阅读说明：本技术 一种丝滑哥弟布的加工工艺 (Processing technology of silky brother cloth ) 是由 李金仓 王松强 刘强 张仁勇 于中正 于 2019-10-13 设计创作，主要内容包括：本发明公开了一种丝滑哥弟布的加工工艺,工艺流程如下,织胚→松布开幅→高温前处理→染人造棉→染锦纶→干布→加硅油成品定型,其中,织胚：选用50SR紧密纺+40D/1F尼龙高弹丝为原料,经纬编织造而成双面结构的珠地面料。该丝滑哥弟布的加工工艺生产的哥弟布增强成衣合身可塑性,提升成品面料水洗撞白色牢度。(The invention discloses a processing technology of silkie cloth, which comprises the following process flows of weaving blank → opening of loose cloth → high-temperature pretreatment → dyeing artificial cotton → dyeing nylon → drying cloth → adding silicone oil to form a finished product, wherein the weaving blank comprises the following components in parts by weight: 50SR compact spinning and 40D/1F nylon high-elastic yarns are selected as raw materials, and the bead ground fabric with a double-sided structure is woven by warps and wefts. The brother cloth produced by the processing technology of the silky brother cloth enhances the fitting plasticity of ready-made clothes and improves the washing and striking color fastness of the finished fabric.)

1. A processing technology of silky brother cloth is characterized in that: the process flow is as follows, weaving blank → opening of loose cloth → high-temperature pretreatment → dyeing artificial cotton → dyeing chinlon → dry cloth → adding silicone oil finished product for shaping, wherein,

weaving embryo: selecting 50SR compact spinning and 40D/1F nylon high-elastic yarns as raw materials, and weaving the raw materials into the bead-ground fabric with a double-sided structure through warp and weft weaving;

loosening cloth and scutching: loosening the rolled gray cloth by a cylindrical cloth loosening machine, then breaking the width of the rolled gray cloth along a width opening line by an overhead width opening machine, and then putting the obtained cloth into a cylinder;

high-temperature pretreatment: adopting Italian Pazoni high-temperature jar for production, adding a penetrant and an oil removing agent into the jar, heating to 120 ℃ and 135 ℃, keeping the temperature for 20-30 minutes, and then carrying out oil removing pre-shrinkage treatment on the gray cloth;

dyeing artificial cotton and chinlon: the active material is adopted to keep the temperature at 50-60 ℃ for 50-65 minutes and then dye the rayon, and then the acid dye is used to keep the temperature at 90-100 ℃ for 15-25 minutes and dye the nylon, and the excellent color fastness is ensured after the full post-treatment;

drying cloth, and preparing fixed silicone oil: after the cloth is dried at the temperature of 155 ℃ for 140 plus materials of the door Fuji 8-box setting machine, the smooth silicone oil is added, and the finished product is set at the temperature of 160 ℃ for 155 plus materials.

The technical field is as follows:

the invention relates to the technical field of textile printing and dyeing, and discloses a processing technology of silky brother cloth.

Background art:

the existing Ge brother cloth is smooth, has more and less stiffness, and limits the body fitting plasticity of ready-made clothes.

The invention content is as follows:

the technical problem to be solved by the invention is to provide a smooth and stiff processing technology of silky brother cloth, and the brother cloth produced by the technology enhances the fit plasticity of ready-made clothes and improves the color fastness of finished fabrics after washing and hitting.

The technical scheme of the invention is to provide a processing technology of silkie cloth, which comprises the following process flows of weaving blank → opening of loose cloth → high-temperature pretreatment → dyeing artificial cotton → dyeing nylon → dry cloth → adding silicone oil for finished product shaping, wherein,

weaving embryo: selecting 50SR compact spinning and 40D/1F nylon high-elastic yarn as raw materials, and weaving the raw materials into the bead ground fabric with a double-sided structure by warp and weft knitting, wherein the width of the bead ground fabric is as follows: 160cm, gram weight: 180 grams per square meter;

loosening cloth and scutching: loosening the rolled gray cloth by a cylindrical cloth loosening machine, then breaking the width of the rolled gray cloth along a width opening line by an overhead width opening machine, and then putting the obtained cloth into a cylinder;

high-temperature pretreatment: produced by adopting an Italian Pazoni high-temperature jar, 1% of TF-107T chemical transfer penetrant and 0.6% of Degao degreaser are added into the jar, and the temperature is raised to 130 ℃ and kept for 30 minutes, and then the blank cloth is subjected to degreasing pre-shrinkage treatment;

dyeing artificial cotton and chinlon: the rayon is dyed by using a beautiful source active material after being kept at 60 ℃ for 60 minutes, and then nylon is dyed by using a polynite acid series dye after being kept at 98 ℃ for 20 minutes, so that the excellent color fastness is ensured after full post-treatment;

drying cloth, and preparing fixed silicone oil: drying cloth at 150 ℃ by using a gate Fuji 8-box setting machine, adding smooth silicone oil, and setting a finished product at 160 ℃.

Compared with the prior art, the invention has the following advantages after the process is adopted: the artificial cotton and the chinlon are blended, so that the stiffness and the smoothness of the fabric are greatly improved, and the fitting plasticity of ready-made clothes is enhanced; before dyeing, the fabric shrinks at 130 ℃ multiplied by 30' at high temperature to make the fabric compact and thick. The rayon and the chinlon are dyed by the active material at the temperature of 60 ℃ and the acid material at the temperature of 98 ℃, and are dyed separately, so that the washing and white hitting fastness of the finished fabric is greatly improved, and the color tone consistency of the rayon and the chinlon is ensured; the finished product is fixed by drying the cloth and then adding the silicone oil, and the qualification of various physical indexes of the finished fabric is guaranteed. The hand feeling is smooth and stiff.

The specific implementation mode is as follows:

the invention is further illustrated with respect to specific embodiments below:

a processing technology of silky brother cloth comprises the following process flows of weaving blank → opening of pine cloth → high-temperature pretreatment → dyeing artificial cotton → dyeing chinlon → dry cloth → adding silicone oil to finish shaping, wherein,

weaving embryo: selecting 50SR compact spinning and 40D/1F nylon high-elastic yarn as raw materials, and weaving the raw materials into the bead ground fabric with a double-sided structure by warp and weft knitting, wherein the width of the bead ground fabric is as follows: 160cm, gram weight: 180 grams per square meter;

loosening cloth and scutching: loosening the rolled gray cloth by a cylindrical cloth loosening machine, then breaking the width of the rolled gray cloth along a width opening line by an overhead width opening machine, and then putting the obtained cloth into a cylinder;

high-temperature pretreatment: produced by adopting an Italian Pazoni high-temperature jar, 1% of TF-107T chemical transfer penetrant and 0.6% of Degao degreaser are added into the jar, and the temperature is raised to 130 ℃ and kept for 30 minutes, and then the blank cloth is subjected to degreasing pre-shrinkage treatment;

dyeing artificial cotton and chinlon: the rayon is dyed by using a beautiful source active material after being kept at 60 ℃ for 60 minutes, and then nylon is dyed by using a polynite acid series dye after being kept at 98 ℃ for 20 minutes, so that the excellent color fastness is ensured after full post-treatment;

drying cloth, and preparing fixed silicone oil: drying cloth at 150 ℃ by using a gate Fuji 8-box setting machine, adding smooth silicone oil, and setting a finished product at 160 ℃.

The invention has the following advantages: the artificial cotton and the chinlon are blended, so that the stiffness and the smoothness of the fabric are greatly improved, and the fitting plasticity of ready-made clothes is enhanced; before dyeing, the fabric shrinks at 130 ℃ multiplied by 30' at high temperature to make the fabric compact and thick. The rayon and the chinlon are dyed by the active material at the temperature of 60 ℃ and the acid material at the temperature of 98 ℃, and are dyed separately, so that the washing and white hitting fastness of the finished fabric is greatly improved, and the color tone consistency of the rayon and the chinlon is ensured; the finished product is fixed by drying the cloth and then adding the silicone oil, and the qualification of various physical indexes of the finished fabric is guaranteed. The hand feeling is smooth and stiff.

The foregoing is illustrative of the preferred embodiments of the present invention only and is not to be construed as limiting the claims.