阅读说明：本技术 一种仿绞胎陶瓷及其制作工艺 (One kind is imitative to twist tire ceramics and its manufacture craft ) 是由 郑泽洽 郑鹏飞 郑衍彬 郑晟亮 于 2019-08-22 设计创作，主要内容包括：本发明涉及陶瓷制造技术领域,具体的涉及一种仿绞胎陶瓷及其制作工艺。该种仿绞胎陶瓷,包括陶瓷坯体,所述陶瓷坯体上依次设有仿绞胎色料层和透明釉料,所述透明釉料的厚度为0.2－0.5mm。本发明提供的仿绞胎陶瓷及其制作工艺,通过移印机动作在陶瓷坯体表面设置仿绞胎色料层,实现仿绞胎陶瓷的艺术效果,该种仿绞胎陶瓷的在陶瓷制品上呈现出不规则的线条线条,且线条的颜色深浅、走向随机性高,纹路灵动,所制备的每一个仿绞胎陶都具有不同的效果。该种仿绞胎陶瓷生产时,由移印机的印头定轴旋转一定角度形成绞胎效果,该种仿绞胎陶瓷提供了一种全新的陶瓷装饰方法,仿绞胎陶瓷加工速度快,适合产业化生产,具有积极的经济效益。(The present invention relates to ceramic fabrication technique fields, are specifically related to a kind of imitate and twist tire ceramics and its manufacture craft.This kind imitative to twist tire ceramics, including ceramic body, be successively arranged on the ceramic body it is imitative twist tire colorant layer and marzacotto, the marzacotto with a thickness of 0.2-0.5mm.Imitative strand tire ceramics provided by the invention and its manufacture craft, imitative strand tire colorant layer is set on ceramic body surface by pad printer movement, realize the imitative artistic effect for twisting tire ceramics, this kind imitative twist tire ceramics irregular lines lines are showed on ceramic, and the shade of lines, move towards randomness height, lines is agile, and the imitative strand tire pottery of each prepared has the effect of different.When this kind of imitative strand tire Production of Ceramics, strand tire effect is formed by the print head System of Rotating about Fixed Axis certain angle of pad printer, this kind of imitative tire ceramics that twist provide a kind of completely new ceramic decoration method, it is fast to imitate strand tire Ceramic manufacturing speed, it is suitble to industrialization production, there is positive economic benefit.)

1. a kind of imitative tire that twists is ceramic, including ceramic body, it is characterised in that: be successively arranged imitative strand tire colorant on the ceramic body Layer and marzacotto, the marzacotto with a thickness of 0.2-0.5mm.

2. imitative strand tire ceramics according to claim 1, it is characterised in that: the imitative strand tire colorant layer includes multilayer, described The imitative identical or different color of color for twisting tire colorant layer of multilayer.

3. imitative strand tire ceramics according to claim 1, it is characterised in that: the imitative material quality percentage for twisting tire colorant layer Than as follows: color material 30-40%, glycerol 10-20%, potassium bichromate 20-30%, fluorite 10-15%, red lead 10-20%.

4. a kind of imitative manufacture craft for twisting tire ceramics, production requires imitative strand tire ceramics, specific steps described in 1-3 any one It is as follows:

Step 1, ceramic body is prepared；

Step 2, ceramic body is moved into ceramic pad printer；

Step 3, after the imitative strand tire colorant of bat printing head adherency, the pushing of bat printing head is made to be transferred to the imitative tire colorant that twists on ceramic；

Step 4, bat printing head is lifted, bat printing head System of Rotating about Fixed Axis certain angle during lifting, makes the imitative tire colorant that twists in ceramic On show irregular lines；

Step 5, marzacotto is applied on ceramic body；

Step 6, after ceramic glaze is dry, it is put into kiln kiln roasting type, firing temperature is 1250 ± 50 DEG C.

5. the imitative manufacture craft for twisting tire ceramics according to claim 3, it is characterised in that: the step 3 and 4 is twisted according to imitative The number of plies of tire colorant layer is repeated as many times.

6. the imitative manufacture craft for twisting tire ceramics according to claim 4, it is characterised in that: the basis is imitative to twist tire colorant layer The selection of color demand the color of imitative strand tire colorant is adhered to when repeating every time.

7. the imitative manufacture craft for twisting tire ceramics according to claim 3, it is characterised in that: the bat printing heading brush speed Degree, rotation speed, rotation angle stochastic and dynamic setting.

8. the manufacture craft of imitative strand tire ceramics according to claim 3 or 6, which is characterized in that the rotation of the bat printing head Angle is 30-180 degree.

9. the manufacture craft of imitative strand tire ceramics according to claim 3 or 6, which is characterized in that the rotation of the bat printing head Speed 300-600r/min.

10. the manufacture craft of imitative strand tire ceramics according to claim 3 or 6, which is characterized in that the printing of the bat printing head Speed 5-8/min.

Technical field

The present invention relates to ceramic fabrication technique fields, are specifically related to a kind of imitate and twist tire ceramics and its manufacture craft.

Background technique

Twist tire ceramics

It twists tire porcelain and refers to that the china clay of two or more different colours rubs up together, mutually twist the decoration figure for forming different color Case is finally burnt into porcelain through overmolding, then last clear frit.Tradition, which twists tire porcelain, to be mixed with porcelain mud and color soil, is obtained and is twisted tire Mud twists air in tire mud using the manual methods discharge such as rubbing up, overlapping, pat again, is then cut into the cell blocks such as item, piece Afterwards, molding is pulled by hand, and the strand tire porcelain decorative pattern made of traditional approach is simple, and speed is slow, and volume production is at high cost.

To solve the above problems, ceramics, which generate enterprise, twists tire ceramics, such as application number using the realization of a large amount of method is imitated For the preparation method of the strand tire ceramics of CN201510563641.2, this kind twist the preparation method of tire ceramics by flow forming process and It twists tire ceramic product to combine, in forming process, the coloring material got ready or the mud containing coloring material is coated in The local location of pug ontology, or by the part of the pug indentation pug ontology containing coloring material, pug to be rolled is obtained, Then roll forming is carried out to it, obtains green compact with the relative rotation of milled head and model, forms irregular texture.

There are the following problems for the preparation method of this kind strand tire ceramics, first is that being only used for the ceramic body of roll forming, uses It is restricted；Second is that in rolling, the pug of coloring material is uniformly pressed into pug ontology, thus while can be formed irregular Texture, but the color of the pug of coloring material is unified, lacks the variation of the depth, compared with traditional strand tire porcelain, lines is stiff.

Summary of the invention

In order to solve the deficiencies in the prior art, the present invention provides the imitative strand tire ceramics of one kind and its manufacture crafts.

To achieve the above object, The technical solution adopted by the invention is as follows: a kind of imitative tire that twists is ceramic, including ceramic body, It is characterized by: be successively arranged on the ceramic body it is imitative twist tire colorant layer and marzacotto, the marzacotto with a thickness of 0.2-0.5mm.

Further, imitating and twisting tire colorant layer includes multilayer, the imitative identical or different face of color for twisting tire colorant layer of the multilayer Color.

Further, imitate twist tire colorant layer material quality percentage it is as follows: color material 30-40%, glycerol 10-20%, Potassium bichromate 20-30%, fluorite 10-15%, red lead 10-20%.

A kind of imitative manufacture craft for twisting tire ceramics makes imitative strand tire ceramics described in above-mentioned any one, and specific steps are such as Under:

Step 1, ceramic body is prepared；

Step 2, ceramic body is moved into ceramic pad printer；

Step 3, after the imitative strand tire colorant of bat printing head adherency, make the pushing of bat printing head that the imitative tire colorant that twists be made to be transferred to ceramic On；

Step 4, bat printing head is lifted, bat printing head System of Rotating about Fixed Axis certain angle during lifting, makes the imitative tire colorant that twists in ceramics Irregular lines are showed on product；

Step 5, marzacotto is applied on ceramic body；

Step 6, after ceramic glaze is dry, it is put into kiln kiln roasting type, firing temperature is 1250 ± 50 DEG C.

Further, step 3 and 4 is repeated as many times according to the imitative number of plies for twisting tire colorant layer.

Further, the imitative face for twisting tire colorant is adhered to when repeating every time according to the imitative color demand selection for twisting tire colorant layer Color.

Further, the bat printing head print speed printing speed, rotation speed, rotation angle stochastic and dynamic setting.

Further, the rotation angle of bat printing head is 30-180 degree.

Further, the rotation speed 300-600r/min of bat printing head.

Further, the print speed printing speed 5-8/min of bat printing head.

Imitative strand tire ceramics provided by the invention and its manufacture craft, are arranged on ceramic body surface by pad printer movement and are imitated Tire colorant layer is twisted, the artistic effect imitated and twist tire ceramics is realized, imitates for this kind and twist showing on ceramic irregularly for tire ceramics Lines lines, and the shade of lines, move towards randomness height, lines is agile, and the imitative tire pottery that twists of each prepared has There is different effects.When this kind of imitative strand tire Production of Ceramics, is formed by the print head System of Rotating about Fixed Axis certain angle of pad printer and twists tire effect, This kind of imitative tire ceramics that twist provide a kind of completely new ceramic decoration method, and the imitative tire Ceramic manufacturing speed that twists is fast, is suitble to industry metaplasia It produces, there is positive economic benefit.

Specific embodiment

Below by way of specific embodiment, the invention will be further described.