阅读说明：本技术 一种机械设备用防锈薄膜 (Antirust film for mechanical equipment ) 是由 尹畅 于 2019-11-23 设计创作，主要内容包括：本发明是一种机械设备用防锈薄膜,包含添加剂和载体,配方中的原料按重量百分比组成分别是：0.5～6%水溶性胶黏剂,10～35%防霉剂,1～10%去离子水,0～3%氨基树脂,0～2.5%流平剂,5～20%耐酸剂,10～20%氯化锌,30～60%催化剂,通过本方法制备的产品,达到实现方便生产和满足气相防锈要求的效果；摒弃了危害人体的亚硝酸盐类气相防锈剂和苯三唑类防锈气相剂,更利于环保和人体健康。(The invention relates to an antirust film for mechanical equipment, which comprises an additive and a carrier, wherein the raw materials in the formula comprise the following components in percentage by weight: 0.5-6% of water-soluble adhesive, 10-35% of mildew preventive, 1-10% of deionized water, 0-3% of amino resin, 0-2.5% of flatting agent, 5-20% of acid-resistant agent, 10-20% of zinc chloride and 30-60% of catalyst, and the product prepared by the method achieves the effects of convenient production and meeting the gas-phase rust prevention requirement; nitrite gas phase rust inhibitors and benzotriazole gas phase rust inhibitors harmful to human bodies are abandoned, and the method is more beneficial to environmental protection and human health.)

一种机械设备用防锈薄膜

技术领域

本发明公开了一种机械设备用防锈薄膜。

背景技术

在机械设备的运输、储存和使用的过程中，经常会发生锈蚀的情况，给人们造成极大的损失，现有的技术中，人们经常使用上漆或者镀层的方法进行防止，然而，这样的一些防锈方法，不仅需要耗费大量的人力、物力，还会造成溶剂对环境的危害，对环境保护十分不利。

发明内容

针对上述现有技术存在的问题，本发明提供一种机械设备用防锈薄膜，达到实现方便生产和满足气相防锈要求的效果；摒弃了危害人体的亚硝酸盐类气相防锈剂和苯***类防锈气相剂，更利于环保和人体健康。

为了实现上述目的，本发明通过以下技术方案实现：一种机械设备用防锈薄膜，配方中的原料按重量百分比组成分别是：0.5～6%水溶性胶黏剂，10～35%防霉剂，1～10%去离子水， 0～3%氨基树脂，0～2.5%流平剂，5～20%耐酸剂，10～20%氯化锌，30～60%催化剂。

有益效果：通过本方法制备的产品，达到实现方便生产和满足气相防锈要求的效果；摒弃了危害人体的亚硝酸盐类气相防锈剂和苯***类防锈气相剂，更利于环保和人体健康。

具体实施方式

实施例1

一种机械设备用防锈薄膜，配方中的原料按重量百分比组成分别是：0.5%水溶性胶黏剂，10%防霉剂，1%去离子水，1%氨基树脂，1%流平剂，5%耐酸剂，10%氯化锌，30%催化剂，此时不能达到实现方便生产和满足气相防锈要求的效果。

实施例2

一种机械设备用防锈薄膜，配方中的原料按重量百分比组成分别是：6%水溶性胶黏剂，35%防霉剂，10%去离子水，3%氨基树脂，2.5%流平剂，20%耐酸剂，20%氯化锌，60%催化剂，此时不利于环保和人体健康。

实施例3

一种机械设备用防锈薄膜，配方中的原料按重量百分比组成分别是：4%水溶性胶黏剂，23%防霉剂，5%去离子水， 1.5%氨基树脂，1.25%流平剂，13%耐酸剂，15%氯化锌，45%催化剂，此时达到实现方便生产和满足气相防锈要求的效果；摒弃了危害人体的亚硝酸盐类气相防锈剂和苯***类防锈气相剂，更利于环保和人体健康。