阅读说明：本技术 错位收缩起皱形态面料的织造方法 (Weaving method of staggered shrinkage wrinkling-shaped fabric ) 是由 吕宏光 于 2020-12-24 设计创作，主要内容包括：本发明涉及错位收缩起皱面料织造的技术领域,特别是涉及一种错位收缩起皱形态面料的织造方法,其实现了产品各项指标的创新性,该产品纹理清晰,立体感强,起泡效果好,创新性强；包括以下步骤：S1、按照工艺要求的经向花型排列和穿综顺序,将经纱穿过停经片和丝线,选用符合工艺要求的钢筘,并按规定的入数完成插箱工作,初步确定品种经密和幅宽,同类品种上机时实施机上结经处理；S2、将穿综好的织轴按照工艺要求上机织造；S3、按照工艺要求对在织或待织品种进行纬纱配备供应；S4、将经纱和纬纱按照工艺要求进行交织；S5验修：按坯布质量评定标准对下机坯布进行检验定等,并对布面疵点进行修补。(The invention relates to the technical field of weaving of staggered shrinkage wrinkling fabrics, in particular to a weaving method of a staggered shrinkage wrinkling form fabric, which realizes the innovativeness of various indexes of a product, and the product has clear texture, strong stereoscopic impression, good bubbling effect and strong innovativeness; the method comprises the following steps: s1, according to the warp pattern arrangement and drafting sequence of the process requirement, the warp yarns pass through the drop wires and the silk yarns, the reeds meeting the process requirement are selected, the box inserting work is completed according to the specified number of the warps, the warp density and the breadth of the variety are preliminarily determined, and the warp tying processing is carried out on the loom when the similar variety is on the loom; s2, weaving the drafted beam on a machine according to the process requirements; s3, supplying weft yarns for the woven or to-be-woven fabric according to the process requirements; s4, interweaving the warp yarns and the weft yarns according to the process requirements; and S5 inspection and repair: and inspecting the grey cloth of the next machine according to the grey cloth quality evaluation standard, and repairing the cloth cover defects.)

1. A weaving method of a fabric in a dislocation shrinkage wrinkling shape is characterized by comprising the following steps:

s1, according to the warp pattern arrangement and drafting sequence of the process requirement, the warp yarns pass through the drop wires and the silk yarns, the reeds meeting the process requirement are selected, the box inserting work is completed according to the specified number of the warps, the warp density and the breadth of the variety are preliminarily determined, and the warp tying processing is carried out on the loom when the similar variety is on the loom;

s2, weaving the drafted beam on a machine according to the process requirements;

s3, supplying weft yarns for the woven or to-be-woven fabric according to the process requirements;

s4, interweaving the warp yarns and the weft yarns according to the process requirements;

and S5 inspection and repair: and inspecting the grey cloth of the next machine according to the grey cloth quality evaluation standard, and repairing the cloth cover defects.

2. The method of weaving a misalignment shrink crepe configuration fabric as in claim 1, wherein the fabric is made by weaving the following materials in an aligned manner: warp direction A adopts 100D/48F terylene discontinuous network yarn, the network point discontinuous ratio is 4/2 cm for 5 times, 2/2 cm for 5 times, 1/2 cm for 5 times, 2/2 cm for 5 times, and 2/2 cm for 5 times, the warp direction B is 100D/48F terylene DTY +40DSP empty bag, and the arrangement ratio of the warp yarn A and the warp yarn B is as follows: A22B1 and A5B1, wherein the weft A adopts 100D/72F cation DTY conventional network yarns, the weft B adopts 100D/48F polyester discontinuous network yarns, and the warp C is 100D/48F cation DTY +40DSP empty bag.

3. The method for weaving a staggered, contracted and wrinkled fabric according to claim 1, wherein the weave structure of the fabric is vertically composed of warps B and horizontally composed of warps C, and when the fabric is contracted simultaneously in the horizontal direction and the vertical direction, the fabric forms a rhombic shape with bubbles, the diamonds are staggered in a crossing manner, the fabric surface presents a strong appearance with a convex style of bubbles, weft three-color wefts are arranged according to a specified proportion, and color horizontal stripes are formed on the fabric surface and are combined with the bubbles.

4. The method for weaving a fabric in a misaligned, contracted and wrinkled state according to claim 1, wherein the step S4 uses 28 warps/cm and 26.5 wefts/cm on the upper machine.

5. The method of weaving a misalignment shrink crepe configuration fabric as in claim 2 wherein the fabric has a loom width of 335 cm and the weaving machine uses a 360 cm electronic dobby, triple jet water jet loom.

6. The weaving method of dislocation and shrinkage wrinkling shape fabric as claimed in claim 2, characterized in that in order to fully play the functions of four raw materials in warp and weft directions, a twice shaping mode is adopted: pre-shrinking is performed between dyeing of products, so that the warp shrinkage is 25%, the weft shrinkage is 20%, sizing is performed again after dyeing, the warp shrinkage is 5%, and the weft shrinkage is 8%, and the shrinking effect of the products is achieved.

7. The method of weaving a slip-shrink creped form of the face fabric of claim 2 wherein the total number of weft cycles is 744, a510, B186, C48.

8. The method of weaving a fabric having an offset shrink crepe configuration according to claim 3, wherein the fabric is designed to have a plain weave and weft weave combination with a 58 x 62 repeat count.

Technical Field

The invention relates to the technical field of weaving of staggered shrinkage wrinkling fabrics, in particular to a weaving method of a staggered shrinkage wrinkling fabric.

Background

Along with the improvement of living standard and the acceleration of life rhythm, people have higher and higher requirements on clothes and home decoration, common clothes and home decoration fabrics cannot meet the requirements of people, and along with the continuous development of scientific technology, textile fabrics meeting different requirements of people are developed endlessly to meet the requirements of consumers. At present, fabric products are almost all planes, jacquard colors and the fabric are in the same plane, the structure of the fabric is expressed by the colors of jacquard colors, and the jacquard colors and the fabric cannot be highlighted because the jacquard colors and the fabric are on the same plane. In order to make the jacquard color of the jacquard product have a three-dimensional relief-like appearance, a new technical method is needed to solve the problem.

Disclosure of Invention

In order to solve the technical problems, the invention provides the weaving method of the staggered shrinkage wrinkling shape fabric, which realizes the innovativeness of various indexes of the product, and has the advantages of clear texture, strong stereoscopic impression, good bubbling effect and strong innovativeness.

The weaving method of the fabric in the dislocation shrinkage wrinkling shape comprises the following steps of:

s1, according to the warp pattern arrangement and drafting sequence of the process requirement, the warp yarns pass through the drop wires and the silk yarns, steel foils meeting the process requirement are selected, the box inserting work is completed according to the specified input number, the warp density and the breadth of the variety are preliminarily determined, and the warp tying processing is carried out on the loom when the same variety is put on the loom;

s2, weaving the drafted beam on a machine according to the process requirements;

s3, supplying weft yarns for the woven or to-be-woven fabric according to the process requirements;

s4, interweaving the warp yarns and the weft yarns according to the process requirements;

and S5 inspection and repair: and inspecting the grey cloth of the next machine according to the grey cloth quality evaluation standard, and repairing the cloth cover defects.

The weaving method of the fabric with the dislocation shrinkage wrinkling shape is characterized in that the fabric is made by arranging and weaving the following materials: warp direction A adopts 100D/48F terylene discontinuous network yarn, the network point discontinuous ratio is 4/2 cm for 5 times, 2/2 cm for 5 times, 1/2 cm for 5 times, 2/2 cm for 5 times, and 2/2 cm for 5 times, the warp direction B is 100D/48F terylene DTY +40DSP empty bag, and the arrangement ratio of the warp yarn A and the warp yarn B is as follows: A22B1 and A5B1, wherein the weft A adopts 100D/72F cation DTY conventional network yarns, the weft B adopts 100D/48F polyester discontinuous network yarns, and the warp C is 100D/48F cation DTY +40DSP empty bag.

The weaving method of the fabric with staggered, contracted and wrinkled forms, disclosed by the invention, has the advantages that the fabric weave structure is vertically composed of warps B and horizontally composed of warps C, when the fabric is transversely and vertically contracted simultaneously, the bubbling rhombic forms are formed, the diamonds are crossed and staggered, the fabric surface presents a strong bubbling and protruding style appearance, weft three-color wefts are arranged according to a specified proportion, the color horizontal stripes are formed on the fabric surface, and the horizontal stripes are combined with the bubbling.

According to the weaving method of the fabric in the dislocation, shrinkage and wrinkling shape, 28 warp threads/cm on the upper machine and 26.5 weft threads/cm on the upper machine are adopted in the step S4.

The weaving method of the fabric in the staggered contraction wrinkling shape has the advantages that the machine width of the fabric is 335 cm, and a 360 cm electronic multi-arm and three-jet water-jet loom is used as a weaving machine.

The weaving method of the fabric in the dislocation shrinkage wrinkling shape adopts a twice shaping mode in order to fully play the functions of four raw materials in warp and weft directions: pre-shrinking is performed between dyeing of products, so that the warp shrinkage is 25%, the weft shrinkage is 20%, sizing is performed again after dyeing, the warp shrinkage is 5%, and the weft shrinkage is 8%, and the shrinking effect of the products is achieved.

According to the weaving method of the fabric in the dislocation shrinkage wrinkling form, the total number of weft circulation is 744, wherein A510, B186 and C48 are provided.

The invention relates to a weaving method of a fabric with dislocation shrinkage wrinkling shape, which adopts a combined weave of plain weave and weft weave, and the cycle number is 58 x 62.

The invention has the beneficial effects that: on the surface fabric of sheet, quilt cover, throw pillow, cushion, (window) curtain etc. commonly used in the imitative family, appear the form of wrinkling of large tracts of land, can strengthen the outward appearance of surface fabric, soft handle, the style is novel to this surface fabric structure is tight, reasonable in design has elegant intention and comfortable practicality and is ready for the favor, and collocation through each item key technology has realized the novelty of each item index of product, and this product texture is clear, and the third dimension is strong, and the froth effect is good, and the novelty is strong.

Detailed Description

The following examples are given to further illustrate the embodiments of the present invention. The following examples are intended to illustrate the invention but are not intended to limit the scope of the invention.

Example 1

The method comprises the following steps:

s1, according to the warp pattern arrangement and drafting sequence of the process requirement, the warp yarns pass through the drop wires and the silk yarns, steel foils meeting the process requirement are selected, the box inserting work is completed according to the specified input number, the warp density and the breadth of the variety are preliminarily determined, and the warp tying processing is carried out on the loom when the same variety is put on the loom;

s2, weaving the drafted beam on a machine according to the process requirements;

s3, supplying weft yarns for the woven or to-be-woven fabric according to the process requirements;

s4, interweaving the warp yarns and the weft yarns according to the process requirements;

and S5 inspection and repair: and inspecting the grey cloth of the next machine according to the grey cloth quality evaluation standard, and repairing the cloth cover defects.

Example 2

Is made by arranging and weaving the following materials: warp direction A adopts 100D/48F terylene discontinuous network yarn, the network point discontinuous ratio is 4/2 cm for 5 times, 2/2 cm for 5 times, 1/2 cm for 5 times, 2/2 cm for 5 times, and 2/2 cm for 5 times, the warp direction B is 100D/48F terylene DTY +40DSP empty bag, and the arrangement ratio of the warp yarn A and the warp yarn B is as follows: A22B1 and A5B1, wherein the weft A adopts 100D/72F cation DTY conventional network yarns, the weft B adopts 100D/48F polyester discontinuous network yarns, and the warp C is 100D/48F cation DTY +40DSP empty bag.

Example 3

The fabric weave structure is composed of warp B in the vertical direction and warp C in the horizontal direction, when the fabric weave structure shrinks horizontally and vertically at the same time, a foaming diamond shape is formed, the diamonds are crossed and staggered, the fabric surface presents a strong foaming convex style appearance, weft three-color weft yarns are arranged according to a specified proportion, color horizontal stripes are formed on the fabric surface, and the horizontal stripes are combined with foaming.

Example 4

In the step S4, 28 warp threads/cm and 26.5 weft threads/cm are adopted.

Example 5

The width of the fabric on the loom is 335 cm, and the weaving machine uses a 360 cm electronic multi-arm and three-jet type water-jet loom.

Example 6

In order to fully exert the functions of the warp and weft raw materials, a twice shaping mode is adopted: pre-shrinking is performed between dyeing of products, so that the warp shrinkage is 25%, the weft shrinkage is 20%, sizing is performed again after dyeing, the warp shrinkage is 5%, and the weft shrinkage is 8%, and the shrinking effect of the products is achieved.

Example 7

The total number of weft cycles is 744, wherein A510, B186 and C48.

Example 8

The fabric design adopts a combined weave of plain weave and weft weave, and the number of cycles is 58 x 62.

The above description is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, several modifications and variations can be made without departing from the technical principle of the present invention, and these modifications and variations should also be regarded as the protection scope of the present invention.