阅读说明：本技术 一种仿真丝面料制备工艺 (Preparation process of silk-like fabric ) 是由 李金仓 王松强 刘强 张仁勇 于中正 于 2020-12-08 设计创作，主要内容包括：本发明公开了一种仿真丝面料制备工艺,它包括以下步骤,首先,将莫代尔87％,氨纶13％混织成氨纶布,进行低温染色、烘干备用；然后,按35g/L的乳木果油加工剂调配好,定型机125℃×20y过浆槽。该仿真丝面料制备工艺生产防面料具有抗氧化功效,并具有真丝般爽滑手感。(The invention discloses a silk-like fabric preparation process, which comprises the following steps of firstly, blending 87% of modal and 13% of spandex into spandex fabric, dyeing at low temperature and drying for later use; then, the processing agent is prepared according to 35g/L shea butter, and the setting machine passes through a stock chest at 125 ℃ multiplied by 20 y. The silk-like fabric produced by the preparation process has an anti-oxidation effect and has a smooth hand feeling like silk.)

1. A silk-like fabric preparation process is characterized by comprising the following steps: which comprises the following steps of,

firstly, mixing 87% of modal and 13% of spandex to weave spandex fabric, and dyeing and drying at low temperature for later use;

then, blending according to 35g/L shea butter processing agent, and carrying out finished product shaping by a 125 ℃ x 20y pulp tank of a shaping machine to form the simulated silk fabric.

2. The process for preparing silk-like fabric according to claim 1, which is characterized in that: the slurry in the slurry tank contains 10% silicon oil.

The technical field is as follows:

the invention relates to the technical field of textile printing and dyeing, in particular to a process for preparing silk-like fabric.

Background art:

along with the improvement of living standard of people, the demand of the market garment materials tends to the development of environmental protection, health care and ultra-soft body feeling, but the existing artificial fibers still lack health care function compared with real silk, are inferior to the real silk in hand feeling and cannot meet high-end demand.

The invention content is as follows:

the invention aims to solve the technical problem of providing a preparation process of a silk-like fabric with silk-like softness, moisture retention, oxidation resistance and a health-care function of preventing skin from being aged too fast.

The technical scheme of the invention is to provide a silk-like fabric preparation process, which comprises the following steps of firstly, mixing 87% of modal and 13% of spandex to weave into spandex fabric, and carrying out low-temperature dyeing and drying for later use;

then, blending according to 35g/L shea butter processing agent, and carrying out finished product shaping by a 125 ℃ x 20y pulp tank of a shaping machine to form the simulated silk fabric.

Preferably, the slurry in the slurry tank contains 10% silicone oil.

Compared with the prior art, the invention has the following advantages after the process is adopted: the artificial fiber has soft hand feeling, is breathable and comfortable to wear, and the silk-like fabric with oxidation resistance, aging resistance and smooth hand feeling like silk is obtained by low-temperature dyeing, has the same hand feeling as silk, and is soft and smooth.

The specific implementation mode is as follows:

the invention is further illustrated with respect to specific embodiments below:

which comprises the following steps of,

firstly, mixing 87% of modal and 13% of spandex to weave spandex fabric, and dyeing and drying at low temperature for later use;

then, blending according to 35g/L shea butter processing agent, and carrying out finished product shaping by a 125 ℃ x 20y pulp tank of a shaping machine to form the simulated silk fabric.

Wherein, the serous fluid in the serous tank contains 10 percent of silicon oil, the low-temperature dyeing is carried out at 85 ℃, and the dye is reactive dye.

Main technical parameters

The pilling (780cN, 600r) is more than or equal to 3; bursting strength (the diameter of the steel ball is 38 plus or minus 0.02mm) (432N) is more than or equal to 150N; washing size change rate (total cellulose fiber content 50% or more) (1 × 5A): straight (-0.8) -7.0- + 3.0%, transverse (-3.1) -9.0- + 2.0%; twist rate after washing (4.3%): less than or equal to 5.0 percent; drying mass per square meter: 186.7g/m²。

By the process, the characteristics of soft hand feeling, air permeability and comfort in wearing and bright dyeing of the artificial fiber are utilized, the artificial fiber is used as the matrix, and the shea butter processing agent with super-soft and smooth hand feeling, oxidation resistance, moisture retention and skin aging prevention is added to form the silk-like health-care functional fabric, so that the silk-like health-care functional fabric is wide in application range and good in market prospect.

The foregoing is illustrative of the preferred embodiments of the present invention only and is not to be construed as limiting the claims. All equivalent structural or equivalent process transformations made by using the contents of the present specification are included in the scope of protection of the present invention.