阅读说明：本技术 一种利用磷化渣生产四元磷酸盐防锈颜料的方法 (Method for producing quaternary phosphate antirust pigment by using phosphated slag ) 是由 左伏根 于 2020-07-06 设计创作，主要内容包括：本发明公开了一种利用磷化渣生产四元磷酸盐防锈颜料的方法：(1)除去磷化渣杂质；(2)将磷化渣放入搅拌器中,加入1～1.5倍的水进行搅拌,加入碱性物质,调整PH值在6～8之间；所述的碱性物质为氢氧化铝或氧化铝和氢氧化钙,氢氧化铝或氧化铝与氢氧化钙的质量比为1∶1.5；(3)液固分离：(4)干燥：干燥后的水份含量不超过1％；(5)粉碎：粉碎至325目以上,得四元磷酸盐防锈颜料,所述的四元磷酸盐为磷酸铁,磷酸锌,磷酸铝和磷酸钙。本发明有如下技术效果：磷酸铁、磷酸锌、磷酸铝、磷酸钙制成防锈涂料复盖在钢铁基材上,与浸入的水分子反应生成磷酸,磷酸与钢铁基材发生反应生成磷化膜,磷化膜是一层极细致致密能与钢铁基材紧密结合的膜,阻隔了水分子和腐蚀性物质对钢铁基材的进一步腐蚀,同时,因为磷酸盐金属离子的存在,与钢铁基材形成了电化学抵制,减少了钢铁基材的电化学反应,达到防锈的目的；实现磷化渣中Fe(+3)、Zn(+2)、PO<Sub>4</Sub>(-3)资源的利用,减少对环境的污染。(The invention discloses a method for producing quaternary phosphate antirust pigment by using phosphated slag, which comprises the following steps: (1) removing the impurities of the phosphated slag; (2) putting the phosphated residues into a stirrer, adding 1-1.5 times of water for stirring, adding an alkaline substance, and adjusting the pH value to 6-8; the alkaline substance is aluminum hydroxide or aluminum oxide and calcium hydroxide, and the mass ratio of the aluminum hydroxide or the aluminum oxide to the calcium hydroxide is 1: 1.5; (3) liquid-solid separation: (4) and (3) drying: the water content after drying is not more than 1%; (5) crushing: and crushing the mixture to be more than 325 meshes to obtain the quaternary phosphate antirust pigment, wherein the quaternary phosphate is iron phosphate, zinc phosphate, aluminum phosphate and calcium phosphate. The invention has the following technical effects: the iron phosphate, the zinc phosphate, the aluminum phosphate and the calcium phosphate are made into the antirust coating to cover the steel base material, the antirust coating reacts with immersed water molecules to generate phosphoric acid, the phosphoric acid reacts with the steel base material to generate a phosphating film, the phosphating film is a layer of extremely fine and compact film which can be tightly combined with the steel base material, the further corrosion of the water molecules and corrosive substances to the steel base material is prevented, and meanwhile, the antirust coating is used for preventing the further corrosion of the water molecules and the corrosive substances toThe existence of the phosphate metal ions forms electrochemical resistance with the steel base material, reduces the electrochemical reaction of the steel base material and achieves the purpose of rust prevention; realizing Fe (+3), Zn (+2) and PO in the phosphated slag 4 The resource is utilized (-3), and the pollution to the environment is reduced.)

一种利用磷化渣生产四元磷酸盐防锈颜料的方法

技术领域

本发明涉及一种磷化渣的资源利用。

背景技术

磷化是常用的表面处理技术,在汽车、化工、船舶、钢丝绳、航天航空及家用电器等行业有着广泛应用。磷化过程中产生的沉淀物质为磷化渣，属于固体危险废料，废物类别为：HW17表面处理废物，废物代码为：346-064-17，经化验其成分含Fe(+3)、Zn(+2)、PO₄(-3)％；过去这些渣被丢弃或随水排放,造成环境污染。

发明内容

本发明的目的是提供一种利用磷化渣生产四元磷酸盐防锈颜料的方法。

本发明的技术方案是：

一种利用磷化渣生产四元磷酸盐防锈颜料的方法：

(1)除去磷化渣杂质；

(2)将磷化渣放入搅拌器中，加入1～1.5倍的水进行搅拌，加入碱性物质，调整PH值在6～8之间；所述的碱性物质为氢氧化铝或氧化铝和氢氧化钙，氢氧化铝或氧化铝与氢氧化钙的质量比为1∶1.5；

(3)液固分离：

(4)干燥：干燥后的水份含量不超过1％；

(5)粉碎：粉碎至325目以上，得四元磷酸盐防锈颜料，所述的四元磷酸盐为磷酸铁，磷酸锌，磷酸铝和磷酸钙。

本发明有如下技术效果：磷酸铁、磷酸锌、磷酸铝、磷酸钙制成防锈涂料复盖在钢铁基材上，与浸入的水分子反应生成磷酸，磷酸与钢铁基材发生反应生成磷化膜，磷化膜是一层极细致致密能与钢铁基材紧密结合的膜，阻隔了水分子和腐蚀性物质对钢铁基材的进一步腐蚀，同时，因为磷酸盐金属离子的存在，与钢铁基材形成了电化学抵制，减少了钢铁基材的电化学反应，达到防锈的目的；实现磷化渣中Fe(+3)、Zn(+2)、PO₄(-3)资源的利用，减少对环境的污染。

具体实施方式

(1)取1000Kg磷化渣，除去磷化渣中的杂质；

(2)将磷化渣放入搅拌器中，加入1200Kg的水进行搅拌，加入碱性物质氢氧化铝、氢氧化钙，氢氧化铝或氧化铝与氢氧化钙的质量比为1∶1.5，调整PH值在6～8之间；氢氧化铝或氧化铝和氢氧化钙与PO₄(-3)反应生成AlPO₄、Ca₃(PO4)₂；

(3)液固分离：

(4)干燥：干燥后的水份含量不超过1％；

(5)粉碎：粉碎至325目以上，得四元磷酸盐防锈颜料，所述的四元磷酸盐为磷酸铁，磷酸锌，磷酸铝和磷酸钙。