阅读说明：本技术 一种铝镁质耐火绝热的通风管道 (Aluminum-magnesium fireproof and heat-insulating ventilating duct ) 是由 陈德东 于 2019-10-22 设计创作，主要内容包括：本发明提供了一种铝镁质耐火绝热的通风管道,包括矩形管和铝镁质耐火绝热板,所述矩形管为金属管,所述矩形管的四个面均包覆有铝镁质耐火绝热板,所述矩形管与铝镁质耐火绝热板之间、相邻铝镁质耐火绝热板之间均通过耐火粘接剂粘接。具有耐火隔热的效果,且重量轻,施工性能好。(The invention provides an aluminum-magnesium fire-resistant heat-insulating ventilating duct which comprises a rectangular pipe and aluminum-magnesium fire-resistant heat-insulating plates, wherein the rectangular pipe is a metal pipe, the four surfaces of the rectangular pipe are respectively coated with the aluminum-magnesium fire-resistant heat-insulating plates, and the rectangular pipe and the aluminum-magnesium fire-resistant heat-insulating plates and the adjacent aluminum-magnesium fire-resistant heat-insulating plates are bonded through fire-resistant bonding agents. Has the effects of fire resistance and heat insulation, light weight and good construction performance.)

1. The utility model provides an almag fire-resistant adiabatic air pipe which characterized in that: including rectangular pipe and almag fire-resistant insulation board, the rectangular pipe is the tubular metal resonator, four faces of rectangular pipe all have the cladding of almag fire-resistant insulation board, all bond through fire-resistant adhesive between rectangular pipe and the almag fire-resistant insulation board, between the adjacent almag fire-resistant insulation board.

2. An almag refractory heat-insulating ventilation duct according to claim 1, characterized in that: the density of the aluminum-magnesium refractory plate is 180-220Kg/m³The heat conductivity coefficient is less than or equal to 0.045W/(m.k).

3. An almag refractory heat-insulating ventilation duct according to claim 2, characterized in that: the aluminum-magnesium refractory insulation plate comprises the following components in parts by mass: 100 parts of refractory fiber, 1-15 parts of calcium aluminate, 1-20 parts of silanol, 1-15 parts of aluminum sulfate, 1-3 parts of oxalic acid, 0.5-2 parts of polyacrylamide and 500 parts of water 200-one.

4. An almag refractory heat-insulating ventilation duct according to claim 3, characterized in that: the aluminum-magnesium refractory insulation plate comprises the following components in parts by mass: 100 parts of refractory fiber, 10-12 parts of calcium aluminate, 10-12 parts of silanol, 7-8 parts of aluminum sulfate, 1 part of oxalic acid, 1 part of polyacrylamide and 380-420 parts of water.

5. An almag refractory heat-insulating ventilation duct according to claim 3, characterized in that: the silanol refers to at least one of methyl silanol, ethyl silanol and tetrahydroxy silanol.

6. An almagnesium refractory heat-insulating ventilation duct according to claim 5, characterized in that: the silanol is tetrahydroxy silanol and methyl or ethyl silanol, and the molar ratio of the tetrahydroxy silanol to the methyl or ethyl silanol is 2-4: 1.

7. an almag refractory heat-insulating ventilation duct according to claim 3, characterized in that: the refractory fiber is selected from any one or combination of more of zirconia, alumina, silica and magnesia fiber.

8. An almag refractory heat-insulating ventilation duct according to claim 7, characterized in that: the fineness of the fiber is 3-15 micrometers, and the length of the fiber is 0.5-30 millimeters.

9. An almag refractory heat-insulating ventilation duct according to claim 3, characterized in that: the preparation process of the aluminum-magnesium refractory insulation plate comprises the following steps:

A. uniformly mixing the powder materials according to the formula proportion;

B. then uniformly mixing the powder material and water according to the formula proportion to prepare a slurry material;

C. uniformly dispersing refractory fiber materials in the slurry, and filling the slurry into a mold;

D. heating, drying, baking and shaping;

E. cooling, demolding, detecting, packaging and warehousing.

10. An almagnesium fire-proof and heat-insulating ventilation duct according to claim 9, characterized in that: the baking and shaping refers to raising the temperature to 500 ℃ at the rate of 100 ℃ per hour and preserving the heat.

Technical Field

The invention belongs to the field of building refractory materials, and particularly relates to an aluminum-magnesium fireproof heat-insulating ventilating duct.

Background

According to the national standard GB51251-2017 building smoke prevention and exhaust system technical standard, in order to prevent flame from burning out a smoke prevention and exhaust air pipe and spreading to other fire-proof subareas, the fire resistance limit of the smoke prevention and exhaust pipeline is required to be not less than 1.0 hour. The existing air duct standard GB/T17428-2009 ventilating duct fire resistance test method emphasizes that fire resistance and heat insulation are combined together, and only fire resistance is not feasible and heat insulation is also required.

The existing building smoke prevention and exhaust air pipe is generally made of sheet metal made of galvanized iron sheets, a hard fireproof plate wraps the outer surface of a metal air pipe, a soft heat insulation layer is arranged between the metal air pipe and the fireproof plate to play the roles of fire prevention and heat insulation, and the problems of large volume and weight, difficulty in construction and waste of manpower and financial resources exist.

CN202209033U discloses an exhaust duct, which is composed of four L-shaped fire-resistant plates, and the fire-resistant plates are connected by fire-resistant adhesive. According to the GB/T17428-2009 ventilation duct fire resistance test method, the fire resistance of the ventilation duct is evaluated from the aspects of integrity and heat insulation. The exhaust duct of this patent is composed of only one layer of rigid fire-resistant plate, and has no composite high-efficiency heat-insulating material, and can keep its integrity when a fire occurs, but when the flame passes through the duct, the surface temperature is too high, and the heat-insulating property can not meet the requirements.

CN203604909U discloses a fireproof composite air duct, which has a fireproof adhesive layer on the outer edge of the metal air duct, an inorganic fireproof material casing on the outer edge of the fireproof adhesive layer, and a fixing plate between the metal air duct and the inorganic fireproof material casing. The air pipe of the patent establishes a connecting bridge between the fireproof shell and the metal pipe by using a T-shaped or L-shaped fixing plate, and the number of the fixing plates is too large, so that the installation is very troublesome; meanwhile, the fireproof shell is required to have higher strength without heat insulation materials, and the heat conductivity coefficient is still higher, so that the heat insulation requirement cannot be met.

Disclosure of Invention

In order to solve the technical problems, the invention provides an aluminum-magnesium fire-resistant and heat-insulating ventilating duct which can meet the fire-resistant limit requirement specified by the national standard, has the fire-resistant and heat-insulating effects, and is light in weight and good in construction performance.

In order to realize the purpose of the invention, the invention adopts the technical scheme that:

the utility model provides an almag fire-resistant adiabatic's air pipe, includes rectangular pipe and almag fire-resistant insulation board, the rectangular pipe is the tubular metal resonator, four faces of rectangular pipe all have almag fire-resistant insulation board, between rectangular pipe and the almag refractory slab, all bond through fire-resistant adhesive between the adjacent almag fire-resistant insulation board.

The density of the aluminum-magnesium refractory plate is 180-220Kg/m³The heat conductivity coefficient is less than or equal to 0.045W/(m.k). The light aluminum-magnesium refractory heat-insulating plate is selected, so that the construction is easy; the aluminum-magnesium refractory heat-insulating plate with low heat conductivity coefficient is selected, so that the ventilation pipe has a fire-resistant function and a superior heat-insulating function.

The outer surface of the aluminum-magnesium refractory plate is also coated with a layer of fireproof coating.

A plurality of hoops are uniformly arranged on the outer surface of the ventilating duct along the direction of the duct.

The existing fire-resistant plate has poor heat insulation effect, the fire-resistant fiber is not uniformly dispersed, and the existing fire-resistant plate cannot be used as a fire-resistant heat insulation material with good performance. The aluminum-magnesium refractory heat-insulating plate comprises the following components in parts by mass: 100 parts of refractory fiber, 1-15 parts of calcium aluminate, 1-20 parts of silanol, 1-15 parts of aluminum sulfate, 1-3 parts of oxalic acid, 0.5-2 parts of polyacrylamide and 500 parts of water 200-one.

The calcium aluminate and the aluminum sulfate in the formula can react to form a porous fluffy refractory material, but the porous fluffy refractory material can be formed only in a larger space in water, otherwise, an effective high-temperature-resistant and heat-insulating material cannot be formed, and the two substances also have the problems of slow reaction speed and precipitation. The addition of polyacrylamide in the formula solves the problem of precipitation, and the polyacrylamide can ensure that the former two substances are stably dispersed in water without precipitation, and form a stable fine porous structure in the whole system. Meanwhile, the addition of the silanol can effectively promote the formation and the stability of a fine porous structure, the oxalic acid has the functions of adjusting the pH value, promoting the reaction and improving the uniformity of the material, and all components have synergistic action to obtain a uniform, fine and porous fluffy material with good heat insulation performance.

Preferably, the following ingredients are included by mass: 100 parts of refractory fiber, 10-12 parts of calcium aluminate, 10-12 parts of silanol, 7-8 parts of aluminum sulfate, 1 part of oxalic acid, 1 part of polyacrylamide and 380-420 parts of water. The synergistic effect is optimal under the mixture ratio.

Preferably, the silanol refers to at least one of methyl silanol, ethyl silanol and tetrahydroxy silanol.

Further preferably, the silanol is tetrahydroxysilicitol and methyl or ethyl silanol, and the molar ratio of tetrahydroxysilicitol to methyl or ethyl silanol is 2-4: 1.

the methyl silanol and the ethyl silanol have slow reaction speed, but have certain hydrophobic effect in the later period, and the tetrahydroxy silanol has fast reaction speed, better uniformity and better mixed use effect.

Preferably, the refractory fiber is selected from any one or combination of more of zirconia, alumina, silica and magnesia.

Further preferably, the fiber fineness is 3-15 micrometers and the length is 0.5-30 millimeters. The fineness of the fiber is 3-15 microns, and the smaller fineness is beneficial to reducing the heat conductivity coefficient.

The invention also provides a preparation process of the aluminum-magnesium refractory insulation plate, which comprises the following steps:

A. uniformly mixing the powder materials according to the formula proportion;

B. then uniformly mixing the powder material and water according to the formula proportion to prepare a slurry material;

C. uniformly dispersing refractory fiber materials in the slurry, and filling the slurry into a mold;

D. heating, drying, baking and shaping;

E. cooling, demolding, detecting, packaging and warehousing.

Preferably, the heating drying is performed at 100 ℃ for 0.5-2 hours, so that the moisture is volatilized, and the water is prevented from boiling violently at higher temperature to destroy the material structure.

Preferably, the baking and shaping refers to raising the temperature to 500 ℃ at the rate of 100 ℃ per hour and keeping the temperature for 1 hour. Too fast a temperature rise may damage the microstructure of the material, causing an increase in the thermal conductivity, and too slow a temperature rise may affect the production efficiency. The thermal conductivity of the temperature raising material is lowest at a rate of 100 ℃ per hour, and the thermal conductivity is affected by too fast or too slow.

The invention has the beneficial effects that:

1. the outer surface of the metal rectangular pipe is coated with the aluminum-magnesium refractory plate, the aluminum-magnesium refractory plate has the functions of fire resistance and heat insulation, the rectangular pipe and the aluminum-magnesium refractory plate are bonded through the refractory bonding agent, the high temperature of 1100 ℃ resistance is achieved, and the fire resistance of the ventilation pipe is guaranteed.

2. The density of the aluminum-magnesium refractory heat-insulating plate is 180-220Kg/m³The light aluminum-magnesium refractory heat-insulating plate is selected, so that the construction is easier; meanwhile, the heat conductivity coefficient of the selected aluminum-magnesium refractory heat-insulating plate is less than or equal to 0.045W/(m.k), so that the heat insulation performance of the ventilation pipe is ensured.

3. The components in the raw materials of the aluminum-magnesium refractory plate have synergistic effect, the calcium aluminate and the aluminum sulfate can react to generate a porous fluffy refractory material, but the porous fluffy refractory material can be formed only in a larger space in water, otherwise, an effective high-temperature-resistant and heat-insulating material cannot be formed, and the two materials have the problems of slow reaction speed and precipitation. The polyacrylamide in the formula can promote the calcium aluminate and the aluminum sulfate to be stably dispersed in water without precipitation, a stable fine porous structure is formed in the whole system, and meanwhile, the addition of the silanol can effectively promote the formation and the stability of the fine porous structure. The components act together to promote the adhesion of the material and form fine pores, the pores are distributed uniformly, and the material performance is improved, so that the refractory heat-insulating material with light weight, low heat conductivity and good construction performance is obtained.

4. Selecting a combination of tetrahydroxy silanol and methyl or ethyl silanol, and controlling the molar ratio to be 2-4: 1. the methyl and ethyl silanol have slow reaction speed, but have certain hydrophobic effect in the later period, and the tetrahydroxy silanol has fast reaction speed, better uniformity and good alcoholicity, and can better promote the formation and the stability of a fine porous structure.

5. According to the preparation process of the refractory plate, the slurry is prepared first and then the fiber is mixed, so that the raw materials are mixed more uniformly; the mould is adopted for baking and forming, and different from the conventional pressing and forming, the light weight and the heat conductivity are considered; baking at a rate of 100 ℃ per hour to 500 ℃ at which the thermal conductivity is lowest.

Drawings

Fig. 1 is a schematic sectional structure view of a ventilation duct of the present invention;

reference numerals: 1. a rectangular tube; 2. an aluminum-magnesium refractory plate; 3. a refractory adhesive layer; 4. a fire-retardant coating.

Detailed Description

In order to more clearly and specifically illustrate the technical solution of the present invention, the present invention is further described by the following embodiments. The following examples are intended to illustrate the practice of the present invention and are not intended to limit the scope of the invention.