阅读说明：本技术 一种网格纹釉及其制备方法 (Grid grain glaze and preparation method thereof ) 是由 谢华闰 谢华一 于 2019-12-12 设计创作，主要内容包括：本发明公开了一种网格纹釉及其制备方法,网格纹釉所使用的釉料的组分及各组分质量份如下：长石粉35-45份,石英15-25份,熔块5-10份,方解石10-15份,粘土15份,滑石3份,氧化锌5份,氧化铁红5～10份,碳酸锰5～10份,氧化铜5～10份,氧化钴2～3份,釉用颜料5份～10份；釉用颜料为釉用黄颜料、釉用绿颜料、釉用蓝颜料、釉用红颜料、釉用紫颜料中的至少一种。本发明的釉面呈现网格纹效果。(The invention discloses a grid pattern glaze and a preparation method thereof, wherein the components and the parts by mass of glaze used for the grid pattern glaze are as follows: 35-45 parts of feldspar powder, 15-25 parts of quartz, 5-10 parts of frit, 10-15 parts of calcite, 15 parts of clay, 3 parts of talcum, 5 parts of zinc oxide, 5-10 parts of iron oxide red, 5-10 parts of manganese carbonate, 5-10 parts of copper oxide, 2-3 parts of cobalt oxide and 5-10 parts of pigment for glaze; the glaze pigment is at least one of yellow glaze pigment, green glaze pigment, blue glaze pigment, red glaze pigment and violet glaze pigment. The glaze of the invention has a grid pattern effect.)

1. The grid glaze is characterized in that the components of the glaze used by the grid glaze and the mass parts of the components are as follows:

35-45 parts of feldspar powder, 15-25 parts of quartz, 5-10 parts of clinker, 10-15 parts of calcite, 15 parts of clay, 3 parts of talcum, 5 parts of zinc oxide, 5-10 parts of iron oxide red, 5-10 parts of manganese carbonate, 5-10 parts of copper oxide, 2-3 parts of cobalt oxide and 5-10 parts of glaze pigment; the glaze pigment is one of yellow glaze pigment, green glaze pigment, blue glaze pigment, red glaze pigment and purple glaze pigment.

2. A method for preparing the grid-grained glaze according to claim 1, characterized in that the method comprises the following steps:

preparing the components of the glaze material according to the mass parts of the components;

preparing materials according to the following steps: water: ball milling is carried out for 10-15 hours by a wet method according to the mass ratio of 1:0.5: 1.5;

sieving the ball-milled glaze with a 160-mesh sieve to prepare glaze slip with the Baume degree of 45-55;

glaze is applied on the mud blank by adopting glaze slip, and the mud blank is baked by oxidizing flame for 4 to 5 hours in the environment of 1250-1260 ℃ after being dried.

Technical Field

The invention relates to a grid pattern glaze and a preparation method thereof.

Background

At present, ceramic products are widely used in China, and the technology for preparing the ceramic products is mature. The traditional ceramic surface decoration method is to glaze the surface of the ceramic product, the glaze layer is smooth and has high brightness, which not only makes the appearance of the ceramic product more beautiful, but also increases the tolerance of the ceramic product. Along with the continuous improvement of living standard of people, the aesthetic requirement is also continuously changed, and the glaze surface is decorated with special textures.

The effect of the grid lines cannot be realized in the existing ceramic product, the grid lines represent original plain and mottled texture, and except for different color representations, the grid lines have rough hand feeling and cracks on the surface, so that the aesthetic requirements of consumers can be met if a grid line glaze with the effect of imitating the grid lines can be developed.

Disclosure of Invention

The technical problem to be solved by the invention is to overcome the defects of the prior art and provide the grid pattern glaze, and the glaze surface of the grid pattern glaze has a grid pattern effect.

The technical scheme for solving the technical problem of the invention is as follows: the grid grain glaze comprises the following glaze materials in parts by mass:

35-45 parts of feldspar powder, 15-25 parts of quartz, 5-10 parts of clinker, 10-15 parts of calcite, 15 parts of clay, 3 parts of talcum, 5 parts of zinc oxide, 5-10 parts of iron oxide red, 5-10 parts of sodium carbonate, 5-10 parts of copper oxide and 5-10 parts of pigment for glaze; the glaze pigment is one of yellow glaze pigment, green glaze pigment, blue glaze pigment, red glaze pigment and purple glaze pigment.

The invention provides a preparation method of grid-grained glaze, which comprises the following steps:

preparing the components of the glaze material according to the mass parts of the components;

preparing materials according to the following steps: water: ball milling is carried out for 10-15 hours by a wet method according to the mass ratio of 1:0.5: 1.5;

sieving the ball-milled glaze with a 160-mesh sieve to prepare glaze slip with the Baume degree of 45-55;

glaze is applied on the mud blank by adopting glaze slip, and the mud blank is baked by oxidizing flame for 4 to 5 hours in the environment of 1250-1260 ℃ after being dried.

After the technical scheme is adopted, the glaze surface of the grid-grain glaze presents the effect of grid grains after being fired by selecting the formula of the grid-grain glaze, and is natural and attractive.

Detailed Description

The invention provides a grid grain glaze and a preparation method thereof, and a person skilled in the art can appropriately improve process parameters by referring to the content. It is expressly intended that all such similar substitutes and modifications apparent to those skilled in the art are deemed to be within the scope of the invention. While the methods and applications of this invention have been described in terms of preferred embodiments, it will be apparent to those of ordinary skill in the art that variations and modifications in the methods and applications described herein, as well as other suitable variations and combinations, may be made to implement and use the techniques of this invention without departing from the spirit and scope of the invention.

The grid grain glaze comprises the following glaze materials in parts by mass:

35-45 parts of feldspar powder, 15-25 parts of quartz, 5-10 parts of clinker, 10-15 parts of calcite, 15 parts of clay, 3 parts of talcum, 5 parts of zinc oxide, 5-10 parts of iron oxide red, 5-10 parts of sodium carbonate, 5-10 parts of copper oxide and 5-10 parts of pigment for glaze; the glaze pigment is one of yellow glaze pigment, green glaze pigment, blue glaze pigment, red glaze pigment and purple glaze pigment.

The invention provides a preparation method of grid-grained glaze, which comprises the following steps:

preparing the components of the glaze material according to the mass parts of the components;

preparing materials according to the following steps: water: ball milling is carried out for 10-15 hours by a wet method according to the mass ratio of 1:0.5: 1.5;

sieving the ball-milled glaze with a 160-mesh sieve to prepare glaze slip with the Baume degree of 45-55;

glaze is applied on the mud blank by adopting glaze slip, and the mud blank is baked by oxidizing flame for 4 to 5 hours in the environment of 1250-1260 ℃ after being dried.

Through the selection of the formula of the grid grain glaze, the glaze surface of the grid grain glaze presents the effect of grid grains after being fired, and is natural and attractive.

In order that the present invention may be more clearly understood, the following detailed description of the present invention is given with reference to specific examples.