阅读说明：本技术 一种夹胶玻璃 (Laminated glass ) 是由 沈宝福 于 2018-09-06 设计创作，主要内容包括：本发明涉及一种夹胶玻璃,包括清洗,夹胶,处理,其特征在于：首先将钢化玻璃进行深层清洗；然后将钢化玻璃和切割好的PVB膜按照层次敷设；并对夹胶玻璃进行加热工序使PVB胶膜软化,玻璃用专用设备加热至175°后保温8小时,然后进行加压,使加热后的PVB胶膜彻底与钢化玻璃结合并流出大于钢化玻璃的胶体,使气泡完全排除；然后,使将加热后的玻璃出炉传送至冷风干燥处理；并将冷却12小时,干燥后的夹胶玻璃切割、磨边、清洗；最后进行成品验收。本发明以透光性、透光率、附着力、粘合度都较高的PVB胶膜作中间层,综合性能优异,避免气体回流产生气泡,从而提高最终夹胶玻璃的质量。(The invention relates to laminated glass, which comprises the steps of cleaning, laminating and processing, and is characterized in that: firstly, deeply cleaning toughened glass; then, laying the toughened glass and the cut PVB film according to layers; heating the laminated glass to soften the PVB adhesive film, heating the glass to 175 ℃ by using special equipment, preserving heat for 8 hours, and pressurizing to ensure that the heated PVB adhesive film is thoroughly combined with the toughened glass and flows out of colloid larger than the toughened glass, so that bubbles are completely removed; then, discharging the heated glass out of the furnace and conveying the heated glass to cold air drying treatment; cooling for 12 hours, cutting, edging and cleaning the dried laminated glass; and finally, checking and accepting the finished product. The PVB adhesive film with high light transmittance, adhesive force and adhesion is used as the interlayer, so that the comprehensive performance is excellent, bubbles generated by gas backflow are avoided, and the quality of the final laminated glass is improved.)

具体实施方式

实施例: 一种夹胶玻璃，包括清洗，夹胶，处理，首先将钢化玻璃进行深层清洗；然后将钢化玻璃和切割好的PVB膜按照层次敷设；并对夹胶玻璃进行加热工序使PVB胶膜软化，玻璃用专用设备加热至175°后保温8小时，然后进行加压，使加热后的PVB胶膜彻底与钢化玻璃结合并流出大于钢化玻璃的胶体，使气泡完全排除；然后，使将加热后的玻璃出炉传送至冷风干燥处理；并将冷却12小时，干燥后的夹胶玻璃切割、磨边、清洗；最后进行成品验收。

其中，使钢化玻璃加压的压力为80MPa。本发明以透光性、透光率、附着力、粘合度都较高的PVB胶膜作中间层，综合性能优异，避免气体回流产生气泡，从而提高最终夹胶玻璃的质量，在恶劣的环境下，玻璃与PVB胶膜不易脱落，同时提高其透光性。市场前景广阔，广泛应用于自动取款机等，要求安全防泛比较高的地方。。

以上仅为本发明实施例的较佳实施例而已，并不用以限制本发明实施例，凡在本发明实施例的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明实施例的保护范围内。