阅读说明：本技术 基于氯乙烯的树脂乳胶组合物及其制备方法 (Vinyl chloride-based resin latex composition and method for preparing the same ) 是由 金汝珍 金载松 辛莲兰 张太荣 于 2018-03-21 设计创作，主要内容包括：本发明提供了一种通过引入固相苯乙烯/丙烯酸树脂来制备机械稳定性大大改善的基于氯乙烯的树脂胶乳组合物的方法,以及由此制备的基于氯乙烯的树脂胶乳组合物。(The present invention provides a method for preparing a vinylchloride-based resin latex composition with greatly improved mechanical stability by incorporating a solid-phase styrene/acrylic resin, and a vinylchloride-based resin latex composition prepared thereby.)

1. A method of preparing a vinylchloride-based resin latex composition, the method comprising:

Mixing a vinylchloride-based resin latex including a vinylchloride-based resin with a solid-phase styrene/acrylic resin to prepare a mixture; and

adding an alkaline additive to the mixture,

Wherein the styrene/acrylic resin is mixed in an amount of 2 to 50 parts by weight with respect to 100 parts by weight of a solid content including the vinylchloride-based resin in the vinylchloride-based resin latex.

2. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the styrene/acrylic resin is an alkali-soluble resin.

3. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the styrene/acrylic resin is a copolymer obtained by polymerizing a styrene-based monomer and an acrylic monomer in a weight ratio of 60:40 to 80: 20.

4. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein a weight average molecular weight (Mw) of the styrene/acrylic resin is 1000 to 20,000 g/mol.

5. The method of preparing a vinyl chloride-based resin latex composition according to claim 1, wherein the vinyl chloride-based resin includes one or more selected from the group consisting of a vinyl chloride homopolymer, a vinyl chloride/vinyl acetate copolymer, and a vinyl chloride/acrylic copolymer.

6. The method of preparing a vinyl chloride-based resin latex composition according to claim 5, wherein the vinyl chloride/vinyl acetate copolymer is obtained by polymerizing a vinyl chloride monomer and a vinyl acetate monomer in a weight ratio of 9:1 to 3: 7.

7. The method of preparing a vinyl chloride-based resin latex composition according to claim 5, wherein the vinyl chloride/acrylic copolymer is obtained by polymerizing a vinyl chloride monomer and an acrylic monomer in a weight ratio of 9:1 to 5: 5.

8. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the vinylchloride-based resin latex has an average particle diameter (D50) of 0.1 μ ι η to 1 μ ι η.

9. the method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the vinylchloride-based resin latex has a weight-average molecular weight of 45,000 to 300,000 g/mol.

10. the method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the vinylchloride-based resin latex includes a vinylchloride homopolymer, and has a weight-average molecular weight of 45,000 to 150,000g/mol and an average particle diameter (D50) of 0.1 to 0.7 μ ι η.

11. The method of preparing a vinyl chloride-based resin latex composition according to claim 1, wherein the vinyl chloride-based resin latex comprises a vinyl chloride/vinyl acetate copolymer obtained by polymerizing a vinyl chloride monomer and a vinyl acetate monomer in a weight ratio of 8:2 to 3:7, and has a weight average molecular weight of 45,000 to 150,000g/mol and an average particle diameter (D50) of 0.1 to 0.7 μ ι η.

12. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the vinylchloride-based resin latex includes a vinylchloride/acrylic copolymer obtained by polymerizing a vinylchloride monomer and an acrylic monomer in a weight ratio of 8:2 to 5:5, and has a weight average molecular weight of 45,000 to 200,000g/mol and an average particle diameter (D50) of 0.1 to 0.7 μ ι η.

13. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein a solid content including the vinylchloride-based resin in the vinylchloride-based resin latex is 30 to 60 wt%.

14. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the basic additive includes one or more selected from ammonia, an amine-based compound, and a hydroxide.

15. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the addition of the basic additive is performed at a temperature of 40 ℃ to 90 ℃.

16. The method of preparing a vinylchloride-based resin latex composition according to claim 1, wherein the basic additive is added in an amount such that the vinylchloride-based resin latex composition has a pH of 7 to 9.

17. A vinylchloride-based resin latex composition comprising a vinylchloride-based resin latex containing a vinylchloride-based resin, a styrene/acrylic resin, and an alkaline additive, wherein the styrene/acrylic resin is included in an amount of 2 to 50 parts by weight, relative to 100 parts by weight of a solid content including the vinylchloride-based resin in the vinylchloride-based resin latex.

Technical Field

The present application is based on and claims priority from korean patent application No. 10-2017-0055673 filed on 28/4/2017, the entire contents of which are incorporated herein by reference.

The present invention relates to a vinylchloride-based resin latex composition with greatly improved mechanical stability and a method for preparing the same.

Background

A vinyl chloride paste resin (hereinafter, referred to as "PSR") is a general-purpose resin that has been widely used for building products, daily necessities (such as wallpaper, artificial leather, fabrics, sheets, films, etc.), and industrial products.

The vinyl chloride paste resin is prepared by preparing a latex by emulsion polymerization or seeded emulsion polymerization in a polymerization system comprising vinyl chloride monomer together with a polymerization initiator, an emulsifier (surfactant), a catalyst and other additives, and then drying the latex to obtain a powdery resin.

The latex is an emulsion mixture of vinyl chloride resin and water generated as a result of polymerization, and its stability varies depending on various factors such as the residual amount of vinyl chloride monomer, the kind and content of emulsifier, and the like.

If the latex is poor in mechanical stability, the vinyl chloride resin in the latex is agglomerated upon application of a shearing force to perform mixing or processing, and as a result, flowability is deteriorated, thereby being difficult to use.

Disclosure of Invention

[ problem ] to provide a method for producing a semiconductor device

In order to solve the problems of the prior art as described above, it is an object of the present invention to provide a vinylchloride-based resin latex composition with greatly improved mechanical stability, and a method for preparing the same.

[ technical solution ] A

To achieve the above objects, one embodiment of the present invention provides a method for preparing a vinylchloride-based resin latex composition, the method including the steps of:

Mixing a vinylchloride-based resin latex including a vinylchloride-based resin with a solid-phase styrene/acrylic resin to prepare a mixture; and

Adding an alkaline additive to the mixture,

Wherein the styrene/acrylic resin is mixed in an amount of 2 to 50 parts by weight with respect to 100 parts by weight of a solid content including the vinylchloride-based resin in the vinylchloride-based resin latex.

another embodiment of the present invention provides a vinylchloride-based resin latex composition prepared by the above-described method, including a vinylchloride-based resin latex containing a vinylchloride-based resin, a styrene/acrylic resin, and an alkaline additive, wherein the styrene/acrylic resin is included in an amount of 2 to 50 parts by weight, relative to 100 parts by weight of a solid content including the vinylchloride-based resin in the vinylchloride-based resin latex.

[ PROBLEMS ] the present invention

According to the method of preparing a vinylchloride-based resin latex composition of the present invention, a vinylchloride-based resin latex is mixed with a solid-phase styrene/acrylic resin, thereby preparing a vinylchloride-based resin latex composition with greatly improved mechanical stability, in which agglomeration of the latex can be prevented without modifying a vinylchloride-based resin itself.

Therefore, the vinylchloride-based resin latex composition prepared according to the preparation method may be effectively applied to PVC leather or textile adhesives, gravure ink adhesives for wallpaper, inkjet printing paper, or film absorbing layers, non-combustible coatings for wood or exterior wall panels, non-combustible coatings for non-woven fabrics, air filters, car carpets, and the like.

Drawings

FIG. 1 is a photograph showing the state of an aqueous latex composition of vinyl chloride/vinyl acetate copolymer resin prepared in example 1 when mixing was performed at 7000rpm for 2 hours.

FIG. 2 is a photograph showing the state of the aqueous latex composition of vinyl chloride/vinyl acetate copolymer resin prepared in comparative example 2 when mixing time was 20 minutes at 7000 rpm.

Detailed Description

Hereinafter, the present invention will be described in more detail. In addition, while the invention is susceptible to various modifications and alternative forms, specific embodiments thereof are shown and described in detail below. It should be understood, however, that the description is not intended to limit the invention to the particular forms disclosed, but on the contrary, the intention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention.

The term "comprises/comprising" when used in this specification is taken to specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but does not preclude the presence or addition of other features, regions, integers, steps, operations, elements, and/or components.

hereinafter, the vinylchloride-based resin latex composition of the present invention and the preparation method thereof will be described in more detail.

The method of preparing a vinylchloride-based resin latex composition according to an embodiment of the present invention may include the steps of:

Mixing a vinylchloride-based resin latex including a vinylchloride-based resin and a solid-phase styrene/acrylic resin to prepare a mixture (step 1); and

Adding a basic additive to the mixture (step 2),

Wherein the styrene/acrylic resin is mixed in an amount of 2 to 50 parts by weight with respect to 100 parts by weight of a solid content including the vinylchloride-based resin in the vinylchloride-based resin latex.

In the present invention, the vinylchloride-based resin latex composition refers to a composition in the form of an emulsion, and may include a solid-phase styrene/acrylic resin dissolved in the vinylchloride-based resin latex including a vinylchloride-based resin, or may include a dispersion of a core-shell structure formed of a vinylchloride-based resin and a styrene/acrylic resin.

Hereinafter, each step of the method of preparing a vinylchloride-based resin latex composition according to an embodiment of the present invention will be described in more detail. Step 1 is a step of preparing a mixture of a vinylchloride-based resin latex including a vinylchloride-based resin and a solid-phase styrene/acrylic resin.

The vinylchloride-based resin latex may have an aqueous dispersion or emulsion form in which primary particles of a vinylchloride-based resin latex having a size of 0.1 μm to several μm and including a vinylchloride-based resin are dispersed in water or deionized water.

in the vinyl chloride-based resin latex, the vinyl chloride-based resin may be a homopolymer obtained by homopolymerizing a vinyl chloride monomer, or a (co) polymer obtained by copolymerizing a vinyl chloride monomer with a comonomer copolymerizable therewith.

The vinylchloride-based resin latex may be prepared by polymerizing vinylchloride monomer alone or by polymerizing vinylchloride monomer with a comonomer copolymerizable therewith. In this regard, the polymerization method is not particularly limited, but may be carried out according to a general polymerization method known in the art to which the present invention pertains, such as fine suspension polymerization, emulsion polymerization, seeded emulsion polymerization, and the like.

For example, the vinyl chloride-based resin latex may be prepared by homogenizing a vinyl chloride monomer alone or a mixture of a vinyl chloride monomer and a comonomer copolymerizable therewith, and optionally an emulsifier and a polymerization initiator, in an aqueous solvent, and then performing fine suspension polymerization, or by mixing a vinyl chloride monomer alone or a mixture of a vinyl chloride monomer and a comonomer copolymerizable therewith with an emulsifier and a water-soluble polymerization initiator in an aqueous medium, and then performing emulsion polymerization or seeded emulsion polymerization.

The comonomer copolymerizable with the vinyl chloride monomer may specifically include vinyl esters such as vinyl acetate, vinyl propionate, vinyl stearate and the like; vinyl ethers having an alkyl group such as methyl vinyl ether, ethyl vinyl ether, octyl vinyl ether, lauryl vinyl ether and the like; vinylidene halides such as vinylidene chloride and the like; unsaturated carboxylic acids and anhydrides thereof such as acrylic acid, methacrylic acid, fumaric acid, maleic acid, itaconic acid, maleic anhydride, itaconic anhydride and the like; unsaturated carboxylic acid esters such as methyl acrylate, ethyl acrylate, monomethyl maleate, dimethyl maleate, butyl benzyl maleate, and the like; aromatic vinyl compounds such as styrene, α -methylstyrene, divinylbenzene and the like; unsaturated nitriles such as acrylonitrile, methacrylonitrile and the like; olefins such as ethylene, propylene, and the like; crosslinkable monomers such as diallyl phthalate and the like, and any one of them or a mixture of two or more of them may be used.

Among them, the comonomer may be vinyl esters or (meth) acrylic acid and esters thereof, more particularly vinyl acetate, acrylic acid, (meth) acrylic acid, or mixtures thereof, in view of improving compatibility with vinyl chloride monomer and compatibility of the polymer with styrene/acrylic resin after polymerization.

More specifically, the vinyl chloride-based resin may be a homopolymer obtained by homopolymerizing a vinyl chloride monomer; or a vinyl chloride/vinyl acetate copolymer or a vinyl chloride/acrylic copolymer obtained by copolymerizing a vinyl chloride monomer with a vinyl acetate-based compound (e.g., vinyl acetate or the like) or an acrylic compound (e.g., acrylic acid or the like) as a comonomer.

These polymers have excellent gelling behavior at the time of molding, and the melt viscosity of the resin can be easily controlled.

Further, when the vinyl chloride-based resin includes a vinyl chloride/vinyl acetate copolymer, the vinyl chloride/vinyl acetate copolymer may be prepared by polymerizing a vinyl chloride monomer and a vinyl acetate monomer in a weight ratio of 9:1 to 3:7, more particularly 8:2 to 3:7, and more particularly 7:3 to 5: 5.

Further, when the vinyl chloride-based resin includes a vinyl chloride/acrylic copolymer, the vinyl chloride/acrylic copolymer may be prepared by polymerizing a vinyl chloride monomer and an acrylic monomer in a weight ratio of 9:1 to 5:5, and more particularly 8:2 to 5: 5.

When the weight ratio of the monomers constituting the copolymer satisfies the above conditions, the gelation behavior and melt viscosity of the resin are easily controlled.

In addition, in order to achieve more excellent dispersibility by controlling polymerization conditions during polymerization, the particle diameter, polymerization degree, or weight average molecular weight of the vinylchloride-based resin latex may be controlled.

Particularly, the average particle diameter (D50) of the vinylchloride-based resin latex useful in the present invention may be 0.1 μm to several μm, and particularly, 0.1 μm to 1 μm. When the vinylchloride-based resin latex has the above-described average particle diameter, excellent dispersibility may be achieved without worrying about agglomeration between vinylchloride-based resin latex particles in the vinylchloride-based resin latex composition, and thus, mechanical stability of the vinylchloride-based resin latex composition may be improved. In addition, in consideration that the effect obtained by controlling the particle diameter of the vinylchloride-based resin latex is significant, the average particle diameter (D50) of the vinylchloride-based resin particles may be more particularly 0.1 μm to 0.5 μm.

Meanwhile, in the present invention, the average particle diameter (D50) of the vinylchloride-based resin latex may be measured by a conventional method for measuring a particle diameter distribution (e.g., optical microscope observation, light scattering measurement, etc.), and particularly, by using a Malvern Zetasizer or a Master Sizer.

In addition, the vinyl chloride-based resin latex useful in the present invention may have a weight average molecular weight (Mw) of about 45,000g/mol to about 300,000 g/mol. When the vinylchloride-based resin latex has a weight average molecular weight within the above-described range, its dispersibility in the vinylchloride-based resin latex composition may be improved, thereby improving mechanical stability. In the present invention, the weight average molecular weight of the vinylchloride-based resin latex is a value according to a polystyrene standard measured by gel permeation chromatography.

As described above, in consideration of the effect of improving the resin latex composition, such as improvement of melt viscosity and dispersibility, is significant by controlling the kind, weight average molecular weight, and average particle diameter of the vinylchloride-based resin in the vinylchloride-based resin latex composition, which may include a vinylchloride homopolymer, and may have a weight average molecular weight of 45,000g/mol to 150,000g/mol and an average particle diameter of 0.1 μm to 0.7 μm (D50).

Further, the vinyl chloride-based resin latex may include a vinyl chloride/vinyl acetate copolymer obtained by polymerizing a vinyl chloride monomer and a vinyl acetate monomer, more particularly, in a weight ratio of 8:2 to 3:7, and more particularly, in a weight ratio of 7:3 to 5:5, and may have a weight average molecular weight of 45,000g/mol to 150,000g/mol and an average particle diameter of 0.1 μm to 0.7 μm (D50).

In addition, the vinylchloride-based resin latex may include a vinylchloride/acrylic copolymer obtained by polymerizing a vinylchloride monomer and an acrylic monomer in a weight ratio of 8:2 to 5:5, and may have a weight average molecular weight of 45,000g/mol to 200,000g/mol and an average particle diameter of 0.1 μm to 0.7 μm (D50).

Further, the solid content including the vinyl chloride-based resin in the vinyl chloride-based resin latex may be 30 to 60% by weight, and more particularly, 40 to 60% by weight, which may vary depending on the polymerization method.

Meanwhile, the styrene/acrylic resin to be mixed with the vinylchloride-based resin latex is a styrene/acrylic copolymer resin obtained by polymerizing a styrene-based monomer and an acrylic monomer, and the styrene/acrylic resin is added during the preparation of the vinylchloride-based resin latex composition according to the present invention to prevent agglomeration of the vinylchloride-based resin, and as a result, it plays a role in improving mechanical stability of the vinylchloride-based resin latex composition.

In addition, the styrene/acrylic resin is an alkali-soluble resin and is used in a solid phase when mixed with the vinylchloride-based resin latex, but the styrene/acrylic resin is dissolved by an alkali additive added in a subsequent step, thereby forming a uniform solution phase.

As a result, even if a shear force is applied to the vinylchloride-based resin latex composition during processing or the like, agglomeration of the vinylchloride-based resin latex can be prevented, thereby improving mechanical stability of the vinylchloride-based resin latex composition.

The shape of the solid phase styrene/acrylic resin may have, but is not particularly limited to, various forms such as a spherical shape, an oval shape, a bar shape, a rectangular shape, a sheet shape, a plate shape, a fiber shape, and the like.

The styrene/acrylic resin may be prepared by polymerizing a styrene-based monomer and an acrylic monomer using a conventional method, in particular, by bulk polymerization or emulsion polymerization.

In this regard, by controlling the kind and content of the monomer substance, the effect obtained by using the styrene/acrylic resin can be further improved.

In particular, the styrene/acrylic resin useful in the present invention may be a copolymer obtained by polymerizing a styrene-based monomer and an acrylic monomer in a weight ratio of 60:40 to 80: 20. The styrene/acrylic resin prepared by polymerizing the monomers in the above weight ratio may have more excellent dispersibility, as well as excellent compatibility with the vinylchloride-based resin, thereby preventing agglomeration of the vinylchloride-based resin, with the result that the mechanical stability of the vinylchloride-based resin latex composition may be further improved. In view of a significant effect, the styrene/acrylic resin may be more particularly a copolymer obtained by polymerizing a styrene-based monomer and an acrylic monomer in a weight ratio of 60:40 to 70: 30.

Meanwhile, the styrene-based monomer that can be used for preparing the styrene/acrylic resin may be styrene alone, or styrene together with an α -alkylstyrene monomer (e.g., α -methylstyrene), in particular. Further, when a mixture of styrene and α -alkylstyrene monomers is used as the styrene monomer, the styrene and the α -alkylstyrene may be mixed in a weight ratio of 50:50 to 90: 10. When they are mixed with each other at the above mixing ratio, more excellent compatibility with respect to the vinyl chloride resin can be achieved.

Furthermore, the acrylic monomer may in particular be acrylic acid alone or acrylic acid together with an alkyl acrylate. Further, when a mixture of acrylic acid and alkyl acrylate is used as the acrylic monomer, acrylic acid and alkyl acrylate may be mixed in a weight ratio of 80:20 to 90: 10. When they are mixed with each other at the above mixing ratio, more excellent compatibility with respect to the vinyl chloride resin can be achieved. Further, the alkyl group in the alkyl acrylate may be a linear or branched alkyl group having 1 to 20 carbon atoms, such as methyl, ethyl, and the like.

In addition, in order to achieve more excellent effect of preventing agglomeration of the vinyl chloride-based resin by controlling polymerization conditions during polymerization reaction, the polymerization degree or weight average molecular weight of the styrene/acrylic resin may be controlled.

In particular, the styrene/acrylic resin may have a weight average molecular weight of 1000g/mol to 20,000 g/mol. When the styrene/acrylic resin has the above-mentioned weight average molecular weight, the styrene/acrylic resin may have more excellent compatibility with respect to the vinylchloride-based resin to prevent agglomeration of the vinylchloride-based resin, and as a result, the mechanical stability of the vinylchloride-based resin latex composition may be further improved. In view of the significant effect, the weight average molecular weight of the styrene/acrylic resin may be more specifically 1500g/mol to 15,000g/mol, and still more specifically 5000g/mol to 14,000 g/mol.

The styrene/acrylic resin may be mixed in an amount of 2 to 50 parts by weight with respect to 100 parts by weight of the solid content including the vinyl chloride-based resin in the vinyl chloride-based resin latex. If the content of the styrene/acrylic resin is less than 2 parts by weight, the effect of improving the mechanical stability of the vinylchloride-based resin latex composition by adding the styrene/acrylic resin is insignificant, and thus agglomeration of the vinylchloride-based resin occurs within several minutes when a shear force is applied. Further, if the styrene/acrylic resin is present in an excess of more than 50 parts by weight, the mechanical stability of the vinylchloride-based resin latex composition may be deteriorated, or the viscosity may be increased, or the styrene/acrylic resin may not be dissolved and be present in a solid phase due to agglomeration and dispersion reduction between the excess styrene/acrylic resin, and as a result, there is a fear that the appearance characteristics of the molded article are deteriorated. In view of the significant effect obtained by controlling the content of the styrene/acrylic resin, the styrene/acrylic resin may be mixed in an amount of, particularly, 2 to 20 parts by weight, and more particularly, 2 to 10 parts by weight, relative to 100 parts by weight of the solid content including the vinyl chloride-based resin in the vinyl chloride-based resin latex.

Next, step 2 in the method of preparing a vinylchloride-based resin latex composition according to one embodiment of the present invention is a step of preparing a vinylchloride-based resin latex composition by adding an alkaline additive to a mixture of the vinylchloride-based resin latex prepared in step 1 and a styrene/acrylic resin.

The basic additive may include ammonia, in particular; amine-based compounds such as DMEA (dimethylethanolamine) and MEA (monoethanolamine); or a hydroxide (e.g., potassium hydroxide, sodium hydroxide, etc.), and either one of them or a mixture of two or more of them may be used. Among them, ammonia may be used in view of the improvement effect obtained by using the basic additive.

When a mixture of the vinylchloride-based resin latex and the styrene/acrylic resin is added, the basic additive serves to neutralize the styrene/acrylic resin, and the addition amount thereof may be determined according to the acid value and amount of the styrene/acrylic resin.

Further, the basic additive may be added to the mixture prepared in step 1 in the form of a solid phase such as a powder, but may be added in the form of a solution phase in consideration of uniform mixing of the basic additive in the mixture and increase in solubility of the resulting styrene/acrylic resin. In particular, the alkaline additive may be added in the form of an aqueous solution, wherein the alkaline additive is dissolved in water at a concentration of 1% (W/V) to 30% (W/V). When an aqueous solution having a concentration within the above range is used, the maximum solubility thereof can also be obtained when an appropriate amount of styrene/acrylic resin is used.

In addition, the basic additive may be added in an amount such that the vinylchloride-based resin latex composition becomes neutral to weakly alkaline, particularly, pH of 7 to 9.

Further, the addition of the basic additive may be performed at a temperature of 40 ℃ to 90 ℃. When the basic additive is added in the above temperature range, the solubility of the styrene/acrylic resin can be further improved. If the temperature is lower than 40 ℃, there is a concern that the solubility of the styrene/acrylic resin is insufficient, and if the temperature is higher than 90 ℃, there is a concern about side reactions (such as degradation of reactants, etc.). More particularly, the addition of the basic additive may be carried out at a temperature of 60 ℃ to 80 ℃.

Further, in order to achieve the above temperature conditions, a process of heating the mixture prepared in step 1 may be optionally performed. In this regard, the heating process may be performed according to a conventional method in the art.

After the addition of the basic additive and optionally further additives, a stirring process may optionally be carried out to increase miscibility.

The stirring process may be performed by a general mixing method. The stirring conditions are not particularly limited, and, for example, a stirring process may be performed at a speed of 500rpm to 3000rpm for several minutes to several hours.

As a result obtained from step 2, a vinylchloride-based resin aqueous latex composition including a styrene/acrylic resin in a vinylchloride-based resin latex including the vinylchloride-based resin is prepared.

The vinylchloride-based resin latex composition prepared according to the above-described method may exhibit significantly improved mechanical stability because the styrene/acrylic resin added in a solid phase may prevent agglomeration of the vinylchloride-based resin.

Therefore, the vinylchloride-based resin latex composition may be effectively applied to PVC leather or textile adhesives, gravure ink adhesives for absorbing layers of wallpaper, inkjet printing paper, or films, non-flammable coatings for wood or exterior wall panels, non-flammable coatings for non-woven fabrics, air filters, car carpets, and the like.

According to another embodiment of the present invention, there is provided a vinylchloride-based resin latex composition prepared by the above-described preparation method.

In particular, the vinylchloride-based resin latex composition may include a vinylchloride-based resin latex including a vinylchloride-based resin, a styrene/acrylic resin, and an alkaline additive, wherein the styrene/acrylic resin may be included in an amount of 2 to 50 parts by weight, relative to 100 parts by weight of the vinylchloride-based resin.

In this regard, the vinylchloride-based resin latex, the styrene/acrylic resin, and the basic additive are the same as described above.

In addition, the vinylchloride-based resin latex composition may be a homogeneous solution phase in which a styrene/acrylic resin is dissolved in a vinylchloride-based resin latex including a vinylchloride-based resin, or an emulsion phase in which a core-shell structure of a vinylchloride-based resin and a styrene/acrylic resin is dispersed.

In addition, the vinylchloride-based resin latex composition may be neutral to weakly alkaline, and particularly, have a pH of 7 to 9, by adding an alkaline additive.

Hereinafter, the present invention will be described in more detail with reference to embodiments according to the present invention. However, these examples are for illustrative purposes only, and the scope of the present invention is not intended to be limited thereby.

< preparation of vinyl chloride/vinyl acetate copolymer resin latex composition >