阅读说明：本技术 一种挤出成型的钙素瓦楞纸 (Extrusion molding's calcium corrugated paper ) 是由 杜威 范海亮 陶香君 邢连成 于 2020-12-25 设计创作，主要内容包括：本发明公开了一种挤出成型的钙素瓦楞纸,其制作过包括配料、制作纸浆、制作原纸、制作纸板以及纸板成型；所述纸浆按照重量份由以下原料组成：植物纤维45-60份、陶瓷纤维40-50份、氢氧化铝20-30份、脲醛树脂5-15份、三聚氰胺甲醛树脂10-20份、淀粉20-30份、氯化石蜡10-20份、醋酸丁酯2-3份、多聚磷酸钠1-1.5份、粉砂1-1.8份、碳酸钙10-20份、抗氧剂2-6份和润滑剂2-10份。本发明一种挤出成型的钙素瓦楞纸由瓦楞纸浆的制作方法制成的瓦楞纸浆放入模具中成型,得到的瓦楞纸板,具有防火、阻燃、耐高温的特性；瓦楞纸板遇水不变形,不受水的侵蚀,具有防水、防潮的特性。(The invention discloses extrusion molding calcium corrugated paper, which is manufactured by burdening, manufacturing paper pulp, manufacturing raw paper, manufacturing paper board and molding the paper board; the paper pulp comprises the following raw materials in parts by weight: 45-60 parts of plant fiber, 40-50 parts of ceramic fiber, 20-30 parts of aluminum hydroxide, 5-15 parts of urea-formaldehyde resin, 10-20 parts of melamine formaldehyde resin, 20-30 parts of starch, 10-20 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1-1.5 parts of sodium polyphosphate, 1-1.8 parts of powder sand, 10-20 parts of calcium carbonate, 2-6 parts of antioxidant and 2-10 parts of lubricant. The extrusion-molded calcium corrugated paper is formed by placing corrugated paper pulp prepared by the corrugated paper pulp manufacturing method into a mold, and the obtained corrugated paper board has the characteristics of fire resistance, flame retardance and high temperature resistance; the corrugated board does not deform when meeting water, is not eroded by water, and has the characteristics of water resistance and moisture resistance.)

1. The extrusion molding calcium corrugated paper is characterized in that the manufacturing process comprises the steps of batching, paper pulp manufacturing, raw paper manufacturing, paper board manufacturing and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

45-60 parts of plant fiber, 40-50 parts of ceramic fiber, 20-30 parts of aluminum hydroxide, 5-15 parts of urea-formaldehyde resin, 10-20 parts of melamine formaldehyde resin, 20-30 parts of starch, 10-20 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1-1.5 parts of sodium polyphosphate, 1-1.8 parts of powder sand, 10-20 parts of calcium carbonate, 2-6 parts of antioxidant and 2-10 parts of lubricant.

2. The extrusion molding calcium corrugated paper as claimed in claim 1, wherein the manufacturing process comprises batching, paper pulp manufacturing, base paper manufacturing, paper board manufacturing and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

50-60 parts of plant fiber, 45-50 parts of ceramic fiber, 25-30 parts of aluminum hydroxide, 7-15 parts of urea-formaldehyde resin, 12-20 parts of melamine formaldehyde resin, 25-30 parts of starch, 15-20 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1.1-1.5 parts of sodium polyphosphate, 1.1-1.8 parts of powder sand, 12-20 parts of calcium carbonate, 3-6 parts of antioxidant and 4-10 parts of lubricant.

3. The extrusion molding calcium corrugated paper as claimed in claim 1, wherein the manufacturing process comprises batching, paper pulp manufacturing, base paper manufacturing, paper board manufacturing and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

50-58 parts of plant fiber, 45-48 parts of ceramic fiber, 25-28 parts of aluminum hydroxide, 7-13 parts of urea-formaldehyde resin, 12-18 parts of melamine formaldehyde resin, 25-28 parts of starch, 15-18 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1.1-1.4 parts of sodium polyphosphate, 1.1-1.7 parts of powder sand, 12-18 parts of calcium carbonate, 3-5 parts of antioxidant and 4-8 parts of lubricant.

4. The extrusion molding calcium corrugated paper as claimed in claim 1, wherein the manufacturing process comprises batching, paper pulp manufacturing, base paper manufacturing, paper board manufacturing and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

53 parts of plant fiber, 45 parts of ceramic fiber, 25 parts of aluminum hydroxide, 10 parts of urea-formaldehyde resin, 15 parts of melamine-formaldehyde resin, 25 parts of starch, 15 parts of chlorinated paraffin, 2.5 parts of butyl acetate, 1.3 parts of sodium polyphosphate, 1.4 parts of powder sand, 15 parts of calcium carbonate, 4 parts of antioxidant and 6 parts of lubricant.

Technical Field

The invention relates to the technical field of corrugated paper, in particular to extrusion-molded calcium corrugated paper.

Background

In recent years, with the progress of industrial technology, the application field of the calcium cellulose materials in packaging is increasingly expanded, and the trend of replacing part of traditional packaging materials such as wood by calcium cellulose boards is a development trend. The project has the advantages of low investment cost, good labor environment, high strength, attractive appearance, moisture resistance, no toxicity, corrosion resistance, high recycling rate and the like, so the project is always the most praised product in packaging materials.

Disclosure of Invention

The invention aims to provide extrusion-molded calcium corrugated paper, which solves the technical defects.

In order to achieve the purpose, the invention provides the following technical scheme:

the extrusion molding calcium corrugated paper is manufactured by burdening, manufacturing paper pulp, manufacturing raw paper, manufacturing paper board and forming the paper board; the paper pulp comprises the following raw materials in parts by weight:

45-60 parts of plant fiber, 40-50 parts of ceramic fiber, 20-30 parts of aluminum hydroxide, 5-15 parts of urea-formaldehyde resin, 10-20 parts of melamine formaldehyde resin, 20-30 parts of starch, 10-20 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1-1.5 parts of sodium polyphosphate, 1-1.8 parts of powder sand, 10-20 parts of calcium carbonate, 2-6 parts of antioxidant and 2-10 parts of lubricant.

The preparation of the extrusion molding calcium-containing corrugated paper comprises batching, paper pulp preparation, raw paper preparation, paper board preparation and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

50-60 parts of plant fiber, 45-50 parts of ceramic fiber, 25-30 parts of aluminum hydroxide, 7-15 parts of urea-formaldehyde resin, 12-20 parts of melamine formaldehyde resin, 25-30 parts of starch, 15-20 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1.1-1.5 parts of sodium polyphosphate, 1.1-1.8 parts of powder sand, 12-20 parts of calcium carbonate, 3-6 parts of antioxidant and 4-10 parts of lubricant.

The preparation of the extrusion molding calcium-containing corrugated paper comprises batching, paper pulp preparation, raw paper preparation, paper board preparation and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

50-58 parts of plant fiber, 45-48 parts of ceramic fiber, 25-28 parts of aluminum hydroxide, 7-13 parts of urea-formaldehyde resin, 12-18 parts of melamine formaldehyde resin, 25-28 parts of starch, 15-18 parts of chlorinated paraffin, 2-3 parts of butyl acetate, 1.1-1.4 parts of sodium polyphosphate, 1.1-1.7 parts of powder sand, 12-18 parts of calcium carbonate, 3-5 parts of antioxidant and 4-8 parts of lubricant.

The preparation of the extrusion molding calcium-containing corrugated paper comprises batching, paper pulp preparation, raw paper preparation, paper board preparation and paper board molding; the paper pulp comprises the following raw materials in parts by weight:

53 parts of plant fiber, 45 parts of ceramic fiber, 25 parts of aluminum hydroxide, 10 parts of urea-formaldehyde resin, 15 parts of melamine-formaldehyde resin, 25 parts of starch, 15 parts of chlorinated paraffin, 2.5 parts of butyl acetate, 1.3 parts of sodium polyphosphate, 1.4 parts of powder sand, 15 parts of calcium carbonate, 4 parts of antioxidant and 6 parts of lubricant.

Compared with the prior art, the invention has the beneficial effects that:

the extrusion-molded calcium corrugated paper is formed by placing corrugated paper pulp prepared by the corrugated paper pulp manufacturing method into a mold, and the obtained corrugated paper board has the characteristics of fire resistance, flame retardance and high temperature resistance; the corrugated board does not deform when meeting water, is not corroded by water and has the characteristics of water resistance and moisture resistance; the corrugated paper pulp has simple manufacturing method, good pulping performance of the raw materials, good quality of the obtained paper pulp, high pulping yield and high fiber bonding force, and provides excellent paper pulp raw materials for manufacturing corrugated paper.

Detailed Description

The technical solution of the present patent will be described in further detail with reference to the following embodiments.

Example 1

The extrusion molding calcium corrugated paper is manufactured by burdening, manufacturing paper pulp, manufacturing raw paper, manufacturing paper board and forming the paper board; the paper pulp comprises the following raw materials in parts by weight:

45 parts of plant fiber, 40 parts of ceramic fiber, 20 parts of aluminum hydroxide, 5-parts of urea-formaldehyde resin, 10 parts of melamine-formaldehyde resin, 20 parts of starch, 10 parts of chlorinated paraffin, 2 parts of butyl acetate, 1 part of sodium polyphosphate, 1 part of powder sand, 10 parts of calcium carbonate, 2 parts of antioxidant and 2 parts of lubricant.

Example 2

The extrusion molding calcium corrugated paper is manufactured by burdening, manufacturing paper pulp, manufacturing raw paper, manufacturing paper board and forming the paper board; the paper pulp comprises the following raw materials in parts by weight:

60 parts of plant fiber, 50 parts of ceramic fiber, 30 parts of aluminum hydroxide, 15 parts of urea-formaldehyde resin, 20 parts of melamine formaldehyde resin, 30 parts of starch, 20 parts of chlorinated paraffin, 3 parts of butyl acetate, 1.5 parts of sodium polyphosphate, 1.8 parts of powder sand, 20 parts of calcium carbonate, 6 parts of antioxidant and 10 parts of lubricant.

Example 3

The extrusion molding calcium corrugated paper is manufactured by burdening, manufacturing paper pulp, manufacturing raw paper, manufacturing paper board and forming the paper board; the paper pulp comprises the following raw materials in parts by weight:

53 parts of plant fiber, 45 parts of ceramic fiber, 25 parts of aluminum hydroxide, 10 parts of urea-formaldehyde resin, 15 parts of melamine-formaldehyde resin, 25 parts of starch, 15 parts of chlorinated paraffin, 2.5 parts of butyl acetate, 1.3 parts of sodium polyphosphate, 1.4 parts of powder sand, 15 parts of calcium carbonate, 4 parts of antioxidant and 6 parts of lubricant.

The extrusion-molded calcium corrugated paper is formed by placing corrugated paper pulp prepared by the corrugated paper pulp manufacturing method into a mold, and the obtained corrugated paper board has the characteristics of fire resistance, flame retardance and high temperature resistance; the corrugated board does not deform when meeting water, is not corroded by water and has the characteristics of water resistance and moisture resistance; the corrugated paper pulp has simple manufacturing method, good pulping performance of the raw materials, good quality of the obtained paper pulp, high pulping yield and high fiber bonding force, and provides excellent paper pulp raw materials for manufacturing corrugated paper.

Although the preferred embodiments of the present patent have been described in detail, the present patent is not limited to the above embodiments, and various changes can be made without departing from the spirit of the present patent within the knowledge of those skilled in the art.