阅读说明：本技术 一种促淋巴循环的体雕磁疗布 (Body carving magnetic therapy cloth promoting lymphatic circulation ) 是由 张惠生 黄飞 于 2019-11-29 设计创作，主要内容包括：本发明提供一种促淋巴循环的体雕磁疗布,包括以下重量份原料：磁性颗粒10～25份、粘合剂20～25份,甲壳素纤维15～22份,剑麻纤维18～23份、紫藤纤维20～28份、生姜纤维15～25份,所述磁性颗粒为铁氧体永磁微粒料,粘合剂为3：1～2重量份比的石菖蒲提取物和艾叶提取物；采用磁性颗粒结合粘合剂、植物纤维,科学配伍进行纺织,调整纺织方法,使得磁性颗粒融入面料中能够与植物纤维充分发挥其作用,人体穿戴后,刺激淋巴,促进血液循环。(The invention provides a body carving magnetic therapy cloth for promoting lymphatic circulation, which comprises the following raw materials in parts by weight: 10-25 parts of magnetic particles, 20-25 parts of adhesive, 15-22 parts of chitin fiber, 18-23 parts of sisal fiber, 20-28 parts of wisteria fiber and 15-25 parts of ginger fiber, wherein the magnetic particles are ferrite permanent magnetic particles, and the adhesive is 3: 1-2 parts by weight of a grass-leaved sweetflag extract and a folium artemisiae argyi extract; the magnetic particles are combined with the adhesive and the plant fibers, the textile is carried out through scientific compatibility, the textile method is adjusted, the magnetic particles are blended into the fabric, the function of the fabric can be fully exerted with the plant fibers, and the magnetic particles stimulate lymph and promote blood circulation after being worn by a human body.)

1. The utility model provides a promote body carving magnetotherapy cloth of lymph circulation which characterized in that: the feed comprises the following raw materials in parts by weight: 10-25 parts of magnetic particles, 20-25 parts of adhesive, 15-22 parts of chitin fiber, 18-23 parts of sisal fiber, 20-28 parts of wisteria fiber and 15-25 parts of ginger fiber, wherein the magnetic particles are ferrite permanent magnetic particles, and the adhesive is 3: 1-2 parts by weight of rhizoma acori graminei extract and folium artemisiae argyi extract.

2. The body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 1, characterized in that: the feed comprises the following raw materials in parts by weight: 18 parts of magnetic particles, 22 parts of adhesive, 18 parts of chitin fiber, 20 parts of sisal fiber, 24 parts of wisteria fiber and 20 parts of ginger fiber, wherein the magnetic particles are ferrite permanent magnetic particles, and the adhesive is 3: 1.5 parts by weight of the grass-leaved sweetflag extract and the folium artemisiae argyi extract.

3. The body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 1, characterized in that: the chitin fiber is prepared by crushing and drying shrimp and crab shell powder, performing ultrasonic treatment, adding acid protease for enzymolysis to obtain chitin, performing deacetylation to generate chitosan, dissolving the chitosan in dilute acetic acid solution to form chitosan spinning solution, and spinning.

4. The body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 1, characterized in that: the acorus gramineus solander extract is prepared by putting crushed acorus gramineus solander powder into an ultrasonic extractor, soaking in 8-28 times of water for 30-80 min, extracting for 80-100 min at the ultrasonic frequency of 50-80 kHz and the temperature of 60-80 ℃, extracting for 1-3 times, and drying.

5. The body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 1, characterized in that: the folium artemisiae argyi extract is prepared by crushing folium artemisiae argyi raw materials, adding an alcohol solvent with the mass concentration of 40-60%, performing reflux extraction for 2-4 times, filtering, and concentrating until the relative density is 1.2-1.5.

6. The body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 3, characterized in that: the protease is one or a combination of trypsin, subtilisin and papain, and the enzymolysis time is 2-8 h.

7. The preparation method of the body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 1, characterized in that:

s1, warp yarns: weaving chitin fibers and sisal fibers into blended yarns with linear density of 17-20 tex, wherein the average width of gaps among the yarns is 80-150 mu m;

s2, weft yarn: weaving the wisteria fibers and the ginger fibers into blended yarns with the linear density of 21-35 tex, wherein the average width of gaps among the yarns is 40-80 mu m;

s3, grey cloth: weaving warp yarns and weft yarns by a weaving machine in a ground weave of 3/1 right twill and a heavy flat edge weave of 2/2 to prepare grey cloth;

s4, magnetic therapy cloth: soaking the grey cloth in an adhesive, soaking in a water bath at 50-80 ℃ for 200-400 min, freeze-drying, taking out the grey cloth, performing electron beam or plasma pre-irradiation treatment, grafting magnetic particles onto the grey cloth, and drying at 100-150 ℃ for 80-120 s to obtain the magnetic therapy cloth.

8. The preparation method of the body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 7, characterized in that: in the step S4, the substrate is irradiated by 43-50 KGy electron beams.

9. The preparation method of the body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 7, characterized in that: in the step S4, the energy generated by the pre-irradiation accelerator is 7-15 Mev, and the irradiation dose rate is 50-80 Gy/S.

10. The body carving magnetic therapy cloth for promoting lymphatic circulation as claimed in claim 1, characterized in that: the magnetic therapy cloth can be used for body carving armpit cloth to promote lymphatic circulation.

Technical Field

The invention relates to the field of textiles, in particular to body carving magnetic therapy cloth for promoting lymphatic circulation.

Background

Lymphatic circulation is one of physiological functional body circulation of human body, lymphatic fluid is interstitial tissue fluid in cells, and flows back into veins through lymphatic vessels, limb lymphedema is formed by edema due to lymphatic return obstruction, rapid accumulation of fluid and protein in superficial soft tissues, and high-concentration protein causes increase of limb osmotic pressure in tissues, so that edema and secondary inflammation are caused, fascia and skin are thickened and rough, and the like. At present, except for improvement of drug treatment, the improvement is carried out by sequentially appearing a medicine patch, a bra, a body shaping clothes and the like through physical stimulation, but many effects are not good, and used cloth and materials are not improved, and phenomena of chest oppression, unsmooth breathing, allergy and the like can be caused.

Disclosure of Invention

In view of this, the invention provides a body carving magnetic therapy cloth for promoting lymphatic circulation, which solves the above problems.

The technical scheme of the invention is realized as follows: a body carving magnetotherapy cloth for promoting lymphatic circulation: the feed comprises the following raw materials in parts by weight: 10-25 parts of magnetic particles, 20-25 parts of adhesive, 15-22 parts of chitin fiber, 18-23 parts of sisal fiber, 20-28 parts of wisteria fiber and 15-25 parts of ginger fiber, wherein the magnetic particles are ferrite permanent magnetic particles, and the adhesive is 3: 1-2 parts by weight of a grass-leaved sweetflag extract and a folium artemisiae argyi extract;

further, promote body carving magnetotherapy cloth of lymph circulation, its characterized in that: the composite material comprises the following raw materials in parts by weight: 18 parts of magnetic particles, 22 parts of adhesive, 18 parts of chitin fiber, 20 parts of sisal fiber, 24 parts of wisteria fiber and 20 parts of ginger fiber, wherein the magnetic particles are ferrite permanent magnetic particles, and the adhesive is 3: 1.5 parts by weight of rhizoma acori graminei extract and folium artemisiae argyi extract;

further, crushing and drying the chitin fiber by shrimp and crab shell powder, performing ultrasonic treatment, adding acid-containing protease for enzymolysis for 2-8 hours to obtain chitin, performing deacetylation to generate chitosan, dissolving the chitosan in a dilute acetic acid solution to form a chitosan spinning stock solution, and spinning to obtain the chitin fiber, wherein the protease is one or a combination of trypsin, subtilisin and papain;

further, the rhizoma acori graminei extract is prepared by placing crushed rhizoma acori graminei powder into an ultrasonic extractor, soaking in 8-28 times of water for 30-80 min, extracting for 80-100 min at an ultrasonic frequency of 50-80 kHz and a temperature of 60-80 ℃, extracting for 1-3 times, and drying to obtain the rhizoma acori graminei extract;

further, the folium artemisiae argyi extract is prepared by crushing folium artemisiae argyi raw materials, adding an alcohol solvent with the mass concentration of 40-60%, performing reflux extraction for 2-4 times, filtering, and concentrating until the relative density is 1.2-1.5;

further, a preparation method of the body carving magnetic therapy cloth for promoting lymphatic circulation comprises the following steps:

s1, warp yarns: weaving chitin fibers and sisal fibers into blended yarns with linear density of 17-20 tex, wherein the average width of gaps among the yarns is 80-150 mu m;

s2, weft yarn: weaving the wisteria fibers and the ginger fibers into blended yarns with the linear density of 21-35 tex, wherein the average width of gaps among the yarns is 40-80 mu m;

s3, grey cloth: weaving warp yarns and weft yarns by a weaving machine in a ground weave of 3/1 right twill and a heavy flat edge weave of 2/2 to prepare grey cloth;

s4, magnetic therapy cloth: soaking gray fabric in an adhesive, soaking in a water bath at 50-80 ℃ for 200-400 min, freeze-drying, taking out the gray fabric, performing 43-50 KGy electron beam radiation or plasma pre-irradiation treatment on the gray fabric, grafting magnetic particles onto the gray fabric, and drying at 100-150 ℃ for 80-120 s to obtain the magnetic therapy cloth, wherein the energy generated by a pre-irradiation accelerator is 7-15 Mev, and the irradiation dose rate is 50-80 Gy/s;

furthermore, the magnetic therapy cloth can be used for body carving armpit cloth to promote lymphatic circulation.

Compared with the prior art, the invention has the beneficial effects that:

the magnetic therapy cloth adopts the magnetic particles combined with the adhesive and the plant fiber, the scientific compatibility is adopted for spinning, the textile method is adjusted, the magnetic particles are blended into the fabric and can fully play the role with the plant fiber, after being worn by a human body, the cells are activated, the lymph is stimulated, and the blood circulation is promoted, wherein, chemically active chitin fiber, sisal fiber, wisteria fiber and ginger fiber are adopted to prepare warp-weft blended yarn, the warp-weft blended yarn has good adsorption, bonding, sterilization, ventilation and other excellent performances, the grassleaf sweelflag rhizome extract and the argy wormwood leaf extract are combined to soak the yarn so as to increase the flexibility of the yarn, the tingling feeling of the fiber is removed, the effect of smoothness is achieved, the comfort of the skin is improved, the ferrite permanent magnetic particles are implanted into the yarn so as to be organically combined together, the magnetic particles can stimulate the acupuncture points of meridian to enable the cloth to have the, the blood reflux rate is improved, and lymph nodes can be effectively reduced.

Detailed Description

In order to better understand the technical content of the invention, specific examples are provided below to further illustrate the invention.

The experimental methods used in the examples of the present invention are all conventional methods unless otherwise specified.

The materials, reagents and the like used in the examples of the present invention can be obtained commercially without specific description.