阅读说明：本技术 一种新型水性纳米保温材料及其制备方法 (Novel water-based nano thermal insulation material and preparation method thereof ) 是由 郭金辉 邵丹 邓有高 赵忠珍 童军 张纪阳 万利环 于 2020-12-21 设计创作，主要内容包括：本发明适用保温材料技术领域,提供一种新型水性纳米保温材料及其制备方法,新型水性纳米保温材料,包括以下组分：纳米硅气凝胶、皂石、淀粉醚、消泡剂、胶粘剂和水；一种新型水性纳米保温材料的制备方法中,通过热高压和超声波的联合使用,以及通过低压和超声波的联合使用,可有效的消除保温材料中的气泡,从而了提高产品质量。(The invention is suitable for the technical field of heat-insulating materials, and provides a novel water-based nano heat-insulating material and a preparation method thereof, wherein the novel water-based nano heat-insulating material comprises the following components: nano-silica aerogel, soapstone, starch ether, a defoaming agent, an adhesive and water; in the preparation method of the novel water-based nano heat-insulating material, bubbles in the heat-insulating material can be effectively eliminated by the combined use of heat and high pressure and ultrasonic waves and the combined use of low pressure and ultrasonic waves, so that the product quality is improved.)

1. The novel water-based nano heat-insulating material is characterized by comprising the following components in parts by weight:

20-40 parts of nano-silica aerogel, 3-5 parts of soapstone, 1-3 parts of starch ether, 0.3-0.5 part of defoaming agent, 0.3-0.5 part of adhesive and 15-35 parts of water.

2. The novel aqueous nano heat-insulating material as claimed in claim 1, characterized by comprising the following components in parts by weight:

25-35 parts of nano-silica aerogel, 3.5-4.5 parts of soapstone, 1.5-2.5 parts of starch ether, 0.35-0.45 part of defoaming agent, 0.35-0.45 part of adhesive and 20-30 parts of water.

3. The novel aqueous nano heat-insulating material as claimed in claim 1, wherein the nano silica aerogel is 30 parts, the soapstone is 4 parts, the starch ether is 2 parts, the defoaming agent is 0.4 part, the adhesive is 0.4 part and the water is 20 parts.

4. The novel aqueous nano heat insulating material according to claim 1, wherein the defoaming agent comprises: emulsified silicone oil, high alcohol fatty acid ester compound, polyoxyethylene polyoxypropylene pentaerythritol ether, polydimethylsiloxane, polyoxyethylene polyoxypropylene amine ether, polyoxypropylene glycerol ether and one or more of polyoxypropylene polyoxyethylene glycerol ether.

5. The novel aqueous nano thermal insulation material according to claim 1, wherein the adhesive comprises: one or more of epoxy resin, polyvinyl acetate, vinyl acetate resin and polyurethane.

6. The preparation method of the novel aqueous nano heat-insulating material according to claim 1, which comprises the following steps:

(1) weighing raw materials in parts by weight: 20-40 parts of nano-silica aerogel, 3-5 parts of soapstone, 1-3 parts of starch ether, 0.3-0.5 part of defoaming agent, 0.3-0.5 part of adhesive and 15-35 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, a defoaming agent, an adhesive and water into a stirring container together, enabling the rotating speed to be 150 r/min-250 r/min, and stirring for 4 min-6 min to be uniform, thus obtaining a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 120-150 ℃, simultaneously inputting high-pressure saturated steam with the pressure of 0.2-0.3MPa into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.2-0.3MPa, simultaneously inputting ultrasonic waves with the pressure of 2000-3000HZ, and stirring for 4-6min to obtain a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, inputting 2000-3000HZ ultrasonic waves, and stirring for 4-6min to obtain the product.

7. The method for preparing a novel aqueous nano heat insulating material according to claim 6, wherein in the step 1), the rotation speed is 200r/min, and the stirring is carried out for 5min to be uniform.

8. The method for preparing a novel aqueous nano heat insulating material according to claim 6, wherein in the step 2), 0.3MPa of high pressure saturated steam is inputted into the stainless steel closed container, so that the pressure of the stainless steel closed container is maintained at 0.3MPa, and at the same time, 2500HZ of ultrasonic wave is inputted, and the stirring is performed for 5 min.

Technical Field

The invention belongs to the technical field of heat insulation materials, and particularly relates to a novel water-based nano heat insulation material and a preparation method thereof.

Background

The heat-insulating material is generally a light, loose, porous and fibrous material. It can be divided into organic materials and inorganic materials according to its composition. The former has better heat insulation performance than the latter, but the latter has better durability than the former. The heat conductivity coefficient is a main index for measuring the performance of the heat-insulating material. The smaller the thermal conductivity, the smaller the amount of heat transferred through the material, the better the thermal insulation performance, the thermal conductivity of the material is determined by the composition, internal structure, volume weight, etc. of the material, and also the average temperature during heat transfer and the water content of the material.

With the development of economy and society, people pay more and more attention to the functions of heat preservation, energy conservation, environmental protection, fire prevention and the like of building materials. At present, the heat insulation materials mainly comprise EPS boards (polystyrene boards), XPS (polystyrene heat insulation boards) and cement foaming heat insulation boards. The existing heat preservation and insulation material has bubbles, so that the quality of the heat preservation and insulation material can be influenced, and the heat preservation and insulation effect can be influenced.

Disclosure of Invention

The invention aims to provide a novel water-based nano thermal insulation material and a preparation method thereof, so as to solve the problems in the background technology.

In order to achieve the purpose, the invention provides a novel water-based nano heat-insulating material which comprises the following components in parts by weight:

20-40 parts of nano-silica aerogel, 3-5 parts of soapstone, 1-3 parts of starch ether, 0.3-0.5 part of defoaming agent, 0.3-0.5 part of adhesive and 15-35 parts of water.

Preferably, the novel water-based nano heat-insulating material comprises the following components in parts by weight:

25-35 parts of nano-silica aerogel, 3.5-4.5 parts of soapstone, 1.5-2.5 parts of starch ether, 0.35-0.45 part of defoaming agent, 0.35-0.45 part of adhesive and 20-30 parts of water.

Preferably, the novel water-based nano heat-insulating material comprises 30 parts of nano silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of defoaming agent, 0.4 part of adhesive and 20 parts of water.

Preferably, the novel aqueous nano thermal insulation material comprises the following components in percentage by weight: emulsified silicone oil, high alcohol fatty acid ester compound, polyoxyethylene polyoxypropylene pentaerythritol ether, polydimethylsiloxane, polyoxyethylene polyoxypropylene amine ether, polyoxypropylene glycerol ether and one or more of polyoxypropylene polyoxyethylene glycerol ether.

Preferably, the novel water-based nano thermal insulation material comprises the following adhesive: one or more of epoxy resin, polyacrylate, polyvinyl acetate, vinyl acetate resin and polyurethane.

Preferably, the preparation method of the novel aqueous nano heat-insulating material specifically comprises the following steps:

(1) weighing raw materials in parts by weight: 20-40 parts of nano-silica aerogel, 3-5 parts of soapstone, 1-3 parts of starch ether, 0.3-0.5 part of defoaming agent, 0.3-0.5 part of adhesive and 15-35 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, a defoaming agent, an adhesive and water into a stirring container together, enabling the rotating speed to be 150 r/min-250 r/min, and stirring for 4 min-6 min to be uniform, thus obtaining a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 120-150 ℃, simultaneously inputting high-pressure saturated steam with the pressure of 0.2-0.3MPa into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.2-0.3MPa, simultaneously inputting ultrasonic waves with the pressure of 2000-3000HZ, and stirring for 4-6min to obtain a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, inputting 2000-3000HZ ultrasonic waves, and stirring for 4-6min to obtain the product.

Preferably, in the step 1), the rotation speed is 200r/min, and the stirring is carried out for 5min to be uniform.

Preferably, in the step 2), 0.3MPa high-pressure saturated steam is input into the stainless steel closed container, so that the air pressure in the stainless steel closed container is maintained at 0.3MPa, and at the same time, 2500HZ ultrasonic waves are input, and stirring is performed for 5 min.

In summary, due to the adoption of the technical scheme, the method has the following beneficial effects:

the invention provides a novel water-based nano heat-insulating material and a preparation method thereof, and the novel water-based nano heat-insulating material has good heat-insulating effect by combined use of nano silica aerogel, soapstone, starch ether, a defoaming agent, an adhesive and water, and simultaneously has high strength and wear resistance.

Detailed Description

In order to make the objects, technical solutions and advantages of the present invention more apparent, the present invention is further described in detail with reference to the following embodiments. It should be understood that the specific embodiments described herein are merely illustrative of the invention and are not intended to limit the invention.

The existing heat preservation and insulation material has bubbles, so that the quality of the heat preservation and insulation material and the heat preservation and insulation effect are influenced; the invention can effectively eliminate air bubbles in the heat-insulating material by the combined use of heat high pressure and ultrasonic waves and the combined use of low pressure and ultrasonic waves, thereby improving the product quality.

Example 1

Weighing raw materials in parts by weight: 20 parts of nano-silica aerogel, 3 parts of soapstone, 1 part of starch ether, 0.3 part of polyoxyethylene polyoxypropylene amine ether, 0.3 part of epoxy resin and 15 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 2

(1) Weighing raw materials in parts by weight: 25 parts of nano-silica aerogel, 3.5 parts of soapstone, 1.5 parts of starch ether, 0.35 part of polyoxyethylene polyoxypropylene amine ether, 0.35 part of epoxy resin and 20 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 3

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxyethylene polyoxypropylene amine ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 4

(1) Weighing raw materials in parts by weight: 35 parts of nano-silica aerogel, 4.5 parts of soapstone, 2.5 parts of starch ether, 0.45 part of polyoxyethylene polyoxypropylene amine ether, 0.45 part of epoxy resin and 30 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 5

(1) Weighing raw materials in parts by weight: 40 parts of nano-silica aerogel, 5 parts of soapstone, 3 parts of starch ether, 0.5 part of polyoxyethylene polyoxypropylene pentaerythritol ether, 0.5 part of epoxy resin and 35 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 140r/min, and stirring for 4min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 6

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxyethylene polyoxypropylene pentaerythritol ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, polyacrylate and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 7

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polydimethylsiloxane, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 8

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxypropylene glycerol ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 9

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxypropylene polyoxyethylene glycerol ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 10

(1) Weighing raw materials in parts by weight: 30 parts of nano-silicon aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of emulsified silicone oil, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 11

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of high-carbon alcohol fatty acid ester compound, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Example 12

(1) Weighing raw materials in parts by weight: 30 parts of nano-silicon aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.2 part of emulsified silicone oil, 0.2 part of higher alcohol fatty acid ester compound, 0.2 part of epoxy resin, 0.2 part of polyvinyl acetate and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, emulsified silicone oil, a high-alcohol fatty acid ester compound, epoxy resin, polyvinyl acetate and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Comparative example 1

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxyethylene polyoxypropylene amine ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, simultaneously inputting 0.3MPa high-pressure saturated steam into the stainless steel closed container, keeping the air pressure in the stainless steel closed container at 0.3MPa, simultaneously inputting 2500HZ ultrasonic waves, stirring for 5min, and obtaining a mixed component B;

(3) stirring the mixed component B in the step 2) for 5min to obtain the product.

Comparative example 2

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxyethylene polyoxypropylene amine ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, stirring for 5min, and obtaining a mixed component B;

(3) extracting saturated steam from the stainless steel closed container in the step 2) to enable the stainless steel closed container to be in a low pressure state of-0.2 MPa, simultaneously inputting 2500HZ ultrasonic waves, and stirring for 5min to obtain the product.

Comparative example 3

(1) Weighing raw materials in parts by weight: 30 parts of nano-silica aerogel, 4 parts of soapstone, 2 parts of starch ether, 0.4 part of polyoxyethylene polyoxypropylene amine ether, 0.4 part of epoxy resin and 25 parts of water; crushing and grinding the nano-silica aerogel, then putting the ground nano-silica aerogel, soapstone, starch ether, polyoxyethylene polyoxypropylene ether, epoxy resin and water into a stirring container together, enabling the rotating speed to be 200r/min, and stirring for 5min to be uniform to obtain a mixed component A;

(2) putting the mixed component A obtained in the step 1) into a stainless steel closed container, keeping the temperature at 140 ℃, stirring for 5min, and obtaining a mixed component B;

(3) stirring the mixed component B in the step 2) for 5min to obtain the product.

TABLE 1

In summary, the following steps: the invention provides a novel water-based nano heat-insulating material and a preparation method thereof, and the novel water-based nano heat-insulating material has good heat-insulating effect by combined use of nano silica aerogel, soapstone, starch ether, a defoaming agent, an adhesive and water, and simultaneously has high strength and wear resistance.

It will be evident to those skilled in the art that the invention is not limited to the details of the foregoing illustrative embodiments, and that the present invention may be embodied in other specific forms without departing from the spirit or essential attributes thereof. The present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description, and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.

Furthermore, it should be understood that although the present description refers to embodiments, not every embodiment may contain only a single embodiment, and such description is for clarity only, and those skilled in the art should integrate the description, and the embodiments may be combined as appropriate to form other embodiments understood by those skilled in the art.