阅读说明：本技术 有序可控多孔硅胶及其制备方法 (Ordered controllable porous silica gel and preparation method thereof ) 是由 季宪泰 郭典 冯晨瑞 秦同 于 2020-11-24 设计创作，主要内容包括：本申请的有序可控多孔硅胶的制备方法,包括：提供一晶格点阵结构,该晶格点阵结构包括至少一个区域,每个区域均由多个晶胞单元构成；向至少一个区域的晶胞单元内注入液态硅胶并固化,形成混合结构；去除所述混合结构中的晶格点阵结构,得到有序可控多孔硅胶。本申请还提供一种利用如上所述的有序可控多孔硅胶的制备方法制备而成的有序可控多孔硅胶。本申请的制备方法简易、高效,且能根据需求控制不同尺度的孔的分配比例和孔的尺寸,能制得高精度的有序可控多孔硅胶。(The preparation method of the ordered controllable porous silica gel comprises the following steps: providing a lattice structure, wherein the lattice structure comprises at least one area, and each area is composed of a plurality of unit cell units; injecting liquid silica gel into the unit cell unit of at least one region and solidifying to form a mixed structure; and removing the lattice structure in the mixed structure to obtain the ordered controllable porous silica gel. The application also provides the ordered controllable porous silica gel prepared by the preparation method of the ordered controllable porous silica gel. The preparation method is simple and efficient, the distribution proportion of the holes with different scales and the sizes of the holes can be controlled according to requirements, and high-precision ordered controllable porous silica gel can be prepared.)

1. A preparation method of ordered controllable porous silica gel is characterized by comprising the following steps:

a. providing a lattice structure, wherein the lattice structure comprises at least one area, and each area is composed of a plurality of unit cell units;

b. injecting liquid silica gel into the unit cell unit of the at least one region and solidifying to form a mixed structure;

c. and removing the lattice structure in the mixed structure to obtain the ordered controllable porous silica gel.

2. The method of claim 1, wherein the material of the lattice structure comprises at least one of polyvinyl alcohol, polyvinyl butyral, and high impact polystyrene.

3. The method of claim 1, wherein the unit cell comprises at least one of a body centered cubic structure, a tetrahedral structure, a pyramidal structure, a three-dimensional Kagome structure, and a woven structure.

4. The method of claim 3, wherein the unit cell is a three-dimensional scaffold formed by connecting a plurality of beams.

5. The method of claim 4, wherein the unit cell units have dimensions in the first, second and third directions within a range of about 20mm, the beam arm has a diameter of about 0.5mm to about 5mm, and any two of the first, second and third directions are perpendicular to each other.

6. The method of claim 3, wherein the lattice structure comprises a plurality of regions, and the unit cell units of the plurality of regions are the same or different.

7. The method of claim 6, wherein the unit cell units of the plurality of regions vary in size periodically.

8. The method according to claim 6, wherein the cell units comprise a first cell unit and a second cell unit, the lattice structure comprises a first region and a second region, a plurality of the first cell units are located in the first region, a plurality of the second cell units are located in the second region, and the first cell units and the second cell units have the same or different sizes and/or structures.

9. The method for preparing ordered controllable porous silica gel according to claim 1, wherein step a further comprises presetting a 3D model of the lattice structure; importing the 3D model into a 3D printer, and setting printing materials and process parameters; printing the lattice structure; in the step b, the liquid silica gel is injected into the unit cell unit of the lattice structure through an injection molding machine.

10. The method of claim 1, wherein in step c, the lattice structure is removed by dissolving the lattice structure in a pre-prepared solution.

11. The method according to claim 1, wherein in step b, the liquid silica gel fills the voids of the lattice structure and partially exposes the lattice structure.

12. An ordered controllable porous silica gel, characterized by being prepared by the method of any one of claims 1 to 11.

Technical Field

The application relates to the technical field of porous silica gel preparation, in particular to ordered controllable porous silica gel and a preparation method thereof.

Background

With the wide application of porous silica gel in industry and industry, the preparation of porous silica gel has also received much attention. At present, porous silica gel mainly has two preparation methods, namely a direct method and an indirect method. The direct method is to directly extrude liquid silica gel by 3D printing and finally prepare a porous structure. However, on one hand, the structure of the porous silica gel prepared by the direct method is simple, and is limited to the vertical pore channel and the horizontal pore channel, and in addition, the accuracy of the porous silica gel directly formed by 3D printing is low due to the high fluidity of the liquid silica gel. The indirect method is to mix and solidify the pore-forming substance and the silica gel material to form a mixed structure, and then remove the pore-forming substance. However, the traditional indirect pore-forming material is difficult to maintain a stable form, the prepared porous silica gel is often uneven in density and gaps, and the sizes of pores are randomly distributed, so that the regulation and control capability of the porous silica gel is greatly reduced, a periodic porous network cannot be obtained, and the distribution proportion of pores with different sizes and the sizes of the pores cannot be controlled according to design requirements.

Therefore, how to prepare the ordered controllable porous silica gel becomes a technical problem to be solved urgently.

Disclosure of Invention

In order to solve the technical problems, the application provides the ordered controllable porous silica gel and the preparation method thereof, which are simple and efficient, and can control the distribution proportion of the pores with different scales and the sizes of the pores according to requirements.

In order to solve the technical problem, the application provides a preparation method of ordered controllable porous silica gel, which comprises the following steps:

a. providing a lattice structure, wherein the lattice structure comprises at least one area, and each area is composed of a plurality of unit cell units;

b. injecting liquid silica gel into the unit cell unit of the at least one region and solidifying to form a mixed structure;

c. and removing the lattice structure in the mixed structure to obtain the ordered controllable porous silica gel.

In one embodiment of the present invention, the material of the lattice structure comprises at least one of polyvinyl alcohol, polyvinyl butyral, high impact polystyrene.

In one embodiment of the present invention, the unit cell unit comprises at least one of a body centered cubic structure, a tetrahedral structure, a pyramidal structure, a three-dimensional Kagome structure, a braid structure.

In one embodiment of the present invention, the unit cell unit is a three-dimensional support structure formed by connecting a plurality of beam arms.

In one embodiment of the present invention, the unit cell units have dimensions in a range of 20mm in each of a first direction, a second direction and a third direction, the beam arm has a diameter of 0.5mm to 5mm, and any two directions of the first direction, the second direction and the third direction are perpendicular to each other.

In one embodiment of the present invention, the lattice structure includes a plurality of regions, and the unit cell units of the plurality of regions are the same or different.

In one embodiment of the present invention, the unit cell units of the plurality of regions vary in size periodically.

In one embodiment of the present invention, the cell units include a first cell unit and a second cell unit, the lattice structure includes a first region and a second region, a plurality of the first cell units are located in the first region, a plurality of the second cell units are located in the second region, and the first cell unit and the second cell unit have the same or different sizes and/or structures.

In an embodiment of the present invention, step a further includes presetting a 3D model of the lattice structure; importing the 3D model into a 3D printer, and setting printing materials and process parameters; printing the lattice structure; in the step b, the liquid silica gel is injected into the unit cell unit of the lattice structure through an injection molding machine.

In one embodiment of the invention, in step c, the lattice structure is removed by dissolving the lattice structure in a pre-prepared solution.

In one embodiment of the present invention, in the step b, the liquid silicone gel fills the gaps of the lattice structure and partially exposes the lattice structure.

The invention also provides the ordered controllable porous silica gel, which is prepared by the preparation method of the ordered controllable porous silica gel.

The preparation method of the ordered controllable porous silica gel comprises the following steps: providing a lattice structure, wherein the lattice structure comprises at least one area, and each area is composed of a plurality of unit cell units; injecting liquid silica gel into the unit cell unit of at least one region and solidifying to form a mixed structure; and removing the lattice structure in the mixed structure to obtain the ordered controllable porous silica gel. The application also provides the ordered controllable porous silica gel prepared by the preparation method of the ordered controllable porous silica gel. The preparation method is simple and efficient, the distribution proportion of the holes with different scales and the sizes of the holes can be controlled according to requirements, and high-precision ordered controllable porous silica gel can be prepared.

Drawings

The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments consistent with the present application and together with the description, serve to explain the principles of the application. In order to more clearly illustrate the technical solutions of the embodiments of the present application, the drawings needed to be used in the description of the embodiments will be briefly described below, and it is obvious for those skilled in the art to obtain other drawings based on these drawings without inventive exercise.

FIG. 1 is a schematic flow chart of the preparation method of the ordered controllable porous silica gel of the present invention.

FIG. 2 is a schematic view of a lattice structure according to a first embodiment of the present invention.

Fig. 3 is a schematic structural diagram of the unit cell in fig. 2.

Fig. 4 is a schematic diagram of a hybrid structure in a first embodiment of the present invention.

FIG. 5 is a schematic view of an ordered controllable porous silica gel according to a first embodiment of the present invention.

FIG. 6 is a schematic view of a lattice structure according to a second embodiment of the present invention.

FIG. 7 is a schematic view of a lattice structure according to a third embodiment of the present invention.

FIG. 8 is a schematic view of a lattice structure of a fourth embodiment of the present invention

Detailed Description

The following description of the embodiments of the present application is provided for illustrative purposes, and other advantages and capabilities of the present application will become apparent to those skilled in the art from the present disclosure.

In the following description, reference is made to the accompanying drawings that describe several embodiments of the application. It is to be understood that other embodiments may be utilized and that mechanical, structural, electrical, and operational changes may be made without departing from the spirit and scope of the present application. The following detailed description is not to be taken in a limiting sense, and the terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the application.

Although the terms first, second, etc. may be used herein to describe various elements in some instances, these elements should not be limited by these terms. These terms are only used to distinguish one element from another.

Also, as used herein, the singular forms "a", "an" and "the" are intended to include the plural forms as well, unless the context indicates otherwise. It will be further understood that the terms "comprises," "comprising," "includes" and/or "including," when used in this specification, specify the presence of stated features, steps, operations, elements, components, items, species, and/or groups, but do not preclude the presence, or addition of one or more other features, steps, operations, elements, components, species, and/or groups thereof. The terms "or" and/or "as used herein are to be construed as inclusive or meaning any one or any combination. Thus, "A, B or C" or "A, B and/or C" means "any of the following: a; b; c; a and B; a and C; b and C; A. b and C ". An exception to this definition will occur only when a combination of elements, functions, steps or operations are inherently mutually exclusive in some way.

FIG. 1 is a schematic flow chart of the preparation method of the ordered controllable porous silica gel of the present invention. Referring to fig. 1, the method for preparing ordered controllable porous silica gel according to the present invention comprises the following steps:

a. providing a lattice structure, wherein the lattice structure comprises at least one region, and each region is composed of a plurality of unit cell units;

b. injecting liquid silica gel into the unit cell unit of at least one region and solidifying to form a mixed structure;

c. and removing the lattice structure in the mixed structure to obtain the ordered controllable porous silica gel.

In a preferred embodiment of the invention, the material of the lattice structure comprises at least one of polyvinyl alcohol, polyvinyl butyral, high impact polystyrene. Wherein the unit cell unit may include at least one of a tetrahedral structure, a pyramidal structure, a three-dimensional Kagome structure, and a braid structure. The lattice structure is a hollow structure, and the liquid silica gel can fill the pores of the lattice structure and partially expose the lattice structure.

In a preferred embodiment of the invention, the lattice structure is removed by dissolving the lattice structure in a pre-prepared solution. When the material of the lattice structure comprises polyvinyl alcohol, the pre-formulation solution dissolving the lattice structure comprises water; when the material of the lattice structure comprises polyvinyl butyral, the pre-prepared solution for dissolving the lattice structure comprises alcohol; where the material of the lattice structure comprises high impact polystyrene, the pre-formulated solution in which the lattice structure is dissolved comprises limonene.

The invention also provides the ordered controllable porous silica gel, which is prepared by the preparation method of the ordered controllable porous silica gel.

The present invention will be described with reference to specific examples.

[ first embodiment ]

Fig. 2 is a schematic diagram of a lattice structure according to a first embodiment of the present invention, fig. 3 is a schematic diagram of a unit cell structure of fig. 2, and fig. 4 is a schematic diagram of a hybrid structure according to the first embodiment of the present invention. Referring to fig. 2 to 4, in this embodiment, the preparation method of the ordered controllable porous silica gel is as follows:

s1: providing a lattice structure 10, wherein the lattice structure 10 includes a region composed of a plurality of unit cell units 11;

s2: injecting liquid silica gel into the unit cell unit 11 of the region and solidifying to form a mixed structure 30;

s3: and removing the lattice structure 10 in the mixed structure 30 to obtain the ordered controllable porous silica gel 20.

In the same region of the lattice structure 10, the unit cells 11 have the same structure and size. That is, in the present embodiment, all the unit cell units 11 have the same structure and are all body-centered cubic structures. Since the cell unit 11 is a three-dimensional support structure formed by connecting a plurality of beams 101, for convenience of description, a first direction X, a second direction Y, and a third direction Z perpendicular to each other in pairs are defined, and the size of the cell unit 11 in a three-dimensional space is defined by describing the size range of the cell unit 10 in the three directions. In other embodiments, the unit cell 11 may further include at least one of a tetrahedral structure, a pyramidal structure, a three-dimensional Kagome structure, and a braid structure.

In the preferred embodiment of the present invention, the unit cell units 11 have a size ranging from 4mm to 10mm in each of the first direction X, the second direction Y and the third direction Z, and the beam arm 101 has a diameter ranging from 0.5mm to 5 mm.

In this embodiment, step S1 includes presetting the 3D model of the lattice structure 10, specifically, presetting the cell unit 11 size to be 10mm, and the beam arm 101 diameter to be 2 mm. And importing the data into a 3D printer to generate a preset track of the 3D printer. And then, selecting polyvinyl alcohol as a printing material for printing, extruding and paving the polyvinyl alcohol to a base plane by a 3D printer according to a preset track, and superposing layer by layer to obtain the lattice structure 10 with millimeter scale periodicity.

In other embodiments, the material of the lattice structure 10 may further include at least one of polyvinyl butyral, high impact polystyrene.

Step S2 further includes placing the prepared lattice structure 10 in an injection mold cavity, preparing a liquid silicone, and coating a release agent on both the injection mold cavity and the lattice structure 10 before injecting the liquid silicone into the lattice structure 10. When the liquid silica gel fills the lattice structure 10 and partially exposes it, it is left to stand for about 30 minutes, then heated to 80 ℃ and kept warm for 10 minutes to cure the liquid silica gel to form the mixed structure 30.

After cooling, the mold is opened and the hybrid structure 30 is removed. And then placing the mixed structure 30 in water with the temperature of more than 95 ℃ for ultrasonic oscillation to dissolve the lattice structure 10 in the water, thereby preparing the ordered controllable porous silica gel 20.

FIG. 5 is a schematic view of an ordered controllable porous silica gel according to a first embodiment of the present invention. Referring to fig. 5, the porous silica gel 20 has a plurality of ordered voids 21 arranged periodically.

In other embodiments, such as when printing the lattice structure 10 using polyvinyl butyral as the 3D printing material, the mixed structure 30 may also be placed in alcohol to dissolve and remove the mixed structure 30.

[ second embodiment ]

FIG. 6 is a schematic view of a lattice structure according to a second embodiment of the present invention. Referring to fig. 1 to fig. 6, the difference between the present embodiment and the first embodiment is that the lattice structure 10 includes two different regions, and the preparation process of the ordered controllable porous silica gel is also different.

Referring to fig. 6, in this embodiment, the preparation method of the ordered controllable porous silica gel is as follows:

s1: a lattice structure 10 including a plurality of unit cell units is provided, the lattice structure 10 includes a first region and a second region, the unit cell units include a first unit cell unit 111 and a second unit cell unit 112, the plurality of first unit cell units 111 are located in the first region, and the plurality of second unit cell units 112 are located in the second region.

S2: injecting liquid silica gel into the first cell unit 111 of the first region and the second cell unit 112 of the second region and curing to form a mixed structure;

s3: and removing the lattice structure 10 in the mixed structure to obtain the ordered controllable porous silica gel.

In the same region of the lattice structure 10, the unit cells 11 have the same structure and size. That is, the first cell unit 111 in the first region has the same structure and size, and the second cell unit 112 in the second region has the same structure and size. In this embodiment, the first cell unit 111 and the second cell unit 112 have the same structure, and have the same size range in three directions (X, Y, Z) (fig. 3), but have different beam diameters. In other embodiments, the first cell unit 111 and the second cell unit 112 may have different structures and sizes.

Since the first cell unit 111 and the second cell unit 112 are each a three-dimensional frame structure formed by connecting a plurality of beams, for convenience of description, a first direction X, a second direction Y, and a third direction Z perpendicular to each other are defined, and the size of the cell unit 11 in a three-dimensional space is defined by describing the size ranges of the first cell unit 111 and the second cell unit 112 in the three directions. In this embodiment, the first cell unit 111 and the second cell unit 112 have a size of 10mm in three directions of X, Y, Z.

Specifically, step S1 includes presetting a 3D model of the lattice structure 10, specifically, presetting the size of the first cell unit 111 to be 10mm by 10mm, and the diameter of the beam arm of the first cell unit 111 to be 0.5 mm; the second cell unit 112 has a size of 10mm, and the beam arm of the second cell unit 112 has a diameter of 2 mm. And importing the data into a 3D printer to generate a preset track of the 3D printer. And then, selecting polyvinyl alcohol as a printing material for printing, extruding and paving the polyvinyl alcohol to a base plane by a 3D printer according to a preset track, and stacking layer by layer to obtain the lattice structure 10 with millimeter-scale periodicity, which comprises a plurality of first unit cell units 111 and a plurality of second unit cell units 112.

In other embodiments, the first cell unit 111 and the second cell unit 112 may have a size ranging from 4mm to 10mm in the first direction X, the second direction Y, and the third direction Z, and the diameter of the beam arm may range from 0.5mm to 5 mm. That is, the dimensions of the first cell unit 111 and the second cell unit 112 in the first direction X, the second direction Y, and the third direction and the beam arm dimension may be selected to have the same value within the above range.

In other embodiments, the material of the lattice structure 10 may further include at least one of polyvinyl butyral, high impact polystyrene.

Step S2 further includes placing the prepared lattice structure 10 in an injection mold cavity, preparing a liquid silicone, and coating a release agent on both the injection mold cavity and the lattice structure 10 before injecting the liquid silicone into the lattice structure 10. And when the liquid silica gel is filled in the lattice structure 10 and part of the lattice structure is exposed, standing for about 30 minutes, then heating to 80 ℃, and preserving heat for 10 minutes to cure the liquid silica gel to form a mixed structure.

After cooling, the mold is opened and the hybrid structure 30 is removed. And then placing the mixed structure 30 in water with the temperature of more than 95 ℃ for ultrasonic oscillation to dissolve the lattice structure 10 in the water, thereby preparing the ordered controllable porous silica gel.

[ third embodiment ]

FIG. 7 is a schematic view of a lattice structure according to a third embodiment of the present invention. Referring to fig. 1 to 7, the difference between the present embodiment and the first embodiment is that the lattice structure 10 includes two different regions, and the preparation process of the ordered controllable porous silica gel is also different.

Referring to fig. 7, in this embodiment, the preparation method of the ordered controllable porous silica gel is as follows:

s1: a lattice structure 10 including a plurality of unit cell units is provided, the lattice structure 10 includes a first region and a second region, the unit cell units include a first unit cell unit 111 and a second unit cell unit 112, the plurality of first unit cell units 111 are located in the first region, and the plurality of second unit cell units 112 are located in the second region.

S2: injecting liquid silica gel into the first cell unit 111 of the first region and the second cell unit 112 of the second region and curing to form a mixed structure;

s3: and removing the lattice structure 10 in the mixed structure 30 to obtain the ordered controllable porous silica gel.

In the same region of the lattice structure 10, the unit cells 11 have the same structure and size. That is, the first cell unit 111 in the first region has the same structure and size, and the second cell unit 112 in the second region has the same structure and size. In this embodiment, the first cell unit 111 and the second cell unit 112 have the same structure, but the beam arms have different diameters, and the size ranges in three directions (X, Y, Z) are not completely the same. In other embodiments, the first cell unit 111 and the second cell unit 112 may have different structures and sizes.

Since the first cell unit 111 and the second cell unit 112 are each a three-dimensional frame structure formed by connecting a plurality of beams, for convenience of description, a first direction X, a second direction Y, and a third direction Z (fig. 3) perpendicular to each other are defined, and the size of the cell unit 11 in a three-dimensional space is defined by describing the size ranges of the first cell unit 111 and the second cell unit 112 in the three directions. In this embodiment, the first unit cell unit 111 has a size of 4mm in the X direction, 4mm in the Y direction, and 10mm in the Z direction. The dimensions of the second cell unit 112 in the three directions of X, Y, Z are all 10 mm.

Specifically, step S1 includes presetting a 3D model of the lattice structure 10, specifically, presetting the size of the first cell unit 111 to be 4mm × 10mm, and presetting the diameter of the beam arm of the first cell unit 111 to be 2 mm; the second cell unit 112 is 10mm, and the beam arm of the first cell unit 111 is 2mm in diameter, and the data is imported into the 3D printer to generate a predetermined trajectory of the 3D printer. And then, selecting polyvinyl alcohol as a printing material for printing, extruding and paving the polyvinyl alcohol to a base plane by a 3D printer according to a preset track, and stacking layer by layer to obtain the lattice structure 10 with millimeter-scale periodicity, which comprises a plurality of first unit cell units 111 and a plurality of second unit cell units 112.

In other embodiments, the first cell unit 111 and the second cell unit 112 may have a size ranging from 4mm to 10mm in the first direction X, the second direction Y, and the third direction Z, and the diameter of the beam arm may range from 0.5mm to 5 mm. That is, the sizes of the first and second cell units 111 and 112 in the first, second, and third directions X, Y, and Z, and the beam arm size may be selected within the above-mentioned ranges.

In other embodiments, the material of the lattice structure 10 may further include at least one of polyvinyl butyral, high impact polystyrene.

Step S2 further includes placing the prepared lattice structure 10 in an injection mold cavity, preparing a liquid silicone, and coating a release agent on both the injection mold cavity and the lattice structure 10 before injecting the liquid silicone into the lattice structure 10. And when the liquid silica gel is filled in the lattice structure 10 and part of the lattice structure is exposed, standing for about 30 minutes, then heating to 80 ℃, and preserving heat for 10 minutes to cure the liquid silica gel to form a mixed structure.

After cooling, the mold is opened and the hybrid structure is taken out. And then placing the mixed structure in water with the temperature of more than 95 ℃ for ultrasonic oscillation to dissolve the lattice structure 10 in the water, thereby preparing the ordered controllable porous silica gel.

[ fourth embodiment ]

FIG. 8 is a schematic view of a lattice structure according to a fourth embodiment of the present invention. Referring to fig. 1 to 8, the difference between the present embodiment and the first embodiment is that the lattice structure 10 includes a plurality of different regions.

Referring to fig. 8, in this embodiment, the preparation method of the ordered controllable porous silica gel is as follows:

s1: a lattice structure 10 is provided comprising a plurality of unit cell units, the lattice structure 10 comprising a plurality of regions, the unit cell units comprising a body centered cubic structure, a three dimensional weave structure and a tetrahedral structure, wherein the beam arm diameter of the body centered cubic structure is gradually changed from left to right from 2mm to 0.5 mm.

S2: injecting liquid silica gel into the lattice structure 10 and solidifying to form a mixed structure;

s3: and removing the lattice structure 10 in the mixed structure to obtain the ordered controllable porous silica gel.

Specifically, step S1 includes presetting a 3D model of the lattice structure 10, specifically, presetting a size of the body-centered cubic structure to be 10mm, and gradually changing a diameter of the beam arm of the body-centered cubic structure from 2mm to 0.5mm from left to right; the three-dimensional braided structure is 10mm by 10mm, and the diameter of the beam arm of the three-dimensional braided structure is 1.5 mm; the size of the tetrahedron structure is 4mm 10mm, and the diameter of the beam arm of the tetrahedron structure is 2 mm; and importing the data into a 3D printer to generate a preset track of the 3D printer. And then, selecting polyvinyl alcohol as a printing material for printing, extruding and paving the polyvinyl alcohol to a base plane by a 3D printer according to a preset track, and superposing layer by layer to obtain the lattice structure 10 which comprises a plurality of unit cell units and has millimeter-scale periodicity.

The above examples are merely illustrative of embodiments of the present invention and are not to be construed as limiting thereof. In other embodiments, the lattice structure 10 may have a plurality of regions, the plurality of regions may be arranged in any combination, and the unit cell unit in each region may include at least one of a body-centered cubic structure, a tetrahedral structure, a pyramidal structure, a three-dimensional Kagome structure, and a braid structure. That is, the number of regions in the lattice structure 10 and the kind of unit cell are not limited.

The preparation method of the ordered controllable porous silica gel comprises the following steps: providing a lattice structure, wherein the lattice structure comprises at least one area, and each area is composed of a plurality of unit cell units; injecting liquid silica gel into the unit cell unit of at least one region and solidifying to form a mixed structure; and removing the lattice structure in the mixed structure to obtain the ordered controllable porous silica gel. The application also provides the ordered controllable porous silica gel prepared by the preparation method of the ordered controllable porous silica gel. The preparation method is simple and efficient, the distribution proportion of the holes with different scales and the sizes of the holes can be controlled according to requirements, and high-precision ordered controllable porous silica gel can be prepared.

As used herein, the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, including not only those elements listed, but also other elements not expressly listed.

The above embodiments are merely illustrative of the principles and utilities of the present application and are not intended to limit the application. Any person skilled in the art can modify or change the above-mentioned embodiments without departing from the spirit and scope of the present invention. Accordingly, it is intended that all equivalent modifications or changes which can be made by those skilled in the art without departing from the spirit and technical spirit of the present invention be covered by the claims of the present invention.