阅读说明：本技术 一种水溶性清洗剂制作方法 (Preparation method of water-soluble cleaning agent ) 是由 莫晶 于 2020-12-08 设计创作，主要内容包括：本发明涉及清洗剂制作技术领域,且公开了一种水溶性清洗剂制作方法,由以下按照质量百分比的原料组成：十二烷基苯磺酸钠：20-40％；盐：5-20％；香精：0.2-1.5％；防腐剂：0.5-5％；全能乳化剂：2-5％；加浓缩高泡剂：1-10％；水：30-50％。该水溶性清洗剂制作方法,保证该清洗剂的制造成本有所减少,降低生产周期便于大量生产,且可以使得该清洗剂保证较低的价格具有较强的清洗能力,同时使得清洗剂的稠度与泡沫产生度均较好,产品较为稳定,不易产生分层,避免发生清洗不彻底、腐蚀基材、效率低的情况。(The invention relates to the technical field of cleaning agent preparation, and discloses a preparation method of a water-soluble cleaning agent, which comprises the following raw materials in percentage by mass: sodium dodecylbenzenesulfonate: 20 to 40 percent; salt: 5 to 20 percent; essence: 0.2 to 1.5 percent; preservative: 0.5 to 5 percent; a totipotent emulsifier: 2 to 5 percent; adding a concentrated high-foaming agent: 1 to 10 percent; water: 30-50 percent. The preparation method of the water-soluble cleaning agent ensures that the manufacturing cost of the cleaning agent is reduced to some extent, reduces the production period, is convenient for mass production, can ensure that the cleaning agent has stronger cleaning capability at lower price, simultaneously ensures that the consistency and the foam generation degree of the cleaning agent are better, has more stable products, is not easy to generate layering, and avoids the situations of incomplete cleaning, substrate corrosion and low efficiency.)

1. The preparation method of the water-soluble cleaning agent is characterized by comprising the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 20 to 40 percent;

salt: 5 to 20 percent;

essence: 0.2 to 1.5 percent;

preservative: 0.5 to 5 percent;

a totipotent emulsifier: 2 to 5 percent;

adding a concentrated high-foaming agent: 1 to 10 percent;

water: 30-50 percent.

2. The preparation method of the water-soluble cleaning agent as claimed in claim 1, wherein the water-soluble cleaning agent is prepared from the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 20 percent;

salt: 5 percent;

essence: 0.2 percent;

preservative: 0.5 percent;

a totipotent emulsifier: 2 percent;

adding a concentrated high-foaming agent: 1 percent;

water: 71.3 percent.

3. The method for preparing a water-soluble cleaning agent according to claim 1, wherein the method comprises the following steps: the composite material consists of the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 30 percent;

salt: 12 percent;

essence: 1.9 percent;

preservative: 2.8 percent;

a totipotent emulsifier: 3.5 percent;

adding a concentrated high-foaming agent: 5 percent;

water: 74.8 percent.

4. The method for preparing a water-soluble cleaning agent according to claim 1, wherein the method comprises the following steps: the composite material consists of the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 40 percent;

salt: 20 percent;

essence: 1.5 percent;

preservative: 5 percent;

a totipotent emulsifier: 5 percent;

adding a concentrated high-foaming agent: 10 percent;

water: 18.5 percent.

5. A method for preparing the water-soluble cleaning agent as claimed in any one of claims 1 to 4, which comprises the following steps:

the first step is as follows: preparing raw materials, respectively weighing the following raw materials: sodium dodecyl benzene sulfonate, salt, essence, preservative, all-round emulsifier, concentrated high-foaming agent and water;

the second step is that: mixing sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water, and stirring uniformly;

the third step: placing the mixed material of sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water into a reaction kettle, and heating and stirring at the temperature of 40-78 ℃ to prepare a heat treatment material;

the fourth step: standing the heat-treated material at 50-70 deg.C for 0.5-2h, cooling to 7-15 deg.C, standing for 1-3 days, and packaging to obtain water-soluble cleaning agent.

6. The method for preparing a water-soluble cleaning agent according to claim 1, wherein the method comprises the following steps: the essence can be aloe, lemon or osmanthus essence.

7. The method for preparing a water-soluble cleaning agent according to claim 1, wherein the method comprises the following steps: and the heating and stirring treatment time in the third step is 2-40 min.

Technical Field

The invention relates to the technical field of cleaning agent preparation, in particular to a preparation method of a water-soluble cleaning agent.

Background

The cleaning agent is a liquid ceramic tile cleaning agent which is mainly prepared by a surfactant, a bactericide, a polishing agent, an imported penetrating agent, a unique brightness factor and other environmental protection technologies; has the characteristics of strong decontamination capability, permeability, bactericidal power, polishing brightness and the like. Can rapidly and thoroughly remove stubborn dirt on the surfaces and in gaps of various ceramic tiles. The unique permeability and polishing brightness factor can remove lime scale, cement scale, joint mixture scale, water rust, electric welding mark, aluminum scratch, metal scratch, black scale, mildew scale, water scale, various paints, various adhesives, various heavy oil stains and the like more rapidly, and when the polishing agent is coated on the surface of a cleaning object, the polishing agent is combined with the dirt or is melted, but the residue of the cleaning agent needs to be cleaned by running water. The water-saving detergent can use the characteristics of the detergent to save water with little or no water.

The existing cleaning agent is too high in manufacturing cost, long in production period, low in price, not strong in oil removal, poor in consistency and foam generation degree, poor in cleaning degree, unstable in product and easy to stratify, and meanwhile the problems of incomplete cleaning, substrate corrosion, low efficiency and the like of the product can occur.

Disclosure of Invention

Aiming at the defects of the prior art, the invention provides a preparation method of a water-soluble cleaning agent, which ensures that the manufacturing cost of the cleaning agent is reduced to some extent, reduces the production period, is convenient for mass production, ensures that the cleaning agent has stronger cleaning capability at lower price, simultaneously has the advantages of better consistency and foam generation degree, more stable product and the like, and solves the problems of overhigh manufacturing cost, longer production period, low price, weak oil removal, poor consistency and foam generation degree, poor cleaning degree, unstable product, easy layering, incomplete cleaning, substrate corrosion and low efficiency of the product.

In order to realize the purposes of ensuring that the manufacturing cost of the cleaning agent is reduced to some extent, reducing the production period and facilitating mass production, ensuring that the cleaning agent has lower price and stronger cleaning capability, and simultaneously ensuring that the consistency and the foam generation degree of the cleaning agent are both better and the product is more stable, the invention provides the following technical scheme: a preparation method of a water-soluble cleaning agent comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 20 to 40 percent;

salt: 5 to 20 percent;

essence: 0.2 to 1.5 percent;

preservative: 0.5 to 5 percent;

a totipotent emulsifier: 2 to 5 percent;

adding a concentrated high-foaming agent: 1 to 10 percent;

water: 30-50 percent.

Preferably, the material comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 20 percent;

salt: 5 percent;

essence: 0.2 percent;

preservative: 0.5 percent;

a totipotent emulsifier: 2 percent;

adding a concentrated high-foaming agent: 1 percent;

water: 71.3 percent.

Preferably, the material comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 30 percent;

salt: 12 percent;

essence: 1.9 percent;

preservative: 2.8 percent;

a totipotent emulsifier: 3.5 percent;

adding a concentrated high-foaming agent: 5 percent;

water: 74.8 percent.

Preferably, the material comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 40 percent;

salt: 20 percent;

essence: 1.5 percent;

preservative: 5 percent;

a totipotent emulsifier: 5 percent;

adding a concentrated high-foaming agent: 10 percent;

water: 18.5 percent.

Preferably, the preparation method of the water-soluble cleaning agent comprises the following steps:

the first step is as follows: preparing raw materials, respectively weighing the following raw materials: sodium dodecyl benzene sulfonate, salt, essence, preservative, all-round emulsifier, concentrated high-foaming agent and water;

the second step is that: mixing sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water, and stirring uniformly;

the third step: placing the mixed material of sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water into a reaction kettle, and heating and stirring at the temperature of 40-78 ℃ to prepare a heat treatment material;

the fourth step: standing the heat-treated material at 50-70 deg.C for 0.5-2h, cooling to 7-15 deg.C, standing for 1-3 days, and packaging to obtain water-soluble cleaning agent.

Preferably, the essence can be aloe, lemon or osmanthus essence.

Preferably, the heating and stirring treatment time in the third step is 2-40 min.

Compared with the prior art, the invention provides a preparation method of a water-soluble cleaning agent, which has the following beneficial effects:

the preparation method of the water-soluble cleaning agent comprises the steps of mixing sodium dodecyl benzene sulfonate, salt, essence, preservative, all-round emulsifier, concentrated high-foaming agent and water, uniformly stirring, then placing the mixed material of the sodium dodecyl benzene sulfonate, the salt, the essence, the preservative, the all-round emulsifier, the concentrated high-foaming agent and the water into a reaction kettle, heating and stirring at the temperature of 40-78 ℃ to prepare a heat treatment material, wherein the heating and stirring time is 2-40min, standing the heat treatment material at the temperature of 50-70 ℃ for 0.5-2h, cooling to the temperature of 7-15 ℃, standing for 1-3 days, subpackaging to obtain the water-soluble cleaning agent, ensuring that the manufacturing cost of the cleaning agent is reduced, reducing the production period, facilitating mass production, ensuring that the cleaning agent has relatively low price and relatively strong cleaning capability, meanwhile, the consistency and the foam generation degree of the cleaning agent are good, the product is stable, layering is not easy to generate, and the situations of incomplete cleaning, substrate corrosion and low efficiency are avoided.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the contents of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

A preparation method of a water-soluble cleaning agent comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 20 to 40 percent;

salt: 5 to 20 percent;

essence: 0.2 to 1.5 percent;

preservative: 0.5 to 5 percent;

a totipotent emulsifier: 2 to 5 percent;

adding a concentrated high-foaming agent: 1 to 10 percent;

water: 30-50 percent.

Example 1

A preparation method of a water-soluble cleaning agent comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 20 percent;

salt: 5 percent;

essence: 0.2 percent;

preservative: 0.5 percent;

a totipotent emulsifier: 2 percent;

adding a concentrated high-foaming agent: 1 percent;

water: 71.3 percent.

The preparation method of the water-soluble cleaning agent comprises the following steps:

the first step is as follows: preparing raw materials, respectively weighing the following raw materials: sodium dodecyl benzene sulfonate, salt, essence, preservative, all-round emulsifier, concentrated high-foaming agent and water; the second step is that: mixing sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water, and stirring uniformly; the third step: placing the mixed material of sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water into a reaction kettle, heating and stirring at the temperature of 40-78 ℃ to prepare a heat treatment material, wherein the heating and stirring treatment time is 2-40 min; the fourth step: standing the heat-treated material at 50-70 deg.C for 0.5-2h, cooling to 7-15 deg.C, standing for 1-3 days, and packaging to obtain water-soluble cleaning agent.

Example 2

A preparation method of a water-soluble cleaning agent comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 30 percent;

salt: 12 percent;

essence: 1.9 percent;

preservative: 2.8 percent;

a totipotent emulsifier: 3.5 percent;

adding a concentrated high-foaming agent: 5 percent;

water: 74.8 percent.

The preparation method of the water-soluble cleaning agent comprises the following steps:

the first step is as follows: preparing raw materials, respectively weighing the following raw materials: sodium dodecyl benzene sulfonate, salt, essence, preservative, all-round emulsifier, concentrated high-foaming agent and water; the second step is that: mixing sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water, and stirring uniformly; the third step: placing the mixed material of sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water into a reaction kettle, heating and stirring at the temperature of 40-78 ℃ to prepare a heat treatment material, wherein the heating and stirring treatment time is 2-40 min; the fourth step: standing the heat-treated material at 50-70 deg.C for 0.5-2h, cooling to 7-15 deg.C, standing for 1-3 days, and packaging to obtain water-soluble cleaning agent.

Example 3

A preparation method of a water-soluble cleaning agent comprises the following raw materials in percentage by mass:

sodium dodecylbenzenesulfonate: 40 percent;

salt: 20 percent;

essence: 1.5 percent;

preservative: 5 percent;

a totipotent emulsifier: 5 percent;

adding a concentrated high-foaming agent: 10 percent;

water: 18.5 percent.

The preparation method of the water-soluble cleaning agent comprises the following steps:

the first step is as follows: preparing raw materials, respectively weighing the following raw materials: sodium dodecyl benzene sulfonate, salt, essence, preservative, all-round emulsifier, concentrated high-foaming agent and water; the second step is that: mixing sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water, and stirring uniformly; the third step: placing the mixed material of sodium dodecyl benzene sulfonate, salt, essence, preservative, omnipotent emulsifier, concentrated high foaming agent and water into a reaction kettle, heating and stirring at the temperature of 40-78 ℃ to prepare a heat treatment material, wherein the heating and stirring treatment time is 2-40 min; the fourth step: standing the heat-treated material at 50-70 deg.C for 0.5-2h, cooling to 7-15 deg.C, standing for 1-3 days, and packaging to obtain water-soluble cleaning agent.

In summary, through comparison of data analysis of the embodiment 1, the embodiment 2, and the embodiment 3, it can be seen that the embodiment 2 can reduce consumption of raw materials to the greatest extent while ensuring cleaning ability of the cleaning machine, save cost, enable the cleaning agent to ensure lower price and have stronger cleaning ability, and enable consistency and foam generation degree of the cleaning agent to be better, the product is more stable, and delamination is not easy to occur.

It is noted that, herein, relational terms such as first and second, and the like may be used solely to distinguish one entity or action from another entity or action without necessarily requiring or implying any actual such relationship or order between such entities or actions. Also, the terms "comprises," "comprising," or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus.

Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.