阅读说明：本技术 增韧pvdf复合材料配方 (Toughening PVDF composite-material formula ) 是由 王海燕 于 2018-05-21 设计创作，主要内容包括：本发明公开了一种增韧PVDF复合材料配方,每100份PVDF中添加LCP 10份、增强剂5份、氯化聚乙烯5份；进一步改进在于：还添加DBDPO阻燃剂5份；增强剂为纳米级CaCO<Sub>3</Sub>。本发明具有较好的阻燃性能,韧性高,结构强度高。(The invention discloses a kind of toughening PVDF composite-material formula, 10 parts of LCP, 5 parts of reinforcing agent, 5 parts of haloflex are added in every 100 parts of PVDF；Further improvement lies in that: also add 5 parts of DBDPO fire retardant；Reinforcing agent is nanoscale CaCO 3 .The present invention has preferable flame retardant property, and toughness is high, and structural strength is high.)

1. a kind of toughening PVDF composite-material formula, 10 parts of LCP, 5 parts of reinforcing agent are added in every 100 parts of PVDF；Its feature exists In: also add 5 parts of haloflex.

2. toughening PVDF composite-material formula according to claim 1, it is characterised in that: also addition DBDPO fire retardant 5 Part.

3. toughening PVDF composite-material formula according to claim 2, it is characterised in that: the reinforcing agent is nanoscale CaCO₃。

Technical field

The present invention relates to a kind of high polymer material formulation, especially a kind of PVDF formula.

Background technique

PVDF addition LCP can improve PVDF processing performance, but toughness is poor.

Summary of the invention

In view of the deficiencies of the prior art, the present invention proposes a kind of toughening PVDF composite materials that can significantly improve toughness to match Side.

The present invention is achieved through the following technical solutions technical goal.

Toughening PVDF composite-material formula adds 10 parts of LCP, 5 parts of reinforcing agent in every 100 parts of PVDF；Its improvements exists In: also add 5 parts of haloflex.

Further improvement lies in that: also add 5 parts of DBDPO fire retardant.

Further improvement lies in that: the reinforcing agent is nanoscale CaCO₃。

Compared with prior art, the present invention having the positive effect that:

1, haloflex is added, toughness of the invention is significantly improved.

2, DBDPO fire retardant is added, can make the present invention that there is preferable flame retardant property.

3, reinforcing agent is nanoscale CaCO₃, significantly improve structural strength.

Specific embodiment

Below with reference to embodiment, the invention will be further described.