阅读说明：本技术 一种防紫外线玻璃 (Ultraviolet-proof glass ) 是由 沈宝福 于 2018-09-06 设计创作，主要内容包括：本发明涉及一种防紫外线玻璃,其特征在于：把抗紫外线EVA胶片夹在两片玻璃中间,用专用设备进行抽真空,将玻璃加热至135°进行保温处理,然后二次加热至175°,再次将玻璃保温120分钟后将玻璃冷却至室温,撤除真空将玻璃成品取出,具有较强的抗紫外线功能。紫外吸收物质添加在玻璃中,与氧和水汽隔离,难以氧化降解,可以长时间的持续作用。(The invention relates to ultraviolet-proof glass, which is characterized in that: the anti-ultraviolet EVA film is clamped between two pieces of glass, vacuum pumping is carried out by special equipment, the glass is heated to 135 degrees for heat preservation treatment, then the glass is heated to 175 degrees for secondary heating, the glass is cooled to room temperature after heat preservation is carried out for 120 minutes, the vacuum is removed, and the finished glass product is taken out, so that the anti-ultraviolet EVA film has a strong anti-ultraviolet function. The ultraviolet absorbing substance is added into the glass, is isolated from oxygen and water vapor, is difficult to oxidize and degrade, and can continuously act for a long time.)

具体实施方式

实施例: 一种防紫外线玻璃，把抗紫外线EVA胶片夹在两片玻璃中间，用专用设备进行抽真空，将玻璃加热至135°进行保温处理，然后二次加热至175°，再次将玻璃保温120分钟后将玻璃冷却至室温，撤除真空将玻璃成品取出，具有较强的抗紫外线功能。

进一步地，基础玻璃成分包括：SiO2、Na2O、CaO、MgO、Al2O3，所述基础玻璃成分为97％-98.8wt％。

本发明的有益效果是：防紫外线玻璃具有有效阻隔紫外线的作用，延长组件抗紫外老化时间，从而延长组件使用寿命。紫外吸收物质添加在玻璃中，与氧和水汽隔离，难以氧化降解，可以长时间的持续作用。

以上仅为本发明实施例的较佳实施例而已，并不用以限制本发明实施例，凡在本发明实施例的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明实施例的保护范围内。