阅读说明：本技术 一种加工首饰的方法 (A method of processing jewellery ) 是由 郭华智 于 2018-05-26 设计创作，主要内容包括：本发明公开的一种加工首饰的方法,将原料置入蜡模中,加工成所需形状胚后通过真空加压机直接一体成形。本发明的优点在于,现将首饰一体成形,节省大量时间,无需人工进行焊接,由于没有焊料的加入,可最完善的保留含金量,最高可达到万足金。(A kind of method for processing jewellery disclosed by the invention, raw material is placed in wax-pattern, is integrally formed after being processed into required shape embryo by vacuum pressed machine.It is an advantage of the current invention that existing that jewellery are integrally formed, the plenty of time is saved, without manually being welded, due to the addition of not no solder, reservation gold content that can be most perfect can reach ten thousand pure golds.)

1. a kind of method for processing jewellery, which is characterized in that this method comprises the following steps:

Raw material is placed in wax-pattern, is integrally formed after being processed into required shape embryo by vacuum pressed machine.

2. the method for processing jewellery according to claim 1, which is characterized in that wax-pattern is passed through five in the method step Axis carving machine makes the mold of different metal materials, different pattern, then raw material is placed in wax-pattern.

3. the method for processing jewellery according to claim 1, which is characterized in that the temperature of the vacuum pressed machine is in 65- 110 degree, air pressure is in 0.8-1.2mpa, pressing time 7-12 second.

Technical field

The invention belongs to jewelry-making processing technique field, specially a kind of method for processing jewellery.

Background technique

The routine techniques for processing jewellery such as bracelet currently on the market is by after the processing of product bulk-breaking, and Combination Welding forms, Such mode can devote a tremendous amount of time, and increase manpower and material resources, due to when welding needing that solder is added, so will lead to finished product The defect of gold content decline, top are only capable of producing the ornaments of thousand pure gold gold contents.

Summary of the invention

The time for processing jewellery for the solution prior art is long, and the technological deficiency for causing finished product gold content to decline, the present invention mentions A kind of method for processing jewellery is supplied, the purpose of realization is that jewellery are integrally formed, the saving plenty of time can be achieved, without artificial It is welded, due to the addition of not no solder, reservation gold content that can be most perfect can reach ten thousand pure golds.

To achieve the goals above, the present invention is the following technical schemes are provided: a kind of side for processing jewellery disclosed by the invention Method includes the following steps: for raw material to be placed in wax-pattern, be processed into after required shape embryo by vacuum pressed machine directly one at Shape.

Further, in order to increase more patterns to the jewellery of processing, layering and internal layer flower are directly realized by mold Wax-pattern is made the mold of different metal materials, different pattern by five axis carving machines, then raw material is placed in wax-pattern by silk.And Layering is to be welded with filigree in the prior art, can be just combined together.

Further, the temperature of the vacuum pressed machine is in 65-110 degree, and air pressure is in 0.8-1.2mpa, pressing time 7-12 Second.The operating condition of vacuum pressed machine can be such that jewellery are integrally formed, and shaping form is good and guarantees process time most It is short, improve production efficiency.

By adopting the above technical scheme, the beneficial effect comprise that can realize jewellery are integrally formed, when saving a large amount of Between, without manually being welded, due to the addition of not no solder, reservation gold content that can be most perfect can reach ten thousand pure golds.