一种双涂层的高光纸制作方法
阅读说明:本技术 一种双涂层的高光纸制作方法 (Method for manufacturing double-coating high-gloss paper ) 是由 唐寒伟 刘志刚 周晓光 刘也 刘大伟 于 2019-09-23 设计创作,主要内容包括:本发明提供了一种双涂层的高光纸制作方法。主要解决了传统的双涂层高光纸耐水性差、光泽度低等问题。本发明使用高光涂层在pet膜上进行涂布,涂布温度为130摄氏度,涂布后使用湿法复合胶水将纸张与带涂层的pet膜复合,固化24h后进行剥离,剥离后得到双涂层高光纸,双涂层高光纸耐水性好,且表面光泽度强,具有良好的印刷适应性。(The invention provides a method for manufacturing double-coating high-gloss paper. Mainly solves the problems of poor water resistance, low glossiness and the like of the traditional double-coating high gloss paper. According to the invention, the high-gloss coating is coated on the pet film at the coating temperature of 130 ℃, the paper and the pet film with the coating are compounded by using wet-process compound glue after coating, the paper and the pet film with the coating are peeled off after curing for 24h, and the double-coating high-gloss paper is obtained after peeling, has good water resistance, strong surface gloss and good printing adaptability.)
技术领域
本发明涉及一种双涂层的高光纸制作方法。
背景技术
目前市场对高光纸张的应用范围较广,应用需求大,但是市面上常规的双图层高光纸张制作工艺较为复杂,耐水性较差,且表面光泽度不高,印刷适应性较低,且成本较为高昂。
发明内容
本发明的目的是为了解决上述现有技术存在的问题,进而提供一种双涂层的高光纸制作方法,耐水性好,且表面光泽度强,具有良好的印刷适应性。。
本发明的目的是通过以下技术方案实现的:
一种双涂层的高光纸制作方法,其步骤如下,
步骤1、使用高光涂层在pet膜上进行涂布,涂布温度为130摄氏度;
步骤2、涂布后使用湿法复合胶水将纸张与带涂层的pet膜复合;
步骤3、固化24h后进行剥离,剥离后得到双涂层高光纸。
本发明的有益效果是:通过采用本发明的技术方案,使用高光涂层在pet膜上进行涂布,涂布温度为130摄氏度,涂布后使用湿法复合胶水将纸张与带涂层的pet膜复合,固化24h后进行剥离,剥离后得到双涂层高光纸,双涂层高光纸耐水性好,且表面光泽度强,具有良好的印刷适应性。
具体实施方式
下面将对本发明做进一步的详细说明:本实施例在以本发明技术方案为前提下进行实施,给出了详细的实施方式,但本发明的保护范围不限于下述实施例。
本实施例所涉及的一种双涂层的高光纸制作方法,其步骤如下,
步骤1、使用高光涂层在pet膜上进行涂布,涂布温度为130摄氏度;
步骤2、涂布后使用湿法复合胶水将纸张与带涂层的pet膜复合;
步骤3、固化24h后进行剥离,剥离后得到双涂层高光纸。
使用高光涂层在pet膜上进行涂布,涂布温度为130摄氏度,涂布后使用湿法复合胶水将纸张与带涂层的pet膜复合,固化24h后进行剥离,剥离后得到双涂层高光纸,双涂层高光纸耐水性好,且表面光泽度强,具有良好的印刷适应性。
以上所述,仅为本发明较佳的具体实施方式,这些具体实施方式都是基于本发明整体构思下的不同实现方式,而且本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明揭露的技术范围内,可轻易想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书的保护范围为准。