阅读说明：本技术 一种防异味吸附面料用的复合材料及其制备方法 (Composite material for odor-resistant adsorption fabric and preparation method thereof ) 是由 许斌 于 2019-11-22 设计创作，主要内容包括：本发明涉及复合材料领域,公开了一种防异味吸附面料用的复合材料,按重量计使用以下原料制成：聚醚醚酮22～32份；聚乙烯12～18份；柠檬酸三丁酯30～110份；2～甲基咪唑1～2份；聚氨酯20～30份；苯乙烯～异戊二烯～苯乙烯嵌段共聚物5～20份；纳米二氧化钛6～10份；碳酸钙22～34份；抗菌剂1～2份；环氧大豆油2～8份；钙锌稳定剂2～6份；抗氧剂0.1～0.5份；清新剂10～30份。还公开了一种防异味吸附面料用的复合材料的制备方法。本申请复合材料制成的脚垫具有水冲洗后清洁度好、防异味的优点,并具有良好的力学性能。并且本申请的复合材料制作工艺简单,制造成本低,适合推广使用。(The invention relates to the field of composite materials, and discloses a composite material for an odor-resistant adsorption fabric, which is prepared from the following raw materials in parts by weight: 22-32 parts of polyether-ether-ketone; 12-18 parts of polyethylene; 30-110 parts of tributyl citrate; 1-2 parts of 2-methylimidazole; 20-30 parts of polyurethane; 5-20 parts of a styrene-isoprene-styrene block copolymer; 6-10 parts of nano titanium dioxide; 22-34 parts of calcium carbonate; 1-2 parts of an antibacterial agent; 2-8 parts of epoxidized soybean oil; 2-6 parts of a calcium zinc stabilizer; 0.1-0.5 part of antioxidant; 10-30 parts of a freshener. Also discloses a preparation method of the composite material for the odor-resistant adsorption fabric. The foot pad made of the composite material has the advantages of being good in cleanliness and peculiar smell prevention after being washed by water, and has good mechanical properties. The composite material is simple in manufacturing process, low in manufacturing cost and suitable for popularization and use.)

1. The composite material for the odor-resistant adsorption fabric is characterized by being prepared from the following raw materials in parts by weight:

2. the composite material for the odor-resistant adsorption fabric as claimed in claim 1, wherein the freshener comprises sweet osmanthus flower, activated carbon, scented wood and lemon essential oil, and the weight ratio of the sweet osmanthus flower, the activated carbon, the scented wood and the lemon essential oil is 1:7-9:1: 3.

3. The composite material for the odor-resistant adsorption fabric as claimed in claim 1, which is prepared from the following raw materials by weight:

4. the composite material for the odor-resistant adsorption fabric as claimed in claim 1, which is prepared from the following raw materials by weight:

5. the composite material for the odor-resistant adsorption fabric as claimed in claim 1, which is prepared from the following raw materials by weight:

6. the preparation method of the composite material for the odor-resistant adsorption fabric is characterized by comprising the following steps of: weighing 22-32 parts of polyether-ether-ketone, 12-18 parts of polyethylene, 30-110 parts of tributyl citrate, 1-2 parts of 2-methylimidazole, 20-30 parts of polyurethane, 6-10 parts of nano titanium dioxide, 22-34 parts of calcium carbonate, 1-2 parts of an antibacterial agent, 2-8 parts of epoxidized soybean oil and 2-6 parts of a calcium-zinc stabilizer according to the weight parts of the raw materials, adding the raw materials into a stirring kettle, and stirring for 25-35 minutes at the temperature of 90-130 ℃ and the rotating speed of 2000-plus-materials 3000 r/min.

7. The preparation method of the composite material for the odor-resistant adsorption fabric, according to claim 6, is characterized by further comprising the following steps: weighing 5-20 parts of styrene-isoprene-styrene block copolymer according to the weight parts of the raw materials, adding the mixture into a stirring kettle, and stirring for 10-20 minutes at the temperature of 100-; weighing 0.1-0.5 part of antioxidant and 10-30 parts of freshener, adding into a stirring kettle, and stirring for 10-30 minutes at the temperature of 120-.

Technical Field

The invention relates to the field of composite materials, and particularly relates to a composite material for an odor-resistant adsorption fabric and a preparation method thereof.

Background

With the popularization of automobiles, automobile foot mats have become indispensable consumer goods for people. The invention patent of application No. CN201510612783.3 discloses a multilayer composite anti-skid breathable flame-retardant material for an automobile foot pad, and the foot pad made of the material has the advantages of good anti-skid breathable flame retardance. However, in addition to the characteristics of comfort, air permeability, skid resistance, flame retardance and the like, the foot pad is also expected to have the functions of self-cleaning, peculiar smell resistance, good mechanical properties and the like, so that research and development of composite materials for the foot pad are hot spots in the industry.

Disclosure of Invention

Aiming at the defects in the prior art, the invention provides a composite material for an odor-resistant adsorption fabric and a preparation method thereof.

In order to solve the technical problem, the invention is solved by the following technical scheme:

the composite material for the odor-resistant adsorption fabric is prepared from the following raw materials in parts by weight:

preferably, the freshener comprises sweet osmanthus, activated carbon, scented wood and lemon essential oil, wherein the weight ratio of the sweet osmanthus, the activated carbon, the scented wood and the lemon essential oil is 1:7-9:1: 3.

Preferably, the composition is prepared from the following raw materials in parts by weight:

preferably, the composition is prepared from the following raw materials in parts by weight:

preferably, the composition is prepared from the following raw materials in parts by weight:

a preparation method of a composite material for an odor-resistant adsorption fabric comprises the following steps: weighing 22-32 parts of polyether-ether-ketone, 12-18 parts of polyethylene, 30-110 parts of tributyl citrate, 1-2 parts of 2-methylimidazole, 20-30 parts of polyurethane, 6-10 parts of nano titanium dioxide, 22-34 parts of calcium carbonate, 1-2 parts of an antibacterial agent, 2-8 parts of epoxidized soybean oil and 2-6 parts of a calcium-zinc stabilizer according to the weight parts of the raw materials, adding the raw materials into a stirring kettle, and stirring for 25-35 minutes at the temperature of 90-130 ℃ and the rotating speed of 2000-plus-materials 3000 r/min.

Preferably, the method further comprises the following steps: weighing 5-20 parts of styrene-isoprene-styrene block copolymer according to the weight parts of the raw materials, adding the mixture into a stirring kettle, and stirring for 10-20 minutes at the temperature of 100-; weighing 0.1-0.5 part of antioxidant and 10-30 parts of freshener, adding into a stirring kettle, and stirring for 10-30 minutes at the temperature of 120-.

Due to the adoption of the technical scheme, the invention has the remarkable technical effects that: the addition of the aromatic agent enables the foot pad made of the composite material to have the advantages of preventing peculiar smell adsorption and reducing peculiar smell, and the addition of the calcium carbonate can improve the mechanical property of the foot pad, so that the foot pad has good bending property and tensile property. The foot pad made of the composite material has the advantages of being good in cleanliness and peculiar smell prevention after being washed by water, and has good mechanical properties. The composite material is simple in manufacturing process, low in manufacturing cost and suitable for popularization and use.

Detailed Description

The present invention will be described in further detail with reference to examples.