阅读说明：本技术 一种花式反光植珠膜的生产工艺 (Production process of flower-type light-reflecting bead planting film ) 是由 吕基德 卢作颖 朱方正 吕俊诚 吕黄思蔓 舒时宇 于 2021-09-15 设计创作，主要内容包括：本发明公开了一种花式反光植珠膜的生产工艺。包括如下步骤：S1、植珠：将玻璃微珠植入于基材上,形成玻璃微珠层；S2、印刷花型：将步骤S1中的玻璃微珠层表面印上带有可水洗的第一介质的花型层,形成第一半成品；S3、镀介质：将步骤S2的第一半成品上镀第二介质,使得玻璃微珠层及花型层的表面均镀有第二介质,形成第二半成品；S4、冲洗：冲洗步骤S3中的第二半成品,将带有可水洗的第一介质的花型层洗除,于玻璃微珠层上形成带有第二介质的花型样式,得到第一前期成品。本发明突破行业难点,可制备出花式反光植珠膜,可形成多种具有七彩反光、高亮反光样式的反光植珠膜,在能够起到反光警示的前提作用下,使得样式更为新颖,用途更为广泛。(The invention discloses a production process of a flower-type light-reflecting bead planting film. The method comprises the following steps: s1, bead planting: implanting glass beads on a substrate to form a glass bead layer; s2, printing patterns: printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product; s3, plating medium: plating a second medium on the first semi-finished product obtained in the step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are plated with the second medium to form a second semi-finished product; s4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product. The invention breaks through the difficult points of the industry, can prepare the flower type reflection bead planting film, can form a plurality of reflection bead planting films with colorful reflection and high-brightness reflection patterns, and has more novel patterns and wider application under the premise of playing the role of reflection warning.)

1. A production process of a flower-type reflective bead planting film is characterized by comprising the following steps: the method comprises the following steps:

s1, bead planting: implanting glass beads on a substrate to form a glass bead layer;

s2, printing patterns: printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product;

s3, plating medium: plating a second medium on the first semi-finished product obtained in the step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are plated with the second medium to form a second semi-finished product;

s4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product.

2. The production process of the flower-type light-reflecting bead planting film according to claim 1, wherein the production process comprises the following steps: the base material in step S1 is a PET film, a composite film of PET and PE, or paper.

3. The production process of the flower-type light-reflecting bead planting film according to claim 1, wherein the production process comprises the following steps: in the step S2, the pattern printing mode adopts rotary screen printing or gravure printing.

4. The production process of the flower-type light-reflecting bead planting film according to claim 1, wherein the production process comprises the following steps: the water-washable first medium in step S2 is a water-washable ink.

5. The production process of the flower-type light-reflecting bead planting film according to claim 1, wherein the production process comprises the following steps: the second medium in step S3 is a non-metallic medium.

6. The production process of the flower-type light-reflecting bead planting film according to claim 5, wherein the production process comprises the following steps: the second medium is zinc sulfide.

7. The production process of the flower-type light-reflecting bead planting film according to claim 1, wherein the production process comprises the following steps: the second medium in step S3 is a metal medium.

8. The production process of the flower-type light-reflecting bead planting film according to claim 7, wherein the production process comprises the following steps: the second medium is aluminum.

9. The production process of the flower-type light-reflecting bead planting film according to claim 1, wherein the production process comprises the following steps: after the step S4, the method further includes the following steps:

and S5, plating a third medium on the first early-stage finished product obtained in the step S4 to obtain a second early-stage finished product.

10. The production process of the flower-type light-reflecting bead planting film according to claim 9, wherein the production process comprises the following steps:

when the second medium is a non-metal medium, the third medium is a metal medium;

when the second medium is a metal medium, the third medium is a non-metal medium.

Technical Field

The invention relates to the technical field of reflective film preparation, in particular to a production process of a flower type reflective bead planting film.

Background

The reflective bead-planting film is a common reflective material, and due to the limitation of the preparation process of the existing reflective bead-planting film, only patterns with single color and single style can be prepared, and how to prepare the fancy reflective bead-planting film is a difficult point which is difficult to break through in the industry.

Disclosure of Invention

The invention provides a production process of a flower-type light-reflecting bead planting film, aiming at the defects in the prior art.

In order to solve the technical problems, the invention is solved by the following technical scheme:

a production process of a flower-type reflective bead planting film comprises the following steps:

s1, bead planting: implanting glass beads on a substrate to form a glass bead layer;

s2, printing patterns: printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product;

s3, plating medium: plating a second medium on the first semi-finished product obtained in the step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are plated with the second medium to form a second semi-finished product;

s4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product.

In the above technical solution, the substrate in step S1 is preferably a PET film, a composite film of PET and PE, or paper.

In the above technical solution, preferably, the pattern printing manner in step S2 is rotary screen printing, gravure printing or other printing manners.

In the above technical solution, the water-washable first medium in step S2 is preferably water-washable ink.

In the above technical solution, the second medium in step S3 is preferably a non-metal medium, and further, the second medium is zinc sulfide.

In the above-described aspect, the second medium in step S3 is preferably a metal medium, and further, the second medium is aluminum.

In the above technical solution, preferably, after the step S4, the method further includes the following steps:

and S5, plating a third medium on the first early-stage finished product obtained in the step S4 to obtain a second early-stage finished product.

In the above technical solution, preferably, when the second medium is a non-metal medium, the third medium is a metal medium; when the second medium is a metal medium, the third medium is a non-metal medium.

The invention has the beneficial effects that:

the invention breaks through the difficult points of the industry, can prepare the flower type reflection bead planting film, can form the reflection bead planting film which comprises gray highlight reflection flower types and transparent reflection flower types, seven-color reflection flower types and transparent reflection flower types and gray highlight reflection flower types and seven-color reflection flower types, and has more novel style under the premise of playing the role of reflection warning.

Detailed Description

The invention is described in further detail below by means of specific embodiments:

example 1:

a production process of a flower-type reflective bead planting film comprises the following steps:

s1, bead planting: implanting glass beads on a substrate to form a glass bead layer, wherein the substrate can be a PET film, a PET and PE composite film or paper, and the bead implanting process can adopt the existing process.

S2, printing patterns: and printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product.

Specifically, a printing layer is printed on the glass bead layer, and the printing layer is composed of a washable first medium, in this embodiment, the first medium is washable ink, and other washable ink, and the washable ink can be shaped when not in contact with water and can be washed away after being washed with water.

In the step, the pattern printing mode adopts rotary screen printing or gravure printing or other printing modes.

S3, plating medium: plating the second medium on the first semi-finished product of step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are both plated with the second medium, thereby forming a second semi-finished product, specifically, because the first medium is the flower-shaped layer, the layer of medium does not completely cover the glass bead layer, when plating the second medium, the second medium can be plated on the glass bead layer without the first medium, and the portion with the first medium can also be plated with the second medium.

S4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product.

In this embodiment, since the second medium is zinc sulfide, a patterned colorful light-reflecting bead-planting film having a patterned colorful light-reflecting portion and a patterned transparent light-reflecting portion can be obtained.

Example 2: the difference from example 1 is that the material of the second medium is different, and the rest is the same.

A production process of a flower-type reflective bead planting film comprises the following steps:

s1, bead planting: implanting glass beads on a substrate to form a glass bead layer, wherein the substrate can be a PET film, a PET and PE composite film or paper, and the bead implanting process can adopt the existing process.

S2, printing patterns: and printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product.

Specifically, a printing layer is printed on the glass bead layer, and the printing layer is composed of a washable first medium, in this embodiment, the first medium is washable ink, and other washable ink, and the washable ink can be shaped when not in contact with water and can be washed away after being washed with water.

In the step, the pattern printing mode adopts rotary screen printing or gravure printing or other printing modes.

S3, plating medium: plating the second medium on the first semi-finished product of step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are both plated with the second medium, thereby forming a second semi-finished product, specifically, because the first medium is the flower-shaped layer, the layer of medium does not completely cover the glass bead layer, when plating the second medium, the glass bead layer without the first medium can be plated with the second medium, and the portion with the first medium can also be plated with the second medium.

S4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product.

In this embodiment, since the second medium is aluminum, a flower-type gray high-brightness reflection bead-planted film having flower-type gray high-brightness portions and flower-type transparent reflection portions can be obtained.

Example 3: compared with the embodiment 1, the difference is that the step 5 is also included, and the rest is the same.

A production process of a flower-type reflective bead planting film comprises the following steps:

s1, bead planting: implanting glass beads on a substrate to form a glass bead layer, wherein the substrate can be a PET film, a PET and PE composite film or paper, and the bead implanting process can adopt the existing process.

S2, printing patterns: and printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product.

Specifically, a printing layer is printed on the glass bead layer, and the printing layer is composed of a washable first medium, in this embodiment, the first medium is washable ink, and other washable ink, and the washable ink can be shaped when not in contact with water and can be washed away after being washed with water.

In the step, the pattern printing mode adopts rotary screen printing or gravure printing or other printing modes.

S3, plating medium: plating the second medium on the first semi-finished product of step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are both plated with the second medium, thereby forming a second semi-finished product, specifically, because the first medium is the flower-shaped layer, the layer of medium does not completely cover the glass bead layer, when plating the second medium, the second medium can be plated on the glass bead layer without the first medium, and the portion with the first medium can also be plated with the second medium.

S4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product.

And S5, plating a third medium on the first early-stage finished product obtained in the step S4 to obtain a second early-stage finished product.

In this embodiment, the third medium is a metal medium, the further metal medium may be a metal material such as aluminum, copper, silver, gold, or the like, and in step S5, the third medium is located at the bottom of the second medium with a pattern, and is blocked by the second medium, so that the third medium at the bottom of the second medium with a pattern cannot be seen on the front or the visible surface of the film when in use, and the third medium located at the transparent portion can be seen when the film is in use, thereby forming the fancy seven-color light-reflecting high-brightness light-reflecting bead-planted film having a seven-color light-reflecting portion with a pattern and a high-brightness light-reflecting portion with a pattern.

Example 4: compared with the embodiment 2, the difference is that the step 5 is also included, and the rest is the same.

A production process of a flower-type reflective bead planting film comprises the following steps:

s1, bead planting: implanting glass beads on a substrate to form a glass bead layer, wherein the substrate can be a PET film, a PET and PE composite film or paper, and the bead implanting process can adopt the existing process.

S2, printing patterns: and printing the surface of the glass bead layer in the step S1 with a pattern layer with a washable first medium to form a first semi-finished product.

Specifically, a patterned layer is coated on the glass bead layer, and the patterned layer is composed of a washable first medium, in this embodiment, the first medium is washable ink, and other washable ink, and the washable ink can be shaped when not in contact with water, and can be washed away after being washed with water.

In the step, the pattern printing mode adopts rotary screen printing or gravure printing or other printing modes.

S3, plating medium: plating the second medium on the first semi-finished product of step S2, so that the surfaces of the glass bead layer and the flower-shaped layer are both plated with the second medium, thereby forming a second semi-finished product, specifically, because the first medium is the flower-shaped layer, the layer of medium does not completely cover the glass bead layer, when plating the second medium, the glass bead layer without the first medium can be plated with the second medium, and the portion with the first medium can also be plated with the second medium.

S4, washing: and (5) washing the second semi-finished product in the step S3, washing off the pattern layer with the washable first medium, and forming a pattern with the second medium on the glass bead layer to obtain a first early-stage finished product.

And S5, plating a third medium on the first early-stage finished product obtained in the step S4 to obtain a second early-stage finished product.

In this embodiment, the third medium is a non-metallic medium, the further non-metallic medium may be zinc sulfide, and in step S5, the third medium located at the bottom of the second medium with the flower pattern is blocked by the second medium, so that the third medium at the bottom of the second medium cannot be seen on the front or visible surface of the film when in use, and the third medium located at the transparent portion can be seen when the film is in use, thereby forming the fancy colorful light-reflecting high-brightness light-reflecting bead-planted film, which has the colorful light-reflecting portion with the flower pattern and the colorful high-brightness light-reflecting portion with the flower pattern.

The difference between the embodiment 4 and the embodiment 3 is that the flower type positions of the colorful reflection and the highlight reflection are different, and two types of fancy colorful reflection and highlight reflection bead planting films can be formed simultaneously according to the difference of media adopted in different stages.

The above examples are only intended to illustrate the technical solution of the present invention, but not to limit it; although the present invention has been described in detail with reference to the foregoing embodiments, it will be understood by those of ordinary skill in the art that: the technical solutions described in the foregoing embodiments may still be modified, or some technical features may be equivalently replaced; and such modifications or substitutions do not depart from the spirit and scope of the corresponding technical solutions of the embodiments of the present invention.