阅读说明：本技术 聚碳酸酯用于制造中空容器的用途 (Polycarbonate is used to manufacture the purposes of hollow container ) 是由 A·S·塞拉克丹 R·K·辛格 P·塔瓦马尼 T·赛德 于 2018-05-08 设计创作，主要内容包括：本发明涉及通过双酚和二芳基碳酸酯的酯交换制备并且具有22000至32000g/mol的粘均分子量Mv、1.8-3.2的定义为Mw/Mn的多分散性、根据ASTM D 1238(1.2kg,300℃)测定的3.0-10g/10min的熔体流动指数、750至2500ppm的弗利斯支化的量的芳族聚碳酸酯用于借助注射吹塑或挤出吹塑法制造具有至少15升的体积的瓶子的用途。(The purposes of the bottle at least 15 liters of volume by injection-blow molding or extrusion blow molding processes manufacture is prepared and is used for the polydispersity that the definition of 22000 to 32000g/mol viscosity average molecular weigh Mv, 1.8-3.2 is Mw/Mn, according to the aromatic polycarbonate of the melt flow index of the 3.0-10g/10min of ASTM D 1238 (1.2kg, 300 DEG C) measurement, the amount of 750 to 2500ppm fries branching the present invention relates to the transesterification by bis-phenol and diaryl carbonate.)