阅读说明：本技术 超高熔体流动性苯乙烯类嵌段共聚物 (Styrenic block copolymers with ultra-high melt flow ) 是由 J·E·弗拉德 X·穆伊德尔曼斯 于 2019-03-21 设计创作，主要内容包括：本发明涉及具有高乙烯基含量、低粘度、低有序-无序温度和改进的加工性能的氢化苯乙烯类嵌段共聚物。氢化苯乙烯类嵌段共聚物可以与最少的添加剂一起挤出或模塑。氢化苯乙烯类嵌段共聚物具有高熔体流动性,从而易于加工,例如注塑、包覆成型、浸渍、挤出、滚塑、搪塑、纤维纺丝、薄膜制造、3D打印和发泡。(The present invention relates to hydrogenated styrenic block copolymers having high vinyl content, low viscosity, low order-disorder temperature and improved processability. The hydrogenated styrenic block copolymer can be extruded or molded with minimal additives. Hydrogenated styrenic block copolymers have high melt flow properties and are therefore easy to process, such as injection molding, overmolding, dipping, extrusion, rotomolding, slush molding, fiber spinning, film making, 3D printing, and foaming.)

1. Having S blocks and E or E₁Block and having the general formula: S-E-S, (S-E)₁)_nA selectively hydrogenated block copolymer of X or a mixture thereof, wherein n has a value of 2 to 6, X is a coupling agent residue, and the molecular weight of the S block is 4,400-5,600 g/mol;

the block copolymer has a solution viscosity of less than 80cP, a polystyrene content in the block copolymer is 25-40 wt%, and up to 50 wt% of the diblock units in the block copolymer have the general formula S-E or S-E₁；

Wherein, prior to hydrogenation:

the S block is a polystyrene block;

the E block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, having a molecular weight of 18,000-26,000 g/mol;

E₁the block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, having a molecular weight of 9,000-13,000 g/mol;

the total vinyl content of the polydiene block is 60-85%; and

wherein, after hydrogenation:

0 to 10% of the styrene double bonds in the block copolymer are reduced, and

at least 80% of the conjugated diene double bonds in the block copolymer are reduced.

2. The block copolymer of claim 1, wherein the order-disorder temperature (ODT) of the block copolymer is less than 230 ℃.

3. The block copolymer of any one of claims 1-2, whereinThe block copolymer has the formula S-E-S, which contains less than 10 wt% of a diblock copolymer of the formula S-E, or has the formula (S-E)₁)_nX, which contains 5 to 50 wt.% of a compound of the formula S-E₁The diblock copolymer of (1).

4. The block copolymer of any one of claims 1-2, wherein the coupling agent is selected from the group consisting of methyl benzoate, silicon tetrachloride, alkoxysilanes, polyepoxides, polyisocyanates, polyimines, polyaldehydes, polyketones, polyanhydrides, polyesters, polyhalides, diesters, methoxysilanes, divinylbenzene, 1,3, 5-benzenetricarbonyl chloride, glycidoxypropyltrimethoxysilane, and oxydipropylbis (trimethoxysilane), and mixtures thereof.

5. The block copolymer of any of claims 1-2, wherein the block copolymer has a solution viscosity of the formula S-E-S and 10-80cP, or has the formula (S-E)₁)_nX and a solution viscosity of 10-50 cP.

6. The block copolymer of any of claims 1-2, wherein the melt index of the block copolymer is 80-600g/10min at 190 ℃ and 2.16kg weight.

7. The block copolymer of any of claims 1-2, wherein the block copolymer has an elongation at break of at least 300%.

8. The block copolymer of claim 1, wherein the tensile strength of the block copolymer is at least 4 MPa.

9. The block copolymer of claim 1, wherein the block copolymer is functionalized with a functional group selected from the group consisting of: fumaric acid, itaconic acid, citraconic acid, acrylic acid, maleic anhydride, itaconic anhydride, citraconic anhydride and derivatives thereof.

10. An adhesive composition comprising:

0 to about 80 wt% of a polyalphaolefin

10 to about 60 weight percent of a tackifying resin, and

10 to about 50 weight percent of the hydrogenated block copolymer of claim 1.

11. A composition, comprising:

the selectively hydrogenated block copolymer of claim 1;

0.001 to 90 wt% of an additive selected from the group consisting of olefin polymers, thermoplastic polyurethanes, thermoplastic copolyesters, styrenic polymers, thermoplastic elastomers, tackifying resins, polymer extender oils, waxes, fillers, lubricants, stabilizers, engineering thermoplastic resins, and mixtures thereof.

12. The composition of claim 11, wherein the additive is a high flow polyolefin having a melt flow rate >40g/10 min.

13. The composition of claim 11 wherein the order-disorder temperature (ODT) of the selectively hydrogenated block copolymer is 140-230 ℃.

14. An article comprising the composition of claim 11, wherein the article is selected from the group consisting of toys, medical devices, films, pipes, profiles, 3D printed articles, sheets, coatings, tapes, strips, moldings, pipes, foams, tapes, fabrics, threads, filaments, ribbons, fibers, webs, overmolded automotive parts, dipped articles, sheet molded articles, hot melt adhesives, tie layers, roofing shingles, films, tire treads, and tire innerlayers, and

wherein the article is formed by injection molding, overmolding, dipping, extrusion, rotational molding, slush molding, fiber spinning, film forming, 3D printing, or foaming.

15. A composition, comprising:

having S blocks and E or E₁Is blocked andhaving the formula S-E-S, (S-E)₁)_nA selectively hydrogenated block copolymer of X or a mixture thereof, wherein n has a value of 2 to 6, X is the residue of a coupling agent, said block copolymer having a styrene content of 29 to 37 weight percent and a viscosity of 10 to 80 cP;

wherein, prior to hydrogenation:

the S block is a polystyrene block and the S block is,

the E block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, having a molecular weight of 18,000-26,000g/mol,

E₁the block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, having a molecular weight of 9,000-13,000g/mol,

the total vinyl content of the polydiene block is 70-85%.

Wherein, after hydrogenation:

0-10% of the styrene double bonds have been hydrogenated;

wherein the block copolymer comprises as grafting monomers from 0.1 to 10 wt% of a functional group selected from the group consisting of: fumaric acid, itaconic acid, citraconic acid, acrylic acid, maleic anhydride, itaconic anhydride, citraconic anhydride and derivatives thereof, and

wherein the selectively hydrogenated block copolymer has an order-disorder temperature (ODT) of less than 230 ℃.

Technical Field

The present invention relates to hydrogenated block copolymers and articles made therefrom.

Background

Summary of The Invention

In one aspect, a hydrogenated styrenic block copolymer is disclosed. The selectively hydrogenated block copolymer has an S block and E or E₁A block, and the general formula: S-E-S, (S-E)₁)_nX or a mixture thereof, wherein n is a value of 2 to 6, X is a coupling agent residue, the molecular weight of the S block is 4,400-5,600g/mol, the solution viscosity of the block copolymer is less than 80 centipoise (cP), the polystyrene content in the block copolymer is of the formula S-E or S-E₁From 25 to 40 wt% up to 50 wt% of diblock units in the block copolymer of (a); wherein the S block, prior to hydrogenation, is a polystyrene block, the E block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene and mixtures thereof, having a molecular weight of 18,000-26,000g/mol, E₁The block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, having a molecular weight of 9,000-13,000g/mol,the total vinyl content of the polydiene block is 60-85%; and wherein after hydrogenation, from 0 to 10% of the styrene double bonds in the block copolymer are reduced, and at least 80% of the conjugated diene double bonds in the block copolymer are reduced.

In another aspect, the invention relates to an article made from the composition, the article being selected from the group consisting of films, 3D printed articles, sheets, coatings, tapes, strips, profiles, moldings, pipes, foams, tapes, fabrics, threads, filaments, ribbons, fibers and webs, and tires.

In another aspect, the article is made by direct extrusion, which can be used alone or in a laminate structure with multiple other layers. In another aspect, the article is a transparent flexible part prepared by any one of injection molding, slush molding, rotational molding, compression molding, and dipping.

Detailed Description

Unless otherwise indicated, the following terms shall have the following meanings.

"vinyl content" refers to the content of conjugated diene by 1, 2-addition polymerization in the case of butadiene or by 1, 2-addition and 3, 4-addition polymerization in the case of isoprene.

The "polystyrene content" or PSC of a block copolymer refers to the wt% of polymerized styrene in the block copolymer, calculated by dividing the sum of the molecular weights of all polystyrene blocks by the total molecular weight of the block copolymer. The PSC can be determined using any suitable method, such as proton Nuclear Magnetic Resonance (NMR).

"molecular weight" refers to the peak molecular weight (Mp) in g/mol of the polymer under consideration as measured by GPC using polystyrene calibration standards of known number average molecular weight. Mp is the molecular weight of the standard at the maximum peak.

The order-disorder transition temperature (ODT) refers to the temperature at which the domain structure of the block copolymer begins to disappear. ODT is defined as the temperature above which zero shear viscosity can be measured by dynamic rheology. ODT temperature may be measured using Dynamic Mechanical Analysis (DMA) and temperature sweeps are made over various frequencies, where ODT is determined as the temperature at which the complex viscosity begins to collapse to a single value regardless of the low frequency.

"melt index" is a measure of the melt flow of a polymer according to ASTM D1238 at 190 ℃ and 2.16kg weight, expressed as grams of polymer passing through the melt rheometer orifice in 10 minutes.

ASTM D412 is a test method for determining the tensile properties of thermoplastic elastomers and vulcanized thermosets. Dumbbells and straight bar coupons or cut ring coupons may be used. In the test, a Mini D die having a dumbbell center width of 0.1 inch and a parallel narrow side center portion of 0.5 inch in length was used to cut the sample, and a drawing rate of 50mm/min was used.

Block copolymer composition: in one embodiment, the composition comprises a copolymer having an S block and either E or E₁Block and having the general formula S-E-S, (S-E)₁)_nA selectively hydrogenated block copolymer of X or a mixture thereof, n having a value of 2 to 6, or 2 to 4, or 2. The block copolymers may be linear sequences or coupled with 2-6 arms. In one embodiment, the hydrogenated block copolymer of the formula S-E-S has less than 10 weight percent of diblock copolymer of the formula S-E, while the formula (S-E)₁)_nThe block copolymer of X has a formula (S-E) of 5 to 40 wt%₁) The diblock copolymer of (1).

Prior to hydrogenation, the S block of the block copolymer may be a polystyrene block having a molecular weight of 4,400-5,600.

Before hydrogenation, E block or E₁The block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof. In one embodiment, the E block is a single polydiene block. The molecular weight of these polydiene blocks may be 18,000-26,000. E₁The block is a polydiene block with a molecular weight of 9,000-13,000.

In one embodiment, the linear sequence configuration has the formula S-E-S, wherein the E block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, and has a molecular weight of 18,000-26,000.

The general formula of the coupling configuration includes:S-E₁–X–E₁-S, and

wherein E₁The block is a polydiene block selected from the group consisting of polybutadiene, polyisoprene, and mixtures thereof, having a molecular weight of 9,000-13,000, and X is an alkoxysilane coupling agent residue.

The block copolymer may be prepared by using an at least bifunctional coupling agent. The linearly coupled block copolymer is made by forming a first S block and an E block, and then contacting the diblock with a bifunctional coupling agent. Radial block copolymers can be prepared by using at least trifunctional coupling agents. An example of a bifunctional coupling agent is methyl benzoate. Other coupling agents that may be used to form the radial block copolymer include, for example, silicon tetrachloride and alkoxysilanes, polyepoxides, polyisocyanates, polyimines, polyaldehydes, polyketones, polyanhydrides, polyesters, polyhalides, diesters, methoxysilanes, divinylbenzene, 1,3, 5-benzenetricarboxylic acid chloride, glycidoxypropyltrimethoxysilane, and oxydipropylbis (trimethoxysilane).

In one embodiment, the coupling agent is of the formula R_x-Si-(OR')_yWherein x is 0 or 1, x + y is 3 or 4, R and R 'are the same or different, R is selected from the group consisting of arylalkyl, straight chain alkyl and branched alkyl, and R' is selected from the group consisting of straight chain and branched alkyl. The aryl group preferably has 6 to 12 carbon atoms. The alkyl group preferably has 1 to 12 carbon atoms, more preferably 1 to 4 carbon atoms. Under melt conditions, these alkoxysilane coupling agents can be further coupled to give functionalities greater than 3. Examples of trialkoxysilanes include methyltrimethoxysilane (MTMS), Methyltriethoxysilane (MTES), Isobutyltrimethoxysilane (IBTMO) and phenyltrimethoxysilane (PhTMO). Preferred dialkoxysilanes are dimethyldimethoxysilane (DMDMS), dimethyldiethoxysilane (DMDES) and Methyldiethoxysilane (MDES).

Preparation of block copolymer: the block copolymer may be prepared by styreneAn alkene and a diene selected from butadiene, isoprene and mixtures thereof. The polymerization is accomplished by contacting the styrene and diene monomers with an organic alkali metal compound in a suitable solvent at a temperature of from-150 ℃ to 300 ℃, preferably 0-100 ℃. Examples of anionic polymerization initiators include those having the general formula RLi_nWherein R is an aliphatic, alicyclic, aromatic or alkyl-substituted aromatic hydrocarbon group having 1 to 20 carbon atoms, and n is 1 to 4. Preferred initiators include n-butyllithium and sec-butyllithium. Methods of anionic polymerization can be found in U.S. Pat. No. 4,039,593 and U.S. reissue patent No. re27,145, which are incorporated herein by reference.

In one embodiment, the linear sequential block copolymer may be prepared by polymerizing styrene to form a first S block, adding a diene to form an E block, and then adding additional styrene to form a second S block.

In another embodiment, by forming the first S block and E₁The block, and then contacting the diblock with a difunctional or trifunctional coupling agent to prepare a coupled block copolymer. The method comprises the step of₁-a coupling reaction between a living polymer of Li and a coupling agent as defined above, wherein Li is lithium.

Relative to the living polymer S-E₁The amount of Li present, the amount of coupling agent used depends mainly on the degree of coupling and on the desired properties of the coupled polymer. Preferably, the coupling agent is used in an amount of 0.35 to 0.7 moles of coupling agent per mole of lithium, or preferably 0.4 to 0.55 moles of coupling agent per mole of lithium, or most preferably 0.45 moles of coupling agent per mole of lithium.

The temperature at which the coupling reaction is carried out can vary within wide limits and is generally the same as the polymerization temperature, for example from 0 to 150 ℃, from 30 to 100 ℃ or from 55 to 80 ℃.

The coupling reaction is generally carried out by simply mixing the coupling agent, neat or in solution, with the living polymer solution. The reaction time may be short and is affected by the mixing rate in the reactor, e.g. 1 minute to 1 hour. Longer coupling times may be required at lower temperatures.

Following the coupling reaction, the attached polymer may be recovered, or the diene portion of the polymer may be selectively hydrogenated. Hydrogenation generally improves the thermal stability, uv stability, oxidative stability and weatherability of the final polymer.

Hydrogenation of block copolymer: in one embodiment, the block copolymer is a hydrogenated block copolymer. The block copolymers can be selectively hydrogenated using the hydrogenation processes disclosed in U.S. Pat. nos. 3,494,942, 3,634,594, 3,670,054, 3,700,633 and RE27,145, which are incorporated herein by reference. Any hydrogenation method that is selective for the double bonds in the conjugated polydiene block such that the aromatic unsaturation in the polystyrene block remains substantially intact can be used to prepare the hydrogenated block copolymer.

In one embodiment, the process employs a catalyst or catalyst precursor comprising a metal (e.g., nickel or cobalt) and a suitable reducing agent, such as an aluminum alkyl. Titanium-based systems are also useful. Hydrogenation can be accomplished in a solvent at a temperature of 20-100 ℃ and a hydrogen partial pressure of 100-. A catalyst concentration of 10 to 500ppm by weight of iron group metal based on the total solution is generally used and contacted under hydrogenation conditions for 60 to 240 minutes. After the hydrogenation is complete, the catalyst and catalyst residues will be separated from the polymer.

To E and/or E₁The large amount of vinyl groups in the block, during polymerization of the diene, can be controlled using art-known control agents, such as diethyl ether and diethoxypropane, to control the microstructure associated with the block copolymer, as disclosed in U.S. Pat. No. Re27,145 and U.S. Pat. No. 5,777,031, which are incorporated by reference.

The hydrogenation may be carried out under conditions such that at least 80% of the conjugated diene double bonds are reduced and at most 10% of the arene double bonds are reduced.

Preparing the block copolymers so that they are at E and/or E before hydrogenation₁The block has 60-85% vinyl groups.

The styrene content of the block copolymer is 25 to 40 wt%. In one embodiment, the coupling efficiency is 50-95%, and in a second embodiment, the coupling efficiency is at least 80%. In some embodiments, after hydrogenation, 0-10% of the styrene double bonds in the S blocks have been hydrogenated.

Functionalization of block copolymers: in some embodiments, the hydrogenated block copolymer is functionalized to include additional functional groups or moieties. Exemplary monomers grafted onto the block copolymer include fumaric acid, itaconic acid, citraconic acid, acrylic acid, maleic anhydride, itaconic anhydride, citraconic anhydride, and derivatives thereof. The preferred grafting monomer is maleic anhydride.

In one embodiment, the hydrogenated block copolymer is maleated by grafting maleic anhydride onto the block copolymer. The maleation of the block copolymers can be carried out in the melt, in solution, or in the solid state, and the process can be continuous or batch-wise. Various free radical initiators, including peroxides and azo compounds, may be used to promote maleation. In some embodiments, the block copolymer comprises 0.1 to 10 weight percent, preferably 0.2 to 5 weight percent, of the graft monomer.

In one embodiment, the hydrogenated styrenic block copolymer is functionalized by reaction with maleic anhydride. Such functionalized polymers have added polarity, which makes them useful where adhesion to metals or other polar polymers is desired, for example in overmolding, tie layers, adhesive and coating applications, or in compatibility with certain engineering thermoplastics (e.g., polyamides or epoxies).

Optional components: in use, the block copolymer composition may also be mixed with other block copolymers, olefin polymers, styrene polymers, tackifying resins, end block resins, engineering thermoplastic resins, and mixtures thereof.

Styrene polymers include, for example, crystalline polystyrene, high impact polystyrene, medium impact polystyrene, styrene/acrylonitrile copolymers, styrene/acrylonitrile/butadiene (ABS) polymers, syndiotactic polystyrene, and styrene/olefin copolymers. Examples of other polymers include polyisobutylene polymers, essentially random ethylene/styrene or propylene/styrene copolymers, preferably containing at least 20 wt% copolymerized styrene monomer; styrene grafted polypropylene polymer; and other block copolymers such as styrene-diene-styrene triblock, radial or radial block polymers, styrene-diene diblock polymers, and hydrogenated versions of these polymers.

Examples of engineering thermoplastic resins include thermoplastic polyesters, thermoplastic polyurethanes, poly (aryl ethers), poly (aryl sulfones), acetal resins, polyamides, nitrile barrier resins, poly (methyl methacrylate), cyclic olefin copolymers, coumarone-indene resins, polyindene resins, poly (methylindene) resins, polystyrene resins, vinyltoluene-alphamethylstyrene resins, alphamethylstyrene resins and polyphenylene ethers, particularly poly (2, 6-dimethyl-1, 4-phenylene ether), and mixtures thereof.

Suitable mid-block compatible resins are C5 resins ((matrix resins of cyclopentadiene, cyclopentene, DCPD, piperylene, etc.), hydrogenated C5 resins, hydrogenated C5/C9 resins, hydrogenated C9 resins, terpene resins, rosin ester resins, hydrogenated rosin ester resins, or combinations thereof.

In some embodiments, the hydrogenated block copolymer is blended with a thermoplastic elastomer or thermoplastic for use in a tire tread formulation as a plasticizer.

In some embodiments, the optional polymer is an olefin polymer, such as ethylene homopolymers, ethylene/alpha-olefin copolymers, propylene homopolymers, propylene/alpha-olefin copolymers, high impact polypropylene, butene homopolymers, butene/alpha-olefin copolymers, and other alpha-olefin copolymers or interpolymers. In other embodiments, the polymer is selected from ethylene/acrylic acid (EAA) copolymers, ethylene/methacrylic acid (EMAA) ionomers, ethylene/vinyl acetate (EVA) copolymers, ethylene/vinyl alcohol (EVOH) copolymers, ethylene/cyclic olefin copolymers, polypropylene homopolymers and copolymers, propylene/styrene copolymers, ethylene/propylene copolymers, polybutylene, ethylene carbon monoxide interpolymers (e.g., ethylene/carbon monoxide (ECO) copolymers, ethylene/acrylic acid/carbon monoxide terpolymers, etc.).

Additive: the block copolymer compositions are characterized by low viscosity and high melt flow, which makes them easy to mold or continuously extrude into shapes or films or spun fibers. This property allows the end user to avoid or at least limit the use of additives that can degrade performance, cause area contamination, smoke, and even build up on the mold and die. Although hydrogenated block copolymers have such low ODT and high melt index that they can be used to prepare articles without the use of processing aids, it is sometimes desirable to use such aids and other additives. Examples include polymer extender oils, waxes, fillers, reinforcing agents, lubricants, stabilizers, and mixtures thereof. In some embodiments, the additive is selected from one or more fillers, such as TiO₂、CaCO₃Carbon black or other pigments.

In one embodiment, the hydrogenated block copolymer is mixed with 0.001 to 10 wt% mineral oil (paraffin, naphthene or aromatic) or 0.001 to 9 wt%, 0.001 to 7.5 wt% and 0.001 to 5 wt% mineral oil.

Properties of the block copolymer: one feature of the hydrogenated block copolymers is that they have a low order-disorder temperature (ODT), which is typically less than 230 ℃. For ODT above 230 ℃, the polymer is more difficult to process, although in some cases ODT greater than 230 ℃ may be useful for certain applications, for example, when the block copolymer is combined with other components to improve processing. Such other components may be thermoplastic polymers, oils, resins, waxes, and the like. In some embodiments, the ODT is 150-.

In some embodiments, the hydrogenated block copolymer has a high melt index to allow for ease of processing, 80 to 600g/10min at 190 ℃ and 2.16kg weight.

In some embodiments, the hydrogenated block copolymer has a toluene solution viscosity (at 25 wt% and 25 ℃) greater than 10cP, or less than 80CP, or 15 to 80cP, or 20 to 50 cP.

In some embodiments, the hydrogenated block copolymer has an elongation at break of at least 300% or to 450%.

In some embodiments, the hydrogenated block copolymer has a tensile strength of at least 4MPa, or at least 6MPa, or equal to or less than 9MPa, as measured on a compression molded film according to ASTM D412.

In some embodiments, the hydrogenated block copolymer has a hysteresis recovery of greater than 35% and a permanent set of less than 35% in the first recovery cycle after elongation to 300%.

Industrial applicability: the hydrogenated block copolymers are widely used in various applications in the form of pure polymers or as a batch. Examples include, for example, toys, medical devices, films, pipes, profiles, 3D printed articles, sheets, coatings, tapes, strips, moldings, pipes, foams, tapes, fabrics, threads, filaments, ribbons, fibers, multiple fibers and webs, over-molding applications for automotive parts, impregnated products for gloves and the like, thermosetting applications (such as sheet molding compounds or bulk molding compounds for pallets), hot melt adhesives, tie layers for functionalized polymers, asphalt formulations, roofing shingles, geomembrane applications. The article may be formed in a process including injection molding, overmolding, dipping, extrusion, rotational molding, slush molding, fiber spinning, film forming, 3D printing, and foaming. In some embodiments, the hydrogenated block copolymer is added to a rubber composition for use in the manufacture of a tire tread or inner layer.

In some embodiments, the hydrogenated block copolymers are used to make a web layer for use in constructing absorbent personal hygiene products such as baby diaper articles, adult incontinence articles, or sanitary napkin articles. In applications such as meltblown articles, the composition may comprise high flow polyolefins having a melt flow rate >40g/10min, polyisobutylene, polybutene, thermoplastic polyurethanes, thermoplastic copolyesters, oils, styrenic block copolymers having a melt flow rate less than 100g/10min, and/or mid-block or end-block resins.

In some embodiments, the hydrogenated block copolymer is used as an additive, e.g., a plasticizer, to a thermoplastic composition or thermoplastic elastomer in an amount of 0.1 to 90 weight percent, or 0.5 to 70 weight percent, or 1 to 50 weight percent, or 5 to 35 weight percent, based on the total weight of the thermoplastic or thermoplastic elastomer composition.

In some embodiments, the hydrogenated block copolymers are used in adhesive formulations, for example, personal hygiene construction adhesives, elastic attachment adhesives, and hot melt adhesives. The formulation may comprise, for example, a blend of 0 to about 80 weight percent of a polyalphaolefin, 10 to about 60 weight percent of a tackifying resin, and 10 to about 50 weight percent of a hydrogenated block copolymer. Examples of tackifying resins include C5 resins (matrix resins of cyclopentadiene, cyclopentene, DCPD, piperylene, and the like), hydrogenated C5 resins, hydrogenated C5/C9 resins, hydrogenated C9 resins, terpene resins, rosin ester resins, hydrogenated rosin ester resins, or combinations thereof.

Examples

The following examples are provided to illustrate the disclosure herein.