阅读说明：本技术 半导体传感器的表面处理 (Surface treatment of semiconductor sensors ) 是由 R.L.西塞罗 M.格雷泽 Y.王 C.E.英曼 J.格雷 J.科斯辛斯基 J.鲍尔 于 2015-07-01 设计创作，主要内容包括：传感器组件包括传感器,其包括传感器表面；以及与所述传感器合作并暴露所述传感器表面的反应位点。所述反应位点包括反应位点表面。表面剂结合于所述反应位点表面或所述传感器表面。所述表面剂包括与所述反应位点表面或所述传感器表面上的布忍司特碱或路易斯酸官能团反应的表面活性官能团并包括不具有供电子对的远端官能团。(The sensor assembly includes a sensor including a sensor surface; and a reaction site cooperating with the sensor and exposing the sensor surface. The reaction sites include reaction site surfaces. A surface agent is bound to the reaction site surface or the sensor surface. The surfactant includes a surface active functional group that reacts with a Bronsted base or Lewis acid functional group on the reaction site surface or the sensor surface and includes a distal functional group that does not have an electron donating pair.)
1. A sensor assembly comprising
A sensor comprising a sensor surface;
a reaction site cooperating with the sensor and exposing the sensor surface, the reaction site comprising a reaction site surface; and
a surfactant bound to the reaction site surface or the sensor surface, the surfactant comprising surface active functional groups that react with the Bronsted base or Lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups that do not have an electron donor pair.
2. The sensor of claim 1, wherein the surface active functional group comprises a silane, a phosphate, a phosphonic acid, a phosphinic acid, a diphosphinic acid, an isocyanate, a catechol, a hydroxamate, an alkoxy derivative thereof, or any combination thereof.
3. The sensor of claim 2, wherein the surface active functional group comprises a silane or an alkoxy derivative thereof.
4. The sensor of claim 2, wherein the surface active functional group comprises a phosphate ester, a phosphonic acid, a phosphinic acid, a diphosphinic acid, alkoxy derivatives thereof, or any combination thereof.
5. The sensor of claim 2, wherein the surface active functional groups comprise isocyanates, catechols, hydroxamates, alkoxy derivatives thereof, or any combination thereof.
6. The sensor of claim 2, wherein the distal functional group comprises an alkyl group or a quaternary ammonium.
7. The sensor of claim 6, wherein the quaternary amine is derived from a secondary, tertiary, or heterocyclic amine.
8. The sensor of claim 7, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
9. The sensor of any one of claims 1 to 8, wherein the surface agent is an alkyltrialkoxysilane, a salt of a quaternary ammonium alkylalkoxysilane, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
10. The sensor of any one of claims 1-9, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
11. The sensor of any one of claims 1-10, wherein the distal functional group has a positive charge.
12. The sensor of any one of claims 1-11, wherein the surface agent is bound in a monolayer.
13. The sensor of any one of claims 1 to 12, wherein the sensor comprises a field effect transistor.
14. The sensor of claim 13, wherein the field effect transistor comprises an ion sensitive field effect transistor.
15. The sensor of any one of claims 1 to 14, wherein the sensor is part of a sensor array and wherein the reaction site is a well of a well array operably coupled to the sensor array.
16. The sensor of any one of claims 1 to 15, wherein the surface agent binds to the sensor surface.
17. The sensor of any one of claims 1-16, wherein the surface agent binds to the reaction site surface.
18. A method of forming a sensor component, the method comprising:
processing a wafer with oxygen plasma, the wafer comprising a plurality of dies, each die of the plurality of dies comprising a sensor array and an array of reaction sites cooperating with the sensor array; and
applying a surfactant to the wafer, the surfactant binding to a surface of the reaction sites or a sensor surface of the sensor array, the surfactant comprising surface active functional groups reactive with a Bronsted base or Lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups having no electron donating pairs.
19. The method of claim 18, further comprising annealing the wafer after applying the surfactant.
20. The method of claim 18 or claim 19, further comprising singulating the wafer into a plurality of grains after applying the surface agent.
21. The method of claim 20, further comprising packaging a die of the plurality of dies.
22. The method of any one of claims 18-21, wherein the surface active functional group comprises a silane, a phosphonic acid, a phosphinic acid, a diphosphinic acid, an isocyanate, a catechol, a hydroxamate, an alkoxy derivative thereof, or any combination thereof.
23. The method of claim 22, wherein the surface active functional group comprises a silane.
24. The method of claim 22, wherein the surface active functional group comprises a phosphonic acid.
25. The method of claim 22, wherein the surface active functional group comprises an isocyanate, a catechol, a hydroxamate, an alkoxy derivative thereof, or any combination thereof.
26. The method of claim 22, wherein the distal functional group comprises an alkyl group or a quaternary ammonium.
27. The method of claim 26, wherein the quaternary amine is derived from a secondary, tertiary, or heterocyclic amine.
28. The method of claim 27, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
29. The method of any one of claims 18-28, wherein the surface agent is an alkyltrialkoxysilane, a salt of a quaternary ammonium alkylalkoxysilane, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
30. The method of any one of claims 18-29, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
31. The method of any one of claims 18-30, wherein the distal functional group has a positive charge.
32. The method of any one of claims 18-31, wherein the surface agent is bound in a monolayer.
33. The method of any one of claims 18 to 32, wherein sensors of the sensor array comprise field effect transistors.
34. The method of claim 33, wherein the field effect transistor comprises an ion sensitive field effect transistor.
35. The method of any one of claims 18 to 34, wherein the surface agent binds to the sensor surface.
36. The method of any one of claims 18 to 35, wherein the surface agent binds to the reaction site surface.
37. A method of processing a sensor assembly, the method comprising:
washing a sensor assembly comprising a sensor cooperating with a reaction site, the sensor comprising a sensor surface and the reaction site comprising a reaction site surface; and
applying a surfactant to the wafer, the surfactant binding to the reaction site surface or the sensor surface, the surfactant comprising surface active functional groups reactive with the Bronsted base or Lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups having no electron donating pair.
38. The method of claim 37, further comprising washing the sensor component with an alcohol after applying the surfactant.
39. The method of claim 37 or claim 38, wherein the surface active functional group comprises a silane, a phosphonic acid, or a combination thereof.
40. The method of claim 39, wherein the surface active functional group comprises a silane.
41. The method of claim 39, wherein the surface active functional group comprises a phosphonic acid.
42. The method of claim 39, wherein the distal functional group comprises an alkyl group or a quaternary ammonium.
43. The method of claim 42, wherein the quaternary amine is derived from a secondary, tertiary, or heterocyclic amine.
44. The method of claim 43, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
45. The method of any one of claims 37 to 44, wherein the surface agent is an alkyltrialkoxysilane, a salt of a quaternary ammonium alkylalkoxysilane, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
46. The method of any one of claims 37-45, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
47. The method of any one of claims 37-46, wherein the distal functional group has a positive charge.
48. The method of any one of claims 37-47, wherein the surface agents are bound in a monolayer.
49. The method of any one of claims 37-48, wherein the sensor comprises a field effect transistor.
50. The method of claim 49, wherein the field effect transistor comprises an ion sensitive field effect transistor.
51. The method of any one of claims 37 to 50, wherein the surface agent binds to the sensor surface.
52. The method of any one of claims 37 to 51, wherein the surface agent binds to the reaction site surface.
Technical Field
The present disclosure relates generally to systems and methods for processing a surface of a semiconductor sensor and the processed semiconductor sensor.
Background
Sensor arrays formed in semiconductor substrates are increasingly used in fields such as analytical chemistry and molecular biology. For example, when an analyte is captured on or near a sensor pad of a sensor array, an analyte or byproduct of a reaction related to the analyte may be detected and used to interpret information about the analyte. In particular, such sensor arrays have been used in genetic analysis, such as gene sequencing or quantitative amplification.
During fabrication, various semiconductor processing techniques may alter the properties of the surface of the sensor array and the surface of the well structures surrounding the sensor array. Such processing can also leave residues on the surface or alter surface oxidation. Such altered surface chemistry may hinder or limit capture of analytes in the vicinity of the sensor. As a result, the utility of such sensor arrays is reduced and the signals produced by such sensor arrays may include erroneous or no data.
Disclosure of Invention
In one example, the surfactant is deposited on a surface adjacent to or on the sensor surface. Such a surfactant may be deposited on the sensor surface when the sensor is in the form of a sensor component or when the sensor is disposed in a wafer prior to singulation of the wafer into dies that can be packaged into sensor components.
In a particular example, the sensor component includes an array of Field Effect Transistor (FET) based sensors and a corresponding array of reaction sites (e.g., wells). One or more surfactants may be disposed on the surface of an array of FET-based sensors or the surface of a well.
Drawings
The present invention may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.
FIG. 1 includes a diagram of an exemplary measurement system.
Fig. 2 includes an illustration of an exemplary measurement assembly.
FIG. 3 includes an illustration of an exemplary array of measurement assemblies.
Fig. 4 includes an illustration of an exemplary well configuration.
FIG. 5 includes an illustration of an exemplary well and sensor configuration.
Fig. 6 and 7 include a flow chart illustrating an exemplary method for processing a semiconductor sensor.
Fig. 8, 9, and 10 include illustrations of exemplary surfactants.
The use of the same reference symbols in different drawings indicates similar or identical items.
Detailed Description
In an exemplary embodiment, a sensor assembly has a sensor and a reaction site cooperatively disposed with the sensor. The reaction sites may be wells, channels, grooves, pits, or other similar structures. For example, the reaction site may be a well. The surface agent may be bound to the side walls of the reaction sites or to the surface of the sensor. The surface agent may include functional groups that react with a Bronsted base structure or a Lewis acid (Lewis acid) structure on the surface and may include remote functional groups that do not have an electron donor pair or lack a Bronsted base or acid functionality. A surface agent may be applied to the surface during wafer processing or after wafer singulation and sensor assembly formation.
In an exemplary embodiment, the sensor assembly includes an array of wells associated with the sensor array. The sensors of the sensor array may include Field Effect Transistor (FET) sensors, such as Ion Sensitive Field Effect Transistors (ISFETs). In one example, the depth or thickness of the well is in the range of 100nm to 10 μm. In another example, the well may have a characteristic diameter in a range of 0.1 μm to 2 μm. The sensor assembly may form part of a sequencing system.
In a particular example, the sequencing system includes a flow cell having a sensing array disposed therein, includes communication circuitry in electronic communication with the sensing array, and includes a receptacle in fluid communication with the flow cell and a fluid control. In an example, fig. 1 illustrates an expanded view and a cross-sectional view of the
FIG. 2 illustrates an enlarged view of the well 201 and sensor 214 as shown at 110 of FIG. 1. The volume, shape, aspect ratio (e.g., bottom width to well depth ratio), and other dimensional characteristics of the wells can be selected based on the nature of the reaction taking place, as well as the reagents, byproducts, or labeling techniques employed, if any. The sensor 214 may be a chemical field effect transistor (chemFET), more particularly an ion sensitive fet (isfet), with a floating gate 218 having a sensor plate 220 optionally separated from the inside of the well by a layer of material 216 defining the sensor surface. Additionally, a conductive layer (not illustrated) may be disposed on the sensor board 220. In one example, the material layer 216 comprises an ion sensitive material layer. The material layer 216 may be a ceramic layer, such as an oxide of zirconium, hafnium, tantalum, aluminum, or titanium, or a nitride of titanium, among others. Alternatively, the material layer 216 may be formed of a metal such as titanium, tungsten, gold, silver, platinum, aluminum, copper, or combinations thereof. In an example, the thickness of the material layer 216 may be in a range of 5nm to 100nm, such as in a range of 10nm to 70nm, in a range of 15nm to 65nm, or even in a range of 20nm to 50 nm.
Although material layer 216 is illustrated as extending beyond the confines of the illustrated FET component, material layer 216 may extend along the bottom of well 201 and optionally along the walls of well 201. The sensor 214 may correspond to (and generate an output signal related to) an amount of charge 224 present on the material layer 216 opposite the sensor plate 220. The change in charge 224 can cause a change in current between the source 221 and drain 222 of the chemFET. In turn, the chemfets can be used directly to provide a current-based output signal or indirectly with additional circuitry to provide a voltage-based output signal. Reactants, wash solutions, and other reagents may move into and out of the well by diffusion mechanism 240.
In one embodiment, the reaction performed in the well 201 may be an analytical reaction that identifies or determines a characteristic or property of an analyte of interest. Such reactions may directly or indirectly generate byproducts that affect the amount of charge near the sensor plate 220. If such byproducts are produced in small amounts or decay rapidly or react with other components, multiple copies of the same analyte may be analyzed simultaneously in well 201 to increase the output signal produced. In an embodiment, multiple copies of the analyte may be attached to the solid support 212 before or after deposition into the well 201. The solid support 212 can be a polymeric matrix, such as a hydrophilic polymeric matrix, such as a hydrogel matrix, and the like. For simplicity and ease of explanation, the solid support 212 is also referred to herein as a polymer matrix.
The well 201 may be defined by a wall structure, which may be formed from one or more layers of material. In an example, the wall structure may have a thickness in a range of 0.01 μm to 10 μm, such as in a range of 0.05 μm to 10 μm, in a range of 0.1 μm to 10 μm, in a range of 0.3 μm to 10 μm, or in a range of 0.5 μm to 6 μm, extending from the lower surface to the upper surface of the well. In particular, the thickness may be in the range of 0.01 μm to 1 μm, such as in the range of 0.05 μm to 0.5 μm or in the range of 0.05 μm to 0.3 μm. The well 201 may have a characteristic diameter of no more than 5 μm, such as no more than 3.5 μm, no more than 2.0 μm, no more than 1.6 μm, no more than 1.0 μm, no more than 0.8 μm, or even no more than 0.6 μm, the characteristic diameter being defined as the cross-sectional area (a) divided by the square root of Pi (e.g., sqrt (4 a/Pi)). In one example, the well 201 may have a characteristic diameter of at least 0.01 μm. In another example, the well 201 may define a volume in the range of 0.05fL to 10pL, such as a volume in the range of 0.05fL to 1pL, 0.05fL to 100fL, 0.05fL to 10fL, or even 0.1fL to 5 fL.
Although fig. 2 illustrates a single wall structure and a single layer of material 216, the system may include one or more wall structure layers, one or more conductive layers, or one or more layers of material. For example, the wall structure may be formed from one or more layers, including an oxide of silicon or TEOS or including a nitride of silicon.
In one specific example illustrated in fig. 3, the system 300 includes a borehole wall structure 302 defining a well array 304 disposed on or operably coupled to a sensor mat of a sensor array. The borehole wall structure 302 defines an upper surface 306. The lower surface 308 associated with the well is disposed on a sensor pad of the sensor array. The borehole wall structure 302 defines a sidewall 310 between the upper surface 306 and the lower surface 308. As described above. The layer of material in contact with the sensor pads of the sensor array may extend along the lower surface 308 of the wells of the well array 304 or along at least a portion of the wall 310 defined by the well wall structure 302 and define a sensor surface. The upper surface 306 may be free of a material layer.
Although the wall surface of fig. 2 is illustrated as extending substantially vertically and outwardly, the wall surface may extend in multiple directions and have a variety of shapes. Substantially vertical means extending in a direction having a component perpendicular to the surface defined by the sensor pad. For example, as shown in FIG. 4, the borehole wall 402 may extend vertically, parallel to a normal component 412 of the surface defined by the sensor pad. In another example, the wall surface 404 extends substantially vertically in an outward direction away from the sensor pad, providing a well opening that is larger than the lower surface area of the well. As shown in fig. 4, wall surface 404 extends in a direction having a perpendicular component parallel to normal component 412 of surface 414. In an alternative example, the wall surface 406 extends substantially vertically in an inward direction, providing an open area that is smaller than the area of the downhole surface. Wall surface 406 extends in a direction having a component parallel to normal component 412 of surface 414.
Although surfaces 402, 404, or 406 are shown by straight lines, some semiconductor or CMOS fabrication methods may produce structures having non-linear shapes. Specifically, the shape of the wall surface (e.g., wall surface 408) and the upper surface (e.g., upper surface 410) may be arcuate or take a variety of non-linear forms. Although the structures and devices illustrated herein are depicted as having linear layers, surfaces, or shapes, the actual layers, surfaces, or shapes produced by semiconductor processing may differ to some extent, possibly including non-linear and arcuate variations of the illustrated embodiments.
FIG. 5 includes an illustration of an exemplary well having a layer of ion sensitive material. For example, the
In another example, as shown in well 506, ion
In a specific example, the
The surface of the sensor (e.g.,
In a particular example, the surface of the
In one example, a surface agent can be bound to the
Distal to this functional group, the surfactant may include a functional group that does not include an electron donor pair or lacks the activity of a buserette base or acid. The distal functional group may be a positively charged functional group or may be a neutral functional group. Exemplary neutral functional groups include alkyl, branched chain alkyl, or cyclic aromatic groups. Exemplary positively charged groups lacking an electron donating pair include quaternary ammonium ion salts derived from secondary amines, tertiary amines, or heterocyclic groups incorporating nitrogen. In another example, the distal functional group can be a nitroso functional group. Exemplary heterocyclic groups incorporating nitrogen include quaternary amines derived from pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, triazolate, or combinations thereof. In particular, the salt may comprise a halide salt of a quaternary ammonium ion, such as a bromide salt. Primary, tertiary or quaternary amines may be bound to the alkyl group, including methyl, ethyl, propyl, butyl or tert-butyl alkyl. In another example, the distal functional group can include a hindered primary, secondary, or tertiary amine, such as an amine hindered by a proximal phosphate, phosphonate, phosphinate, or silane group, or a combination thereof. In one particular example, the distal functional group can include biotin or a derivative thereof.
In one example, the distal functional group can be bound to the surface-reactive functional group by an amide, alkyl, alkoxy, aryl, or polyether or thioether moiety, or a combination thereof. For example, the distal functional group and the surface-reactive functional group can be separated by an alkyl moiety having from 1 to 16 carbons, e.g., from 1 to 12 carbons. In one example, the alkyl moiety can have from 8 to 12 carbons, such as from 10 to 12 carbons. In another example, the alkyl moiety can have from 1 to 6 carbons, such as from 1 to 4 carbons or from 1 to 3 carbons. In particular, the surfactant comprising a hindered amine distal functional group can have an alkyl moiety having from 1 to 6 carbons, such as from 1 to 4 carbons or from 1 to 3 carbons. In another example, the alkoxy moiety can have a number of carbons in a range similar to the alkyl moiety. In another example, the polyether moiety can have 1 to 10 ether units, each ether unit having 1 to 4 carbons, e.g., 1 to 3 carbons. For example, the polyether moiety can have 1 to 6 ether units, such as 1 to 4 ether units.
In one particular example, the surfactant includes a silane surface-reactive functional group. Exemplary surfactants include alkyltrialkoxysilanes, such as octyldecyltriethoxysilane, octyldecyltrimethoxysilane, propyltrimethoxysilane (F of fig. 8), or combinations thereof; quaternary ammonium alkylalkoxysilane salts such as butylammonium trimethoxysilane (a of fig. 8), methylammonium benztrimethoxysilane (B of fig. 8), uronium-or thiouronium-silane (E of fig. 8), methoxy-N-silane (C of fig. 8), short butylammonium trimethoxysilane (D of fig. 8), or combinations thereof; fluorinated or chlorinated derivatives thereof; derivatives thereof; or a combination thereof. Exemplary quaternary salts include the chlorine or bromine salts of such quaternary ammonium alkyltrialkoxysilanes. Such silane surfactants can be bound to semimetals or metal oxides. Some silane-based surfactants can bond indiscriminately to the sidewall surface or to the sensor surface.
In another example, the surfactant can be a phosphonic acid-based surfactant. Exemplary surfactants include alkyl phosphoric acids, such as octadecyl phosphonic acid; chloride or bromide salts of quaternary aminophosphonic acids, such as imidazolium phosphates (e.g., 1-methyl-3- (dodecyl phosphate) imidazolium, see D of FIG. 9, or 1-methyl-3- (hexyl phosphate) imidazolium, see E of FIG. 9), trimethylammonium bromide (12-dodecyl phosphate), methylammonium phosphonic acid (B of FIG. 9), ethylammonium phosphonic acid (C of FIG. 9), tripropylammonium bromide (12-dodecyl phosphate), tributylammonium bromide (12-dodecyl phosphate); methyltriazolium bromide (12-dodecylphosphate) (F in fig. 9); imidazolium (6-hexylphosphate); a pyridylalkyl phosphoric acid (e.g., a of fig. 9); a phenylalkyl phosphonic acid; (1-amino-1-phenylmethyl) phosphonic acid; fluorinated or chlorinated derivatives thereof; derivatives thereof; or any combination thereof. In another example, the surfactant can be a biotin alkyl phosphonic acid (e.g., the structure of fig. 10, where R represents oxygen, nitrogen, sulfur, a polyether, or a combination thereof). In one example, phosphates and phosphonates may preferentially bind to the sensor surface.
In another example, the phosphonic acid-based surfactant may include more than one phosphonic acid surface active functional group. For example, the surfactant may be a dibasic phosphonic acid comprising two phosphonic acid surface active functional groups, such as alendronic acid or derivatives thereof. In particular, the surfactant may be a multidentate phosphonic acid-based surfactant, e.g., comprising more than one phosphonic acid functional group coupled to a central moiety, e.g., a tertiary amine or an alkanediamine, that serves as a remote group. For example, the surfactant can be a functionalized aminobis (alkylphosphonic acid), such as a biotin-functionalized aminobis (methylenephosphonic acid), an aminotri (alkylphosphonic acid), such as an aminotri (methylenephosphonic acid), ether derivatives thereof, or combinations thereof. In another example, the surfactant can be an alkanediamine tetra (alkylphosphonic acid), such as ethylenediamine tetra (methylenephosphonic acid) (see G of fig. 9). In another example, the surfactant can be diethylenetriaminepenta (methylene phosphonic acid), hexamethylenediamine tetra (methylene phosphonic acid), tetramethylenediamine tetra (methylene phosphonic acid), or any combination thereof. In another example, the surfactant is a phenyl diphosphonic acid, a functionalized derivative thereof, or a combination thereof.
In another example, the surface agent can be a catechol, such as a catecholamine, a nitrocatechol, a nitrocatecholamine, a derivative thereof, or a combination thereof. For example, the catechol can comprise dopamine, nitrodopamine, norepinephrine, epinephrine, esters thereof, or combinations thereof. In a specific example, the catechol is dopamine or nitrodopamine.
In another example, the surfactant can include isocyanate or hydroxamate surface active functional groups.
In particular, the surface agent may be applied on the sensor device. The sensor device may include a plurality of sensor pads and wells optionally defined on the sensor pads. The surface agent may be applied to adhere to the well sidewall, may be applied to the sensor pad surface, or a combination thereof. In one example, the sensor device includes a cover disposed over the well and the sensor pad and defines a flow volume or flow channel over the sensor pad and the well. The surface agent or combination of surface agents may be applied as a solution through a flow cell or a flow volume to contact the well or sensor pad.
For example, as shown in fig. 6, method 600 includes optionally heating the sensor assembly, as shown at 602. The sensor assembly may include a set of wells disposed on the sensor pad and a cover defining a flow volume or flow channel over the wells and the sensor pad. The sensor assembly may be warmed to a temperature in the range of 35 ℃ to 100 ℃, such as a temperature in the range of 40 ℃ to 75 ℃ or even in the range of 45 ℃ to 65 ℃. Optionally, the temperature of the sensor assembly may be maintained at a temperature throughout the process range, or the fluid may be applied at a temperature throughout the process range.
The sensor assembly may be washed, as shown at 604. Optionally, the sensor assembly can be washed with an acid or base detergent. For example, the sensor component may be washed with a base solution, e.g. comprising a sodium hydroxide solution at a concentration in a range between 50mM and 2M, e.g. in a range of 50mM to 1M or in a range of 50mM to 200 mM. After the application of the caustic solution, the sensor assembly may be incubated in the presence of the caustic solution for a time in the range of 15 seconds to 5 minutes, such as in the range of 30 seconds to 2 minutes or in the range of 45 seconds to 90 seconds.
Alternatively or additionally, the sensor assembly may be incubated in the presence of an acid solution. The acid solution may be an aqueous solution or may be a non-aqueous solution. In particular, the sensor assembly may be incubated in the presence of the acid solution for a time in the range of 30 seconds to 10 minutes, such as in the range of 45 seconds to 5 minutes or in the range of 90 seconds to 150 seconds.
Exemplary acids in the acid solution may include sulfonic acids, phosphonic acids, or combinations thereof. The acid solution may further comprise an organic solvent. Exemplary sulfonic acids include alkyl sulfonic acids, alkyl aryl sulfonic acids, or combinations thereof. Exemplary alkyl sulfonic acids include alkyl groups having 1 to 18 carbons, e.g., 1 to 14 carbons, 1 to 10 carbons, or 1 to 5 carbons. In another example, the alkyl group of the alkylsulfonic acid has from 10 to 14 carbons. For example, the alkyl sulfonic acid can include methane sulfonic acid, ethane sulfonic acid, propane sulfonic acid, butane sulfonic acid, or combinations thereof. In another example, the alkyl group can be functionalized, for example, with a terminal functional group, as opposed to a sulfonic functional group. Exemplary functionalized alkylsulfonic acids include alkylsulfonic acids functionalized with terminal amine groups, such as taurine. In another example, the alkyl group of the sulfonic acid can be halogenated, e.g., fluorinated.
In another example, the sulfonic acid comprises an alkylaryl sulfonic acid. The alkyl aryl sulfonic acid (e.g., alkyl benzene sulfonic acid) can include an alkyl group having 1 to 20 carbons. For example, the alkyl group can have 9 to 18 carbons, such as 10 to 14 carbons. In one embodiment, the alkyl aryl sulfonic acid comprises dodecylbenzene sulfonic acid. The dodecylbenzene sulfonic acid may be in a purified form of at least 90%, for example at least 95% of the alkylarylsulfonic acids having an alkyl group with 12 carbons. Alternatively, the dodecylbenzene sulfonic acid may comprise a blend of alkylbenzene sulfonic acids having an alkyl group with an average of 12 carbons. The alkyl aryl sulfonic acids may be alkylated at mixed positions along the alkyl chain. In another example, the alkyl group can have 1 to 6 carbons. For example, the alkyl aryl sulfonic acid can include toluene sulfonic acid.
The acid solution may have a concentration of 10mM to 500mM of an acid (e.g., sulfonic acid). For example, the acid solution may have a concentration of 50mM to 250mM of acid. In another example, the acid solution includes 0.5 wt% to 25 wt% acid, such as sulfonic acid. For example, the acid solution can include 1 wt% to 10 wt% acid, such as 2.5 wt% to 5 wt% acid, such as sulfonic acid.
The organic solvent in the acid solution is a non-aqueous solvent having a solubility for an acid (e.g., sulfonic acid) of at least the above-mentioned concentration. In one example, the organic solvent can be aprotic. The organic solvent may be a non-polar organic solvent. In another example, the organic solvent can be a polar aprotic solvent. In one example, the organic solvent may have a normal boiling point in the range of 36 ℃ to 345 ℃. For example, the normal boiling point may be in the range of 65 ℃ to 275 ℃. In another example, the normal boiling point may be in the range of 65 ℃ to 150 ℃. Alternatively, the normal boiling point is in the range of 150 ℃ to 220 ℃.
In a specific example, the non-polar organic solvent includes an alkane solvent, an aromatic solvent, or a combination thereof. The alkane solvent can have from 6 to 20 carbons. For example, the alkane can have 6 to 14 carbons, such as 6 to 9 carbons. Alternatively, the alkane can have from 10 to 14 carbons. In one embodiment, the alkane is a linear alkane. For example, the alkane solvent can include pentane, hexane, heptane, octane, decane, undecane, dodecane, or combinations thereof. In another example, the alkane is halogenated. Exemplary branched paraffins may include hydrogenated dimers of C11 or C12 alpha olefins.
In another example, the organic solvent may comprise a polar aprotic solvent. For example, the polar aprotic solvent can include tetrahydrofuran, ethyl acetate, acetone, dimethylformamide, acetonitrile, dimethylsulfoxide, N-methylpyrrolidone (NMP), or a combination thereof. In another example, the organic solvent may be free of ether solvents, and may include, for example, dimethylformamide, acetonitrile, dimethylsulfoxide, or a combination thereof.
Detergents may also include detergents using alcohols, such as ethanol or isopropanol, or alcohol/water mixtures. Alcohol detergents are particularly useful when using acid solutions in non-aqueous solvents.
In another example, washing the sensor assembly may include one or more, e.g., one, two, or three, cycles of washing by an acid solution, an alcohol, or an alkali solution. Alternatively, the system may utilize a single acid wash followed by an alcohol wash or a single alkaline wash followed by an aqueous wash or an alcohol/water wash.
After washing, the sensor assembly may optionally be washed with alcohol and dried, as shown at 606. For example, the sensor component may be further rinsed with alcohol, and the alcohol is evaporated, for example, by vacuum drawing air through the flow cell or by applying dry nitrogen through the flow cell.
A surface agent may be applied to the chip as shown at 608. For example, the surfactant can be incorporated into the solution, applied over the sensor component, and incubated on the sensor component for a time between 1 minute and 2 hours. For example, the sensor component may be incubated in the presence of the surfactant solution for a time in the range of 1 minute to 100 minutes, such as in the range of 5 minutes to 75 minutes, in the range of 5 minutes to 60 minutes, in the range of 5 minutes to 30 minutes, or in the range of 5 minutes to 15 minutes. The incubation temperature may be in the range of 35 ℃ to 100 ℃, for example 40 ℃ to 80 ℃ or 45 ℃ to 70 ℃.
In one example, the surfactant solution may include a solvent, such as an alcohol (e.g., ethanol or isopropanol), N-methylpyrrolidone (NMP), Dimethylformamide (DMF), or a combination thereof. Optionally, the solution may include water. The amount of surfactant may range from 0.1 wt% to 10 wt%, for example from 0.1 wt% to 7 wt%. Specifically, the exemplary silane-based surfactant may be present in the solution in an amount in the range of 2 wt.% to 7 wt.%, such as in the range of 4 wt.% to 6 wt.%. Exemplary phosphonic acid surfactants may be present in an amount in the range of 0.1 wt.% to 2 wt.%, such as in the range of 0.1 wt.% to 1 wt.% or in the range of 0.3% to 0.8%.
After the surfactant is applied, the sensor assembly can be washed and dried, as shown at 610. For example, the sensor component can be washed with an alcohol, such as ethanol or isopropanol, and dried.
In another example, the surface agent is applied under the wafer level prior to singulation and formation of the semiconductor chip sensor assembly. The wafer may include a plurality of dies. Each die may include an array of sensors and a set of reaction sites defined to cooperate with the sensors. For example, a well may be formed in the surface layer to expose the sensor pad of the sensor. In one example, the wafer may be processed in a manner similar to the sensor component as described with respect to fig. 6, before the wafer is singulated and then the individual dies are packaged into a sensor component including a flow cell lid and a substrate.
In another example, the wafer may be treated with oxygen plasma followed by application of a surface agent. For example, fig. 7 illustrates an
As shown at 704, a surfactant solution may be applied to the wafer. The wafer may be inserted into a bath comprising a solution of a surfactant and a solvent. In one example, the solvent solution may include N-methylpyrrolidone (NMP) and water. Alternatively, the solvent solution may comprise an alcohol or an alcohol/water mixture. The concentration of the surfactant in the surfactant solution may range from 1mg/ml to 10 mg/ml. For example, the concentration may be in the range of 1mg/ml to 7mg/ml or 2mg/ml to 6 mg/ml. The bath may be maintained at a temperature in the range of 35 ℃ to 100 ℃, such as in the range of 40 ℃ to 90 ℃, in the range of 50 ℃ to 85 ℃, or in the range of 60 ℃ to 80 ℃. The wafer may be incubated in the surfactant solution for a period of time in the range of 10 minutes to 120 minutes, such as a period of time in the range of 30 minutes to 90 minutes or a period of time in the range of 45 minutes to 75 minutes.
The wafer may be washed and dried as shown at 706. For example, the wafer may be washed in an NMP/water solution and then washed in water. The wafer may then be dried.
Optionally, the wafer may be annealed as shown at 708. For example, the wafer may be held at an elevated temperature for an extended period of time. For example, the wafer may be annealed at a temperature in the range of 50 ℃ to 150 ℃, such as in the range of 70 ℃ to 135 ℃ or in the range of 90 ℃ to 110 ℃. The wafer may be annealed in an air atmosphere. Alternatively, the wafer may be annealed in an inert atmosphere, such as a nitrogen or helium atmosphere. The wafer may be annealed for a time in the range of 30 minutes to 5 hours, for example, in the range of 1 hour to 4 hours.
The wafer may be singulated into individual dies, as shown at 710. Each die may be packaged into a sensor assembly as shown at 712. For example, the die may be applied to a circuit substrate and a wire bonded to the substrate. A lid may be applied over the die to form the runner. Furthermore, the substrate/die components may be encapsulated to further secure the die to the substrate and protect the wire bonds or interconnects.
Embodiments of the above-described sensor assemblies and methods provide technical advantages related to an increase in critical signals from the sensor assembly. In particular, the sensor assembly may exhibit higher critical signals, faster response, and less buffering.
Examples of the invention
A sensor element was prepared using butylammonium trimethoxysilane (BATS) according to the following protocol. BATS was obtained from GELEST, part number SIT 8422.0.
The chips were treated with dodecylbenzene sulfonic acid (DBSA).
Attachment port extender
Undecane with 5% DBSA (100. mu.L) at 50 ℃ for 2min (freshly prepared solution daily, stored at 50 ℃)
2X 200. mu.L Isopropanol (IPA) wash
1X 200. mu.L of Nanofiltration (NF) water wash
1min 100mMNaOH(200μL)
1X 200. mu.L NF Water Wash
1X 200. mu.L IPA wash
Remove port expander and remove IPA under vacuum
This was repeated two more times for a total of 3 cycles of DBSA/NaOH.
A5% BATS solution was prepared. To prepare 1mL of solution: 200 μ L BATS (25% in DMF) with 750 μ L absolute ethanol and 50 μ L NF water.
The DBSA cleaned chips were placed in a 4oz can equipped with 1.5mL tubes filled with 95% EtOH.
Add 200. mu.L BATS solution to the chip, ensuring that the inlet and outlet wells are completely filled.
The can was carefully sealed with a lid.
The mixture was placed in an oven at 70 ℃ for 1 hour.
The can was removed from the oven and the chip was removed from the can.
The top and port of the chip were washed with 1mL of ethanol (the chip was held on a large vessel).
A1 mL pipette tip equipped with a non-filtered 20 μ L tip was used to push 3X 1mL of ethanol through the chip.
Ethanol was removed from the chip with vacuum.
Example 2
The sensor assembly (ION Torrent available from Life technologies corporation) was assembled using the following protocolTMProton II) was treated with imidazole phosphoric acid (ImPA). The ImPA solution included 50% isopropanol/50% diH2O with 5 mg/mLImPA.
Cleaning of
1. The chip was placed on a hot plate at 50 ℃ and allowed to briefly warm (about 30 seconds).
2. 100 μ L of 5% DBSA solution was added.
3. Incubate for 5 minutes.
4. The chip was washed with 2X 200. mu.L of partial undecane.
5. The chip was washed with IPA and dried by vacuum suction (or nitrogen flow if vacuum was not available).
ImPA deposition
1. The washed dry chips were placed on a hot plate at 50 ℃ and allowed to warm briefly.
2. Enough ImPA solution was loaded to fill the flow cell and two ports (approximately 150. mu.L)
3. Incubate for 10 minutes.
4. The ports are emptied by vacuum aspiration (with pipetting if vacuum is not available).
5. The chip was washed with 3X 200. mu.L of a 50% isopropanol solution.
6. The chip was washed with IPA and dried by vacuum suction (or nitrogen flow if vacuum was not available).
Example 3
Using the following protocol, a sensor assembly (ION Torrent available from Life technologies, Inc.)TMProton II) was treated with trimethoxyammonium bromide 12-dodecylphosphonate (MAPA). MAPA solution included 5mg/mL ImPA in diH 2O.
Cleaning-
1. The chip was placed on a hot plate at 50 ℃ and allowed to briefly warm (about 30 seconds).
2. 100 μ L of 5% DBSA solution was added.
3. Incubate for 5 minutes.
4. The chip was washed with 2X 200. mu.L of partial undecane.
5. The chip was removed from the hot plate and rinsed with 200 μ L of undecane.
6. The chip was rinsed with 2X 200. mu.L IPA followed by 200. mu.L ultrapure water.
7. The chip was washed with IPA and dried by vacuum suction (or nitrogen flow if vacuum was not available).
MAPA deposition-
1. A5 mg/mL aqueous solution was prepared (MAPA: trimethoxyammonium bromide 12-dodecylphosphonate SIK 7722-10). The solution was sonicated briefly to completely dissolve the MAPA solid.
2. The washed dry chips were placed in a sealable glass container equipped with a 1.5mL tube containing water.
3. Load enough MAPA solution into each chip to fill the flow cell and two ports (about 150. mu.L)
4. The lid is placed on the glass container and fastened.
5. The container with the chip was transferred to a 90 ℃ oven and incubated for 1 hour.
6. The container is removed from the oven and the chip is removed from the container.
7. The ports are emptied by vacuum aspiration (with pipetting if vacuum is not available).
8. The chip was washed with 3X 200. mu.L of 50% isopropanol solution.
9. The chip was washed with IPA and dried by vacuum suction (or nitrogen flow if vacuum was not available).
Example 4
The wafer including the sensor die to be converted into sensor chips (ION Torrent from life technologies) was processed using the following process before dicing and packagingTMProton II sensor) was treated with ImPA:
1. an 8-inch wafer containing the grains of the MW sensor structure was oxygen plasma cleaned at 200 mtorr at 500 watts for 5 minutes.
2. The wafer was removed and immediately immersed in a solution of 1mg/mL ImPA in 50/50NMP water at 70 deg.C for one hour.
3. The wafer was removed and immediately immersed in 50/50 NMP/water solution for rinsing. Stirring briefly.
4. The wafer was removed and immersed in a nanopure water bath.
5. Rinsed with additional nanopure water.
6. Dried with a stream of nitrogen.
7. Annealing was carried out at 100 ℃ for two hours.
Example 5
The wafer including the sensor die to be converted into sensor chips (ION Torrent from life technologies) was processed using the following process before dicing and packagingTMProton II sensor) was treated with ImPA:
the plasma cleaner was run for a period (5 minutes, 300 watts, 150 mtorr oxygen) before introducing the wafer. The wafer is placed on a center pedestal in the plasma cleaner. The plasma was run for 5 minutes with a 300 watt plasma clean with 150 millitorr oxygen.
The following solutions (25% NMP/75% water with 5mg/mL ImPA) were prepared: 1 g of ImPA, 50mL of NMP and 150mL of water. Sonication was briefly performed to completely dissolve the ImPA.
Once the wafer was plasma cleaned, the wafer was immediately placed in a petri dish and covered with ImPA solution. The second petri dish was inverted to serve as a lid. The mixture was placed in an oven at 70 ℃ for 1 hour. The covered petri dish was removed from the oven. The wafers were rinsed by immersion in a clean petri dish containing fresh 25% NMP/75% water. Swirl to aid rinsing. Petri dishes containing ImPA were washed with 25/75NMP water mixture and filled with fresh 25/75NMP to serve as a second wash bath. The wafer was transferred to a second bath and spun to aid rinsing. The 25/75NMP water bath was repeated a third time again.
After completing three NMP/water washes, the wafers were transferred to Petri dishes containing nanopure water for the first water wash. Swirl to aid rinsing. The wafer was immersed in two or more water baths, 3 total NMP/water rinses and 3 water only rinses (the wafer was alternated between the two petri dishes for initial treatment).
The wafer was removed and dried with a stream of nitrogen. Stored in a wafer carrier for transport for assembly.
In a first aspect, a sensor assembly includes a sensor including a sensor surface; a reaction site cooperating with the sensor and exposing the sensor surface, the reaction site comprising a reaction site surface; and a surfactant bound to the reaction site surface or the sensor surface, the surfactant comprising surface active functional groups that react with the bronsted base or lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups that do not have an electron donor pair.
In a second aspect, a method of forming a sensor assembly includes treating a wafer with oxygen plasma, the wafer including a plurality of dies, each die of the plurality of dies including a sensor array and an array of reaction sites cooperating with the sensor array; and applying a surfactant to the wafer, the surfactant binding to a surface of the reaction sites or a surface of sensors of the sensor array, the surfactant comprising surface active functional groups that react with the bronsted base or lewis acid functional groups on the reaction site surfaces or the sensor surfaces and comprising distal functional groups that do not have electron donating pairs.
In a third aspect, a method of processing a sensor assembly includes washing a sensor assembly, the sensor assembly including a sensor cooperating with a reaction site, the sensor including a sensor surface and the reaction site including a reaction site surface; and applying a surfactant to the wafer, the surfactant being bound to the reaction site surface or the sensor surface, the surfactant comprising surface active functional groups that react with the bronsted base or lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups that do not have electron donating pairs.
In an example of the second and third aspects, the method further comprises washing the sensor assembly with an alcohol after applying the surfactant.
In another example of the second aspect and examples above, the method further comprises annealing the wafer after applying the surfactant.
In another example of the second aspect and examples above, the method further comprises singulating the wafer into a plurality of dies after applying the surface agent. For example, the method may further comprise packaging the grains of the plurality of grains.
In an example of the first, second, and third aspects and examples above, the surface active functional group comprises a silane, a phosphonic acid, or a combination thereof. For example, the surface active functional group includes a silane. In another example, the surface active functional group comprises phosphonic acid. In another example, the distal functional group comprises an alkyl group or a quaternary ammonium. For example, the quaternary amine is derived from a secondary, tertiary or heterocyclic amine. In one example, the heterocyclic amine includes pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
In another example of the first, second, and third aspects and examples above, the surfactant is an alkyltrialkoxysilane, a quaternary ammonium alkylalkoxysilane salt, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
In another example of the first, second, and third aspects and examples above, the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
In another example and the above example of the first, second and third aspects, the distal functional group has a positive charge.
In another example of the first, second and third aspects and examples above, the surface agent is bound in a monolayer.
In another example of the first, second and third aspects and examples above, the sensor comprises a field effect transistor. For example, the field effect transistor comprises an ion sensitive field effect transistor.
In another example of the first, second and third aspects and examples above, the sensor is part of a sensor array and wherein the reaction site is a well of a well array operatively coupled to the sensor array.
In another example of the first, second and third aspects and examples above, the surface agent is bound to the sensor surface.
In another example of the first, second and third aspects and examples above, the surface agent is bound to the reaction site surface.
In a fourth aspect, a sensor assembly includes a sensor including a sensor surface; a reaction site cooperating with the sensor and exposing the sensor surface, the reaction site comprising a reaction site surface; and a surface agent bound to the reaction site surface or the sensor surface. The surfactant includes a surface active functional group that reacts with the sensor surface and includes a distal functional group. The surface active functional group may include a phosphate, a phosphonic acid, a phosphinic acid, a diphosphinic acid, a multidentate phosphate or phosphonate, a polyphosphate, an alkoxy derivative thereof, or any combination thereof. The distal functional group comprises ammonium.
In a fifth aspect, a method of processing a sensor assembly includes washing the sensor assembly. The sensor assembly includes a sensor cooperating with a reaction site. The sensor comprises a sensor surface and the reaction sites comprise reaction site surfaces. The method further includes applying a surfactant to the wafer. The surfactant includes a surface active functional group that reacts with the sensor surface and includes a distal functional group. The surface active functional group may include a phosphate, a phosphonic acid, a phosphinic acid, a diphosphinic acid, a multidentate phosphate or phosphonate, a polyphosphate, an alkoxy derivative thereof, or any combination thereof. The distal functional group includes an amine.
In a sixth aspect, a method of forming a sensor assembly includes treating a wafer with oxygen plasma. The wafer may include a plurality of dies. Each die of the plurality of dies includes a sensor array and an array of reaction sites cooperating with the sensor array. The method further includes applying a surfactant to the wafer. The surfactant includes a surface active functional group that reacts with the sensor surface and includes a distal functional group. The surface active functional group may include a phosphate, a phosphonic acid, a phosphinic acid, a diphosphinic acid, a multidentate phosphate or phosphonate, a polyphosphate, an alkoxy derivative thereof, or any combination thereof. The distal functional group includes an amine.
In an example of the above aspect and in the above example, the surface active functional group comprises a phosphate ester, a phosphonic acid, a phosphinic acid, an alkoxy derivative thereof, or any combination thereof.
In another example of the above aspect and the above example, the amine is derived from a secondary amine, a tertiary amine, or a heterocyclic amine. For example, the heterocyclic amine includes pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or combinations thereof.
In another example of the above aspect and in the above examples, the surfactant is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
In another example of the above aspect and in the above examples, the surfactant comprises a chloride or bromide salt of a quaternary amino phosphoric acid, methylammonium phosphonic acid, ethylammonium phosphonic acid, (12-dodecylphosphonic acid) methyltriazolium bromide, (6-hexylphosphonic acid) imidazolium, pyridylalkyl phosphoric acid, (1-amino-1-phenylmethyl) phosphonic acid, fluorinated or chlorinated derivatives thereof, or any combination thereof.
In another example of the above aspect and in the above example, the surfactant comprises imidazole phosphonic acid.
In another example of the above aspect and in the above example, the surfactant comprises (12-dodecyl phosphate) methyltriazolium bromide.
In another example of the above aspect and in the above example, the surfactant comprises a functionalized amino bis (alkyl phosphonic acid).
In another example of the above aspect and in the above example, the surface agent comprises a bisphosphonic acid or a multidentate phosphonic acid. For example, the surfactant comprises diethylenetriamine penta (methylene phosphonic acid), hexamethylenediamine tetra (methylene phosphonic acid), tetramethylenediamine tetra (methylene phosphonic acid), or any combination thereof.
In another example of the above aspect and the above example, the surfactant is bound in a monolayer.
In another example of the above aspect and in the above example, the sensor comprises a field effect transistor. For example, the field effect transistor comprises an ion sensitive field effect transistor.
In another example of the above aspect and in the above example, the sensor is part of a sensor array and wherein the reaction site is a well of a well array operably coupled to the sensor array.
In another example of the above aspect and in the above example, the surface agent is bound to the sensor surface.
In another example of the above aspect and in the above example, the surface agent is bound to the reaction site surface.
In an example of the fifth aspect and examples above, the method further comprises washing the sensor assembly with an alcohol after applying the surfactant.
In another example of the above aspect and the above example, wherein the distal functional group has a positive charge.
In an example of the sixth aspect and examples above, the method further comprises annealing the wafer after applying the surfactant.
In another example of the sixth aspect and examples above, the method further comprises singulating the wafer into a plurality of dies after applying the surface agent. For example, the method further comprises packaging the grains of the plurality of grains.
It should be noted that not all of the activities described in the above general description or examples are required, that a portion of a particular activity may not be required, and that one or more further activities may be performed in addition to those described. Again, the order in which activities are listed is not necessarily the order in which they are performed.
In the foregoing specification, the concepts have been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the present invention as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of present invention.
As used herein, the terms "comprises," "comprising," "includes," "including," "has," or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of features is not necessarily limited to only those features but may include other features not expressly listed or inherent to such process, method, article, or apparatus. In addition, unless expressly stated to the contrary, "or" means an inclusive or, and not an exclusive or. For example, any one of the following satisfies condition a or B: a is true (or present) and B is false (or not present), a is false (or not present) and B is true (or present), and both a and B are true (or present).
Similarly, the use of "a/an" is used to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.
Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature or element of any or all the claims.
After reading this specification, skilled artisans will appreciate that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, reference to a value stated in a range includes each value within that range.
The present application also includes the following:
1. a sensor assembly comprising
A sensor comprising a sensor surface;
a reaction site cooperating with the sensor and exposing the sensor surface, the reaction site comprising a reaction site surface; and
a surfactant bound to the reaction site surface or the sensor surface, the surfactant comprising a surface active functional group that reacts with the sensor surface and comprises a distal functional group, the surface active functional group comprising a phosphate, a phosphonic acid, a phosphinic acid, a bisphosphonic acid, a multidentate phosphate or phosphonate, a polyphosphate/phosphonate, an alkoxy derivative thereof, or any combination thereof, the distal functional group comprising an amine.
2. The sensor of item 1, wherein the surface active functional group comprises a phosphate ester, a phosphonic acid, a phosphinic acid, alkoxy derivatives thereof, or any combination thereof.
3. The sensor of item 1 or item 2, wherein the amine is derived from a secondary, tertiary, or heterocyclic amine.
4. The sensor of item 3, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
5. The sensor of any one of claims 1 to 4, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
6. The sensor of any one of claims 1 to 5, wherein the surface agent comprises a chloride or bromide salt of a quaternary amino phosphoric acid, methylammonium phosphonic acid, ethylammonium phosphonic acid, (12-dodecylphosphonic acid) methyltriazolium bromide, (6-hexylphosphonic acid) imidazolium, pyridylalkyl phosphoric acid, (1-amino-1-phenylmethyl) phosphonic acid, fluorinated or chlorinated derivatives thereof, or any combination thereof.
7. The sensor of any one of claims 1 to 6, wherein the surface agent comprises imidazole phosphonic acid.
8. The sensor of any one of claims 1 to 7, wherein the surface agent comprises (12-dodecyl phosphate) methyltriazolium bromide.
9. The sensor of any one of claims 1 to 8, wherein the surface agent comprises a functionalized aminobis (alkylphosphonic acid).
10. The sensor of any one of claims 1 to 9, wherein the surface agent comprises a bisphosphonic acid or a multidentate phosphonic acid.
11. The sensor of any one of claims 10, wherein the surface agent comprises diethylenetriamine penta (methylene phosphonic acid), hexamethylenediamine tetra (methylene phosphonic acid), tetramethylenediamine tetra (methylene phosphonic acid), or any combination thereof.
12. The sensor of any one of claims 1 to 11, wherein the surface agent is bound in a monolayer.
13. The sensor of any one of claims 1 to 12, wherein the sensor comprises a field effect transistor.
14. The sensor of item 13, wherein the field effect transistor comprises an ion sensitive field effect transistor.
15. The sensor of any one of claims 1 to 14, wherein the sensor is part of a sensor array and wherein the reaction site is a well of a well array operably coupled to the sensor array.
16. The sensor of any one of claims 1 to 15, wherein the surface agent binds to the sensor surface.
17. The sensor of any one of claims 1 to 16, wherein the surface agent binds to the reaction site surface.
18. A method of processing a sensor assembly, the method comprising:
washing a sensor assembly comprising a sensor cooperating with a reaction site, the sensor comprising a sensor surface and the reaction site comprising a reaction site surface; and
applying a surfactant to the wafer, the surfactant comprising a surface active functional group that reacts with the sensor surface and comprising a distal functional group, the surface active functional group comprising a phosphate, a phosphonic acid, a phosphinic acid, a bisphosphonic acid, a multidentate phosphate or phosphonate, a polyphosphate/phosphonate, alkoxy derivatives thereof, or any combination thereof, the distal functional group comprising an amine.
19. The method of item 18, further comprising washing the sensor component with an alcohol after applying the surfactant.
20. The method of item 18 or item 19, wherein the amine is derived from a secondary, tertiary, or heterocyclic amine.
21. The method of item 20, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
22. The method of any one of claims 18 to 21, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
23. The method of any one of claims 18 to 22, wherein the surface agent comprises a chloride or bromide salt of a quaternary amino phosphoric acid, methylammonium phosphonic acid, ethylammonium phosphonic acid, (12-dodecylphosphonic acid) methyltriazolium bromide, (6-hexylphosphonic acid) imidazolium, pyridylalkyl phosphoric acid, (1-amino-1-phenylmethyl) phosphonic acid, fluorinated or chlorinated derivatives thereof, or any combination thereof.
24. The method of any one of claims 18 to 23, wherein the surface agent comprises imidazole phosphonic acid.
25. The method of any one of claims 18 to 24, wherein the surfactant comprises (12-dodecyl phosphate) methyltriazolium bromide.
26. The method of any one of claims 18 to 25, wherein the surfactant comprises a functionalized aminobis (alkylphosphonic acid).
27. The method of any one of items 18 to 26, wherein the surface agent comprises a bisphosphonic acid or a multidentate phosphonic acid.
28. The method of item 27, wherein the surfactant comprises diethylenetriamine penta (methylene phosphonic acid), hexamethylenediamine tetra (methylene phosphonic acid), tetramethylenediamine tetra (methylene phosphonic acid), or any combination thereof.
29. The method of any one of claims 18 to 28, wherein the distal functional group has a positive charge.
30. The method of any one of claims 18 to 29, wherein the surface agent is bound in a monolayer.
31. The method of any one of claims 18 to 30, wherein the sensor comprises a field effect transistor.
32. The method of item 31, wherein the field effect transistor comprises an ion sensitive field effect transistor.
33. The method of any one of claims 18 to 32, wherein the surface agent binds to the sensor surface.
34. The method of any one of claims 18 to 33, wherein the surface agent binds to the reaction site surface.
35. A method of forming a sensor component, the method comprising:
processing a wafer with oxygen plasma, the wafer comprising a plurality of dies, each die of the plurality of dies comprising a sensor array and an array of reaction sites cooperating with the sensor array; and
applying a surfactant to the wafer, the surfactant comprising a surface active functional group that reacts with the sensor surface and comprising a distal functional group, the surface active functional group comprising a phosphate, a phosphonic acid, a phosphinic acid, a bisphosphonic acid, a multidentate phosphate or phosphonate, a polyphosphate/phosphonate, alkoxy derivatives thereof, or any combination thereof, the distal functional group comprising an amine.
36. The method of item 35, further comprising annealing the wafer after applying the surfactant.
37. The method of item 35 or item 36, further comprising singulating the wafer into a plurality of dies after applying the surface agent.
38. The method of item 37, further comprising packaging the grains of the plurality of grains.
39. The method of any one of claims 35 to 38, wherein the amine is derived from a secondary, tertiary, or heterocyclic amine.
40. The method of item 39, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
41. The method of any one of items 35 to 40, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
42. The method of any one of items 35 to 41, wherein the surface agent comprises a chloride or bromide salt of a quaternary amino phosphoric acid, methylammonium phosphonic acid, ethylammonium phosphonic acid, (12-dodecylphosphonic acid) methyltriazolium bromide, (6-hexylphosphonic acid) imidazolium, pyridylalkyl phosphoric acid, (1-amino-1-phenylmethyl) phosphonic acid, fluorinated or chlorinated derivatives thereof, or any combination thereof.
43. The method of any one of items 35 to 42, wherein the surface agent comprises imidazole phosphonic acid.
44. The method of any one of items 35 to 43, wherein the surfactant comprises (12-dodecyl phosphate) methyltriazolium bromide.
45. The method of any one of items 35 to 44, wherein the surfactant comprises a functionalized aminobis (alkylphosphonic acid).
46. The method of any one of items 35 to 45, wherein the surface agent comprises a bisphosphonic acid or a multidentate phosphonic acid.
47. The method of item 46, wherein the surfactant comprises diethylenetriamine penta (methylene phosphonic acid), hexamethylenediamine tetra (methylene phosphonic acid), tetramethylenediamine tetra (methylene phosphonic acid), or any combination thereof.
48. The method of any one of claims 35 to 47, wherein the distal functional group has a positive charge.
49. The method of any one of items 35 to 48, wherein the surface agent is bound in a monolayer.
50. The method of any one of items 35 to 49, wherein the sensors of the sensor array comprise field effect transistors.
51. The method of clause 50, wherein the field effect transistor comprises an ion sensitive field effect transistor.
52. The method of any one of items 35 to 51, wherein the surface agent binds to the sensor surface.
53. The method of any one of items 35 to 52, wherein the surface agent binds to the reaction site surface.
54. A sensor assembly comprising
A sensor comprising a sensor surface;
a reaction site cooperating with the sensor and exposing the sensor surface, the reaction site comprising a reaction site surface; and
a surfactant bound to the reaction site surface or the sensor surface, the surfactant comprising surface active functional groups that react with the Bronsted base or Lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups that do not have an electron donor pair.
55. The sensor of clause 54, wherein the surface active functional group comprises a silane, a phosphate, a phosphonic acid, a phosphinic acid, a diphosphinic acid, an isocyanate, a catechol, a hydroxamate, an alkoxy derivative thereof, or any combination thereof.
56. The sensor of item 55, wherein the surface active functional group comprises a silane or an alkoxy derivative thereof.
57. The sensor of item 55, wherein the surface active functional group comprises a phosphate ester, a phosphonic acid, a phosphinic acid, a diphosphinic acid, alkoxy derivatives thereof, or any combination thereof.
58. The sensor of clause 55, wherein the surface-active functional groups comprise isocyanates, catechols, hydroxamates, alkoxy derivatives thereof, or any combination thereof.
59. The sensor of item 55, wherein the distal functional group comprises an alkyl or quaternary ammonium.
60. The sensor of item 59, wherein the quaternary amine is derived from a secondary, tertiary, or heterocyclic amine.
61. The sensor of item 60, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
62. The sensor of any one of claims 54 to 61, wherein the surface agent is an alkyltrialkoxysilane, a salt of a quaternary ammonium alkylalkoxysilane, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
63. The sensor of any one of items 54 to 62, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
64. The sensor of any one of claims 54-63, wherein the distal functional group has a positive charge.
65. The sensor of any one of items 54 to 64, wherein the surface agent is bound in a monolayer.
66. The sensor of any one of items 54 to 65, wherein the sensor comprises a field effect transistor.
67. The sensor of item 66, wherein the field effect transistor comprises an ion sensitive field effect transistor.
68. The sensor of any one of items 54 to 67, wherein the sensor is part of a sensor array and wherein the reaction site is a well of a well array operably coupled to the sensor array.
69. The sensor of any one of items 54 to 68, wherein the surface agent binds to the sensor surface.
70. The sensor of any one of items 54 to 69, wherein the surface agent binds to the reaction site surface.
71. A method of forming a sensor component, the method comprising:
processing a wafer with oxygen plasma, the wafer comprising a plurality of dies, each die of the plurality of dies comprising a sensor array and an array of reaction sites cooperating with the sensor array; and
applying a surfactant to the wafer, the surfactant binding to a surface of the reaction sites or a sensor surface of the sensor array, the surfactant comprising surface active functional groups reactive with a Bronsted base or Lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups having no electron donating pairs.
72. The method of item 71, further comprising annealing the wafer after applying the surfactant.
73. The method of item 71 or item 72, further comprising singulating the wafer into a plurality of dies after applying the surface agent.
74. The method of item 73, further comprising packaging the grains of the plurality of grains.
75. The method of any one of items 71-74, wherein the surface active functional group comprises a silane, a phosphonic acid, a phosphinic acid, a diphosphinic acid, an isocyanate, a catechol, a hydroxamate, an alkoxy derivative thereof, or any combination thereof.
76. The method of clause 75, wherein the surface active functional group comprises a silane.
77. The method of clause 75, wherein the surface active functional group comprises a phosphonic acid.
78. The method of clause 75, wherein the surface-active functional groups comprise isocyanates, catechols, hydroxamates, alkoxy derivatives thereof, or any combination thereof.
79. The method of item 75, wherein the distal functional group comprises an alkyl or quaternary ammonium.
80. The method of item 79, wherein the quaternary amine is derived from a secondary, tertiary, or heterocyclic amine.
81. The method of clause 80, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
82. The method of any one of items 71 to 81, wherein the surfactant is an alkyltrialkoxysilane, a salt of a quaternary ammonium alkylalkoxysilane, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
83. The method of any one of items 71 to 82, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
84. The method of any one of items 71-83, wherein the distal functional group has a positive charge.
85. The method of any one of items 71 to 84, wherein the surface agent is bound in a monolayer.
86. The method of any one of items 71 to 85, wherein the sensors of the sensor array comprise field effect transistors.
87. The method of clause 86, wherein the field effect transistor comprises an ion sensitive field effect transistor.
88. The method of any one of items 71 to 87, wherein the surface agent binds to the sensor surface.
89. The method of any one of items 71 to 88, wherein the surface agent binds to the reaction site surface.
90. A method of processing a sensor assembly, the method comprising:
washing a sensor assembly comprising a sensor cooperating with a reaction site, the sensor comprising a sensor surface and the reaction site comprising a reaction site surface; and
applying a surfactant to the wafer, the surfactant binding to the reaction site surface or the sensor surface, the surfactant comprising surface active functional groups reactive with the Bronsted base or Lewis acid functional groups on the reaction site surface or the sensor surface and comprising distal functional groups having no electron donating pair.
91. The method of item 90, further comprising washing the sensor component with an alcohol after applying the surfactant.
92. The method of clause 90 or clause 91, wherein the surface active functional group comprises a silane, a phosphonic acid, or a combination thereof.
93. The method of clause 92, wherein the surface active functional group comprises a silane.
94. The method of clause 92, wherein the surface active functional group comprises a phosphonic acid.
95. The method of item 92, wherein the distal functional group comprises an alkyl or quaternary ammonium.
96. The method of item 95, wherein the quaternary amine is derived from a secondary, tertiary, or heterocyclic amine.
97. The method of item 96, wherein the heterocyclic amine comprises pyrrolidine, pyrrole, imidazole, piperidine, pyridine, pyrimidine, purine, or a combination thereof.
98. The method of any one of items 90 to 97, wherein the surfactant is an alkyltrialkoxysilane, a salt of a quaternary ammonium alkylalkoxysilane, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
99. The method of any one of items 90 to 98, wherein the surface agent is an alkyl phosphonic acid, a salt of a quaternary amino phosphoric acid, a fluorinated or chlorinated derivative thereof, a derivative thereof, or a combination thereof.
100. The method of any one of items 90 to 99, wherein the distal functional group has a positive charge.
101. The method of any one of items 90 to 100, wherein the surface agent is bound in a monolayer.
102. The method of any one of items 90 to 102, wherein the sensor comprises a field effect transistor.
103. The method of
104. The method of any one of items 90 to 103, wherein the surface agent binds to the sensor surface.
105. The method of any one of items 90 to 104, wherein the surface agent binds to the reaction site surface.
- 上一篇：一种医用注射器针头装配设备
- 下一篇：生物传感器