阅读说明：本技术 一种雪尼尔双面绒面料的加工工艺 (Processing technology of chenille double-faced velvet fabric ) 是由 唐海国 石大均 田春生 黄伟 朱伟强 于 2019-11-26 设计创作，主要内容包括：本发明公开了一种雪尼尔双面绒面料的加工工艺,工艺流程如下,织胚→染色→缸中硅油→干布→梳毛→成定,其中,织胚：采用纬编提花编织布、雪妮尔全涤毛纱,用双面针法编织成双面绒面料。该雪尼尔双面绒面料的加工工艺制得的成品具有非常好的面料保暖功能和穿着舒适性,并且使绒毛更加蓬松厚实,提升面料档次。(The invention discloses a processing technology of chenille two-sided velvet fabric, which comprises the following process flows of weaving blank → dyeing → silicone oil in a cylinder → dry cloth → carding → finishing, wherein the weaving blank: the weft-knitted jacquard woven cloth and the Xuenier polyester wool yarn are adopted to be woven into the double-faced velvet fabric by a double-faced needle method. The finished product made by the processing technology of the chenille double-faced velvet fabric has a good fabric warm-keeping function and wearing comfort, fluff is enabled to be more fluffy and thick, and the grade of the fabric is improved.)

1. A processing technology of chenille double-faced velvet fabric is characterized in that: the process flow is as follows, weaving blank → dyeing → silicone oil in the vat → dry cloth → wool combing → finalizing, wherein,

weaving embryo: weaving a double-sided velvet fabric;

dyeing: 1% degreasing agent, 0.4% K-EC yellow brown, 1% HAC, 0.13% S-2GH ruby, 0.1% leveling agent, 0.275% HGL deep blue, and a temperature of 135 ℃ multiplied by 30';

silicon oil in the cylinder: cooling with 0.2g/L citric acid and 3g/L888L for 20min, and taking out;

drying the cloth: 8-box door Fuji setting machine is multiplied by 26 meters/min at 140 ℃;

combing: carding fluffs lightly on two sides of the carding machine;

and (3) finalizing: and (3) carrying out finished product shaping by 0.2g/L citric acid and 10g/L soft-feel silicone oil at 130 ℃ for 30 m/min.

2. The processing technology of the chenille double-faced pile fabric according to claim 1, characterized in that: the double-faced pile fabric is knitted by weft knitting jacquard woven cloth and chenille full polyester wool yarns.

3. The processing technology of the chenille double-faced pile fabric according to claim 1, characterized in that: combing until the hair surface is vertical.

The technical field is as follows:

the invention relates to the technical field of textile printing and dyeing, and discloses a processing technology of chenille double-faced velvet fabric.

Background art:

the existing chenille corduroy fabric is insufficient in heat retention and limited in use.

The invention content is as follows:

the invention aims to solve the technical problem of providing a processing technology of a looped pile fabric with a bright suction and discharge function, which is comfortable to wear and has strong bright and suction and discharge functions.

The technical scheme of the invention is to provide a processing technology of chenille double-sided velvet fabric, which is characterized in that: the process flow is as follows, weaving blank → dyeing → silicone oil in the vat → dry cloth → wool combing → finalizing, wherein,

weaving embryo: weft knitting jacquard weaving cloth and chenille full polyester wool yarns are adopted to be woven into a width by a double-faced needle method: 152cm of double-sided velvet fabric with the gram weight of 450-480g/m 2;

dyeing: 1% degreasing agent 3302, 0.4% K-ECO yellow brown, 1% HAC, 0.13% S-2GH ruby, 0.1% leveling agent 3000core, 0.275% HGL deep blue, 135 ℃ x 30';

silicon oil in the cylinder: 0.2g/L citric acid, 3g/L888L (Hanbang) cold running for 20 min;

drying the cloth: 8-box door Fuji setting machine is multiplied by 26 meters/min at 140 ℃;

combing: lightly combing fluff on two sides of a carding machine based on the vertical state of the fluff side;

and (3) finalizing: 0.2g/L citric acid and 10g/L soft silicone oil are used for shaping finished products at 130 ℃ by 30 m/min, and 8-box Mengfush shaping machine is used.

Compared with the prior art, the invention has the following advantages after the process is adopted: the style of the fabric is changed into a double-faced velvet effect through the change of weaving, so that the warm keeping function and the wearing comfort of the fabric are enhanced; the two sides of the finished product are carded, so that the fluff is more fluffy and thick, and the grade of the fabric is improved.

The specific implementation mode is as follows:

the invention is further illustrated with respect to specific embodiments below:

a processing technology of chenille double-faced velvet fabric is characterized in that: the process flow is as follows, weaving blank → dyeing → silicone oil in the vat → dry cloth → wool combing → finalizing, wherein,

weaving embryo: weft knitting jacquard weaving cloth and chenille full polyester wool yarns are adopted to be woven into a width by a double-faced needle method: 152cm of double-sided velvet fabric with the gram weight of 450-480g/m 2;

dyeing: 1% degreasing agent 3302, 0.4% K-ECO yellow brown, 1% HAC, 0.13% S-2GH ruby, 0.1% leveling agent 3000core, 0.275% HGL deep blue, 135 ℃ x 30';

silicon oil in the cylinder: 0.2g/L citric acid, 3g/L888L (Hanbang) cold running for 20 min;

drying the cloth: 8-box door Fuji setting machine is multiplied by 26 meters/min at 140 ℃;

combing: lightly combing fluff on two sides of a carding machine based on the vertical state of the fluff side;

and (3) finalizing: 0.2g/L citric acid and 10g/L soft silicone oil are used for shaping finished products at 130 ℃ by 30 m/min, and 8-box Mengfush shaping machine is used.

The foregoing is illustrative of the preferred embodiments of the present invention only and is not to be construed as limiting the claims.