the present invention, 15.0 wt% of the acid-modified polyethylene resin was contained within the range defined by the present invention, and 10.0 wt% of the terminal OH group-containing polyolefin was contained within the range defined by the present invention. The total amount of other resins is also within the range specified in the present invention.

In example 22X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 22X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 22X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 23X, the acrylic resin contained 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, within the ranges specified in the present invention.

In example 23X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 23X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 23X, the organic acid contained glutaric acid in an amount of 1.0 wt% and 12-hydroxystearic acid in an amount of 2.0 wt% within the range defined by the present invention. The total amount of glutaric acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 23X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 23X, the materials were compatible without being separated, and sufficient effects were obtained in compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 24X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 24X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 24X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 24X, 1.0 wt% of dodecanedioic acid and 2.0 wt% of 12-hydroxystearic acid were contained as the organic acid within the ranges defined by the present invention. The total amount of dodecanedioic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 24X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 24X, the materials were compatible without being separated, and sufficient effects were obtained in compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 25X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 25X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 25X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 25X, the organic acid contained 2.0 wt% of adipic acid in the range defined by the present invention and 1.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 25X, the organohalogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined by the present invention.

In example 25X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 26X, as the acrylic resin, 7.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 26X, as the acrylic resin, 7.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 26X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 26.0 wt% of a hydrogenated rosin, and 14.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 26X, the organic acid contained glutaric acid in an amount of 1.0 wt%, adipic acid in an amount of 1.0 wt%, dodecanedioic acid in an amount of 1.0 wt%, hydrogenated dimer acid in an amount of 1.0 wt%, and 12-hydroxystearic acid in an amount of 7.0 wt% within the range specified by the present invention. The total amount of each organic acid is also within the range specified in the present invention. In example 26X, 5.0 wt% of triallyl isocyanurate 6 bromide was contained as the organic halogen compound within the range defined by the present invention.

In example 26X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 27X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 27X, as the acrylic resin, 5.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 27X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention. In example 27X, the other resin contained 9.0 wt% of a polyethylene resin within the range defined in the present invention.

In example 27X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 27X, the amine contained 1.0 wt% of 2-phenylimidazole within the range defined by the present invention. In example 27X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 27X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 28X, as the acrylic resin, 5.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 28X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene cooligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 28X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 28X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. Further, in example 28X, the amine contained 2-undecylimidazole in an amount of 10.0 wt% within the range specified by the present invention. In example 28X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound.

In example 28X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 29X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 29X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene cooligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 29X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 20.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 29X, the organic acid contained 1.0% by weight of adipic acid in the range defined by the present invention and 2.0% by weight of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 29X, the organic halogen compound contained trans-2, 3-dibromo-2-butene-1, 4-diol in an amount of 2.0 wt% within the range defined by the present invention.

In example 29X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 30X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 30X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 30X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 22.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 30X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 30X, the organic halogen compound contained triallyl isocyanurate 6 bromide in an amount of 10.0 wt% within the range defined in the present invention.

In example 30X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 31X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 31X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 31X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 31X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 31X, the organic halogen compound contained 2.0 wt% of 2,2,2, -tribromoethanol within the range defined by the present invention.

In example 31X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 32X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 32X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 32X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 31.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 32X, 1.0 wt% of adipic acid was contained within the range defined by the present invention, and 2.0 wt% of 12-hydroxystearic acid was contained within the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 32X, 1.0 wt% of ethylamine/HBr was contained as the amine hydrohalide within the range specified by the present invention.

In example 32X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 33X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 33X, the acrylic resin contained 15.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 33X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 33X, the organic acid contained 1.0 wt% of adipic acid in the range defined by the present invention and 2.0 wt% of 12-hydroxystearic acid in the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 33X, the amine hydrohalide contained 2.5% by weight of N, N-diethylaniline HBr within the range specified by the present invention.

In example 33X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 34X, as the acrylic resin, 30.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 34X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 20.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 34X, 1.0% by weight of adipic acid was contained within the range defined by the present invention, and 2.0% by weight of 12-hydroxystearic acid was contained within the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 34X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound. In example 34, isodecyl acid phosphate was contained in an amount of 10.0 wt% in the range defined by the present invention as the organophosphorus compound.

In example 34X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 35X, as the acrylic resin, 30.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 35X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 25.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention.

In example 35X, 1.0 wt% of adipic acid was contained within the range defined by the present invention, and 2.0 wt% of 12-hydroxystearic acid was contained within the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In example 35X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound. In example 35X, 5.0 wt% of silicone oil was contained as the silicone within the range specified by the present invention.

In example 35X, the materials were compatible without being separated, and a sufficient effect was obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 36X, as the acrylic resin, 15.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 36X, as the acrylic resin, 10.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention. The total amount of each acrylic resin is also within the range specified in the present invention.

In example 36X, 30.0 wt% of an acrylic-modified hydrogenated rosin, 30.0 wt% of a hydrogenated rosin, and 5.0 wt% of a rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. The ratio of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is also within the range specified in the present invention. In example 36X, the other resin contained 5.0 wt% of a polyethylene resin within the range defined by the present invention.

In example 36X, the organic acid contained 1.0 wt% of adipic acid within the range defined by the present invention. In example 36X, the amine contained 1.0 wt% of 2-phenylimidazole within the range defined by the present invention. In example 36X, the content of 2, 3-dibromo-1, 4-butanediol was 2.0 wt% in the range defined in the present invention as the organic halogen compound. The amine hydrohalide salt contained ethylamine HBr in an amount of 0.5 wt% and N, N-diethylaniline HBr in an amount of 0.5 wt% within the range defined by the present invention. The total amount of the respective amine hydrohalide salts is also within the range specified in the present invention.

In example 36X, the materials were compatible without being separated, and sufficient effects were obtained in compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In contrast, in comparative example 1X, as the acrylic resin, an acrylic oligomer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, which were determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), was not included, and 30.0 wt% of a butyl acrylate polymer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) exceeding 4000 was included as the acrylic polymer.

In comparative example 1X, 30.0 wt% of acrylic-modified hydrogenated rosin, 30.0 wt% of hydrogenated rosin, and 5.0 wt% of rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is within the range specified in the present invention. In comparative example 1X, the organic acid contained 1.0 wt% of adipic acid and 2.0 wt% of 12-hydroxystearic acid within the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In comparative example 1X, the organic halogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined in the present invention.

In comparative example 1X, each material was separated into two or more components, and no effect was obtained on compatibility. In addition, the residue was not sufficiently solidified, and the reliability of the temperature cycle could not be evaluated.

In comparative example 2X, the acrylic resin contained no acrylic oligomer or acrylic polymer. In comparative example 2X, 30.0 wt% of acrylic-modified hydrogenated rosin, 60.0 wt% of hydrogenated rosin, and 5.0 wt% of rosin ester were contained as the rosin-based resin. The total amount of the rosin-based resin is out of the range specified in the present invention. In comparative example 2X, 1.0 wt% of adipic acid was contained within the range defined by the present invention, and 2.0 wt% of 12-hydroxystearic acid was contained within the range defined by the present invention. The total amount of adipic acid and 12-hydroxystearic acid is also within the range specified in the present invention. In comparative example 2X, the organic halogen compound contained 2.0 wt% of 2, 3-dibromo-1, 4-butanediol within the range defined in the present invention.

In comparative example 2X, the residue was solidified, but cracks were observed in the residue, and no effect was obtained in terms of reliability of temperature cycle. Further, since acrylic resin was not contained, compatibility was not evaluated.

From the above, a resin composition for soldering containing an acrylic resin having a number average molecular weight (Mn) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), an acrylic resin having a number average molecular weight (Mn) and a weight average molecular weight (Mw) of 500 or more and less than 2000 obtained by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a rosin resin, wherein the rosin resin and the acrylic resin are not uniform and are prevented from being layered.

Further, the resin composition for soldering containing the acrylic resin and the rosin resin having the molecular weights within the above ranges is excellent in heat cycle reliability, and can suppress cracking of the resin composition for soldering which is cured after heating.

Thus, the solder resin composition of the present embodiment is suitable for a flux for soldering, and can be used in a solder composition such as a resin core solder or a flux coating solder, and can suppress formation of a residue layer. In addition, the residue is made flexible, and the residue can be prevented from cracking.

These effects are not inhibited by the inclusion of other resins, other organic acids as activators, amine hydrohalides, and organic halogen compounds within the ranges specified in the present invention. Further, even if the solvent or other additives are contained within the range defined in the present invention, there is no problem.

< evaluation of solder wettability, compatibility, and temperature cycle reliability in flux >

The fluxes of the first embodiment were prepared in the compositions shown in tables 8 to 13 below, and the solder wettability, compatibility, and temperature cycle reliability were verified. Further, with respect to the flux of the second embodiment, fluxes of examples and comparative examples were prepared with compositions shown in tables 14 to 19 below, and solder wettability, compatibility, and temperature cycle reliability were verified. The composition ratios in tables 8 to 13 and 14 to 19 are wt% based on 100 of the total amount of the flux.

< evaluation of solder wettability >

(1) Verification method

The solder wettability was evaluated by applying the flux of each example and each comparative example to a Cu plate, mounting a solder ball on the flux applied to the Cu plate, reflow-soldering the solder ball, and then measuring the solder wet spread diameter. In the reflow step, a reflow apparatus having a peak temperature of 250 ℃ was used, and the temperature was increased from 35 ℃ to 250 ℃ in units of 1 ℃ every 1 second, and after reaching 250 ℃, heat treatment was performed for 30 seconds. The solder ball had a composition described as Sn-3Ag-0.5Cu, and contained 3.0 mass% of Ag and 0.5 mass% of Cu, with the balance being Sn (96.5 mass%). The diameter of the solder ball is 0.3 mm.

(2) Criterion for judgment

O: the solder has an expanded diameter of 510 μm or more.

X: the solder has an expanded diameter of less than 510 μm.

< evaluation of compatibility >

(1) Verification method

The flux of examples and comparative examples was heated and stirred to adjust the compatibility, and stored at room temperature for 48 hours. The stored flux was left at 25 ℃ and visually checked.

(2) Criterion for judgment

Good: the materials are not separately soluble.

X: each material is separated into two or more components.

< evaluation of reliability of temperature cycle >

(1) Verification method

(2) Criterion for judgment

O: no cracks were found in the residue

X: cracks were found to occur in the residue

< comprehensive evaluation >

O: the solder wettability evaluation, compatibility evaluation and temperature cycle reliability evaluation are good

X: any or all of solder wettability evaluation, compatibility evaluation, and temperature cycle reliability evaluation are expressed in

[ Table 8]

[ Table 9]

[ Table 10]

[ Table 11]

[ Table 12]

[ Table 13]

Examples 1Y to 10Y are examples in which an acrylic resin was changed in the flux of the first embodiment. In example 1Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer A shown in Table 1 within the range specified by the present invention. The acrylic oligomer a was a butyl acrylate oligomer having a number average molecular weight (Mn) of 853.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 1Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio (weight ratio) of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one rosin resin or the total weight of two or more rosin resins is within the range specified in the present invention.

In example 1Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the range of the content of other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 1Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 1Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 1Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 1Y, the spreading diameter of the solder satisfies the above criteria, and a sufficient effect is obtained on the wettability of the solder. In addition, the materials are compatible without being separated, and a sufficient effect is obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 2Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer B shown in Table 1 within the range specified in the present invention. The acrylic oligomer B was a butyl acrylate oligomer having a number average molecular weight (Mn) of 982.40 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1097.53 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 2Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention, similarly to example 1Y. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 2Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 2Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined in the present invention. In example 2Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 2Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 2Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 3Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer C shown in Table 1 within the range specified by the present invention. The acrylic oligomer C was a butyl acrylate oligomer having a number average molecular weight (Mn) of 1096.51 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1236.01 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 3Y, as in example 1Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 3Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 3Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 3Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 3Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 3Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 4Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer D shown in Table 1 within the range specified by the present invention. The acrylic oligomer D is an alkyl acrylate oligomer having a number average molecular weight (Mn) of 1315.06 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1507.79 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 4Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention, similarly to example 1Y. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 4Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 4Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 4Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 4Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 4Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 5Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer E shown in Table 1 within the range specified by the present invention. The acrylic oligomer E was a butyl methacrylate oligomer having a number average molecular weight (Mn) of 757.93 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 844.62 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 5Y, as in example 1Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 5Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 5Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 5Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 5Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 5Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 6Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer F shown in Table 1 within the range specified by the present invention. The acrylic oligomer F was an isotridecyl methacrylate oligomer having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 6Y, as in example 1Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 6Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 6Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 6Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 6Y, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in the range defined in the present invention as a metal deactivator, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in the range defined in the present invention as a nitrogen compound-based metal deactivator, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 6Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 7Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer G shown in Table 1 within the range specified by the present invention. The acrylic oligomer G was an acrylic acid-butyl acrylate co-oligomer having a number average molecular weight (Mn) of 518.79 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention

Hereinafter, in example 7Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention, similarly to example 1Y. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 7Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 7Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 7Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 7Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 7Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 8Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer H shown in Table 1 within the range specified by the present invention. The acrylic oligomer H was an acrylic acid-butyl acrylate co-oligomer having a number average molecular weight (Mn) of 846.23 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 925.36 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 8Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention, similarly to example 1Y. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 8Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 8Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 8Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 8Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 8Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 9Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer I shown in Table 1 within the range specified by the present invention. The acrylic oligomer I is a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 841.10 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 9Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention, similarly to example 1Y. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 9Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 9Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 9Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 9Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 9Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 10Y, the acrylic resin contained 20.0 wt% of the acrylic oligomer J shown in Table 1 within the range specified by the present invention. The acrylic oligomer J was a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 921.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1047.26 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 10Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention, similarly to example 1Y. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 10Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 10Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 10Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 10Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 10Y, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 11Y is an example containing a plurality of acrylic resins. In example 11Y, as the acrylic resin, 2.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of a butyl acrylate oligomer (acrylic oligomer B) having a number average molecular weight (Mn) of 982.40 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1097.53 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of a butyl acrylate oligomer (acrylic oligomer C) having a number average molecular weight (Mn) of 1096.51 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1236.01 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of an alkyl acrylate oligomer (acrylic oligomer D) having a number average molecular weight (Mn) of 1315.06 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1507.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of a butyl methacrylate oligomer (acrylic oligomer E) having a number average molecular weight (Mn) of 757.93 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 844.62 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer H) having a number average molecular weight (Mn) of 846.23 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 925.36 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

In example 11Y, the acrylic resin contained 2.0 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer J) having a number average molecular weight (Mn) of 921.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1047.26 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention.

Hereinafter, in example 11Y, as in example 1Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 11Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 11Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 11Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 11Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 11Y in which an acrylic resin was added in combination, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 12Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 12Y, the acrylic resin contained 15.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 12Y, no rosin-based resin was contained.

In example 12Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 2.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 12Y, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention, 1.0 wt% of ethylamine HBr as an amine hydrohalide was contained as an active agent within the range defined by the present invention, and 1.0 wt% of N, N-diethylaniline HBr as an amine hydrohalide was contained as an active agent within the range defined by the present invention. The total content of the two or more amine hydrohalide salts is within the range specified in the present invention.

In example 12Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 12Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 12Y, which contained no rosin resin and contained amine hydrohalide as an activator in addition to dimer acid, other organic acid, and amine, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 13Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 13Y, the acrylic resin contained 15.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 13Y, no rosin-based resin was contained.

In example 13Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 3.5 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 13Y, 1.0 wt% of 2-phenylimidazole as an amine was contained as the activator in the range defined by the present invention, 1.0 wt% of trans-2, 3-dibromo-2-butene-1, 4-diol as an organic halogen compound was contained as the activator in the range defined by the present invention, and 1.5 wt% of triallyl isocyanurate 6 bromide as an organic halogen compound was contained as the activator in the range defined by the present invention. The total content of the two or more organic halogen compounds is within the range specified in the present invention.

In example 13Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 13Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 38.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 13Y, which contained no rosin resin and an organic halogen compound as an active agent in addition to dimer acid, other organic acid, and amine, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 14Y, as the acrylic resin, 5.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 14Y, the acrylic resin contained 5.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 14Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 14Y, 20.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 14Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 14Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 14Y, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in the range defined in the present invention as a metal deactivator, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in the range defined in the present invention as a nitrogen compound-based metal deactivator, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 14Y in which the content of the acrylic resin, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins was reduced to the lower limit within the range specified by the present invention, the solder wettability was sufficiently improved. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 15Y, as the acrylic resin, 7.5 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 15Y, as the acrylic resin, 5.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 15Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 15Y, 17.5 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 15Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 15Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 15Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 15Y in which the content of the acrylic resin, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins was reduced to a lower limit within the more preferable range specified in the present invention, sufficient effects were also obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 16Y, as the acrylic resin, 10.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 16Y, as the acrylic resin, 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 16Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 16Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 16Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 16Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 16Y, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in the range defined in the present invention as a metal deactivator, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in the range defined in the present invention as a nitrogen compound-based metal deactivator, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 16Y in which the content of the acrylic resin, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins, and the total weight of two or more rosin resins were increased to exceed the lower limit of the more preferable range specified in the present invention, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 17Y, the acrylic resin contained 13.5 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 17Y, as the acrylic resin, 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 17Y, the rosin-based resin contained 11.5 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 17Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 17Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 17Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 17Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 17Y in which the content of the acrylic resin was increased, the content of the rosin resin was decreased, and the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins was the lower limit of the most preferable range specified in the present invention, sufficient effects were obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 18Y, the acrylic resin contained 15.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 18Y, as the acrylic resin, 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 18Y, the rosin-based resin contained 10.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 18Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 18Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 18Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 18Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 18Y in which the content of the acrylic resin was increased, the content of the rosin resin was decreased, the weight of one or more acrylic resins, and the ratio of the total weight of two or more acrylic resins to the weight of one or more rosin resins exceeded the lower limit of the most preferable range specified in the present invention, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 19Y, 17.5 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 19Y, as the acrylic resin, 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 19Y, the rosin-based resin contained 7.5 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 19Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 19Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 19Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 19Y, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in the range defined in the present invention as a metal deactivator, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in the range defined in the present invention as a nitrogen compound-based metal deactivator, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 19Y in which the content of the acrylic resin was increased, the content of the rosin resin was decreased, the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins was further increased, and the lower limit of the most preferable range defined in the present invention was exceeded, a sufficient effect was obtained on the solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 20Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 20Y, the acrylic resin contained 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 20Y, the rosin-based resin contained 5.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 20Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 20Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 20Y, 2.0 wt% of hydrogenated castor oil as an ester-based thixotropic agent was contained within the range defined by the present invention as a thixotropic agent, and 2.0 wt% of a bisamide-based thixotropic agent as an amide-based thixotropic agent was contained within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 20Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 20Y in which the content of the acrylic resin was increased, the content of the rosin resin was decreased, and the ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins was set to the upper limit within the most preferable range specified in the present invention, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 21Y is an example containing a plurality of rosin-based resins. In example 21, as the acrylic resin, 20.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 21Y, as the rosin resin, 3.0 wt% of the acrylic-modified hydrogenated rosin was contained within the range defined by the present invention, 2.0 wt% of the maleic-modified hydrogenated rosin was contained within the range defined by the present invention, 2.0 wt% of the phenol-modified rosin was contained within the range defined by the present invention, 2.0 wt% of the disproportionated rosin was contained within the range defined by the present invention, 2.0 wt% of the hydrogenated rosin was contained within the range defined by the present invention, 2.0 wt% of the polymerized rosin was contained within the range defined by the present invention, and 2.0 wt% of the rosin ester was contained within the range defined by the present invention.

The total content of the respective rosin-based resins is within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 21Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 21Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 21Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 21Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 21Y in which a rosin-based resin was compounded, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 22Y is an example containing a resin other than the acrylic resin and the rosin resin. In example 22Y, the acrylic resin contained 16.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 22Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention. In example 22, the other resin contained 4.0 wt% of the polyolefin resin within the range specified by the present invention.

In example 22Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 22Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 22Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 22Y, the hindered phenol-based metal deactivator bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] was contained in an amount of 2.9% by weight within the range defined by the present invention as the metal deactivator, and the nitrogen compound-based metal deactivator N- (2H-1,2, 4-triazol-5-yl) salicylamide was contained in an amount of 0.1% by weight within the range defined by the present invention as the metal deactivator, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 22Y containing another resin, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 23Y is an example containing a variety of other resins. In example 23Y, 12.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as an acrylic resin within the ranges specified in the present invention.

In example 23Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention. In example 23Y, the other resin contained 4.0 wt% of the polyolefin resin within the range defined by the present invention, and contained 4.0 wt% of the acid-modified polyolefin resin within the range defined by the present invention. The total content of the other resins is within the range specified in the present invention.

In example 23Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 23Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 23Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 23Y, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in the range defined in the present invention as a metal deactivator, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in the range defined in the present invention as a nitrogen compound-based metal deactivator, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 23Y in which another resin was added in combination, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 24Y is an example in which the kind of other organic acid is changed. In example 24Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 24Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 24Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of dodecanedioic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and dodecanedioic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 24Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 24Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 24Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 24Y in which the kind of other organic acid was changed, sufficient effects were obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 25Y is an example without other organic acids. In example 25Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 25Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 25Y, 17.0 wt% of dimer acid was contained as an active agent in the range specified by the present invention, and no other organic acid was contained.

In example 25Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 25Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 25Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 25Y containing no other organic acid, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 26Y is an example containing no organic acid. In example 26Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 26Y, as the acrylic resin, 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 26Y, the rosin-based resin contained 16.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 26Y, dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, and other organic acids were not contained.

In example 26Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 26Y, trans-2, 3-dibromo-2-butene-1, 4-diol as an organic halogen compound was contained by 2.0 wt% as an active agent within the range defined by the present invention, and triallyl isocyanurate 6 bromide as an organic halogen compound was contained by 3.0 wt% within the range defined by the present invention. The total content of the two or more organic halogen compounds is within the range specified in the present invention. In example 26, ethylamine HBr as an amine hydrohalide salt was contained in an amount of 0.5 wt% within the range defined by the present invention, and N, N-diethylaniline HBr as an amine hydrohalide salt was contained in an amount of 0.5 wt% within the range defined by the present invention. The total content of the two or more amine hydrohalide salts is within the range specified in the present invention.

In example 26Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 26Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 26Y containing no dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, or other organic acid, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 27Y to example 35Y varied the combination of active agents. In example 27Y, as the acrylic resin, 20.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 27Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 27Y, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 27Y, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range specified by the present invention. In example 27Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 27Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained diethylene glycol hexyl ether in an amount of 43.0 wt% within the range specified in the present invention.

In example 27Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 28Y, as the acrylic resin, 20.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 28Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 28Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of glutaric acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 28Y, 2.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 28Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 28Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained diethylene glycol hexyl ether in an amount of 43.0 wt% within the range specified in the present invention.

In example 28Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 29Y, as the acrylic resin, 20.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 29Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 29Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of glutaric acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 29Y, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range defined by the present invention. In example 29Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 29Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained diethylene glycol hexyl ether in an amount of 43.0 wt% within the range specified in the present invention.

In example 29Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 30Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 30Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 30Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 1.5 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 1.5 wt% of glutaric acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and glutaric acid is within the range of the content of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 30Y, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range specified by the present invention. In example 30Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 30Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained diethylene glycol hexyl ether in an amount of 43.0 wt% within the range specified in the present invention.

In example 30Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 31Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 31Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 31Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 2.5 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 2.5 wt% of glutaric acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and glutaric acid is within the range of the content of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 31Y, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range defined by the present invention. In example 31Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 31Y, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 41.0 wt% of diethylene glycol hexyl ether within the range specified in the present invention.

In example 31Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 32Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 32Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 32Y, 11.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 32Y, no amine was contained. In example 32Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 32Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 32Y in which the combination of the active agents was changed and no amine was contained, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 33Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 33Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 33Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 33Y, the active agent contained 2-phenyl-4-methylimidazole as an amine in an amount of 1.0 wt% in the range defined by the present invention. In example 33Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 33Y, the hindered phenol-based metal deactivator bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] was contained in an amount of 2.9 wt% within the range defined in the present invention as the metal deactivator, and the nitrogen compound-based metal deactivator N- (2H-1,2, 4-triazol-5-yl) salicylamide was contained in an amount of 0.1 wt% within the range defined in the present invention as the metal deactivator, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 33Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 34Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 34Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 34Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 2.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 1.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 34Y, 4.0 wt% of 2-phenylimidazole as an amine was contained as an activator in the range defined by the present invention, and 4.0 wt% of 2-phenyl-4-methylimidazole as an amine was contained in the range defined by the present invention. The total content of two or more amines is within the range specified in the present invention. In example 34Y, the ester-based thixotropic agent contained hydrogenated castor oil in an amount of 2.0 wt% in the range defined by the present invention as the thixotropic agent.

In example 34Y, as the metal deactivator, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.0 wt% within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 34Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 35Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 35Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 35Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 35Y, 2.0 wt% of 2-phenylimidazole as an amine was contained as the activator in the range defined by the present invention, and 2.0 wt% of 2, 3-dibromo-1, 4-butanediol as the organic halogen compound was contained as the activator in the range defined by the present invention. In example 35Y, the ester-based thixotropic agent contained hydrogenated castor oil in an amount of 2.0 wt% in the range defined by the present invention as the thixotropic agent.

In example 35Y, as the metal deactivator, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.0 wt% within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 35Y in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 36Y is an example in which the amount of the thixotropic agent was changed, and in example 36Y, 20.0 wt% of isotridecyl methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 36Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 36Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 36Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 36Y, the ester-based thixotropic agent contained hydrogenated castor oil in an amount of 7.0 wt% in the range defined by the present invention as the thixotropic agent.

In example 36Y, the metal deactivator was not contained, and the rest of the solvent contained diethylene glycol hexyl ether in an amount of 40.0 wt% within the range specified by the present invention.

In example 36Y in which the content of the thixotropic agent was increased and the metal deactivator was not contained, sufficient effects were obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 37Y is an example in which the kinds of the thixotropic agent and the solvent were changed. In example 37Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin.

In example 37Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 37Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 37Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 37Y, the amide-based thixotropic agent contained in an amount of 3.0 wt% within the range defined by the present invention as the thixotropic agent.

In example 37Y, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 41.0 wt% of diethylene glycol ethylhexyl ether within the range specified in the present invention.

In example 37Y in which the kinds of the thixotropic agent and the solvent were changed, sufficient effects were obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 38Y is an example in which the kinds of the thixotropic agent, the metal deactivator, and the solvent were changed. In example 38Y, 20.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 38Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In example 38Y, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 38Y, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 38Y, the amide-based thixotropic agent contained in the amount of 3.0 wt% in the range defined by the present invention as the thixotropic agent.

In example 38Y, N' -hexamethylenebis [3- [3, 5-di-tert-butyl-4-hydroxyphenyl ] propionamide as a hindered phenol-based metal deactivator was contained in an amount of 2.9% by weight as a metal deactivator in the range defined in the present invention, N- [2H-1,2, 4-triazol-5-yl ] salicylamide as a nitrogen compound-based metal deactivator was contained in an amount of 0.1% by weight as a nitrogen compound-based metal deactivator in the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 41.0 wt% of diethylene glycol ethylhexyl ether within the range specified in the present invention.

In example 38Y in which the kinds of the thixotropic agent, the metal deactivator, and the solvent were changed, a sufficient effect was also obtained on the solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In contrast, in comparative example 1Y, 25.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In comparative example 1Y, the acrylic resin contained 20.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In comparative example 1Y, the resin composition contained 4.0 wt% of the polyolefin resin and 4.0 wt% of the acid-modified polyolefin resin in the ranges specified in the present invention as the other resins, except for the rosin-based resin. The content of two or more other resins is within the range specified in the present invention.

In comparative example 1Y, the ester-based thixotropic agent contained hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent contained bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention as thixotropic agents without containing an active agent. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In comparative example 1Y, the hindered phenol-based metal deactivator bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] was contained in an amount of 2.9 wt% within the range defined in the present invention, the nitrogen compound-based metal deactivator N- (2H-1,2, 4-triazol-5-yl) salicylamide was contained in an amount of 0.1 wt% within the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In comparative example 1Y containing no active agent, effects were obtained in terms of compatibility and reliability of temperature cycle, but no effect was obtained on solder wettability.

In comparative example 2Y, as the acrylic resin, an acrylic oligomer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, which were determined by mass analysis using a time-of-flight mass spectrometer (TOF-MS), was not contained, and a butyl acrylate polymer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) exceeding 4000 was contained as an acrylic polymer in an amount of 20.0 wt%.

In comparative example 2Y, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. The ratio of the weight of one or more acrylic resins to the weight of one or more rosin resins is within the range specified in the present invention.

In comparative example 2Y, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In comparative example 2Y, the activator contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined in the present invention. In comparative example 2Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In comparative example 2Y, the hindered phenol-based metal deactivator bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] was contained in an amount of 2.9 wt% within the range defined in the present invention, and the nitrogen compound-based metal deactivator N- (2H-1,2, 4-triazol-5-yl) salicylamide was contained in an amount of 0.1 wt% within the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In comparative example 2Y, an acrylic oligomer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, which were measured by a mass spectrometry method using a time-of-flight mass spectrometer (TOF-MS), was not included, and an acrylic polymer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) exceeding 4000 was included, and an effect was obtained on solder wettability, but each material was separated into two or more components, and no effect was obtained in terms of compatibility. In addition, the residue was not sufficiently solidified, and the reliability of the temperature cycle could not be evaluated.

In comparative example 3Y, the acrylic resin contained neither an acrylic oligomer nor an acrylic polymer. In comparative example 3Y, the rosin-based resin contained 35.0 wt% or more of the acrylic-modified hydrogenated rosin in an amount exceeding the range defined in the present invention.

In comparative example 3Y, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In comparative example 3Y, the activator contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined in the present invention. In comparative example 3Y, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In comparative example 3Y, the hindered phenol-based metal deactivator bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] was contained in an amount of 2.9 wt% within the range defined in the present invention, and the nitrogen compound-based metal deactivator N- (2H-1,2, 4-triazol-5-yl) salicylamide was contained in an amount of 0.1 wt% within the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In comparative example 3Y containing no acrylic resin, the solder wettability was improved. However, although the residue was solidified, cracks were observed in the residue, and no effect was obtained in terms of reliability of temperature cycle. Further, since acrylic resin was not contained, compatibility was not evaluated.

[ Table 14]

[ Table 15]

[ Table 16]

[ Table 17]

[ Table 18]

[ Table 19]

Examples 1Z to 10Z are examples in which an acrylic resin is changed in the flux of the second embodiment containing a polyethylene-based resin or a polypropylene-based resin, or a polyethylene-based resin and a polypropylene-based resin.

In example 1Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer a shown in table 1 within the range specified by the present invention. The acrylic oligomer a was a butyl acrylate oligomer having a number average molecular weight (Mn) of 853.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin resin within the range specified by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene resin (pe.pp resin) within the range specified by the present invention. The ratio (weight ratio) of the weight of one acrylic resin or the total weight of two or more acrylic resins to the weight of one polyethylene-polypropylene resin or the total weight of two or more polyethylene-polypropylene resins is within the range specified in the present invention.

In example 1Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 1Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 1Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 1Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 1Z, the spreading diameter of the solder satisfies the above criteria, and a sufficient effect is obtained on the wettability of the solder. In addition, the materials are compatible without being separated, and a sufficient effect is obtained in terms of compatibility. Further, no crack was found in the residue, and a sufficient effect was obtained in terms of reliability of the temperature cycle.

In example 2Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer B shown in table 1 within the range specified by the present invention. The acrylic oligomer B was a butyl acrylate oligomer having a number average molecular weight (Mn) of 982.40 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1097.53 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 2Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 2Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 2Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 2Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 2Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 2Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 3Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer C shown in table 1 within the range specified by the present invention. The acrylic oligomer C was a butyl acrylate oligomer having a number average molecular weight (Mn) of 1096.51 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1236.01 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 3Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 3Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 3Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 3Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 3Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 3Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 4Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer D shown in table 1 within the range specified by the present invention. The acrylic oligomer D is an alkyl acrylate oligomer having a number average molecular weight (Mn) of 1315.06 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1507.79 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 4Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 4Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 4Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 4Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 4Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 4Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 5Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer E shown in Table 1 within the range specified by the present invention. The acrylic oligomer E was a butyl methacrylate oligomer having a number average molecular weight (Mn) of 757.93 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 844.62 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 5Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 5Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 5Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 5Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 5Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 5Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 6Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer F shown in table 1 within the range specified by the present invention. The acrylic oligomer F was an isotridecyl methacrylate oligomer having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 6Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 6Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 6Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 6Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 6Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 6Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 7Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer G shown in table 1 within the range specified by the present invention. The acrylic oligomer G was an acrylic acid-butyl acrylate co-oligomer having a number average molecular weight (Mn) of 518.79 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 7Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as the rosin-based resin within the range defined by the present invention, and 9.0 wt% of a polyethylene resin was contained as the polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 7Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 7Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 7Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 7Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 33.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 7Z in which the content of the polyethylene-polypropylene resin was increased, and the ratio of the weight of one or more acrylic resins to the weight of one or more polyethylene-polypropylene resins was set to the lower limit within the more preferable range specified in the present invention, the solder wettability was also sufficiently improved. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 8Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer H shown in Table 1 within the range specified by the present invention. The acrylic oligomer H was an acrylic acid-butyl acrylate co-oligomer having a number average molecular weight (Mn) of 846.23 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 925.36 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

In example 8Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as the rosin-based resin within the range defined by the present invention, and 7.0 wt% of a polyethylene resin was contained as the polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 8Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 8Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 8Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 8Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 35.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 8Z in which the content of the polyethylene-polypropylene resin was increased, the ratio of the weight of one or more acrylic resins to the weight of one or more polyethylene-polypropylene resins was more than the lower limit of the more preferable range specified in the present invention, the sufficient effect of wettability to solder was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 9Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer I shown in table 1 within the range specified by the present invention. The acrylic oligomer I is a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 841.10 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 9Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 9Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 9Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 9Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 9Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 9Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 10Z, the acrylic resin contained 18.0 wt% of the acrylic oligomer J shown in table 1 within the range specified by the present invention. The acrylic oligomer J was a butyl acrylate-polyethylene co-oligomer having a number average molecular weight (Mn) of 921.86 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1047.26 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention.

Hereinafter, in example 10Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 10Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 10Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 10Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 10Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 10Z, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 11Z is an example containing a plurality of acrylic resins. In example 11Z, as the acrylic resin, 1.8 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of a butyl acrylate oligomer (acrylic oligomer B) having a number average molecular weight (Mn) of 982.40 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1097.53 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of a butyl acrylate oligomer (acrylic oligomer C) having a number average molecular weight (Mn) of 1096.51 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1236.01 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of an alkyl acrylate oligomer (acrylic oligomer D) having a number average molecular weight (Mn) of 1315.06 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1507.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of a butyl methacrylate oligomer (acrylic oligomer E) having a number average molecular weight (Mn) of 757.93 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 844.62 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer H) having a number average molecular weight (Mn) of 846.23 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 925.36 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer I) having a number average molecular weight (Mn) of 841.10 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 914.14 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

In example 11Z, the acrylic resin contained 1.8 wt% of a butyl acrylate-polyethylene co-oligomer (acrylic oligomer J) having a number average molecular weight (Mn) of 921.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1047.26 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention.

Hereinafter, in example 11Z, as in example 1Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as a rosin-based resin within the range defined by the present invention, and 2.0 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 11Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 11Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. Further, in example 11Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 11Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 11Z in which an acrylic resin was added in combination, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 12Z is an example in which the content of the polyethylene-polypropylene resin (pe.pp resin) was changed. In example 12Z, as the acrylic resin, 19.8 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 12Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as the rosin-based resin within the range specified by the present invention, and 0.2 wt% of a polyethylene resin was contained as the polyethylene-polypropylene-based resin (pe.pp resin) within the range specified by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 12Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 12Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 12Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 12Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 12Z in which the content of the polyethylene-polypropylene resin (pe.pp resin) was reduced, sufficient effects were obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Examples 13Z and 14Z are examples in which the type of polyethylene-polypropylene resin (pe.pp resin) was changed. In example 13Z, as the acrylic resin, 19.8 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 13Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as the rosin-based resin within the range defined by the present invention, and 0.2 wt% of acid-modified polyethylene resin was contained as the polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 13Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 13Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 13Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 13Z, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.9% by weight as a metal deactivator in the range defined in the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in an amount of 0.1% by weight as a nitrogen compound-based metal deactivator in the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 13Z in which the kind of polyethylene-polypropylene resin (pe.pp resin) was changed, sufficient effects were obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 14Z, as the acrylic resin, 19.8 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 14Z, 15.0 wt% of acrylic-modified hydrogenated rosin was contained as the rosin-based resin within the range defined by the present invention, and 0.2 wt% of oxidized polyethylene resin was contained as the polyethylene-polypropylene-based resin (pe.pp resin) within the range defined by the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 14Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 14Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 14Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 14Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 14Z in which the kind of polyethylene-polypropylene resin (pe.pp resin) was changed, sufficient effects were obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Examples 15Z to 17Z are examples containing a plurality of polyethylene-polypropylene resins (pe.pp resins). In example 15Z, as the acrylic resin, 19.7 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 15Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 15Z, as the polyethylene-polypropylene resin (pe.pp resin), the polyethylene resin was contained in an amount of 0.1 wt% within the range defined by the present invention, the acid-modified polyethylene resin was contained in an amount of 0.1 wt% within the range defined by the present invention, and the oxidized polyethylene resin was contained in an amount of 0.1 wt% within the range defined by the present invention. The total content of the two or more polyethylene-polypropylene resins (pe.pp resins) is within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 15Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 15Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 15Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 15Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 15Z in which a polyethylene-polypropylene resin (pe.pp resin) was added in combination, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 16Z, as the acrylic resin, 19.4 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 16Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 16Z, as the polyethylene-polypropylene resin (pe.pp resin), 0.1 wt% of a polyethylene resin within the range defined by the present invention, 0.1 wt% of an acid-modified polyethylene resin within the range defined by the present invention, 0.1 wt% of an oxidized polyethylene resin within the range defined by the present invention, 0.1 wt% of a polypropylene resin within the range defined by the present invention, 0.1 wt% of an acid-modified polypropylene resin within the range defined by the present invention, and 0.1 wt% of an oxidized polypropylene resin within the range defined by the present invention were contained. The total content of the two or more polyethylene-polypropylene resins (pe.pp resins) is within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 16Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 16Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 16Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 16Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 16Z in which a polyethylene-polypropylene resin (pe.pp resin) was added in combination, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 17Z, as the acrylic resin, 14.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 17Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 17Z, the polyethylene-polypropylene resin (pe.pp resin) contained 3.0 wt% of the polyethylene resin within the range defined by the present invention and 3.0 wt% of the acid-modified polyethylene resin within the range defined by the present invention. The total content of the two or more polyethylene-polypropylene resins (pe.pp resins) is within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 17Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 17Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 17Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 17Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 17Z in which a polyethylene-polypropylene resin (pe.pp resin) was added in combination, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 18Z, as the acrylic resin, 14.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 18Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 18Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of the polyethylene resin within the range defined by the present invention and 4.0 wt% of the polypropylene oxide resin within the range defined by the present invention. The total content of the two or more polyethylene-polypropylene resins (pe.pp resins) is within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 18Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 18Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 18Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 18Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 18Z in which a polyethylene-polypropylene resin (pe.pp resin) was added in combination, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 19Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 19Z, the acrylic resin contained 15.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, within the ranges specified in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 19Z, no rosin-based resin was contained. In example 19Z, the acid-modified polyethylene resin (pe. pp resin) was contained in an amount of 2.0 wt% within the range defined in the present invention as the polyethylene-polypropylene resin. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 19Z, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 2.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 19Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent in the range specified by the present invention, 1.0 wt% of ethylamine HBr as an amine hydrohalide was contained as an active agent in the range specified by the present invention, and 1.0 wt% of N, N-diethylaniline HBr as an amine hydrohalide was contained as an active agent in the range specified by the present invention. The total content of the two or more amine hydrohalide salts is within the range specified in the present invention.

In example 19Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 19Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 19Z, which contained no rosin resin and contained amine hydrohalide as an activator in addition to dimer acid, other organic acid, and amine, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 20Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 20Z, the acrylic resin contained 15.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 20Z, the rosin-based resin was not contained. In example 20Z, the acid-modified polyethylene resin (pe. pp resin) was contained in an amount of 2.0 wt% within the range defined in the present invention as the polyethylene-polypropylene resin. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 20Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 3.5 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 20Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as the active agent within the range defined by the present invention, 1.0 wt% of trans-2, 3-dibromo-2-butene-1, 4-diol as an organic halogen compound was contained as the active agent within the range defined by the present invention, and 1.5 wt% of triallyl isocyanurate 6 bromide as an organic halogen compound was contained as the active agent within the range defined by the present invention. The total content of the two or more organic halogen compounds is within the range specified in the present invention.

In example 20Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 20Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 38.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 20Z, which contained no rosin resin and an organic halogen compound as an active agent in addition to dimer acid, other organic acid, and amine, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 21Z, as the acrylic resin, 5.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 21Z, the acrylic resin contained 5.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 21Z, the rosin-based resin contained 13.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 21Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 21Z, 20.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 21Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 21Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 21Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 21Z in which the content of the acrylic resin was at the lower limit of the more preferable range specified in the present invention, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 22Z, as the acrylic resin, 7.5 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 22Z, the acrylic resin contained 5.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 22Z, the rosin-based resin contained 13.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 22Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 22Z, 17.5 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 22Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 22Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 22Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 22Z in which the content of the acrylic resin was reduced, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 23Z is an example containing a plurality of rosin-based resins. In example 23Z, as the acrylic resin, 18.0 wt% of a butyl acrylate oligomer (acrylic oligomer a) having a number average molecular weight (Mn) of 853.86 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 900.42 determined by mass spectrometry using a time of flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 23Z, as the rosin-based resin, 3.0 wt% of acrylic-modified hydrogenated rosin was contained within the range defined by the present invention, 2.0 wt% of maleic-modified hydrogenated rosin was contained within the range defined by the present invention, 2.0 wt% of phenol-modified rosin was contained within the range defined by the present invention, 2.0 wt% of disproportionated rosin was contained within the range defined by the present invention, 2.0 wt% of hydrogenated rosin was contained within the range defined by the present invention, 2.0 wt% of polymerized rosin was contained within the range defined by the present invention, and 2.0 wt% of rosin ester was contained within the range defined by the present invention.

The total content of the respective rosin-based resins is within the range defined in the present invention. In example 23Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 23Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 23Z, 1.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 23Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 23Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 23Z in which a rosin-based resin was compounded, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 24Z is an example in which the kind of other organic acid is changed. In example 24Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 24Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 24Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of the polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 24Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of dodecanedioic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and dodecanedioic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 24Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 24Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 24Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 24Z in which the kind of other organic acid was changed, sufficient effects were obtained with respect to solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 25Z is an example without other organic acids. In example 25Z, as the acrylic resin, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 25Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 25Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 25Z, 17.0 wt% of dimer acid as an active agent was contained within the range specified in the present invention, and no other organic acid was contained.

In example 25Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 25Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 25Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 25Z containing no other organic acid, a sufficient effect on solder wettability was also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 26Z is an example without organic acid. In example 26Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 26Z, as the acrylic resin, 10.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In example 26Z, 16.0 wt% of an acrylic-modified hydrogenated rosin was contained as the rosin-based resin within the range defined by the present invention. In example 26Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of the polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 26Z, dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, and other organic acids were not contained.

In example 26Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 26Z, trans-2, 3-dibromo-2-butene-1, 4-diol as an organic halogen compound was contained in an amount of 2.0 wt% as an activator in the range defined by the present invention, and triallyl isocyanurate 6 bromide as an organic halogen compound was contained in an amount of 3.0 wt% as an activator in the range defined by the present invention. The total content of the two or more organic halogen compounds is within the range specified in the present invention. In example 26Z, 0.5 wt% of ethylamine HBr as an amine hydrohalide salt was contained as the active agent within the range defined by the present invention, and 0.5 wt% of N, N-diethylaniline HBr as an amine hydrohalide salt was contained as the active agent within the range defined by the present invention. The total content of the two or more amine hydrohalide salts is within the range specified in the present invention.

In example 26Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 26Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 26Z containing no dimer acid, hydrogenated dimer acid, trimer acid, hydrogenated trimer acid, and other organic acids, sufficient effects on solder wettability were also obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 27Z to example 35Z are examples in which the combination of active agents is changed. In example 27Z, as the acrylic resin, 21.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 27Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 27Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 27Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 27Z, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range specified by the present invention. In example 27Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 27Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 27Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 28Z, as the acrylic resin, 21.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 28Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 28Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 28Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of glutaric acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 28Z, 2.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention. In example 28Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 28Z, as the metal deactivator, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained within the range defined in the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained within the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 28Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 29Z, as the acrylic resin, 21.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained within the ranges specified in the present invention.

In example 29Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 29Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 29Z, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of glutaric acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 29Z, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range specified by the present invention. In example 29Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 29Z, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.9% by weight as a metal deactivator in the range defined in the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in an amount of 0.1% by weight in the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 29Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 30Z, as the acrylic resin, 21.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS) and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained within the ranges defined in the present invention.

In example 30Z, the rosin-based resin contained 15.0 wt% of an acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 30Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 30Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 1.5 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 1.5 wt% of glutaric acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and glutaric acid is within the range of the content of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 30Z, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range specified by the present invention. In example 30Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 30Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 30Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 31Z, the acrylic resin contained 19.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention.

In example 31Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 31Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 31Z, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 2.5 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 2.5 wt% of glutaric acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and glutaric acid is within the range of the content of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 31Z, 2.0 wt% of 2-phenylimidazoline as an amine was contained as an active agent within the range specified by the present invention. In example 31Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 31Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 31Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 32Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 32Z, the rosin-based resin contained 15.0 wt% of an acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 32Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 32Z, 11.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In addition, there is no amine in example 32Z. In example 32Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 32Z, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.9% by weight as a metal deactivator in the range defined in the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained in an amount of 0.1% by weight in the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 32Z in which the combination of the active agents was changed and no amine was contained, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 33Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention was contained as the acrylic resin within the ranges defined in the present invention.

In example 33Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 33Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 33Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 33Z, the active agent contained 2-phenyl-4-methylimidazole as an amine in an amount of 1.0 wt% in the range defined by the present invention. In example 33Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In example 33Z, the metal deactivator included bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator in an amount of 2.9 wt% within the range defined by the present invention, and N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator in an amount of 0.1 wt% within the range defined by the present invention, and the total amount of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 33Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 34Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 34Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 34Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 34Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 2.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 1.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 34Z, 4.0 wt% of 2-phenylimidazole as an amine was contained as an active agent within the range defined by the present invention, and 4.0 wt% of 2-phenyl-4-methylimidazole as an amine was contained within the range defined by the present invention. The total content of two or more amines is within the range specified in the present invention. In example 34Z, 2.0 wt% of hydrogenated castor oil as an ester-based thixotropic agent was contained as the thixotropic agent within the range defined by the present invention.

In example 34Z, as the metal deactivator, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.0 wt% within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 34Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In example 35Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 35Z, the rosin-based resin contained 15.0 wt% of an acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 35Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 35Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 35Z, 2.0 wt% of 2-phenylimidazole as an amine was contained as the activator in the range defined by the present invention, and 2.0 wt% of 2, 3-dibromo-1, 4-butanediol as the organic halogen compound was contained as the activator in the range defined by the present invention. In example 35Z, 2.0 wt% of hydrogenated castor oil as an ester-based thixotropic agent was contained as the thixotropic agent within the range defined by the present invention.

In example 35Z, as the metal deactivator, bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained in an amount of 2.0 wt% within the range defined in the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In example 35Z in which the combination of the active agents was changed, a sufficient effect was obtained on solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 36Z is an example of changing the amount of the thixotropic agent, and in example 36Z, 18.0 wt% of isotridecyl methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges as defined in the present invention was contained as the acrylic resin within the ranges as defined in the present invention.

In example 36Z, the rosin-based resin contained 15.0 wt% of an acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 36Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 36Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 36Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 36Z, the ester-based thixotropic agent contained hydrogenated castor oil in an amount of 7.0 wt% in the range defined by the present invention as the thixotropic agent.

In example 36Z, the metal deactivator was not contained, and the balance of the solvent contained diethylene glycol hexyl ether in an amount of 40.0 wt% within the range specified by the present invention.

In example 36Z, which contains an increased amount of a thixotropic agent and does not contain a metal deactivator, a sufficient effect on solder wettability was obtained. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 37Z is an example in which the kinds of thixotropic agents and solvents were changed. In example 37Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 37Z, the rosin-based resin contained 15.0 wt% of an acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 37Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 37Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 37Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. In example 37Z, the amide-based thixotropic agent contained in an amount of 3.0 wt% in the range defined by the present invention as the thixotropic agent.

In example 37Z, as the metal deactivator, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator was contained within the range defined in the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator was contained within the range defined in the present invention, and the total content of two or more metal deactivators was within the range defined in the present invention. The balance of the solvent contained 41.0 wt% of diethylene glycol ethylhexyl ether within the range specified in the present invention.

In example 37Z in which the kinds of the thixotropic agent and the solvent were changed, a sufficient effect was obtained on the solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

Example 38Z is an example in which the kinds of the thixotropic agent, the metal deactivator, and the solvent are changed. In example 38Z, 18.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention was contained as the acrylic resin within the ranges specified in the present invention.

In example 38Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In example 38Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of a polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In example 38Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In example 38Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined by the present invention. Further, in example 38Z, 3.0 wt% of a bisamide-based thixotropic agent as an amide-based thixotropic agent was contained as the thixotropic agent within the range defined by the present invention.

In example 38Z, N' -hexamethylenebis [3- [3, 5-di-tert-butyl-4-hydroxyphenyl ] propionamide as a hindered phenol-based metal deactivator was contained in an amount of 2.9% by weight in the range defined by the present invention as a metal deactivator, N- [2H-1,2, 4-triazol-5-yl ] salicylamide as a nitrogen compound-based metal deactivator was contained in an amount of 0.1% by weight in the range defined by the present invention as a nitrogen compound-based metal deactivator, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 41.0 wt% of diethylene glycol ethylhexyl ether within the range specified in the present invention.

In example 38Z in which the kinds of the thixotropic agent, the metal deactivator, and the solvent were changed, a sufficient effect was obtained on the solder wettability. In addition, a sufficient effect is obtained in terms of compatibility. Further, a sufficient effect is obtained in terms of reliability of the temperature cycle.

In contrast, in comparative example 1Z, the acrylic resin contained 25.0 wt% of isotridecanol methacrylate oligomer (acrylic oligomer F) having a number average molecular weight (Mn) of 1028.82 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 1138.20 as determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

In comparative example 1Z, the acrylic resin contained 20.0 wt% of an acrylic acid-butyl acrylate co-oligomer (acrylic oligomer G) having a number average molecular weight (Mn) of 518.79 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), a weight average molecular weight (Mw) of 625.29 determined by mass spectrometry using a time-of-flight mass spectrometer (TOF-MS), and a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges defined in the present invention, within the ranges defined in the present invention.

The total content of each acrylic resin is within the range specified in the present invention. In comparative example 1Z, the resin composition contained 4.0 wt% of a polyethylene resin and 4.0 wt% of an oxidized polypropylene resin in the ranges specified in the present invention as a polyethylene-polypropylene resin (pe.pp resin) without containing a rosin resin. The total content of the two or more polyethylene-polypropylene resins (pe.pp resins) is within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In comparative example 1Z, the active agent was not contained, and the ester-based thixotropic agent included hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent in an amount of 2.0 wt% in the range of the present invention were included as the thixotropic agent. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In comparative example 1Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In comparative example 1Z containing no active agent, effects were obtained in terms of compatibility and reliability of temperature cycle, but no effect was obtained on solder wettability.

In comparative example 2Z, acrylic oligomers having a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, which were determined by mass analysis using a time-of-flight mass spectrometer (TOF-MS), were not included as acrylic resins, and butyl acrylate polymers having a number average molecular weight (Mn) and a weight average molecular weight (Mw) exceeding 4000 were included as acrylic polymers at 18.0 wt%.

In comparative example 2Z, the rosin-based resin contained 15.0 wt% of the acrylic-modified hydrogenated rosin within the range defined in the present invention. In comparative example 2Z, the polyethylene-polypropylene resin (pe.pp resin) contained 2.0 wt% of the polyethylene resin within the range defined in the present invention. The ratio of the weight of one kind of acrylic resin or the total weight of two or more kinds of acrylic resins to the weight of one kind of polyethylene-polypropylene resin or the total weight of two or more kinds of polyethylene-polypropylene resins is within the range specified in the present invention.

In comparative example 2Z, 10.0 wt% of dimer acid was contained as the active agent in the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent in the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent in the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In comparative example 2Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined in the present invention. In comparative example 2Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In comparative example 2Z, 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator contained within the range defined by the present invention was contained as a metal deactivator, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitride-based metal deactivator contained within the range defined by the present invention was contained as a metal deactivator, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In comparative example 2Z, which contained an acrylic polymer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) exceeding 4000, without containing an acrylic oligomer having a number average molecular weight (Mn) and a weight average molecular weight (Mw) within the ranges specified in the present invention, which were determined by a mass spectrometry method using a time-of-flight mass spectrometer (TOF-MS), the solder wettability was improved, but each material was separated into 2 or more components, and no effect was obtained in terms of compatibility. In addition, the residue was not sufficiently solidified, and the reliability of the temperature cycle could not be evaluated.

In comparative example 3Z, the acrylic resin contained no acrylic oligomer or acrylic polymer. In comparative example 3Z, 34.8 wt% of acrylic-modified hydrogenated rosin exceeding the range defined in the present invention was contained as a rosin-based resin, and 0.2 wt% of a polyethylene resin was contained as a polyethylene-polypropylene-based resin (pe.pp resin) within the range defined in the present invention.

In comparative example 3Z, 10.0 wt% of dimer acid was contained as the active agent within the range defined by the present invention, 4.0 wt% of succinic acid as the other organic acid was contained as the active agent within the range defined by the present invention, and 3.0 wt% of adipic acid as the other organic acid was contained as the active agent within the range defined by the present invention. The total content of succinic acid and adipic acid is within the content range of the other organic acids specified in the present invention. In addition, the total content of dimer acid and other organic acids is within the range specified in the present invention.

In comparative example 3Z, the active agent contained 2-phenylimidazole as an amine in an amount of 1.0 wt% within the range defined in the present invention. In comparative example 3Z, the ester-based thixotropic agent was hydrogenated castor oil in an amount of 2.0 wt% and the amide-based thixotropic agent was bisamide-based thixotropic agent in an amount of 2.0 wt% within the range defined by the present invention. The total content of the two or more thixotropic agents is within the range specified in the present invention.

In comparative example 3Z, the metal deactivator included 2.9 wt% of bis [3- (3-tert-butyl-4-hydroxy-5-methylphenyl) propionic acid ] [ ethylenebis (oxyethylene) ] as a hindered phenol-based metal deactivator within the range defined by the present invention, and 0.1 wt% of N- (2H-1,2, 4-triazol-5-yl) salicylamide as a nitrogen compound-based metal deactivator within the range defined by the present invention, and the total content of two or more metal deactivators was within the range defined by the present invention. The balance of the solvent contained 40.0 wt% of diethylene glycol hexyl ether in the range specified in the present invention.

In comparative example 3Z, which did not contain an acrylic resin, the solder wettability was improved. However, although the residue was solidified, cracks were observed in the residue, and no effect was obtained in terms of reliability of temperature cycle. Further, since acrylic resin was not contained, compatibility was not evaluated.

(examples of Sn-As)

< evaluation of thickening Effect of solder paste >

The thickening-inhibiting effect of solder pastes prepared using the fluxes of example 1Y and example 1Z and solder alloys having the compositions shown in tables 20 to 25 below was also verified. A flux for example 1Y shown in Table 8 and example 1Z shown in Table 14, and a flux having an alloy composition shown in tables 20 to 25 and satisfying JIS Z3284-1: 2014, the solder powders of the size (particle size distribution) of symbol 4 in table 2 of the powder size classification are mixed to prepare solder paste. The mass ratio of the soldering flux to the soft solder powder is that the soldering flux: solder powder 11: 89.

(1) Verification method

The obtained solder paste was measured according to JIS Z3284-3: 2014 "4.2 viscosity characteristics test", a rotational viscometer (PCU-205, manufactured by MALCOM corporation) is used, and the rotational speed: 10rpm, measurement temperature: the viscosity was measured continuously at 25 ℃ for 12 hours. Then, the initial viscosity (viscosity after stirring for 30 minutes) and the viscosity after 12 hours were compared, and the thickening-inhibiting effect was evaluated based on the following criteria.

(2) Criterion for judgment

O: viscosity after 13 hours ≤ initial viscosity × 1.2: little increase in viscosity with time, good

X: viscosity after 13 hours > initial viscosity x 1.2: increase in viscosity with time, failure

[ Table 20]