阅读说明：本技术 一种低弹性模量高塑性钛合金及其制备方法和应用 (Low-elastic-modulus high-plasticity titanium alloy and preparation method and application thereof ) 是由 张兵 贾元智 甘致聪 张钰哲 李健 刘延国 马明臻 刘日平 于 2020-12-08 设计创作，主要内容包括：本发明属于钛合金技术领域,具体涉及一种低弹性模量高塑性钛合金及其制备方法和应用。本发明提供的低弹性模量高塑性钛合金,包括以下质量百分含量的元素：Fe 1.5～2.5％,Nb 12～18％,Sn 4～6％,Zr 4～10％,余量为Ti和不可避免的杂质；所述低弹性模量高塑性钛合金的值为2.75～2.86,值为2.35～2.44。本发明所述低弹性模量高塑性钛合金由无毒的Fe、Nb、Sn、Zr和Ti组成,具有良好的生物相容性；通过各元素的协同配合,降低了钛合金的弹性模量且提高了塑性。实验结果表明,本发明提供的低弹性模量高塑性钛合金弹性模量为59～70GPa,延伸率为20.4～41.6％。(The invention belongs to the technical field of titanium alloy, and particularly relates to a low-elastic-modulus high-plasticity titanium alloy and a preparation method and application thereof. The titanium alloy with low elastic modulus and high plasticity provided by the invention comprises the following elements in percentage by mass: 1.5-2.5% of Fe, 12-18% of Nb, 4-6% of Sn, 4-10% of Zr, and the balance of Ti and inevitable impurities; of said low modulus of elasticity high plasticity titanium alloy The value is 2.75 to 2.86, the value is 2.35 to 2.44. The titanium alloy with low elastic modulus and high plasticity consists of nontoxic Fe, Nb, Sn, Zr and Ti, and has good biocompatibility; through the synergistic cooperation of all elements, the elastic modulus of the titanium alloy is reduced and the plasticity is improved. Experimental results show that the titanium alloy with low elastic modulus and high plasticity provided by the invention has the elastic modulus of 59-70 GPa and the elongation of 20.4-41.6%.)

1. The titanium alloy with low elastic modulus and high plasticity is characterized by comprising the following elements in percentage by mass:

1.5-2.5% of Fe, 12-18% of Nb, 4-6% of Sn, 4-10% of Zr, and the balance of Ti and inevitable impurities;

of said low modulus of elasticity high plasticity titanium alloyThe value is 2.75 to 2.86,a value of 2.35 to 2.44, saidValue sumValues were calculated according to formula I and formula II, respectively:

the elements in formula I and formula II are in mole percent.

2. The low elastic modulus high plasticity titanium alloy according to claim 1, wherein the low elastic modulus high plasticity titanium alloy has an elastic modulus of not more than 70GPa and an elongation of not less than 20.4%.

3. The method for producing a low-elastic-modulus high-plasticity titanium alloy according to claim 1 or 2, which is characterized by comprising the following steps:

mixing and smelting alloy raw materials, and cooling to obtain an alloy ingot;

and sequentially carrying out hot rolling and quenching on the alloy ingot to obtain the low-elasticity-modulus high-plasticity titanium alloy.

4. The method of claim 3, wherein the melting is vacuum non-consumable arc melting; the vacuum degree of the back bottom in the smelting equipment in the smelting process is less than or equal to 2.0 multiplied by 10^-2Pa; the current of the vacuum non-consumable arc melting is 300-500A, and the voltage is 15-30V.

5. The preparation method according to claim 3 or 4, wherein the smelting comprises melting and furnace cooling which are carried out alternately, and the melting time is more than or equal to 8 times; the melting time is 5-9 min/time.

6. The preparation method according to claim 3, wherein the hot rolling temperature is 780-880 ℃, and the rolling reduction of each pass is independently 7-10%; the thickness of the hot-rolled plate obtained after hot rolling is 3-4 mm.

7. The method according to claim 6, wherein the hot rolling further comprises maintaining the temperature of the product after each rolling pass; the temperature for heat preservation is 780-880 ℃, and the time is 5-8 min.

8. The preparation method according to claim 3, wherein the quenching is carried out at a holding temperature of 800-850 ℃ for 5-10 min.

9. Use of the low elastic modulus high plasticity titanium alloy according to any one of claims 1 to 2 or the low elastic modulus high plasticity titanium alloy prepared by the preparation method according to any one of claims 3 to 8 in preparing force bearing implant materials.

Technical Field

The invention belongs to the technical field of titanium alloy, and particularly relates to a low-elastic-modulus high-plasticity titanium alloy and a preparation method and application thereof.

Background

The medical alloy has high strength, good toughness and bending fatigue resistance, and excellent processing performance, and is the most extensive force bearing implant material in clinical application. The medical alloy mainly comprises three medical materials of stainless steel, cobalt-chromium alloy and titanium alloy, wherein the titanium alloy is the medical alloy with the best biocompatibility currently known. In practice, medical alloys with high elastic modulus for implantation are prone to osteoporosis, aseptic loosening, muscle atrophy and even surgical failure due to stress shielding. Clinical tests and mechanical experiments show that the elastic modulus (40-150 GPa) of the titanium alloy is closer to that of human bones (10-40 GPa) than that of stainless steel (about 200GPa) and cobalt-chromium alloy (about 235GPa), and technicians also continuously seek to obtain the titanium alloy closer to that of the human bones. For example, the elastic modulus of a Ti-13Nb-13Zr alloy (as-cast state) developed in the United states is 79-84 GPa, but the elastic modulus of the alloy is still high, so that the stress shielding problem is easy to generate; the Ti-29Nb-13Ta-4.6Zr alloy designed by Niinomi in Japan has the elastic modulus of about 55GPa, but has the plasticity of only 5 percent, thereby being not beneficial to the processing and forming of the titanium alloy; the medical titanium alloy TC4 ELI and Ti-6Al-7Nb which are most widely used at home and abroad have high elastic modulus (100-120 GPa) and are easy to generate stress shielding problem, the alloy has low plasticity (6-15 percent) and limits the processing forming and service life of the alloy, and in addition, toxic elements Al and V in the alloy can induce related diseases after long-term accumulation in a human body. Based on the application of medical titanium alloy in the special environment of human body, the current titanium alloy can not give consideration to both low elastic modulus and high plasticity on the basis of excellent biocompatibility.

Disclosure of Invention

In view of the above, the present invention aims to provide a low elastic modulus and high plasticity titanium alloy, which has the characteristics of excellent biocompatibility, low elastic modulus and high plasticity, and meets the use requirements of medical alloys.

In order to achieve the purpose of the invention, the invention provides the following technical scheme:

the invention provides a low-elasticity modulus high-plasticity titanium alloy which comprises the following elements in percentage by mass:

1.5-2.5% of Fe, 12-18% of Nb, 4-6% of Sn, 4-10% of Zr, and the balance of Ti and inevitable impurities;

of said low modulus of elasticity high plasticity titanium alloyThe value is 2.75 to 2.86,a value of 2.35 to 2.44, saidValue sumValues were calculated according to formula I and formula II, respectively:

2.790 Ti% +3.099 Nb% +3.086 Zr% +2.283 Sn% +2.651 Fe% formula I,

2.447 Ti% +2.424 Nb% +2.934 Zr% +2.100 Sn% +0.969 Fe% of formula II,

the elements in formula I and formula II are in mole percent.

Preferably, the elastic modulus of the low-elastic-modulus high-plasticity titanium alloy is less than or equal to 70GPa, and the elongation is more than or equal to 20.4%.

The invention also provides a preparation method of the titanium alloy with low elastic modulus and high plasticity, which comprises the following steps:

mixing and smelting alloy raw materials, and cooling to obtain an alloy ingot;

and sequentially carrying out hot rolling and quenching on the alloy ingot to obtain the low-elasticity-modulus high-plasticity titanium alloy.

Preferably, the smelting is vacuum non-consumable arc smelting; the vacuum degree of the back bottom in the smelting equipment in the smelting process is less than or equal to 2.0 multiplied by 10^-2Pa; the current of the vacuum non-consumable arc melting is 300-500A, and the voltage is 15-30V.

Preferably, the smelting comprises alternately carrying out melting and furnace cooling, and the melting times are more than or equal to 8 times; the melting time is 5-9 min/time.

Preferably, the hot rolling temperature is 780-880 ℃, and the rolling reduction of each pass is independently 7-10%; the thickness of the hot-rolled plate obtained after hot rolling is 3-4 mm.

Preferably, the hot rolling further comprises heat preservation of the product obtained by rolling after each pass of rolling; the temperature for heat preservation is 780-880 ℃, and the time is 5-8 min.

Preferably, the heat preservation temperature of quenching is 800-850 ℃, and the heat preservation time is 5-10 min.

The invention also provides application of the low-elastic modulus high-plasticity titanium alloy in the technical scheme or the low-elastic modulus high-plasticity titanium alloy prepared by the preparation method in the technical scheme in preparation of a load-bearing implant material.

The invention provides a low-elasticity modulus high-plasticity titanium alloy which comprises the following elements in percentage by mass: fe 15-2.5%, 12-18% of Nb, 4-6% of Sn, 4-10% of Zr, and the balance of Ti and inevitable impurities; of said low modulus of elasticity high plasticity titanium alloyThe value is 2.75 to 2.86,a value of 2.35 to 2.44, saidValue sumValues were calculated according to formula I and formula II, respectively:

2.790 Ti% +3.099 Nb% +3.086 Zr% +2.283 Sn% +2.651 Fe% formula I,

2.447 Ti% +2.424 Nb% +2.934 Zr% +2.100 Sn% +0.969 Fe% of formula II,

the elements in formula I and formula II are in mole percent.

In the invention, the low-elastic-modulus high-plasticity titanium alloy consists of nontoxic Fe, Nb, Sn, Zr and Ti, does not contain toxic elements such as Al, Cr, V, Ni and the like, and is favorable for the low-elastic-modulus high-plasticity titanium alloy to have good biocompatibility; ti provides a main element; nb is infinitely dissolved in the beta titanium alloy, which is beneficial to stabilizing beta phase, and the bond energy between Nb and Ti is high, so that the elastic modulus of the alloy can be effectively reduced; zr and Sn have higher solid solubility in Ti, exist in a form of a substitutional solid solution, have higher bond energy with Ti, and are beneficial to reducing the elastic modulus of the alloy; fe exists in a substitutional solid solution form in the beta titanium alloy, so that the beta phase transformation point can be obviously reduced, the beta titanium alloy is stabilized, and the strength of the low-elasticity-modulus high-plasticity titanium alloy is improved. In the inventionAll elements exist in a solid solution state, and intermetallic compounds are not formed among all elements, so that the improvement of the elastic modulus can be effectively avoided. In addition, the elements are higher than Ti alloyAndthe values show that the bond energy of each element and Ti is higher, which is beneficial to reducing the elastic modulus of the titanium alloy.

Experimental results show that the low-elastic-modulus high-plasticity titanium alloy provided by the invention has the elastic modulus of 59-70 GPa and low elastic modulus; the yield strength is 525.9-619.8 MPa, and the yield strength is high; the fracture strength is 727.4-830.1 MPa, the fracture strength is high, and the mechanical property is good; the elongation is 20.4-41.6%, the elongation is high, and the plastic property is excellent.

Drawings

FIG. 1 is a metallographic structure chart of a low-elastic-modulus high-plasticity titanium alloy obtained in example 1;

FIG. 2 is a drawing of a standard drawing of a tensile specimen in a tensile test;

FIG. 3 is a graph showing tensile mechanical properties of examples 1 to 4.

Detailed Description

The invention provides a low-elasticity modulus high-plasticity titanium alloy which comprises the following elements in percentage by mass:

1.5-2.5% of Fe, 12-18% of Nb, 4-6% of Sn, 4-10% of Zr, and the balance of Ti and inevitable impurities;

of said low modulus of elasticity high plasticity titanium alloyThe value is 2.75 to 2.86,a value of 2.35 to 2.44, saidValue sumValues were calculated according to formula I and formula II, respectively:

2.790 Ti% +3.099 Nb% +3.086 Zr% +2.283 Sn% +2.651 Fe% formula I,

2.447 Ti% +2.424 Nb% +2.934 Zr% +2.100 Sn% +0.969 Fe% of formula II,

the elements in formula I and formula II are in mole percent.

In the invention, the titanium alloy with low elastic modulus and high plasticity comprises 1.5-2.5% of Fe by mass percentage, preferably 1.6-2.4%, and more preferably 1.7-2.3%. In the invention, Fe exists in the titanium alloy in the form of a substitutional solid solution, so that the beta transformation point can be obviously reduced, and the beta titanium alloy is stabilized. And the strength of the low-elasticity-modulus high-plasticity titanium alloy is improved.

In the invention, the titanium alloy with low elastic modulus and high plasticity comprises 12-18% of Nb by mass percentage, preferably 12.5-17.5%, and more preferably 13-17%. In the invention, Nb is infinitely dissolved in the titanium alloy, which is beneficial to stabilizing beta phase, and the bond energy between Nb and Ti is high, thereby effectively reducing the elastic modulus of the alloy.

In the invention, the titanium alloy with low elastic modulus and high plasticity comprises 4-6% of Sn by mass percentage, preferably 4.2-5.8%, and more preferably 4.5-5.5%. In the present invention, Sn may be substituted and dissolved in the titanium alloy to lower the elastic modulus of the alloy.

In the invention, the titanium alloy with low elastic modulus and high plasticity comprises 4-10% of Zr by mass percentage, preferably 4.5-9.5%, and more preferably 5-9%. In the invention, Zr can be infinitely replaced and dissolved in the titanium alloy, so that the elastic modulus of the alloy is reduced.

In the present invention, the low modulus of elasticity high plasticity titanium alloy includes, in mass percentage, Ti and unavoidable impurities as the balance. In the present invention, the inevitable impurities are preferably C and/or O. In the present invention, the total content of the inevitable impurities is preferably 0.5 wt.% or less.

In the present invention, the low elastic modulus high plasticity titanium alloyThe value is 2.75 to 2.86, preferably 2.77 to 2.84;the value is 2.35 to 2.44, preferably 2.26 to 2.43; whereinValue sumValues were calculated according to formula I and formula II, respectively:

2.790 Ti% +3.099 Nb% +3.086 Zr% +2.283 Sn% +2.651 Fe% formula I,

2.447 Ti% +2.424 Nb% +2.934 Zr% +2.100 Sn% +0.969 Fe% of formula II,

the elements in formula I and formula II are in mole percent.

The Bo value is an indication of the strength of the covalent bond between Ti and the alloying element; md is a representation of the d-orbital energy in relation to the element's radius and electronegativity. The high values of Bo and Md indicate a corresponding higher intensity and energy. The average value of Bo values is used in the inventionMeasuring the strength of covalent bonds of elements in the titanium alloy; average value of Md valueThe value measures the d-orbital energy in the titanium alloy.

In the present invention, the elastic modulus of the low-elastic-modulus high-plasticity titanium alloy is preferably 70GPa or less; the elongation is preferably 20.4% or more.

The invention also provides a preparation method of the titanium alloy with low elastic modulus and high plasticity, which comprises the following steps:

mixing and smelting alloy raw materials, and cooling to obtain an alloy ingot;

and sequentially carrying out hot rolling and quenching on the alloy ingot to obtain the low-elasticity-modulus high-plasticity titanium alloy.

In the present invention, unless otherwise specified, the respective materials are commercially available products well known to those skilled in the art.

The alloy raw materials are mixed, smelted and cooled to obtain the alloy ingot.

In the present invention, the element content of the alloy raw material is the same as the element content of the low-elastic modulus high-plasticity titanium alloy in the above technical solution, and is not described herein again.

In the invention, the alloy raw material is preferably a metal simple substance of Ti, Fe, Nb, Zr and Sn; in the invention, the purity of the alloy raw material is preferably more than or equal to 99.9%. The shape of the alloy raw material is not particularly limited in the invention, and the shape of the alloy raw material known to those skilled in the art can be adopted.

In the present invention, the melting is preferably vacuum non-consumable arc melting. In the invention, the smelting equipment is preferably a vacuum non-consumable smelting furnace. In the invention, the vacuum degree of the back bottom in the smelting equipment during smelting is preferably less than or equal to 2.0 multiplied by 10^-2Pa. In the invention, the current of the vacuum non-consumable arc melting is preferably 300-500A, and more preferably 340-460A; the voltage is preferably 15 to 30V, and more preferably 17 to 28V.

In the invention, the smelting comprises melting and furnace cooling which are carried out alternately, and the melting frequency is preferably more than or equal to 8 times; the melting time is preferably 5-9 min/time, and more preferably 6-8 min/time.

In the present invention, the cooling is preferably furnace cooling.

After the alloy ingot is obtained, the alloy ingot is sequentially subjected to hot rolling and quenching to obtain the low-elasticity-modulus high-plasticity titanium alloy.

In the invention, the rolling temperature of the hot rolling is preferably 780-880 ℃, more preferably 790-850 ℃, and most preferably 800 ℃; in the invention, the amount of reduction of each pass of rolling in the hot rolling is preferably 7-10% independently, and more preferably 7.5-9.5%; the rolling pass is preferably 7 to 13, and more preferably 8 to 11. The hot rolling pressing amount of the invention is beneficial to ensuring the integrity of crystal grains, preventing the crystal grains from being broken and refined and further beneficial to ensuring the alloy to have good plasticity. In the present invention, the thickness of the hot-rolled sheet obtained after the hot rolling is preferably 3 to 4mm, and more preferably 3.2 to 3.8 mm. In the present invention, the hot rolling apparatus is preferably a two-roll mill; in an embodiment of the present invention, the hot rolling apparatus is preferably a type 200 two roll mill.

Before hot rolling, the invention preferably carries out primary heat treatment on the alloy ingot; the heat preservation temperature of the primary heat treatment is preferably 800-850 ℃, and more preferably 800-840 ℃; the heat preservation time is preferably 50-60 min, and more preferably 52-58 min. In the present invention, the apparatus for the preliminary heat treatment is preferably a heat treatment furnace. According to the invention, the alloy ingot is preheated through primary heat treatment, so that the hot rolling is favorably carried out; and proper preheating time is set, so that the crystal grains of the alloy ingot are prevented from growing under the condition of reaching the set hot rolling temperature, and the weakening of alloy strength and plasticity caused by the growth of the crystal grains of the alloy ingot is avoided.

In the invention, the hot rolling preferably comprises heat preservation of the product obtained by rolling after each pass of rolling; the temperature of the heat preservation is preferably 780-880 ℃, more preferably 790-850 ℃, and most preferably 800 ℃; the time is preferably 5 to 8min, more preferably 5.5 to 7.5 min.

In the invention, the trip reaction exists in the hot rolling process, which is beneficial to improving the plasticity of the titanium alloy.

In the invention, the heat preservation temperature of quenching is preferably 800-850 ℃, and more preferably 810-840 ℃; the heat preservation time is preferably 5-10 min, and more preferably 6-8 min. The quenching condition of the invention is not only beneficial to ensuring that the all-beta structure is kept at room temperature, but also beneficial to preventing the crystal grains from growing, and avoids the reduction of the alloy strength and plasticity caused by the growth of the alloy crystal grains.

In the present invention, the cooling means after quenching is preferably water cooling. According to the invention, the quenched product is cooled to room temperature by water, so that the low-elasticity-modulus high-plasticity titanium alloy is obtained.

The invention also provides application of the low-elastic modulus high-plasticity titanium alloy in the technical scheme or the low-elastic modulus high-plasticity titanium alloy prepared by the preparation method in the technical scheme in preparation of a load-bearing implant material.

The invention is not particularly limited in this application, and can be applied to bearing implant materials well known to those skilled in the art.

In order to further illustrate the present invention, the following examples are given to describe the low elastic modulus high plasticity titanium alloy and the preparation method and application thereof in detail, but they should not be construed as limiting the scope of the present invention. It is to be understood that the described embodiments are merely exemplary of the invention, and not restrictive of the full scope of the invention. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

The reagents used in the examples are all commercially available.

Example 1

The titanium alloy with low elastic modulus and high plasticity is designed to have the following element compositions in percentage by mass: 15% of Nb, 2% of Fe, 5% of Sn, 5% of Zr, and the balance of Ti and inevitable impurities,the value of the number of the bits is 2.812,a value of 2.423;

according to the designed element composition of the titanium alloy with low elastic modulus and high plasticity, the alloy raw materials are mixed and then placed in a vacuum non-consumable arc melting furnace, and the vacuum degree of the back bottom before melting is less than or equal to 1.8 multiplied by 10^-2Pa, then carrying out vacuum non-consumable arc melting under the conditions of 400A and 20V, in the melting process, after 6min of melting each time, cooling along with the furnace, re-melting, carrying out co-melting for 8 times, and finally cooling to obtain an alloy ingot with the average height of 18.0 mm;

keeping the temperature of the obtained alloy ingot in a heat treatment furnace at 800 ℃ for 50min, and then placing the alloy ingot in a 200-type two-roll rolling mill for hot rolling, wherein the reduction of each pass in the hot rolling is 1.35mm, the number of rolling passes is 11, the rolled product is placed in the heat treatment furnace at 800 ℃ between each pass for heat preservation for 5 ℃, and a hot rolled plate with the thickness of 4mm is obtained after the hot rolling;

and (3) keeping the temperature of the hot rolled plate at 800 ℃ for 5min for quenching, and then cooling the hot rolled plate to room temperature by water to obtain the low-elasticity-modulus high-plasticity titanium alloy (marked as Ti15Nb5Zr5Sn2 Fe).

Metallographic structure test was performed on the titanium alloy with low elastic modulus and high plasticity obtained in this example, and the obtained alloy structure diagram is shown in fig. 1. As can be seen from fig. 1, the low modulus of elasticity high plasticity titanium alloy obtained in this example is composed of a single β phase.

Example 2

The titanium alloy with low elastic modulus and high plasticity is designed to have the following element compositions in percentage by mass: 14% of Nb, 2% of Fe, 5% of Sn, 6% of Zr, and the balance of Ti and inevitable impurities,the value of the number of the bits is 2.812,a value of 2.426;

the preparation method was the same as that of example 1, and the low-elastic-modulus high-plasticity titanium alloy (noted as Ti14Nb6Zr5Sn2Fe) was obtained.

Example 3

The titanium alloy with low elastic modulus and high plasticity is designed to have the following element compositions in percentage by mass: 13% of Nb, 2% of Fe, 5% of Sn, 7% of Zr,the balance being Ti and unavoidable impurities,the value of the number of the bits is 2.812,a value of 2.429;

the preparation method was the same as that of example 1, and the low-elastic-modulus high-plasticity titanium alloy (noted as Ti13Nb7Zr5Sn2Fe) was obtained.

Example 4

The titanium alloy with low elastic modulus and high plasticity is designed to have the following element compositions in percentage by mass: 12% of Nb, 2% of Fe, 5% of Sn, 8% of Zr, and the balance of Ti and inevitable impurities,the value of the number of the bits is 2.812,a value of 2.432;

the preparation method was the same as that of example 1, and the low-elastic-modulus high-plasticity titanium alloy (noted as Ti12Nb8Zr5Sn2Fe) was obtained.

Comparative example 1

The titanium alloy comprises the following elements in percentage by mass: 12% of Nb, 2% of Fe, 5% of Sn, 8% of Zr, and the balance of Ti and inevitable impurities;the value of the number of the bits is 2.812,the value was 2.432.

The heat treatment mode is 500 ℃ quenching; the other preparation steps were the same as in example 1 to obtain a titanium alloy.

Through microscopic observation, the alloy structure of the titanium alloy in the comparative example is alpha + beta phase.

Comparative example 2

Taking the traditional medical titanium alloy Ti-6Al-7Nb as an example, the traditional medical titanium alloy Ti-6Al-7Nb comprises the following elements in percentage by mass: 6% of Al, 7% of Nb and the balance of Ti and inevitable impurities (toxic element Al is present).

The preparation procedure was the same as in example 1.

The size of the test part of the tensile sample is 20mm multiplied by 2mm multiplied by 3mm, and the specific size of the tensile sample is shown in figure 2; a mechanical property test is carried out on the low elastic modulus high plasticity titanium alloy obtained in the embodiment 1-4 and the titanium alloy obtained in the comparative example 1-2 by a universal mechanical experiment machine (model: INSTRON-5982) with an extensometer, the test result is shown in a table 1, and the obtained tensile mechanical property graph is shown in a figure 3.

TABLE 1 Performance test results for examples 1-4 and comparative examples 1-2

As can be seen from Table 1, the titanium alloy with low elastic modulus and high plasticity provided by the invention has the elastic modulus of 59-70 GPa and low elastic modulus; the yield strength is 525.9-619.8 MPa, and the yield strength is high; the fracture strength is 727.4-830.1 MPa, the fracture strength is high, and the mechanical property is good; the elongation is 20.4-41.6%, the elongation is high, and the plastic property is excellent.

As can be seen from FIG. 3, the second elastic modulus high plasticity titanium alloy provided by the invention has a lower elastic modulus and good plasticity.

The foregoing is only a preferred embodiment of the present invention, and it should be noted that, for those skilled in the art, various modifications and decorations can be made without departing from the principle of the present invention, and these modifications and decorations should also be regarded as the protection scope of the present invention.