阅读说明：本技术 一种新型复合阻燃剂及其制备方法 (Novel composite flame retardant and preparation method thereof ) 是由 张海燕 张顺华 胡慧敏 胡荣军 于 2020-06-29 设计创作，主要内容包括：本发明公开了一种新型复合阻燃剂及其制备方法,是在微乳液中制备层状有机改性的水滑石,将其与磷氮系阻燃剂混合均匀,制得新型符合阻燃剂。本发明的方法操作简单、易行,易于工业化生产,实现了无机阻燃剂水滑石与磷氮系阻燃剂复合阻燃剂体系。与纯磷氮系阻燃材料相比,本发明的复合阻燃剂有优良阻燃性能,同时抑烟效果显著,符合无卤、低烟、环保的阻燃要求。(The invention discloses a novel composite flame retardant and a preparation method thereof, which is to prepare layered organic modified hydrotalcite in microemulsion and uniformly mix the layered organic modified hydrotalcite with a phosphorus-nitrogen flame retardant to prepare the novel composite flame retardant. The method has simple and easy operation and easy industrial production, and realizes the composite flame retardant system of the inorganic flame retardant hydrotalcite and the phosphorus-nitrogen flame retardant. Compared with pure phosphorus-nitrogen flame retardant materials, the composite flame retardant disclosed by the invention has excellent flame retardant performance, is remarkable in smoke suppression effect, and meets the flame retardant requirements of no halogen, low smoke and environmental protection.)

具体实施方式

下面通过具体实施例，对本发明的技术方案进行进一步的具体说明。本发明的实施并不局限于下面的实施例，对本发明所做的任何形式上的变通和/或改变都将落入本发明保护范围。

实施例1：

在烧瓶中加入20gN-月桂酰基谷氨酸钠，300mlH2O和500g辛烷，使用1mol· L-1的NaOH溶液调节pH到10.0，搅拌均匀后加入硝酸镁5g，硝酸铝4g，同时用NaOH溶液控制 pH=10.0，升温到100℃反应12h，产物离心洗涤干燥后得到有机改性的水滑石。

将5份层状水滑石，加入到含30份磷氮系阻燃剂溶液中，溶剂为二甲苯和丙酮的混合液(二甲苯:丙酮=1:1) ，搅拌均匀，研磨3h，125℃挥发掉溶剂，得到新型复合阻燃剂。

实施例2：

在烧瓶中加入20g十二烷基磷酸单酯钾，400mlH2O和600g辛烷，使用2mol·L-1的 NaOH溶液调节pH到10.0，搅拌均匀后加入硝酸镁10g，硝酸铝2g，同时用NaOH溶液控制 pH=10.0，升温到100℃反应12h，产物离心洗涤干燥后得到有机改性的水滑石。

将10份层状水滑石，加入到到含30份份磷氮系阻燃剂溶液中，溶剂为二甲苯和丙酮的混合液(二甲苯:丁酮=1:4) ，搅拌均匀，研磨3h，125℃挥发掉溶剂，得到新型复合阻燃剂。

实施例3：

在烧瓶中加入10g壬基酚醚(EO=10)磷酸单酯钾盐，500mlH2O和200g辛烷，使用3mol.L-1的NaOH溶液调节pH到9.0，搅拌均匀后加入硝酸镁10g，硝酸铝2g，同时用NaOH溶液控制pH=9.0.升温到120℃反应12h，产物离心洗涤干燥后得到有机改性的水滑石。

将10份层状水滑石，加入到含30份磷氮系阻燃剂溶液中，溶剂为二甲苯和丙酮的混合液(二甲苯:丙酮=1:3)，搅拌均匀，研磨3h，125℃挥发掉溶剂，得到新型复合阻燃剂。