一种无机配体修饰的CdSe/CdS@ZnO量子点的制备方法
阅读说明：本技术 一种无机配体修饰的CdSe/CdS@ZnO量子点的制备方法 (Preparation method of inorganic ligand modified CdSe/CdS @ ZnO quantum dot ) 是由 张雷 王超男 于 2021-06-08 设计创作，主要内容包括：本发明公开了一种无机配体修饰的CdSe/CdS@ZnO量子点的制备方法,将CdSe/CdS核壳量子点通过正丁醚进行经提纯后,采用乙醇胺对其表面改性,再包覆无机ZnO溶胶作为表面配体,得到无机配体修饰的CdSe/CdS@ZnO量子点。本发明无机量子点的制备方法,可以有效解决传统胶体量子点表面有机配体存在的问题,进而增强量子点的光学性能及其稳定性,而且仍可稳定分散于有机溶剂,保持基于各种溶液环境的量子点光电器件的制备优势。本发明提出的制备方法简单且高效,有利于促进量子点光电器件商业化应用。(The invention discloses a preparation method of inorganic ligand modified CdSe/CdS @ ZnO quantum dots. The preparation method of the inorganic quantum dot can effectively solve the problems of the organic ligand on the surface of the traditional colloidal quantum dot, further enhance the optical performance and the stability of the quantum dot, can be stably dispersed in an organic solvent, and keeps the preparation advantages of quantum dot photoelectric devices based on various solution environments. The preparation method provided by the invention is simple and efficient, and is beneficial to promoting the commercial application of the quantum dot photoelectric device.)
技术领域
本发明涉及纳米材料领域，具体涉及一种无机配体修饰的CdSe/[email protected]量子点的制备方法；该方法增强了量子点的光学性能和光学稳定性，有助于实现胶体半导体量子点在光电器件上的实际应用。
背景技术
由于半导体量子点具有大的比表面积，其表面存在的大量活性原子及悬挂键容易引起表面缺陷态，极易形成非辐射复合中心，这会严重降低量子点的荧光量子产率和非线性光学性质。在制备过程中引入的表面活性剂，除了调节量子点的成核与生长动力学过程以及控制量子点的尺寸和形状外还起到表面配体的作用，不仅可以提供足够的空间或静电排斥力使量子点在溶液中稳定分散、防止发生团聚，还可以钝化表面陷阱态，从而提高量子点的光学性能。虽然表面有机配体的存在可以改善表面性质、提高荧光量子产率，但这种软钝化的量子点的光学性能稳定性比较差。同时，表面有机配体修饰过程也可能在量子点表面引入缺陷。对于实际的发光应用，通常选择在量子点表面外延生长无机壳层，形成核壳异质结构半导体量子点。研究结果表明，较厚的无机壳层对核量子点的保护效果更好。
目前，这种无机壳层在一定程度上能够有效钝化核量子点表面的缺陷态，以及隔绝周围环境（氧气、水分等）对量子点光学性能的直接干扰。然而，随着量子点光电器件应用技术的兴起，厚壳层结构不利于电荷平衡注入的缺点凸显，在一定程度上阻碍了量子点电致LED器件的发光效率。同时，随着壳层厚度的增加，电子波函数也将逐渐扩散到厚壳层中，因而量子点光学性质也很能容易受到表面有机配体不稳定因素的影响，进而量子点的光学性能稳定性受到了严峻挑战。因此，迫切需要寻找到一种新的方法使量子点既具有优异的光学性能及稳定性，又能够解决实际应用中的关键问题。
- 上一篇：一种医用注射器针头装配设备
- 下一篇：一种复合膜层用BOE蚀刻液