阅读说明：本技术 纳米氧化锌抗菌抗病毒喷剂及其制备方法和应用 (Nano zinc oxide antibacterial and antiviral spray and preparation method and application thereof ) 是由 常彬彬 李勇 廖宇涛 于 2020-04-27 设计创作，主要内容包括：本发明涉及一种纳米氧化锌抗菌抗病毒喷剂及其制备方法和应用,所述纳米氧化锌抗菌抗病毒喷剂包括以下重量份数的组分：纳米氧化锌分散液50-80份、除醛剂0.5-7份、润湿剂0.3-5.0份、防冻剂0.2-5.0份、渗透剂0.2-5.2份和去离子水20-42份,其中所述纳米氧化锌分散液包括以下重量份数的组分：氧化锌粉体5-40份、分散剂3-30份和去离子水53-67份。本发明为一种具有抗病毒功能兼具防霉、抗菌和除醛等功能的液体喷剂,安全性高且对人和动物无刺激,适合于家庭以及各种办公场所使用,持久性高。(The invention relates to a nano-zinc oxide antibacterial antiviral spray, a preparation method and an application thereof, wherein the nano-zinc oxide antibacterial antiviral spray comprises the following components in parts by weight: 50-80 parts of nano zinc oxide dispersion liquid, 0.5-7 parts of aldehyde removing agent, 0.3-5.0 parts of wetting agent, 0.2-5.0 parts of antifreezing agent, 0.2-5.2 parts of penetrating agent and 20-42 parts of deionized water, wherein the nano zinc oxide dispersion liquid comprises the following components in parts by weight: 5-40 parts of zinc oxide powder, 3-30 parts of dispersant and 53-67 parts of deionized water. The liquid spray has the functions of resisting viruses, resisting bacteria, removing aldehyde and the like, has high safety, no stimulation to people and animals, is suitable for being used in families and various office places, and has high durability.)

1. A nano zinc oxide antibacterial antiviral spray is characterized in that: the paint comprises the following components in parts by weight: 50-80 parts of nano zinc oxide dispersion liquid, 0.5-7 parts of aldehyde removing agent, 0.3-5.0 parts of wetting agent, 0.2-5.0 parts of antifreezing agent, 0.2-5.2 parts of penetrating agent and 20-42 parts of deionized water.

2. The nano zinc oxide antibacterial antiviral spray as claimed in claim 1, characterized in that: the nano zinc oxide dispersion comprises the following components in parts by weight: 5-40 parts of zinc oxide powder, 3-30 parts of dispersant and 53-67 parts of deionized water, wherein the nano zinc oxide dispersion is prepared by the following method: weighing zinc oxide powder, a dispersing agent and deionized water according to the formula ratio, putting the zinc oxide powder, the dispersing agent and the deionized water into a stirrer, stirring into uniform mixed liquid, pouring the mixed liquid into a sand mill for grinding for 4-12h to obtain the nano zinc oxide dispersion liquid.

3. The nano zinc oxide antibacterial antiviral spray as claimed in claim 2, characterized in that: the grain diameter D100 of the zinc oxide powder is less than 5um, the content of the zinc oxide powder is more than or equal to 99.9 percent, and the grain diameter D50 of the nano zinc oxide in the nano zinc oxide dispersion liquid is less than 90 nm.

4. The nano zinc oxide antibacterial antiviral spray as claimed in claim 2, characterized in that: the dispersing agent is at least one of stearic acid, ethylene bis stearamide, polyethylene glycol, fatty alcohol-polyoxyethylene ether, polyacrylic acid anionic surfactant and carboxylate-sulfonate-nonionic terpolymer.

5. The nano zinc oxide antibacterial antiviral spray as claimed in claim 1, characterized in that: the aldehyde removing agent is 2-imidazolidinone or amino acid.

6. The nano zinc oxide antibacterial antiviral spray according to claim 5, characterized in that: the amino acid is alanine, polylysine or arginine.

7. The nano zinc oxide antibacterial antiviral spray as claimed in claim 1, characterized in that: the wetting agent is polyvinyl alcohol or pharmaceutical grade polyvinylpyrrolidone, the penetrating agent is an anionic penetrating agent or a nonionic penetrating agent, and the antifreezing agent is at least one of isopropanol, ethylene glycol, propylene glycol and diethylene glycol.

8. The nano zinc oxide antibacterial antiviral spray according to claim 7, characterized in that: the anionic penetrant is sodium sulfamate or sodium di-sec-octyl maleate sulfonate; the non-ionic penetrating agent is one of fatty alcohol polyoxyethylene ether, alkylphenol polyoxyethylene ether and sec-octanol polyoxyethylene ether, wherein the alkylphenol polyoxyethylene ether is one of nonylphenol polyoxyethylene ether, octylphenol polyoxyethylene ether and dodecyl polyoxyethylene ether.

9. A method for preparing the nano zinc oxide antibacterial antiviral spray as claimed in any one of claims 1 to 8, which is characterized in that: the method comprises the following steps:

the method comprises the following steps: weighing deionized water and an aldehyde removing agent according to the formula ratio, stirring in a stirrer, and stirring at the rotating speed of 500-;

step two: the rotating speed of the stirrer is reduced to 500r/min for 300-.

10. The use of the nano zinc oxide antibacterial and antiviral spray as claimed in any one of claims 1 to 8, characterized in that: when in use, the spray and the common wall coating are uniformly mixed according to the weight ratio of 1:8-12 to obtain the multifunctional coating, and then the multifunctional coating is painted or coated on the surface of the indoor wall.

Technical Field

The invention relates to a spray, in particular to a nano zinc oxide antibacterial antiviral spray, a preparation method and application thereof.

Background

The terms of antivirus, mildew-proof, antibiosis and formaldehyde removal are getting more and more attention of people, corresponding products and patents are increased gradually, certain product sprays with the functions of formaldehyde removal, antibiosis, mildew prevention and the like can be seen on the market, but the sprays do not have the comprehensive antivirus function, so that the problem of indoor air purification cannot be thoroughly solved by the products.

Aiming at viruses, moulds, bacteria, formaldehyde and the like which are harmful to the living health of human bodies indoors, the composite product which has the functions of high-efficiency antivirus, mould prevention, antibiosis and formaldehyde removal is developed.

Disclosure of Invention

In order to overcome the defects, the invention provides the nano zinc oxide antibacterial antiviral spray which is prepared by taking inorganic nano zinc oxide as a main functional material and adding an aldehyde removing agent, a wetting agent and other auxiliary materials, has the antiviral function, has the functions of mildew prevention, antibiosis, aldehyde removal and the like, has high safety and has no stimulation to people and animals.

The technical scheme adopted by the invention for solving the technical problem is as follows:

the nano zinc oxide antibacterial antiviral spray comprises the following components in parts by weight: 50-80 parts of nano zinc oxide dispersion liquid, 0.5-7 parts of aldehyde removing agent, 0.3-5.0 parts of wetting agent, 0.2-5.0 parts of antifreezing agent, 0.2-5.2 parts of penetrating agent and 20-42 parts of deionized water.

Preferably, the nano zinc oxide dispersion liquid comprises the following components in parts by weight: 5-40 parts of zinc oxide powder, 3-30 parts of dispersant and 53-67 parts of deionized water, wherein the nano zinc oxide dispersion is prepared by the following method: weighing zinc oxide powder, a dispersing agent and deionized water according to the formula ratio, putting the zinc oxide powder, the dispersing agent and the deionized water into a stirrer, stirring into uniform mixed liquid, pouring the mixed liquid into a sand mill for grinding for 4-12h to obtain the nano zinc oxide dispersion liquid.

Preferably, the grain diameter D100 of the zinc oxide powder is less than 5um, the content of the zinc oxide powder is more than or equal to 99.9 percent, and the grain diameter D50 of the nano zinc oxide in the nano zinc oxide dispersion liquid is less than 90 nm.

Preferably, the dispersant is at least one of stearic acid, ethylene bis stearamide, polyethylene glycol, fatty alcohol-polyoxyethylene ether, polyacrylic anionic surfactant and carboxylate-sulfonate-nonionic terpolymer.

Preferably, the aldehyde removing agent is 2-imidazolidinone or an amino acid, wherein the amino acid is alanine, polylysine or arginine.

Preferably, the wetting agent is polyvinyl alcohol or pharmaceutical grade polyvinylpyrrolidone, the penetrating agent is an anionic penetrating agent or a nonionic penetrating agent, and the antifreezing agent is at least one of isopropanol, ethylene glycol, propylene glycol and diethylene glycol.

Preferably, the anionic penetrant is sodium sulfamate or sodium di-sec-octyl maleate sulfonate; the non-ionic penetrating agent is one of fatty alcohol polyoxyethylene ether, alkylphenol polyoxyethylene ether and sec-octanol polyoxyethylene ether, wherein the alkylphenol polyoxyethylene ether is one of nonylphenol polyoxyethylene ether, octylphenol polyoxyethylene ether and dodecyl polyoxyethylene ether.

The invention also provides a preparation method of the nano zinc oxide antibacterial antiviral spray, which comprises the following steps:

the method comprises the following steps: weighing deionized water and an aldehyde removing agent according to the formula ratio, stirring in a stirrer, and stirring at the rotating speed of 500-;

step two: the rotating speed of the stirrer is reduced to 500r/min for 300-.

The invention also provides an application of the nano zinc oxide antibacterial antiviral spray, when in application, the spray and the common wall coating are uniformly mixed according to the weight ratio of 1:8-12 to obtain a multifunctional coating, and then the multifunctional coating is painted or coated on the surface of an indoor wall.

The invention has the beneficial effects that: the spray is prepared by taking inorganic nano zinc oxide as a main functional material and adding an aldehyde removing agent, a wetting agent and other auxiliary materials, wherein zinc oxide powder, a dispersing agent and deionized water are independently stirred and ground, the particle size D50 of nano zinc oxide in the finally obtained nano zinc oxide dispersion liquid is less than 90nm, any one-dimensional size of the surface of the nano zinc oxide in the nano zinc oxide dispersion liquid can reach below 20nm, then the obtained nano zinc oxide dispersion liquid is further evenly mixed with an aldehyde removing agent, a wetting agent, an antifreezing agent, a penetrating agent and deionized water to obtain the antibacterial and antiviral spray, the spray is a liquid spray with the functions of resisting virus, resisting bacteria and removing aldehyde, has high safety, no stimulation to human and animals and high durability, is suitable for being used in families and various office places, and can be directly atomized by a spray can and sprayed on the wall surface of a room when in use; the multifunctional paint can also be mixed with common wall paint according to a certain proportion to form multifunctional paint, and then the multifunctional paint is painted on the wall surface of a room, so that a proper use method can be adopted according to different occasions.

Drawings

FIG. 1 is an SEM image of zinc oxide in a nano zinc oxide dispersion of example 1.

Detailed Description

The technical solutions in the embodiments of the present invention will be clearly and completely described below with reference to the embodiments of the present invention, and it is obvious that the described embodiments are only a part of the embodiments of the present invention, and not all of the embodiments. All other embodiments, which can be derived by a person skilled in the art from the embodiments given herein without making any creative effort, shall fall within the protection scope of the present invention.

The nano zinc oxide antibacterial antiviral spray comprises the following components in parts by weight: 50-80 parts of nano zinc oxide dispersion liquid, 0.5-7 parts of aldehyde removing agent, 0.3-5.0 parts of wetting agent, 0.2-5.0 parts of antifreezing agent, 0.2-5.2 parts of penetrating agent and 20-42 parts of deionized water. Further preferably, the weight parts of each component are as follows: 55-70 parts of nano zinc oxide dispersion liquid, 1.5-5.5 parts of aldehyde removing agent, 0.5-1.0 part of wetting agent, 0.4-2.0 parts of antifreezing agent, 1.5-3.5 parts of penetrating agent and 20-42 parts of deionized water. The spray is prepared by taking inorganic nano zinc oxide as a main functional material and adding auxiliary materials such as an aldehyde removing agent, a wetting agent and the like, is a liquid spray with the functions of resisting viruses, resisting bacteria, removing aldehydes and the like, has high safety, no stimulation to people and animals, is suitable for being used in families and various office places, and has high durability; when in use, the spray can be directly sprayed on the wall surface of a room by adopting an atomization method.

The nano zinc oxide dispersion comprises the following components in parts by weight: 5-40 parts of zinc oxide powder, 3-30 parts of dispersant and 53-67 parts of deionized water, wherein the nano zinc oxide dispersion is prepared by the following method: weighing zinc oxide powder, a dispersing agent and deionized water according to the formula ratio, putting the zinc oxide powder, the dispersing agent and the deionized water into a stirrer, stirring into uniform mixed liquid, pouring the mixed liquid into a sand mill for grinding for 4-12h to obtain the nano zinc oxide dispersion liquid. Further preferably, 25-35 parts of zinc oxide powder, 8-12 parts of a dispersing agent and 53-67 parts of deionized water, and the better grinding time is 8-12h, because the nano-scale zinc oxide can show good antibacterial, mildew-proof, aldehyde-removing and antiviral effects, and the dispersing agent can enable the zinc oxide to be dispersed to reach the nano-scale zinc oxide, the nano-scale zinc oxide is dispersed by adopting a dispersing solution, the nano-scale zinc oxide, the dispersing agent, the deionized water, a rapid aldehyde-removing factor, a film-forming agent and the like are directly added into a stirrer to be uniformly stirred in the prior art, and then grinding and other operations are carried out to obtain the spray, but the nano-scale zinc oxide in the spray cannot be sufficiently dispersed, and the antiviral effect is poor. According to the invention, the zinc oxide powder, the dispersing agent and the deionized water are stirred and ground separately to obtain the nano zinc oxide dispersion liquid finally, wherein the particle size D50 of the nano zinc oxide is less than 90nm, and then the obtained nano zinc oxide dispersion liquid is further uniformly mixed with the aldehyde removing agent, the wetting agent, the antifreezing agent, the penetrating agent and the deionized water to obtain the antibacterial and antiviral spray.

The grain diameter D100 of the zinc oxide powder is less than 5um, the content of the zinc oxide powder is more than or equal to 99.9 percent, and the grain diameter D50 of the nano zinc oxide in the nano zinc oxide dispersion liquid is less than 90 nm. After a plurality of tests, the particle size of the nano zinc oxide in the nano zinc oxide dispersion liquid is controlled to be D50 less than 90nm, and the single-dimensional size of any one surface of the nano zinc oxide in the nano zinc oxide dispersion liquid obtained by the grinding method can reach below 20nm, so that the spray can achieve good antibacterial and antiviral effects.

The dispersing agent is at least one of stearic acid, ethylene bis stearamide, polyethylene glycol, fatty alcohol-polyoxyethylene ether, polyacrylic acid anionic surfactant and carboxylate-sulfonate-nonionic terpolymer.

The aldehyde removing agent is 2-imidazolidinone or amino acid, wherein the amino acid is alanine, polylysine or arginine. The amino acid formaldehyde removal method utilizes the basic reaction principle that formaldehyde can be combined with amino acid (the basic structure of human protein) to generate hydroxymethyl derivatives and water, and the generated hydroxymethyl derivatives are harmless to human bodies, are nontoxic and tasteless in the whole reaction process, are not released for the second time, cannot cause secondary pollution, and are a very safe formaldehyde removal method.

The wetting agent is polyvinyl alcohol or pharmaceutical grade polyvinylpyrrolidone, the penetrating agent is an anionic penetrating agent or a nonionic penetrating agent, and the antifreezing agent is at least one of isopropanol, ethylene glycol, propylene glycol and diethylene glycol. The wetting agent can enable the solid material to be more easily wetted by water, and the surface tension or the interfacial tension of the solid material is reduced, so that water can spread on the surface of the solid material or penetrate into the surface of the solid material to wet the solid material; the penetrant aids in the penetration of the solvent into the fixing substance; the antifreeze can prevent the spray from solidifying at low temperature.

The anionic penetrant is sodium sulfamate or sodium di-sec-octyl maleate sulfonate; the non-ionic penetrating agent is one of fatty alcohol polyoxyethylene ether, alkylphenol polyoxyethylene ether and sec-octanol polyoxyethylene ether, wherein the alkylphenol polyoxyethylene ether is one of nonylphenol polyoxyethylene ether, octylphenol polyoxyethylene ether and dodecyl polyoxyethylene ether.

A preparation method of nano zinc oxide antibacterial antiviral spray comprises the following steps:

the method comprises the following steps: weighing deionized water and an aldehyde removing agent according to the formula ratio, stirring in a stirrer, and stirring at the rotating speed of 500-;

step two: the rotating speed of the stirrer is reduced to 500r/min for 300-.

When the nano zinc oxide antibacterial antiviral spray is applied, the spray and common wall paint are uniformly mixed according to the weight ratio of 1:8-12 to obtain multifunctional paint, and then the multifunctional paint is painted or coated on the surface of an indoor wall. The spray is directly mixed with common wall paint according to the weight ratio of 1:8-12, wherein the common wall paint accounts for 8-12 parts by weight, the nano zinc oxide antibacterial and antiviral spray accounts for 1 part by weight, the multifunctional paint with the functions of resisting mildew, resisting bacteria, removing aldehyde and the like can be obtained after even stirring, and finally the multifunctional paint is painted on the surface of a wall. Therefore, after the multifunctional paint is coated, other measures for removing aldehyde, preventing mildew, resisting bacteria or viruses and the like are not needed indoors, the use is very convenient, and the multifunctional paint has very strong practicability. Of course, conventional methods of use may also be employed: the spray is directly atomized by a spray can and then sprayed on the wall surface of a room. The two using methods can achieve the beneficial effects of indoor formaldehyde removal, mildew prevention, antibiosis or antivirus.

Preparation of the first, examples and comparative examples