阅读说明：本技术 一种用于抛釉砖的耐磨釉料及其制备方法 (Wear-resistant glaze for glazed brick and preparation method thereof ) 是由 罗强 李苏波 钟保民 徐瑜 于 2020-08-11 设计创作，主要内容包括：本发明公开了一种用于抛釉砖的耐磨釉料及其制备方法,耐磨釉料的原料包括生釉料粉、1号熔块粉和2号熔块粉；生釉料粉包括以下重量百分比的原料：高岭土8～12%、煅烧高岭土10～18%、石英12～20%、白云石12～20%、烧滑石8～15%、霞石8～15%、氧化锌5～10%、硫酸钡3～6%和碳酸锶6～12%；1号熔块粉的原料包括锆英砂和硫酸钡,2号熔块粉的原料包括高岭土、烧滑石、萤石和硫酸钡。本发明所述釉料中含有硫酸钡,能够改善发色情况,避免产品在烧成时,红色和黄色陶瓷喷墨墨水出现色差的问题,在不影响硬度和耐磨性的情况下,增加耐磨釉料的透明度。(The invention discloses a wear-resistant glaze for glazed tiles and a preparation method thereof, wherein the wear-resistant glaze comprises raw glaze powder, No. 1 clinker powder and No. 2 clinker powder; the raw glaze powder comprises the following raw materials in percentage by weight: 8-12% of kaolin, 10-18% of calcined kaolin, 12-20% of quartz, 12-20% of dolomite, 8-15% of calcined talc, 8-15% of nepheline, 5-10% of zinc oxide, 3-6% of barium sulfate and 6-12% of strontium carbonate; the raw materials of the No. 1 clinker powder comprise zircon sand and barium sulfate, and the raw materials of the No. 2 clinker powder comprise kaolin, calcined talc, fluorite and barium sulfate. The glaze material contains barium sulfate, so that the color development condition can be improved, the problem of color difference of red and yellow ceramic ink-jet ink during sintering of the product is avoided, and the transparency of the wear-resistant glaze material is improved under the condition of not influencing the hardness and the wear resistance.)

1. The wear-resistant glaze for glazed tiles is characterized in that: the raw materials of the wear-resistant glaze comprise raw glaze powder, No. 1 fusion cake powder and No. 2 fusion cake powder;

the raw glaze powder comprises the following raw materials in percentage by weight: 8-12% of kaolin, 10-18% of calcined kaolin, 12-20% of quartz, 12-20% of dolomite, 8-15% of calcined talc, 8-15% of nepheline, 5-10% of zinc oxide, 3-6% of barium sulfate and 6-12% of strontium carbonate;

the raw materials of the No. 1 fusion cake powder comprise zircon sand and barium sulfate, and the raw materials of the No. 2 fusion cake powder comprise kaolin, calcined talc, fluorite and barium sulfate.

2. The wear-resistant glaze for glazed tiles as claimed in claim 1, wherein: the weight ratio of the raw glaze powder to the No. 1 fusion cake powder to the No. 2 fusion cake powder is (5-7): (1-3) and (1-3).

3. The wear-resistant glaze for glazed tiles as claimed in claim 1, wherein: the light transmittance of the No. 1 fusion cake powder is 26.5-28.5%, and the Mohs hardness is 4 grade; the light transmittance of the No. 2 fusion cake powder is 23.5-25.5%, and the Mohs hardness is 5 grade.

4. The wear-resistant glaze for glazed tiles as claimed in claim 1, wherein: the fineness of the zircon sand is 400 meshes.

5. The wear-resistant glaze for glazed tiles as claimed in claim 1, wherein: the mass percentage content of barium sulfate in the No. 1 fusion cake powder is less than or equal to 5%, and the mass percentage content of barium sulfate in the No. 2 fusion cake powder is less than or equal to 5%.

6. The wear-resistant glaze for glazed tiles as claimed in claim 5, wherein: the No. 1 fusion cake powder comprises the following raw materials in percentage by weight: 35-42% of kaolin, 14-20% of quartz, 10-15% of calcined talc, 10-16% of calcite, 2-8% of zinc oxide, 0-3% of strontium carbonate, 1-3% of zircon sand, 1-3% of borax, 4-10% of nepheline and 2-5% of barium sulfate.

7. The wear-resistant glaze for glazed tiles as claimed in claim 5, wherein: the No. 2 clinker powder comprises the following raw materials in percentage by weight: 60-68% of kaolin, 20-26% of calcined talc, 1-5% of quartz, 2-6% of fluorite and 2-5% of barium sulfate.

8. A preparation method of wear-resistant glaze for glazed tiles is characterized by comprising the following steps: the preparation method of the wear-resistant glaze material is used for preparing the wear-resistant glaze material for the glazed brick as claimed in any one of claims 1 to 7, and comprises the following steps:

preparing No. 1 fusion cake powder: mixing the raw materials of the No. 1 fusion cake powder according to the proportion and preparing the mixture into powder; firing the raw materials at high temperature, discharging, cooling with water to obtain No. 1 clinker powder, powdering, sieving and drying the prepared No. 1 clinker powder, and taking 100-mesh screen underflow for later use;

preparing No. 2 fusion cake powder: mixing the raw materials of the No. 2 clinker powder according to the proportion and preparing the mixture into powder; firing the raw materials at high temperature, discharging, cooling with water to obtain No. 2 clinker powder, pulverizing the prepared No. 2 clinker powder, sieving, drying, and taking 100-mesh screen underflow for later use;

preparing raw glaze powder: uniformly mixing the raw glaze powder raw materials according to the proportion;

mixing the fusion cake powder with the raw glaze powder: and (3) adding water into the No. 1 fusion cake powder, the No. 2 fusion cake powder and the raw glaze powder prepared in the steps according to the proportion, ball-milling for 8-10 h to obtain glaze slurry, controlling the fineness to be 325 meshes, and ageing for more than 48h to obtain the wear-resistant glaze, wherein the mass fraction of the surplus is 0.8-1.2%.

9. The method for preparing a wear-resistant glaze for glazed tiles as claimed in claim 8, wherein: the temperature curve for preparing the No. 1 clinker powder by high-temperature firing comprises the following steps:

(1) heating to 300 deg.C from normal temperature, and taking 90 min;

(2) heating from 300 deg.C to 1100 deg.C, and taking 90 min;

(3) heating from 1100 deg.C to 1520 deg.C, and taking 60 min;

(4) preserving the temperature at 1520 ℃ for 30 min;

(5) cooling from 1520 deg.C to 1400 deg.C, and taking 10 min;

(6) keeping the temperature at 1400 ℃ for 20 min;

(7) cooling from 1400 deg.C to 900 deg.C, and taking 60 min.

10. The method for preparing a wear-resistant glaze for glazed tiles as claimed in claim 8, wherein: the temperature curve for high-temperature firing of the No. 2 clinker powder comprises:

(1) heating to 300 deg.C from normal temperature, and taking 90 min;

(2) heating from 300 deg.C to 1100 deg.C, and taking 90 min;

(3) heating from 1100 deg.C to 1400 deg.C, and taking 55 min;

(4) increasing the temperature from 1400 ℃ to 1520 ℃ for 5 min;

(5) cooling from 1520 deg.C to 1400 deg.C, and taking 10 min;

(6) keeping the temperature at 1400 ℃ for 20 min;

(7) cooling from 1400 deg.C to 900 deg.C, and taking 60 min.

Technical Field

The invention relates to the field of glazed tile glaze materials, in particular to a wear-resistant glaze material for glazed tiles and a preparation method thereof.

Background

The glazed brick prepared from the glaze with low wear resistance is easy to grind, the product with poor wear resistance has long service time, the reduction of glossiness is obvious, the surface is dull, and the appearance is seriously affected. At present, the content of alumina in the glaze is increased by introducing superfine corundum micropowder into the glaze, so that the hardness of the glaze is increased, and the wear resistance of the glaze is improved to a certain extent.

However, in practical application, it is found that although corundum or calcined alumina is added into the formula to improve the hardness of the glaze, the melting temperature of the material is too high, and the formula design needs to consider enough cosolvent, so that the amount of glass phase is too much, and the effect of improving the wear resistance is not obvious. In addition, the existing raw material also needs to consider the requirements of the glaze spraying process, a large amount of high-activity aluminum materials such as kaolin cannot be used, but the application of other high-aluminum materials can cause the problems of poor wear resistance and poor color development of the glaze. The dark-colored glaze polishing product has extremely high requirements on the light transmittance and the color development effect of the glaze, the existing glaze polishing material is difficult to balance the problem of contradiction between the wear resistance and the color development of the formula of the glaze, and the condition of color difference easily occurs in red and yellow areas in the glaze polishing product.

Disclosure of Invention

The invention aims to provide a wear-resistant glaze material for glazed tiles and a preparation method thereof, so as to solve the problems.

In order to achieve the purpose, the invention adopts the following technical scheme:

the invention provides a wear-resistant glaze for glazed bricks, which comprises raw glaze powder, No. 1 clinker powder and No. 2 clinker powder;

the raw glaze powder comprises the following raw materials in percentage by weight: 8-12% of kaolin, 10-18% of calcined kaolin, 12-20% of quartz, 12-20% of dolomite, 8-15% of calcined talc, 8-15% of nepheline, 5-10% of zinc oxide, 3-6% of barium sulfate and 6-12% of strontium carbonate;

the raw materials of the No. 1 fusion cake powder comprise zircon sand and barium sulfate, and the raw materials of the No. 2 fusion cake powder comprise kaolin, calcined talc, fluorite and barium sulfate.

In the wear-resistant glaze for glazed tiles, the weight ratio of the raw glaze powder to the No. 1 fusion block powder to the No. 2 fusion block powder is (5-7): (1-3) and (1-3).

In the wear-resistant glaze for the glazed brick, the light transmittance of the No. 1 fusion block powder is 26.5-28.5%, and the Mohs hardness is 4 grade; the light transmittance of the No. 2 fusion cake powder is 23.5-25.5%, and the Mohs hardness is 5 grade.

In the wear-resistant glaze for the glazed brick, the fineness of the zircon sand is 400 meshes.

In the wear-resistant glaze for glazed bricks, the mass percentage content of barium sulfate in No. 1 fusion block powder is less than or equal to 5%, and the mass percentage content of barium sulfate in No. 2 fusion block powder is less than or equal to 5%.

In the wear-resistant glaze for glazed tiles, the No. 1 clinker powder comprises the following raw materials in percentage by weight: 35-42% of kaolin, 14-20% of quartz, 10-15% of calcined talc, 10-16% of calcite, 2-8% of zinc oxide, 0-3% of strontium carbonate, 1-3% of zircon sand, 1-3% of borax, 4-10% of nepheline and 2-5% of barium sulfate.

In the wear-resistant glaze for glazed tiles, the No. 2 clinker powder comprises the following raw materials in percentage by weight: 60-68% of kaolin, 20-26% of calcined talc, 1-5% of quartz, 2-6% of fluorite and 2-5% of barium sulfate.

The invention provides a preparation method of a wear-resistant glaze for glazed tiles, which is used for preparing the wear-resistant glaze for glazed tiles and comprises the following steps:

preparing No. 1 fusion cake powder: mixing the raw materials of the No. 1 fusion cake powder according to the proportion and preparing the mixture into powder; firing the raw materials at high temperature, discharging, cooling with water to obtain No. 1 clinker powder, powdering, sieving and drying the prepared No. 1 clinker powder, and taking 100-mesh screen underflow for later use;

preparing No. 2 fusion cake powder: mixing the raw materials of the No. 2 clinker powder according to the proportion and preparing the mixture into powder; firing the raw materials at high temperature, discharging, cooling with water to obtain No. 2 clinker powder, pulverizing the prepared No. 2 clinker powder, sieving, drying, and taking 100-mesh screen underflow for later use;

preparing raw glaze powder: uniformly mixing the raw glaze powder raw materials according to the proportion;

mixing the fusion cake powder with the raw glaze powder: and (3) adding water into the No. 1 fusion cake powder, the No. 2 fusion cake powder and the raw glaze powder prepared in the steps according to the proportion, ball-milling for 8-10 h to obtain glaze slurry, controlling the fineness to be 325 meshes, and ageing for more than 48h to obtain the wear-resistant glaze, wherein the mass fraction of the surplus is 0.8-1.2%.

In the preparation method of the wear-resistant glaze for glazed tiles, the temperature curve for preparing No. 1 clinker powder by high-temperature firing comprises the following steps:

(1) heating to 300 deg.C from normal temperature, and taking 90 min;

(2) heating from 300 deg.C to 1100 deg.C, and taking 90 min;

(3) heating from 1100 deg.C to 1520 deg.C, and taking 60 min;

(4) preserving the temperature at 1520 ℃ for 30 min;

(5) cooling from 1520 deg.C to 1400 deg.C, and taking 10 min;

(6) keeping the temperature at 1400 ℃ for 20 min;

(7) cooling from 1400 deg.C to 900 deg.C, and taking 60 min.

In the preparation method of the wear-resistant glaze for glazed tiles, the temperature curve of high-temperature firing of the No. 2 clinker powder comprises the following steps:

(1) heating to 300 deg.C from normal temperature, and taking 90 min;

(2) heating from 300 deg.C to 1100 deg.C, and taking 90 min;

(3) heating from 1100 deg.C to 1400 deg.C, and taking 55 min;

(4) increasing the temperature from 1400 ℃ to 1520 ℃ for 5 min;

(5) cooling from 1520 deg.C to 1400 deg.C, and taking 10 min;

(6) keeping the temperature at 1400 ℃ for 20 min;

(7) cooling from 1400 deg.C to 900 deg.C, and taking 60 min.

Has the advantages that:

(1) the wear-resistant glaze for the glazed brick contains kaolin, calcined kaolin and calcined talc, and in the high-temperature process, cordierite microcrystals are separated out from the components such as the kaolin, the calcined kaolin and the calcined talc on unmelted aggregate, so that the hardness of the glaze is enhanced, the glaze is prevented from being rubbed by hard objects, the wear resistance of the glaze can be obviously improved, and the glaze layer has high transparency and good color development;

(2) barium sulfate is also introduced into the wear-resistant glaze, so that the high-temperature viscosity of the frit is increased, the growth of cordierite crystals is inhibited, the microcrystallization of cordierite is facilitated, and the transparency of the glaze is further increased;

(3) barium sulfate provides barium oxide and sulfur elements for the wear-resistant glaze, and the sulfur-containing compound enables the color development of the glaze to be yellowish-red in the oxidation environment of the kiln, so that the problem of poor color development effect of red and yellow in the glazed brick is solved under the condition of not influencing the hardness and wear resistance of the wear-resistant glaze.

Detailed Description

The technical solution of the present invention is further explained by the following embodiments.

The invention provides a wear-resistant glaze for glazed bricks, which comprises raw glaze powder, No. 1 clinker powder and No. 2 clinker powder;

the raw glaze powder comprises the following raw materials in percentage by weight: 8-12% of kaolin, 10-18% of calcined kaolin, 12-20% of quartz, 12-20% of dolomite, 8-15% of calcined talc, 8-15% of nepheline, 5-10% of zinc oxide, 3-6% of barium sulfate and 6-12% of strontium carbonate;

the raw materials of the No. 1 fusion cake powder comprise zircon sand and barium sulfate, and the raw materials of the No. 2 fusion cake powder comprise kaolin, calcined talc, fluorite and barium sulfate.

In the prior art, the hardness of the glaze is generally increased by increasing the content of alumina to improve the scratch resistance of the glaze layer, thereby improving the wear resistance of the glaze. However, in fact, the hardness and the wear resistance of the glaze do not have a linear relationship, and the crystal phase and the unmelted aggregate in the glaze layer affect the important reason of the wear resistance of the glaze. The use of alumina or other materials that increase the glaze hardness is greater, the degree of fusion with the glass body decreases, and the surface hardness of the glaze layer increases, but alumina or other materials that increase the glaze hardness tend to fall off during surface rubbing, and the abrasion resistance deteriorates. In addition, the content of alumina or other materials for improving the glaze hardness is increased, the addition amount of the cosolvent is also increased, so that the glaze layer has more glass phase, and the wear resistance and the hardness are reduced; however, if the glaze layer has too little vitreous phase, the transparency of the glaze is lowered.

The raw glaze powder contains kaolin, calcined kaolin and calcined talc, is fully melted into Si-Al-Mg-Ca molten glass body under the high-temperature condition, and can separate out cordierite microcrystal and anorthite microcrystal on unmelted aggregate. In the firing process, the surface of the glaze layer is crystallized on the basis of the glass body, and cordierite microcrystals and anorthite microcrystals are separated out, and the cordierite crystals have the characteristics of transparency, high hardness and the like and simultaneously have good mechanical properties. Therefore, the cordierite crystal can enhance the hardness of the glaze, avoid the glaze from being rubbed by hard objects, obviously increase the wear resistance of the glaze, and the glaze layer has high transparency and good color development.

Because the surface of the crystal has a certain shape, the transparent crystal forms micron-scale or nano-scale protrusions on the surface of the glaze layer, so that the surface appearance of the glaze layer is changed, the friction coefficient of the glaze surface can be increased, and the anti-skid property of the glaze surface is enhanced. Because the size of the bulge is small, dirt is not easy to collect, and the glaze surface still has good easy-to-clean performance.

The fusion cake powder No. 1 is a high-transparency and high-wear-resistance fusion cake, and the raw materials of the fusion cake powder contain zircon sand and barium sulfate. At high temperature, a small amount of zircon sand is dissolved in the glass melt, and the rest residual part is inlaid in the glass melt by superfine free zircon sand so as to improve the hardness and the wear resistance of the glaze surface; the strontium carbonate plays roles of fluxing and enhancing the color development of the glaze; and the introduction of barium sulfate increases the high-temperature viscosity of the clinker, inhibits the growth of cordierite crystals and is beneficial to the microcrystallization of cordierite.

The No. 2 clinker powder is a cordierite microcrystalline clinker, has the characteristics of high hardness, wear resistance and high light transmittance, and is originallyThe material contains kaolin, calcined talc, fluorite and barium sulfate. The kaolin and the calcined talc are fully reacted at high temperature, a large amount of cordierite microcrystals can be crystallized, and the hardness and the wear resistance of the No. 2 clinker powder are obviously improved. Barium sulfate in the No. 2 clinker powder can improve the color development condition, and the problem of color difference of red and yellow ceramic ink-jet ink when the product is fired is avoided. The fluorine element in fluorite generates SiF with silicon and aluminum elements respectively under the high temperature condition₄、AlF₃Small amount of SiF₄And AlF₃The high-temperature volatile ceramic glaze material volatilizes and leaves, so that the expansion coefficient of No. 2 fusion cake powder is increased, and the expansion coefficient of the wear-resistant glaze material is adjusted to be matched with the expansion coefficient of a blank by changing the addition amount of the No. 2 fusion cake powder.

Specifically, the weight ratio of the raw glaze powder to the No. 1 fusion cake powder to the No. 2 fusion cake powder is (5-7): (1-3) and (1-3). The raw glaze powder, the No. 1 clinker powder and the No. 2 clinker powder all contain barium sulfate, the barium sulfate is decomposed into barium oxide and sulfur trioxide under the firing condition of a kiln, and a small amount of residual barium sulfate is dissolved in a glass melt; barium oxide and sulfur elements are introduced into the wear-resistant glaze, and the color development of the glaze is yellowish-red in the presence of a sulfur-containing compound in the oxidation environment of a kiln, so that the problem of poor color development effect of red and yellow in a glazed brick is solved without affecting the hardness and wear resistance of the wear-resistant glaze, and the transparency of the glaze is improved. In addition, under the high-temperature condition, a large amount of fluxing ions such as calcium, magnesium and the like exist in the formula, and after the barium ions are introduced into the formula system, the silicon-aluminum-barium stone can be generated and can be matched with cordierite crystals, so that the hardness of the glaze surface is improved, and the wear resistance is improved.

The raw glaze powder plays a role in adjusting the color development of the wear-resistant glaze and maintaining the stability of the performance of the glaze slip in the wear-resistant glaze. The No. 1 fusion cake powder mainly plays a role in improving the glaze hardness and adjusting the expansion coefficient of the glaze, and the No. 2 fusion cake powder mainly plays a role in improving the glaze hardness and transparency. The wear-resistant glaze has good performances of hardness, wear resistance, transparency and the like.

In the most preferred embodiment, the weight ratio of the raw glaze powder, the number 1 frit powder and the number 2 frit powder is 6:2: 2.

Specifically, the light transmittance of the No. 1 fusion cake powder is 26.5-28.5%, and the Mohs hardness is 4 grade; the light transmittance of the No. 2 fusion cake powder is 23.5-25.5%, and the Mohs hardness is 5 grade. The melting point is 1580 ℃ at the cordierite nucleation temperature of about 1400 ℃ and the barium sulfate decomposition temperature of 1600 ℃, and the frit viscosity is high when the barium sulfate is about 1400 ℃; in the firing process of No. 1 or No. 2 fused mass powder, the glass melt has large diffusion resistance and inhibits the growth of cordierite crystals, so that the cordierite melt is subjected to microcrystallization, and the transparency of the wear-resistant glaze is increased under the condition of not influencing the hardness and the wear resistance.

Specifically, the fineness of the zircon sand is 400 meshes. The melting point of the zircon sand is 2340-2550 ℃, the hardness of the zircon sand is 7.5-8 ℃, the zircon sand is dissolved in the glaze by 3-5% at high temperature, and the rest zircon sand is embedded in the glass melt, so that the hardness and the wear resistance of the glaze are improved. As a simple alternative, zircon sand of 400 mesh or less may be selected.

Specifically, the mass percentage content of barium sulfate in the No. 1 clinker powder is less than or equal to 5%, and the mass percentage content of barium sulfate in the No. 2 clinker powder is less than or equal to 5%.

When the mass percentage content of barium sulfate is more than 5%, the barium sulfate causes the high-temperature viscosity of the No. 1 fusion cake powder or the No. 2 fusion cake powder to increase in the temperature rising process, and the barium sulfate is dissolved on the surface of the No. 1 fusion cake powder or the No. 2 fusion cake powder in a solid manner; as the viscosity increases, barium sulfate will form lumps on the surface of No. 1 or No. 2 frit powder. A large amount of solid solution with high viscosity is accumulated on the surface at the dissolving temperature of 1400 ℃, the No. 1 or No. 2 clinker powder expands outwards in the gas volatilization process, the expansion amount is large, so that the powder is separated from the lower layer liquid phase, and when the temperature reaches 1520 ℃, the viscosity of the upper layer material is too large, barium sulfate is agglomerated on the surface and cannot be dissolved into the No. 1 or No. 2 clinker powder again.

In a preferred embodiment, the No. 1 clinker powder comprises the following raw materials in percentage by weight: 35-42% of kaolin, 14-20% of quartz, 10-15% of calcined talc, 10-16% of calcite, 2-8% of zinc oxide, 0-3% of strontium carbonate, 1-3% of zircon sand, 1-3% of borax, 4-10% of nepheline and 2-5% of barium sulfate. The No. 1 fusion cake powder generates a small amount of zirconia by introducing zircon sand, so that the aim of improving the hardness of a glaze surface is fulfilled; the introduction of barium sulfate increases the high-temperature viscosity of the clinker, which is beneficial to the microcrystallization of cordierite.

Specifically, the No. 2 clinker powder comprises the following raw materials in percentage by weight: 60-68% of kaolin, 20-26% of calcined talc, 1-5% of quartz, 2-6% of fluorite and 2-5% of barium sulfate.

In a preferred embodiment, the No. 2 clinker powder comprises the following raw materials in percentage by weight: 60-68% of kaolin, 20-26% of calcined talc, 1-5% of quartz, 2-6% of fluorite and 2-5% of barium sulfate. The fluorine element in fluorite generates SiF with silicon and aluminum elements respectively under the condition of high temperature₄、AlF₃(ii) a Under high temperature conditions, a small amount of SiF₄And AlF₃And volatilizing to increase the expansion coefficient of the No. 2 clinker powder, and adjusting the proportion of the No. 2 clinker powder in the wear-resistant glaze to adjust the expansion coefficient of the wear-resistant glaze, so that the expansion coefficient of the wear-resistant glaze is matched with that of the blank. In addition, calcium ions are introduced into fluorite, and under the high-temperature condition, the calcium ions are combined with oxygen to form calcium oxide, so that the effect of reducing the high-temperature viscosity of No. 2 clinker powder is achieved, and the problem of overhigh high-temperature viscosity caused by overlarge consumption of barium sulfate is avoided.

The invention provides a preparation method of a wear-resistant glaze for glazed tiles, which is used for preparing the wear-resistant glaze for glazed tiles and comprises the following steps:

preparing No. 1 fusion cake powder: mixing the raw materials of the No. 1 fusion cake powder according to the proportion and preparing the mixture into powder; firing the raw materials at high temperature, discharging, cooling with water to obtain No. 1 clinker powder, powdering, sieving and drying the prepared No. 1 clinker powder, and taking 100-mesh screen underflow for later use;

preparing No. 2 fusion cake powder: mixing the raw materials of the No. 2 clinker powder according to the proportion and preparing the mixture into powder; firing the raw materials at high temperature, discharging, cooling with water to obtain No. 2 clinker powder, pulverizing the prepared No. 2 clinker powder, sieving, drying, and taking 100-mesh screen underflow for later use;

preparing raw glaze powder: uniformly mixing the raw glaze powder raw materials according to the proportion;

mixing the fusion cake powder with the raw glaze powder: and (3) adding water into the No. 1 fusion cake powder, the No. 2 fusion cake powder and the raw glaze powder prepared in the steps according to the proportion, ball-milling for 8-10 h to obtain glaze slurry, controlling the fineness to be 325 meshes, and ageing for more than 48h to obtain the wear-resistant glaze, wherein the mass fraction of the surplus is 0.8-1.2%.

In the preparation method, because the No. 1 clinker powder contains strontium carbonate, borax and barium sulfate and the No. 2 clinker powder contains barium sulfate and fluorite, bubbles are produced under the high-temperature condition in the firing process of the No. 1 clinker powder and the No. 2 clinker powder; firing No. 1 clinker powder and No. 2 clinker powder in advance, mixing with raw glaze powder again, can be when preparing No. 1 clinker powder and No. 2 clinker powder, the gas that produces under the high temperature condition of discharge reduces the probability that the gas pocket appears in the glaze of wear-resisting frit, avoids the pollutant to gather on the gas pocket, is difficult to the problem of cleaing away to promote the anti-soil ability of glaze.

Specifically, the temperature curve for preparing the No. 1 clinker powder by high-temperature firing comprises the following steps:

(1) heating to 300 deg.C from normal temperature, and taking 90 min;

(2) heating from 300 deg.C to 1100 deg.C, and taking 90 min;

(3) heating from 1100 deg.C to 1520 deg.C, and taking 60 min;

(4) preserving the temperature at 1520 ℃ for 30 min;

(5) cooling from 1520 deg.C to 1400 deg.C, and taking 10 min;

(6) keeping the temperature at 1400 ℃ for 20 min;

(7) cooling from 1400 deg.C to 900 deg.C, and taking 60 min.

The temperature curve of the high-temperature sintering of the No. 1 clinker powder comprises three stages of a slow heating process, a rapid heating process from 1400 ℃ to 1520 ℃, a rapid cooling process from 1520 ℃ to 1400 ℃ and a heat preservation process at 1400 ℃.

In the process of slowly raising the temperature, crystal water, gas oxides and volatile substances in the minerals can be volatilized at high temperature; then, carrying out a rapid cooling process to form cordierite crystal nuclei and simultaneously avoid the continuous increase of cordierite crystals so as to achieve the purpose of cordierite micro-crystallization; after the heat preservation is carried out at 1400 ℃ for 20min, the components of the No. 1 fusion cake powder are stable, and after the heat preservation is carried out through water quenching, the cordierite microcrystalline state in the No. 1 fusion cake powder is obvious, so that the transparency of the wear-resistant glaze is higher. After heat preservation is carried out at 1400 ℃ for 20min, the components of the No. 1 clinker powder are stable, and after water quenching and cooling, the cordierite microcrystalline state in the No. 1 clinker powder is obvious, so that the transparency of the wear-resistant glaze is higher.

Specifically, the temperature curve of high-temperature firing of the No. 2 clinker powder comprises:

(1) heating to 300 deg.C from normal temperature, and taking 90 min;

(2) heating from 300 deg.C to 1100 deg.C, and taking 90 min;

(3) heating from 1100 deg.C to 1400 deg.C, and taking 55 min;

(4) increasing the temperature from 1400 ℃ to 1520 ℃ for 5 min;

(5) cooling from 1520 deg.C to 1400 deg.C, and taking 10 min;

(6) keeping the temperature at 1400 ℃ for 20 min;

(7) cooling from 1400 deg.C to 900 deg.C, and taking 60 min.

The nucleation temperature of cordierite is about 1400 ℃, cordierite crystal nucleus is formed through rapid cooling, the diffusion resistance of glass melt is large, and the growth of crystal is inhibited, so that the cordierite melt is subjected to microcrystallization, and three sections of slow heating process, rapid heating process from 1400 ℃ to 1520 ℃, rapid cooling process from 1520 ℃ to 1400 ℃ and heat preservation process at 1400 ℃ are included in the temperature curve of high-temperature firing of No. 2 clinker powder.

In the process of slowly raising the temperature, crystal water, gas oxides and volatile substances in the minerals can be volatilized at high temperature; then, a rapid heating process is carried out, so that the crystal structure of cordierite is more stable, and the wear resistance of the frit is improved; then, performing a rapid cooling process, wherein the melting temperature of barium sulfate reaches 1580 ℃, and the temperature needs to be raised in order to decompose the barium sulfate as much as possible; meanwhile, the viscosity of the melt can be adjusted by rapid temperature rise so as to be suitable for forming cordierite crystal nuclei, and when the cordierite crystal nuclei are formed, the cordierite crystals are prevented from being continuously increased, so that the purpose of cordierite micro-crystallization is achieved; after the heat preservation is carried out at 1400 ℃ for 20min, the components of the No. 2 fusion cake powder are stable, and after the heat preservation is carried out through water quenching, the cordierite microcrystalline state in the No. 2 fusion cake powder is obvious, so that the transparency of the wear-resistant glaze is higher.

The No. 1 and No. 2 clinker powders are subjected to microcrystallization treatment, and a large number of cordierite microcrystals are formed in the glaze layer during firing, so that the transparency of the formula and the color development of the glaze are greatly improved on the premise of not influencing the wear resistance and hardness.

And (3) performance testing:

1. mohs hardness determination: and (4) stably placing the polished tile sample on a hard support with the facing upwards. The surface of a sample is scribed by selecting standard ores with different Mohs values from small to large, the surface of the sample is scribed uniformly and vertically by applying force through a new ore cutting edge, the force application needs to be moderate, and the cutting edge of the standard ore cannot be broken by excessive force application to form double-line or multi-line scribing traces. The lowest hardness value which just can generate obvious scratches is taken as the test result, and the lowest value of all the test values of the test sample is taken as the test result.

2. And (3) determining the wear resistance: GB/T3810.7-2016, part 7 of the ceramic tile testing method: glazed product

The test method in the determination of the abrasion resistance of the surface of the tile tests the abrasion resistance of the glaze of the product, and the abrasion resistance of the ceramic tile is evaluated by placing a grinding medium on the glaze and rotating the glaze and observing and comparing a worn sample with an unworn sample.

3. And (3) antifouling rating measurement: the pollution agent for testing the pollution resistance of the ceramic tile comprises a paste pollution agent, a pollution agent capable of generating an oxidation reaction, a pollution agent capable of generating a film, olive oil and the like, wherein the pollution resistance is classified into 1-5 grades according to the difficulty of cleaning, and the higher the grade is, the better the pollution resistance is.

4. Determination of the light transmittance of the glaze: distributing glaze powder on the blank powder, wherein the thickness of the glaze powder is 5mm, the thickness of the blank powder is 2mm, pressing the blank powder into blocks by a press, and after sintering in a kiln, throwing off the blank to process the blocks into sheets; and measuring the direct sunlight transmittance of the building glass by using the GB/T2680-94 measuring method to obtain the light transmittance.

5. And (3) abrasion determination: before the abrasion resistance is measured, the mass of the sample is weighed, and after the abrasion resistance is measured, the sample is weighed again, and the difference between the unworn mass and the abraded mass is the abrasion.